CN104558862A - Abrasion-resistant and flame-retardant rubber formula - Google Patents

Abrasion-resistant and flame-retardant rubber formula Download PDF

Info

Publication number
CN104558862A
CN104558862A CN201410813415.0A CN201410813415A CN104558862A CN 104558862 A CN104558862 A CN 104558862A CN 201410813415 A CN201410813415 A CN 201410813415A CN 104558862 A CN104558862 A CN 104558862A
Authority
CN
China
Prior art keywords
parts
rubber
flame
abrasion
formula
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410813415.0A
Other languages
Chinese (zh)
Inventor
张洪涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI XIEZHIXING INFORMATION SYSTEM ENGINEERING Co Ltd
Original Assignee
HEFEI XIEZHIXING INFORMATION SYSTEM ENGINEERING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI XIEZHIXING INFORMATION SYSTEM ENGINEERING Co Ltd filed Critical HEFEI XIEZHIXING INFORMATION SYSTEM ENGINEERING Co Ltd
Priority to CN201410813415.0A priority Critical patent/CN104558862A/en
Publication of CN104558862A publication Critical patent/CN104558862A/en
Pending legal-status Critical Current

Abstract

The invention discloses an abrasion-resistant and flame-retardant rubber formula, wherein the rubber in the formula comprises the following raw materials in parts by weight: 30 to 40 parts of ethylene propylene diene monomer rubber, 8 to 11 parts of zinc oxide, 7 to 9 parts of a plasticizer, 9 to 12 parts of stearic acid, 6 to 10 parts of an accelerant, 10 to 20 parts of chloroprene rubber, 3 to 6 parts of a vulcanization accelerator, 1 to 3 parts of a coupling agent and 2 to 4 parts of a foaming agent. A rubber material prepared according to the formula has high flame retardance, and also has high abrasion resistance, high elasticity and a damping function.

Description

A kind of abrasion resistant fire blocking rubber compounding
Technical field
The present invention relates to rubber compounding technical field, be specifically related to a kind of abrasion resistant fire blocking rubber compounding.
Background technology
Flame retardant properties is the important indicator judging rubber product quality, and in currently available products, flame retardant properties aspect exists certain defect, can not meet the demands.Flame retardant rubber, refers to and can delay to catch fire, reduce flame propagation velocity, and after leaving external flame, the rubber of the rapid self-extinguish of himself combustion flame energy.The glue kind of flame retardant rubber is selected to follow following principle: rubber itself has flame retardant resistance, and during burning, thermal value is little, has excellent high-temperature heat-resistance.
Summary of the invention
For the deficiency that prior art exists, the object of the present invention is to provide a kind of abrasion resistant fire blocking rubber compounding, there is good flame retardant resistance, there is good wear resisting property simultaneously.
For achieving the above object, this invention takes following technical scheme:
A kind of abrasion resistant fire blocking rubber compounding, it is made up of the raw material of following parts by weight:
Terpolymer EP rubber 30-40 part, zinc oxide 8-11 part, softening agent 7-9 part, stearic acid 9-12 part, promotor 6-10 part, chloroprene rubber 10-20 part, vulcanization accelerator 3-6 part, coupling agent 1-3 part, whipping agent 2-4 part.
The invention has the beneficial effects as follows: elastomeric material of the present invention has good flame retardant resistance, there is good wear resisting property simultaneously good springiness, to there is shock-absorbing function.
Embodiment
Embodiment 1
A kind of abrasion resistant fire blocking rubber compounding, it is made up of the raw material of following parts by weight:
Terpolymer EP rubber 35 parts, 10 parts, zinc oxide, 8 parts, softening agent, stearic acid 11 parts, promotor 8 parts, chloroprene rubber 15 parts, vulcanization accelerator 5 parts, coupling agent 2 parts, whipping agent 3 parts.
Embodiment 2
A kind of abrasion resistant fire blocking rubber compounding, it is made up of the raw material of following parts by weight:
Terpolymer EP rubber 30 parts, 8 parts, zinc oxide, 7 parts, softening agent, stearic acid 9 parts, promotor 6 parts, chloroprene rubber 10 parts, vulcanization accelerator 3 parts, coupling agent 1 part, whipping agent 2 parts.
Embodiment 3
A kind of abrasion resistant fire blocking rubber compounding, it is made up of the raw material of following parts by weight:
Terpolymer EP rubber 40 parts, 11 parts, zinc oxide, 9 parts, softening agent, stearic acid 12 parts, promotor 10 parts, chloroprene rubber 20 parts, vulcanization accelerator 6 parts, coupling agent 3 parts, whipping agent 4 parts.

Claims (2)

1. an abrasion resistant fire blocking rubber compounding, is characterized in that: it is made up of the raw material of following parts by weight:
Terpolymer EP rubber 30-40 part, zinc oxide 8-11 part, softening agent 7-9 part, stearic acid 9-12 part, promotor 6-10 part, chloroprene rubber 10-20 part, vulcanization accelerator 3-6 part, coupling agent 1-3 part, whipping agent 2-4 part.
2. a kind of abrasion resistant fire blocking rubber compounding according to claim 1, is characterized in that: it is made up of the raw material of following parts by weight:
Terpolymer EP rubber 35 parts, 10 parts, zinc oxide, 8 parts, softening agent, stearic acid 11 parts, promotor 8 parts, chloroprene rubber 15 parts, vulcanization accelerator 5 parts, coupling agent 2 parts, whipping agent 3 parts.
CN201410813415.0A 2014-12-24 2014-12-24 Abrasion-resistant and flame-retardant rubber formula Pending CN104558862A (en)