CN104549965A - Door paint coating method - Google Patents
Door paint coating method Download PDFInfo
- Publication number
- CN104549965A CN104549965A CN201410813267.2A CN201410813267A CN104549965A CN 104549965 A CN104549965 A CN 104549965A CN 201410813267 A CN201410813267 A CN 201410813267A CN 104549965 A CN104549965 A CN 104549965A
- Authority
- CN
- China
- Prior art keywords
- paint
- brushing
- coating
- color
- priming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of coating of paint and in particular relates to a door paint coating method being simple to use. The door paint coating method is characterized in that ash is supplemented before coating the paint, so that the coated color is even; the door paint is coated with putty for 2-3 times, thereby ensuring the door surface to be flat and smooth; base paint is more conveniently brushed; a Griss coloring agent is also brushed on the base paint, thereby well adjusting the brightness of the color and improving layering sense of the coating color and the definition of wood grains; the base paint and finish paint are brushed for 2-3 times, thereby preventing the paint from falling off in the using process; simultaneously, the color is coated prior to the paint, so that the color can be retained for a longer time; the effects of not changing color and not fading color can be realized.
Description
Technical field
The present invention relates to oil paint coating field, relate to the coating process of a kind of paint in particular.
Technical background
Application is a system engineering, to the coating that the process on coated article surface, coating process and dry three basic working procedure and selection are suitable for before it comprises application, coat system reasonable in design, determines good operating environmental condition, carries out the important steps such as quality, process management and Technological Economy.
In daily life, we are modal is exactly door, we can see door miscellaneous, and the door that these vary in color, and all to adopt paint to carry out application, but in existing paint coating process, there are very many defects, such as, after application, air spots is sliding, so just very unsightly, or uneven color, or after using one end, paint can come off.
Summary of the invention
The technical problem to be solved in the present invention is to provide the coating process of a kind of paint.
For solving the problems of the technologies described above, the invention provides the coating process of a kind of paint, comprising the following steps:
(1) dust of application shop front cover, foreign material, soft flocks are cleaned out, and use oil putty to carry out batch scraping 2-3 time and polishing, until make coating surface smooth;
(2) mediation paint, control the viscosity of paint and thick dilution, uniform stirring makes the color and luster of paint consistent with viscous consistency;
(3) carry out priming to the shop front, when brushing, direction is consistent, and adopts diligent method of being stained with whisk broom to brush;
(4) after priming paint is painted with after drying in 5-7 hour, primed surface is coated with one deck Ge Lisi colouring agent, and direction during japanning is consistent with the direction of priming;
(5) after the drying of Ge Lisi colouring agent, mend putty again, after polishing, remove surface dirt, and opposite house external coating second time priming paint, brushing method is identical with first pass, and brushing direction is vertical with first pass brushing direction;
(6) after priming paint is painted with, the shop front is put well and dries, painting finish paint was being carried out to the shop front in second day;
(7) in the process being coated with finish paint, brushing method is identical with prime method, but in painting process, constantly will stir finish paint, moves and want steadily during brushing, and speed wants consistent.
Further, the method for described japanning should be carried out under 25-28 DEG C of environment, and the painting ETL estimated time of loading of entirety is 2 days.
Further, described putty is a kind of thick slurry coating material, in order to remove coated article rugged defect on the surface.
The beneficial effect of employing technique scheme is: the coating process of a kind of paint of the present invention, use simple, carry out benefit ash before painting, after can making application, color is even, and adopt putty to criticize to scrape 2-3 time, ensure that the flat smooth of the shop front, it is more convenient to make when priming, on priming paint, brush Ge Lisi colouring agent simultaneously, the light and shade depth of color can well be adjusted, increase the stereovision of film color and the definition of wood grain, and prime and finish paint time all brush 2-3 time, what can prevent from use painting comes off, first to do after look paint simultaneously, color can be made to keep more permanent, reach nondiscolouring and non-fading effect.
Detailed description of the invention
Embodiment 1
Paint a coating process, comprise the following steps:
(1) dust of application shop front cover, foreign material, soft flocks are cleaned out, and use oil putty to carry out batch scraping 2 times and polishing, until make coating surface smooth;
(2) mediation paint, control the viscosity of paint and thick dilution, uniform stirring makes the color and luster of paint consistent with viscous consistency;
(3) carry out priming to the shop front, when brushing, direction is consistent, and adopts diligent method of being stained with whisk broom to brush;
(4) after priming paint is painted with after drying in 5 hours, primed surface is coated with one deck Ge Lisi colouring agent, and direction during japanning is consistent with the direction of priming;
(5) after the drying of Ge Lisi colouring agent, mend putty again, after polishing, remove surface dirt, and opposite house external coating second time priming paint, brushing method is identical with first pass, and brushing direction is vertical with first pass brushing direction;
(6) after priming paint is painted with, the shop front is put well and dries, painting finish paint was being carried out to the shop front in second day;
(7) in the process being coated with finish paint, brushing method is identical with prime method, but in painting process, constantly will stir finish paint, moves and want steadily during brushing, and speed wants consistent.
Further, the method for described japanning should be carried out under 25 DEG C of environment, and the painting ETL estimated time of loading of entirety is 2 days.
Further, described putty is a kind of thick slurry coating material, in order to remove coated article rugged defect on the surface.
Embodiment 2
Paint a coating process, comprise the following steps:
(1) dust of application shop front cover, foreign material, soft flocks are cleaned out, and use oil putty to carry out batch scraping 3 times and polishing, until make coating surface smooth;
(2) mediation paint, control the viscosity of paint and thick dilution, uniform stirring makes the color and luster of paint consistent with viscous consistency;
(3) carry out priming to the shop front, when brushing, direction is consistent, and adopts diligent method of being stained with whisk broom to brush;
(4) after priming paint is painted with after drying in 7 hours, primed surface is coated with one deck Ge Lisi colouring agent, and direction during japanning is consistent with the direction of priming;
(5) after the drying of Ge Lisi colouring agent, mend putty again, after polishing, remove surface dirt, and opposite house external coating second time priming paint, brushing method is identical with first pass, and brushing direction is vertical with first pass brushing direction;
(6) after priming paint is painted with, the shop front is put well and dries, painting finish paint was being carried out to the shop front in second day;
(7) in the process being coated with finish paint, brushing method is identical with prime method, but in painting process, constantly will stir finish paint, moves and want steadily during brushing, and speed wants consistent.
Further, the method for described japanning should be carried out under 28 DEG C of environment, and the painting ETL estimated time of loading of entirety is 2 days.
Further, described putty is a kind of thick slurry coating material, in order to remove coated article rugged defect on the surface.
Claims (3)
1. a coating process for door paint, is characterized in that: comprise the following steps:
(1) dust of application shop front cover, foreign material, soft flocks are cleaned out, and use oil putty to carry out batch scraping 2-3 time and polishing, until make coating surface smooth;
(2) mediation paint, control the viscosity of paint and thick dilution, uniform stirring makes the color and luster of paint consistent with viscous consistency;
(3) carry out priming to the shop front, when brushing, direction is consistent, and adopts diligent method of being stained with whisk broom to brush;
(4) after priming paint is painted with after drying in 5-7 hour, primed surface is coated with one deck Ge Lisi colouring agent, and direction during japanning is consistent with the direction of priming;
(5) after the drying of Ge Lisi colouring agent, mend putty again, after polishing, remove surface dirt, and opposite house external coating second time priming paint, brushing method is identical with first pass, and brushing direction is vertical with first pass brushing direction;
(6) after priming paint is painted with, the shop front is put well and dries, painting finish paint was being carried out to the shop front in second day;
(7) in the process being coated with finish paint, brushing method is identical with prime method, but in painting process, constantly will stir finish paint, moves and want steadily during brushing, and speed wants consistent.
2. the coating process of a kind of paint according to claim 1, is characterized in that: the method for described japanning should be carried out under 25-28 DEG C of environment, and the painting ETL estimated time of loading of entirety is 2 days.
3. the coating process of a kind of paint according to claim 1, is characterized in that: described putty is a kind of thick slurry coating material, in order to remove coated article rugged defect on the surface.