CN107987690A - A kind of environmentally-friendly coating method of timber - Google Patents

A kind of environmentally-friendly coating method of timber Download PDF

Info

Publication number
CN107987690A
CN107987690A CN201711139929.2A CN201711139929A CN107987690A CN 107987690 A CN107987690 A CN 107987690A CN 201711139929 A CN201711139929 A CN 201711139929A CN 107987690 A CN107987690 A CN 107987690A
Authority
CN
China
Prior art keywords
parts
timber
environmentally
putty
coating method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711139929.2A
Other languages
Chinese (zh)
Inventor
刘立忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangshan Haiwei Technology Co Ltd
Original Assignee
Jiangshan Haiwei Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangshan Haiwei Technology Co Ltd filed Critical Jiangshan Haiwei Technology Co Ltd
Priority to CN201711139929.2A priority Critical patent/CN107987690A/en
Publication of CN107987690A publication Critical patent/CN107987690A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of environmentally-friendly coating method of timber, comprise the following steps：Door-plate sand paper is polished, completely scrapes organic gas absorption putty, polishing, brush oil colours, then brushes 25 times aqueous environment protection paints, polishes, and waxing, last wax polish is polished.

Description

A kind of environmentally-friendly coating method of timber
Technical field
The present invention relates to technical field of construction and decoration materials, the environmentally-friendly coating method of especially a kind of timber.
Background technology
The harmful substance that timber produces is mainly derived from artificial wood-based planet and paint.It should be appreciated that when choosing timber Its environmental protection index is burst size of methanal≤1.5mg/L, dissoluble lead≤90mg/kg, soluble cadmium≤75mg/kg, soluble chromium ≤60mg/kg.Formaldehydeless pollutant release, there is the spy such as light, rigid good, waterproof, anti-corrosion, Anti-moth-eating, sound insulation, insulation, fire-retardant Preferred during the timber of point, its material is nailable, sawable, planable as timber, and feel has wooden warm, and distributes timber Delicate fragrance.Just there are enough guarantees to the health of household.
CN106939141A discloses a kind of timber environmental protection maintenance material and preparation method thereof, by weight, by following Component is prepared：8-16 parts of methyl-silicone oil, 3-9 parts of oleic acid, 6-18 parts of evening primrose oil, 3-9 parts of White Mineral Oil, tea oil 4-11 Part, 3-9 parts of fat of Oromaius norvaehollandeae, 5-10 parts of olive oil, 3-9 parts of lecithin, 5-12 parts of Lavender, 4-9 parts of fish ester, epoxy cottonseed oil 10-20 parts, the invention also discloses a kind of preparation method of above-mentioned timber environmental protection maintenance material, comprise the following steps that：By methyl Silicone oil, oleic acid, evening primrose oil, White Mineral Oil, tea oil, fat of Oromaius norvaehollandeae, olive oil, lecithin, Lavender, fish ester, epoxy cotton Seed oil mixes, and after being then heated to 60-80 DEG C, after stirring evenly, is cooled to 15-30 DEG C, that is, timber ring is prepared Maintenance material.The present invention has the advantages that timber maintenance effect is good, environment not easy to pollute.
CN104552536A discloses a kind of formaldehydeless mopping method of environmentally protective solid wood door and window, is related to mopping method skill Art field, pass sequentially through stock, raw processing, shaping, polishing basic unit, Base coating, first pass varnishing, dry, secondary polishing, two Secondary mopping, dry again, three times polishing, three times mopping and dry and polishing come complete mopping work.The environmentally protective reality The formaldehydeless mopping method of Wood-door window can separate solid wood door and window with air, and when being air-dried, the moisture in woodenware is slowly As outer evaporation, the place that woodenware is mutually linked can be made to fluff, if there was dampness in the air, the moisture of outside goes to the inside, can be wood Device distending, deformation, and can be with favorable moth-proof, and paint films can be anti-oxidant, prevents solid wood door and window from being damaged by external air oxidation It is bad and more beautiful, environmentally protective.
CN202689866U is related to a kind of purification environmental-protection timber, and timber surrounding is pine outline border, in the middle part of timber is a core, door Core outsourcing density board panel, the door cored structure are bridge mechanical plate, i.e., the door core inner is equipped with some vertical holes and horizontal stroke Hole, vertical hole are communicated with Heng Dong, and the timber stent hole that the board or plank at both sides of a bedside or a door leaf is stayed up and down communicates to form spiracle with corresponding hole of indulging, via exhaling Ventilation inside and outside sucker timber.Some vertical holes of the door core inner and horizontal hole and spiracle surface spraying are applied without photocatalyst Layer.Activated carbon, drier are added in the spiracle.Timber decomposable asymmetric choice net formaldehyde of the present invention, toluene, TVOC etc. are harmful Material, has the function of that inside and outside ventilation purifies the air of a room.
Although the high timber product of the pernicious gas content such as formaldehyde is forbidden by country, due to adding for timber product Work characteristic, in the existing timber product of in the market, still can contain the pernicious gases such as certain formaldehyde, and manufacture it is this kind of containing The cost of the timber product of the pernicious gases such as certain formaldehyde is higher.
The content of the invention
The purpose of the present invention is：A kind of environmentally-friendly coating method of timber is provided, overcomes disadvantages mentioned above, it is characterised in that is following Step：
A kind of environmentally-friendly coating method of timber, comprises the following steps
Door-plate sand paper is polished, completely scrapes organic gas absorption putty, polishing, brush oil colours, then brushes 2-5 all over aqueous environment protection paint, mill Light, waxing, last wax polish are polished.
The preparation method of the aqueous environment protection paint is：
By weight, in a kettle add 100 parts of aqueous alkide resin, 1-5 parts of carbon fiber, three（Tetramethyl-ring amyl group）Lanthanum 0.001-0.01 parts, 1-5 parts of nano-calcium carbonate, 1-4 parts of polysiloxanes, 1-4 parts of poly amic acid, 1-4 parts of fluorine carbon levelling agent, has 1-4 parts of machine silicon levelling agent, grinding uniformly obtain aqueous environment protection paint.
The preparation method of described organic gas absorption putty is：
By weight, by 100 parts of putty, 0.01-0.1 parts of phenyl high flow rate Ago-Gels, 1-4 parts of carbon nanotubes, 1-5 parts of shells Glycan is uniformly mixed, and organic gas absorption putty is made.
The raw material is commercial product.
The product of the present invention has the advantages that：
The mould proof timber of the present invention can effectively prevent that timber is too mouldy greatly because humidity changes, so as to prevent timber mouldy and become Shape.
Embodiment
Following instance is only to further illustrate the present invention, is not limitation the scope of protection of the invention.
Embodiment 1
A kind of environmentally-friendly coating method of timber, comprises the following steps
Door-plate sand paper to be polished, completely scrapes organic gas absorption putty, polishing, brush oil colours, then brushes 3 times aqueous environment protection paints, polishes, Waxing, last wax polish are polished.
The preparation method of the aqueous environment protection paint is：
By weight, in a kettle add 100 parts of aqueous alkide resin, 2 parts of carbon fiber, three（Tetramethyl-ring amyl group）Lanthanum 0.003 part, 3 parts of nano-calcium carbonate, 2 parts of polysiloxanes, 2 parts of poly amic acid, 2 parts of fluorine carbon levelling agent, organosilicon levelling agent 12 Part, grinding uniformly obtains aqueous environment protection paint.
The preparation method of described organic gas absorption putty is：
By weight, 100 parts of putty, 0.0,3 part of phenyl high flow rate Ago-Gel, 2 parts of carbon nanotubes, 2 parts of chitosans are mixed Close uniform, obtained organic gas absorption putty.
The raw material is commercial product.
Embodiment 2
A kind of environmentally-friendly coating method of timber, comprises the following steps
Door-plate sand paper to be polished, completely scrapes organic gas absorption putty, polishing, brush oil colours, then brushes 2 times aqueous environment protection paints, polishes, Waxing, last wax polish are polished.
The preparation method of the aqueous environment protection paint is：
By weight, in a kettle add 100 parts of aqueous alkide resin, 1 part of carbon fiber, three（Tetramethyl-ring amyl group）Lanthanum 0.001 part, 1 part of nano-calcium carbonate, 1 part of polysiloxanes, 1 part of poly amic acid, 1 part of fluorine carbon levelling agent, organosilicon levelling agent 1 Part, grinding uniformly obtains aqueous environment protection paint.
The preparation method of described organic gas absorption putty is：
By weight, by 100 parts of putty, 0.01 part of phenyl high flow rate Ago-Gel, 1 part of carbon nanotubes, 1 part of chitosan mixing Uniformly, organic gas absorption putty is made.
Embodiment 3
A kind of environmentally-friendly coating method of timber, comprises the following steps
Door-plate sand paper is polished, completely scrapes organic gas absorption putty, polishing, brush oil colours, then brushes 2-5 all over aqueous environment protection paint, mill Light, waxing, last wax polish are polished.
The preparation method of the aqueous environment protection paint is：
By weight, in a kettle add 100 parts of aqueous alkide resin, 5 parts of carbon fiber, three（Tetramethyl-ring amyl group）Lanthanum 0.01 Part, 5 parts of nano-calcium carbonate, 4 parts of polysiloxanes, 4 parts of poly amic acid, 4 parts of fluorine carbon levelling agent, 4 parts of organosilicon levelling agent, grinding Uniformly obtain aqueous environment protection paint.
The preparation method of described organic gas absorption putty is：
By weight, by 100 parts of putty, 0.1 part of phenyl high flow rate Ago-Gel, 4 parts of carbon nanotubes, 5 parts of chitosan mixing Uniformly, organic gas absorption putty is made.
Comparative example 1
It is added without three（Tetramethyl-ring amyl group）Lanthanum, other conditions are the same as embodiment 1.
Comparative example 2
Phenyl high flow rate Ago-Gel is added without, other conditions are the same as embodiment 1.
Comparative example 3
Carbon nanotubes is added without, other conditions are the same as embodiment 1.
Comparative example 4
Carbon fiber is added without, other conditions are the same as embodiment 1.
Comparative example 5
Organic gas absorption putty is added without, other conditions are the same as embodiment 1.
Embodiment 4
The modeling timber material burst size of methanal grade of embodiment 1-3 and comparative example 1-3 is examined respectively, and concrete outcome is shown in Table 1.See below Table.

Claims (3)

1. a kind of environmentally-friendly coating method of timber, it is characterised in that comprise the following steps：
Door-plate sand paper is polished, completely scrapes organic gas absorption putty, polishing, brush oil colours, then brushes 2-5 all over aqueous environment protection paint, mill Light, waxing, last wax polish are polished.
A kind of 2. environmentally-friendly coating method of timber described in claim 1, it is characterised in that the preparation of the aqueous environment protection paint Method is：
By weight, in a kettle add 100 parts of aqueous alkide resin, 1-5 parts of carbon fiber, three（Tetramethyl-ring amyl group）Lanthanum 0.001-0.01 parts, 1-5 parts of nano-calcium carbonate, 1-4 parts of polysiloxanes, 1-4 parts of poly amic acid, 1-4 parts of fluorine carbon levelling agent, has 1-4 parts of machine silicon levelling agent, grinding uniformly obtain aqueous environment protection paint.
3. the environmentally-friendly coating method of a kind of timber described in claim 1, it is characterised in that organic gas adsorbs the preparation of putty Method is：By weight, by 100 parts of putty, 0.01-0.1 parts of phenyl high flow rate Ago-Gels, 1-4 parts of carbon nanotubes, 1-5 Part chitosan is uniformly mixed, and organic gas absorption putty is made.
CN201711139929.2A 2017-11-16 2017-11-16 A kind of environmentally-friendly coating method of timber Pending CN107987690A (en)