CN104532472A - Anti-bacteria and mite-proof modified cotton batting and preparation method - Google Patents
Anti-bacteria and mite-proof modified cotton batting and preparation method Download PDFInfo
- Publication number
- CN104532472A CN104532472A CN201410802981.1A CN201410802981A CN104532472A CN 104532472 A CN104532472 A CN 104532472A CN 201410802981 A CN201410802981 A CN 201410802981A CN 104532472 A CN104532472 A CN 104532472A
- Authority
- CN
- China
- Prior art keywords
- bat
- cotton
- fiber
- acarien
- modification
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-bacteria and mite-proof modified cotton batting and a preparation method. The components of the cotton batting comprise anion mite-proof type fiber and/or anti-bacteria cleancool, low melting point fiber and cotton. The preparation method comprise: weighting raw materials, evenly mixing and stirring the raw materials, conducting opening, edulcoration and combing on the mixed materials to form sheets, forming original cotton wadding by overlapping the sheets, humidifying the original cotton wadding, increasing the temperature ranging from 130 DEG C to 180 DEG C and maintaining the temperature, adding pressure to shape the original cotton wadding, carrying out grinding on the shaped original cotton wadding, and obtaining the condensation heat energy modified cotton batting. According to the anti-bacteria and mite-proof modified cotton batting and the preparation method, the component proportion is reasonable, the processing and manufacturing is easy, the heat retention capability is stable, the cotton batting is difficult to be affected with damp, and the traditional cotton batting manufacturing technology is changed. By adding the fluffy effect, the additional air permeability and the autonomous anti-bacteria and mite-proof function to the cotton batting, the service life of the cotton batting is prolonged, the sleeping environment is effectively improved, the sleeping effect is improved, and the cotton batting is applicable to industrialized mass production.
Description
Technical field
The invention discloses a kind of antibiosis anti-acarien modification bat and preparation method, belong to textiles preparing technical field.
Background technology
Tradition bat generally adopts plantation gined cotton of getting to be made into through cleaning, bullet pine, combing, shaping lapping yarn, grinding, has the advantages that hygroscopicity is strong, warming, healthy; But because Lint fiber only possesses stronger hygroscopicity, warmth retention property, and be string, be bacterium, the viral fiber articles easily gathering and live away from home, make bat and human contact, the as easy as rolling off a log human contact of allowing infects; The comfortableness of bat, health, security can not ensure, finished product bat is prevention infection reprocessing is very loaded down with trivial details problem.Therefore provide a kind of healthy harmless, warmth retention property stable, autonomous antibiosis anti-acarien bat becomes demand to solve above-mentioned existing Problems existing.
Summary of the invention
The object of the invention is to overcome the deficiency of prior art and provide a kind of reasonable mixture ratio of components, processing and manufacturing is easy, and warmth retention property is stablized, and not easily goes up tide, has antibiosis anti-acarien modification bat and the preparation method of the anti-mite function of fluffy, durable antibiotic lastingly.
A kind of antibiosis anti-acarien modification of the present invention bat, comprises following component, forms by mass percentage:
Functional fibre 5-40%, be preferably 10-40%, more excellent is 15-35%, and optimum is 20-33%;
Low-melting fiber 5-20%, be preferably 8-20%, more excellent is 10-18%, and optimum is 15-18%; Cotton 35-80%, be preferably 38-75%, more excellent is 44-70%, and optimum is 50-60%;
Each constituent mass percent and be 100%.
A kind of antibiosis anti-acarien modification of the present invention bat, described functional fibre is selected from least one in anion anti-mite fiber type, antibacterial health synthetic fibre fiber.
A kind of antibiosis anti-acarien modification of the present invention bat, the anti-mite fiber type of described anion is Lu's card fiber that Jiangsu blue product fiber development in science and technology Co., Ltd produces, antibacterial health synthetic fibre fiber is the nanometer metallic silver anti-bacterial fibre that Shanghai Sinotextiles Corporation Ltd. produces, be used alone the effect that any one has all had, but the while of two kinds, result of use is better.
A kind of antibiosis anti-acarien modification of the present invention bat, described anion anti-mite type Lu card fibre number is 0.8D-6.7D (D is the abbreviation of DENIER, refers under official regain, the weight grams of the fiber of 9000 meters long), and length is 33-64 millimeter.
A kind of antibiosis anti-acarien modification of the present invention bat, the fiber number of described nanometer metallic silver anti-bacterial fibre is 3.3-16.5D, and length is 44-61mm.
A kind of antibiosis anti-acarien modification of the present invention bat, the fusing point of described low-melting fiber is 130-175 DEG C.
A kind of antibiosis anti-acarien modification of the present invention bat, described low-melting fiber is the LMP fiber that Sichuan Huvis chemical fibre Co., Ltd produces.
A kind of antibiosis anti-acarien modification of the present invention bat, described low-melting fiber fiber number is 3D-6.7D, and length is 38-64mm.
A kind of antibiosis anti-acarien modification of the present invention bat, described cotton is more than three grades or three grades state's storage gined cottons, and state's storage gined cotton rank is determined (325-131 rank) by GB1103--1999 standard.
The preparation method of a kind of antibiosis anti-acarien modification of the present invention bat, comprises the steps:
The first step: take the anti-mite fiber type of anion, health synthetic fibre fiber, low-melting fiber, cotton mixing and stirring respectively by the bat constituent mass proportioning of design, obtain mixed material;
Second step: by mixed material after shredding, removal of impurities, combing in flakes, lamination forms raw cotton flocculus, and raw cotton flocculus thickness is 5-40cm;
3rd step: raw cotton flocculus is sent into baking box, is warming up to 130-180 DEG C, insulation 2-10 minute, outlet, pressurization sizing is to design thickness, and grinding, obtains antibiosis anti-acarien modification bat.
The preparation method of a kind of antibiosis anti-acarien modification of the present invention bat, in the 3rd step, preferred warming temperature is 135-175 DEG C, and temperature retention time is 2-8 minute; More preferably warming temperature is 135-155 DEG C, and temperature retention time is 2-5 minute.
The preparation method of a kind of antibiosis anti-acarien modification of the present invention bat, after described bat cloth parcel, quilting, trimming, bound edge, obtains antibiosis anti-acarien cotton-wadded quilt.
The preparation method of a kind of antibiosis anti-acarien modification of the present invention bat, parcel bat cloth is selected from the one in cotton, polyester-mixed cotton cloth, nonwoven fabric.
The preparation method of a kind of antibiosis anti-acarien modification of the present invention bat, described trimming adopts synchronous side to cut flat seam machine to carry out car to bat edge and cut process, form fixing sizing edge protection.
The preparation method of a kind of antibiosis anti-acarien modification of the present invention bat, described bound edge adopts cloth hypotenuse bar to be wrapped up by synchronous bound edge flat seam machine edge protection of will shaping.
The present invention, owing to adopting said components proportioning and preparation method, by adding low-melting fiber and anion mite-assistant fiber, argent anti-bacterial fibre in cotton fiber, through heating, insulation, on the one hand, guarantees the abundant melting of LMP fiber and generating portion gasification; On the other hand, make the anti-mite compound in Lu's card fiber and polyester fiber produce covalent bond, be evenly attached on all polyester fibers; Negative ion tourmaline nano particle in Lu's card fiber and the nano-Ag particles in argent anti-bacterial fibre are fully activated, and a part adheres to cotton fiber surface, and a part enters in the hollow cavity of cotton fiber or infiltrates in the LMP fiber of melting; Negative ion tourmaline uniform particles is distributed in comforter batt fiber, anion releasing, promote to strengthen anti-mite and argent antibacterial effect, subsequently, adopt pressurization sizing, can make the LMP fiber rapid solidification of melting and be connected with cotton fiber to bond to form network structure, the connection between strengthening cotton fiber and Lu's card fiber, antibacterial metal silver fiber, fixed effect, effectively improve elasticity and the permeability of bat.
The present invention is by controlling heating-up temperature; guaranteeing that negative ion tourmaline nano particle and nano metal Argent grain activate and while being evenly distributed in bat matrix; guarantee that again particle can not break, can continue to play autonomous antibacterial functions, effectively promote the comfortableness that cotton-wadded quilt uses.
The present invention is by controlling uniform stirring, and anion mite-assistant fiber and cotton fiber are uniformly distributed, and guarantee that anti-mite compound covalent bond is evenly formed, and plays anti-mite effect effectively comprehensively;
The present invention is by grinding, and when pressure grinding, time general control 5-8 minute, makes batting surface form minor spiral fiber head, effectively promote batting surface fibre density and fiber bonding strength.
Parcel cloth and bat quilting are integrated by the present invention, cut flat seam machine by synchronous side, carry out edge car cut process to bat body, form fixing sizing edge protection; Effectively can improve the stability of bat shape.
The present invention uses cloth slanted bar limit, and by the process of synchronous bound edge flat seam machine, edge protection of shaping wraps up, and again reinforces the combination of fabric and bat; Avoid fiber to overflow, effectively improve safety in utilization; Meanwhile, make the not yielding positioning in limit, do not rupture, not discontinue, flatness are good, overall structure is stable, durability is high; .
The present invention wraps up fabric and uses unlike material and figure, and have polyester-cotton blend, cotton textiles, tribute silk, regenerated celulose fibre fabric, figure has jacquard weave, stamp etc., and bound edge cloth also arbitrarily can be arranged in pairs or groups according to aesthetic; Bat body permanent shaping after making, smooth, attractive in appearance, soft, fluffy.
Advantages of the present invention under:
1, the present invention is by low-melting fiber infiltration or consolidation nano-tourmaline particle, metallic silver particles, and comparatively by force, wash resistant, elasticity, antibacterial effect retention time are long for nano particle and fibrous binding force;
2, the present invention is by controlling heating-up temperature, and guaranteeing that low-melting fiber link is bonded as netted entirety, the fixing anti-mite compound of covalent bond is on polyester fiber post, and function normal homogeneous plays, and anti-mite function keeps lasting;
3, because Lu's card fiber, health synthetic fibre fiber bodies are polyester fibers, there is loose structure, gas permeability, elasticity and bulkiness are good, the cotton fiber that beneficial support elasticity is not good enough, by the fibroplastic network structure of LMP, it is the entirety that an elasticity and permeability are good that cotton fiber, Lu's card fiber, health synthetic fibre fiber are connected, and the gas permeability of whole bat and elasticity strengthen, fluffy not knot tying lastingly, effectively improves bat inner ventilation effect; Make bat have the function of the anti-mite of fluffy, durable antibiotic lastingly, do not affect the serviceability of bat simultaneously.
When 4, using, negative ion tourmaline particle release anion, to effect that human body has Promote immunity power to strengthen, and volatilization is lasting, improves cotton-wadded quilt using function;
5, owing to the addition of some polyesters fibrid, the moisture pick-up properties of cotton-wadded quilt declines greatly, and the more existing cotton-wadded quilt of the gas permeability of cotton-wadded quilt of the present invention is good in addition, self has autonomous antibacterial functions, therefore, can realize the object of the invention.
6. before water logging,
The present invention develop bat gas permeability be more than 1.07 times of common bat;
The present invention develop bat elasticity be more than 2.65 times of common bat;
Bat that the present invention develops, its anticolibacillary efficiency reaches more than 96.2%, the efficiency of anti-candida albicans reaches more than 46.33%, the efficiency of anti-Staphylococcus aureus reaches more than 95.28%, the efficiency of anti-pneumobacillus reaches more than 77.3%, and anti-mite effect reaches more than 63%;
Through 10 water loggings, (be equivalent to use 5-8) after dry,
The present invention develop bat gas permeability attenuation amplitude be less than or equal to 21mm/s; And the attenuation amplitude of existing common bat is more than or equal to 47mm/s; And its gas permeability is more than 1.2 times of common bat;
The present invention develop more than 3.45 times that bat elasticity is common bat;
Bat that the present invention develops, its anticolibacillary efficiency reaches more than 94.9%, the efficiency of anti-candida albicans reaches more than 45.21%, the efficiency of anti-Staphylococcus aureus reaches more than 93.7%, the efficiency of anti-pneumobacillus reaches more than 73.8%, and anti-mite effect reaches more than 58%.
Compared with prior art, the present invention changes composition and the manufacture craft of traditional bat, increases the lofting effect of bat, additional gas permeability and autonomous antibiosis anti-acarien function; extend bat service life; effective improving water flood environment, promotes sleeper effect, also helps the health of protection user simultaneously.
In a word, the component of bat of the present invention is reasonable in design, each component and preparation technology synergy under, the bat that the present invention is developed has lasting lofting effect, good heat insulation effect and superior lasting antibiosis anti-acarien performance.
Detailed description of the invention:
Product prepared by the embodiment of the present invention, adopts following methods to check its performance parameter:
1, gas permeability, detects by GB/T 5453-1997 requirement;
2, anti-microbial property, detects staphylococcus aureus, pneumobacillus by FZT01021-1992; Escherichia coli, Candida albicans is detected by GBT20944.3-2008 requirement;
3, elasticity, detects by FZ/T81005-2006 requirement;
4, drive mite effect, detect by GB/T24253-2009 requirement;
Embodiment 1:
A kind of antibiosis anti-acarien modification bat, constituent mass proportioning is:
Anion anti-mite Lu card fiber 10% that Jiangsu blue product fiber development in science and technology Co., Ltd produces, health synthetic fibre fiber 10%, Huvis low-melting fiber 10%, cotton 70%,
Lu's card fibre number is 6.7D, and length is 64 millimeters;
Health synthetic fibre fibre number is 3D, and length is 38 millimeters;
The fusing point of Huvis low-melting fiber is 135 DEG C; Fiber number is 4D, and length is 51 millimeters;
Cotton is three grades of state's storage gined cottons.
A preparation method for antibiosis anti-acarien modification bat, comprises the steps:
The first step: take anion anti-mite Lu card fiber, health synthetic fibre fiber, low-melting fiber, cotton mixing and stirring respectively by the bat constituent mass proportioning of design, obtain mixed material;
Second step: by mixed material after shredding, removal of impurities, combing in flakes, lamination forms raw cotton flocculus, and raw cotton flocculus thickness is 10cm; Described shredding, removal of impurities, combing adopt this area common process to carry out;
3rd step: raw cotton flocculus is sent into baking box, is warming up to 145 DEG C, is incubated 8 minutes, outlet, pressurization sizing is to design thickness, and grinding, obtains antibiosis anti-acarien modification bat; Pressurization sizing adopts water-cooled pressure roller to the roll extrusion of raw cotton flocculus, cooling and shaping.
In the present embodiment, after the antibiosis anti-acarien modification bat cloth parcel of preparation, quilting, trimming, bound edge, obtain antibiosis anti-acarien modification cotton-wadded quilt;
Parcel antibiosis anti-acarien modification bat cloth is cotton; Trimming adopts synchronous side to cut flat seam machine to carry out car to bat edge and cut process, form fixing sizing edge protection; Bound edge adopts cloth hypotenuse bar to be wrapped up by synchronous bound edge flat seam machine edge protection of will shaping.
Bat prepared by the present embodiment is after testing:
Gas permeability is 315mm/s; Elasticity is 81%; Antibacterial functions: Escherichia coli bacteriostasis rate 96.2%, Candida albicans bacteriostasis rate 46.33%, staphylococcus aureus slip 95.28%, pneumobacillus slip 77.3%; Drive mite rate 63%;
After repeating 10 water loggings, 80-100 DEG C oven dry, after testing:
Gas permeability is 296mm/s; Elasticity is 75%; Antibacterial functions: Escherichia coli bacteriostasis rate 95.6%, Candida albicans bacteriostasis rate 45.21%, staphylococcus aureus slip 93.7%, pneumobacillus slip 73.8%, drives mite rate 58%.
Comparative example 1:
Adopting uses the same method detects the new cotton-wadded quilt of tradition:
Gas permeability is 292mm/s; Elasticity is 32.8%;
After repeating 10 water loggings, 80-100 DEG C oven dry, after testing:
Gas permeability is 245mm/s; Elasticity is 24.6%.
As can be seen from embodiment 1 and comparative example 1, the present invention only adds a small amount of anion anti-mite Lu card fiber (10wt%), health synthetic fibre fiber (10wt%), Huvis low-melting fiber (10wt%), but its gas permeability, elasticity have had significant lifting, especially flexible lifting is the most remarkable, and this is on pretreatment, and inventor does not also expect.
Embodiment 2:
A kind of antibiosis anti-acarien modification bat, constituent mass proportioning is:
Anion anti-mite Lu card fiber 10% that Jiangsu blue product fiber development in science and technology Co., Ltd produces, health synthetic fibre fiber 20%, Huvis low-melting fiber 15%, cotton 55%,
Lu's card fibre number is 6.7D, and length is 64 millimeters;
Health synthetic fibre fibre number is 3D, and length is 38 millimeters;
The fusing point of Huvis low-melting fiber is 135 DEG C; Fiber number is 4D, and length is 51 millimeters;
Cotton is three grades of state's storage gined cottons.
A preparation method for antibiosis anti-acarien modification bat, comprises the steps:
The first step: take anion anti-mite Lu card fiber, health synthetic fibre fiber, low-melting fiber, cotton mixing and stirring respectively by the bat constituent mass proportioning of design, obtain mixed material;
Second step: by mixed material after shredding, removal of impurities, combing in flakes, lamination forms raw cotton flocculus, and raw cotton flocculus thickness is 10cm; Described shredding, removal of impurities, combing adopt this area common process to carry out;
3rd step: raw cotton flocculus is sent into baking box, is warming up to 145 DEG C, is incubated 8 minutes, outlet, pressurization sizing is to design thickness, and grinding, obtains antibiosis anti-acarien modification bat; Pressurization sizing adopts water-cooled pressure roller to the roll extrusion of raw cotton flocculus, cooling and shaping.
In the present embodiment, after the antibiosis anti-acarien modification bat cloth parcel of preparation, quilting, trimming, bound edge, obtain antibiosis anti-acarien modification cotton-wadded quilt;
Parcel antibiosis anti-acarien modification bat cloth is cotton; Trimming adopts synchronous side to cut flat seam machine to carry out car to bat edge and cut process, form fixing sizing edge protection; Bound edge adopts cloth hypotenuse bar to be wrapped up by synchronous bound edge flat seam machine edge protection of will shaping.
Bat prepared by the present embodiment is after testing:
Gas permeability is 325mm/s; Elasticity is 86%; Antibacterial functions: Escherichia coli bacteriostasis rate 98.82%, Candida albicans bacteriostasis rate 51.76%, staphylococcus aureus slip 98.88%, pneumobacillus slip 79.6%; Drive mite rate 65%;
After repeating 10 water loggings, 80-100 DEG C oven dry, after testing:
Gas permeability is 304mm/s; Elasticity is 81%; Survey antibacterial functions: Escherichia coli bacteriostasis rate 95.6%, Candida albicans bacteriostasis rate 49.55%, staphylococcus aureus slip 97.3%, pneumobacillus slip 75.1%, drive mite rate 61%;
Comparative example 2:
Adopting uses the same method detects the new cotton-wadded quilt of tradition:
Gas permeability is 292mm/s; Elasticity is 32.8%;
After repeating 10 water loggings, 80-100 DEG C oven dry, after testing:
Gas permeability is 245mm/s; Elasticity is 24.6%;
Embodiment 3:
A kind of antibiosis anti-acarien modification bat, constituent mass proportioning is:
Anion anti-mite Lu card fiber 15% that Jiangsu blue product fiber development in science and technology Co., Ltd produces, health synthetic fibre fiber 10%, Huvis low-melting fiber 10%, cotton 65%,
Lu's card fibre number is 6.7D, and length is 64 millimeters;
Health synthetic fibre fibre number is 3D, and length is 38 millimeters;
The fusing point of Huvis low-melting fiber is 135 DEG C; Fiber number is 4D, and length is 51 millimeters;
Cotton is three grades of state's storage gined cottons.
A preparation method for antibiosis anti-acarien modification bat, comprises the steps:
The first step: take anion anti-mite Lu card fiber, health synthetic fibre fiber, low-melting fiber, cotton mixing and stirring respectively by the bat constituent mass proportioning of design, obtain mixed material;
Second step: by mixed material after shredding, removal of impurities, combing in flakes, lamination forms raw cotton flocculus, and raw cotton flocculus thickness is 10cm; Described shredding, removal of impurities, combing adopt this area common process to carry out;
3rd step: raw cotton flocculus is sent into baking box, is warming up to 145 DEG C, is incubated 8 minutes, outlet, pressurization sizing is to design thickness, and grinding, obtains antibiosis anti-acarien modification bat; Pressurization sizing adopts water-cooled pressure roller to the roll extrusion of raw cotton flocculus, cooling and shaping.
In the present embodiment, after the antibiosis anti-acarien modification bat cloth parcel of preparation, quilting, trimming, bound edge, obtain antibiosis anti-acarien modification cotton-wadded quilt;
Parcel antibiosis anti-acarien modification bat cloth is cotton; Trimming adopts synchronous side to cut flat seam machine to carry out car to bat edge and cut process, form fixing sizing edge protection; Bound edge adopts cloth hypotenuse bar to be wrapped up by synchronous bound edge flat seam machine edge protection of will shaping.
Bat prepared by the present embodiment is after testing:
Gas permeability is 318mm/s; Elasticity is 82%; Antibacterial functions: Escherichia coli bacteriostasis rate 96.2%, Candida albicans bacteriostasis rate 50.56%, staphylococcus aureus slip 96.7%, pneumobacillus slip 78.2%, drives mite rate 72%;
After repeating 10 water loggings, 80-100 DEG C oven dry, after testing:
Gas permeability is 305mm/s; Elasticity is 80%; Antibacterial functions: Escherichia coli bacteriostasis rate 94.9%, Candida albicans bacteriostasis rate 48.72%, staphylococcus aureus slip 94.88%, pneumobacillus slip 74.9%, drives mite rate 70%;
Comparative example 3:
Adopting uses the same method detects the new cotton-wadded quilt of tradition:
Gas permeability is 292mm/s; Elasticity is 32.8%;
After repeating 10 water loggings, 80-100 DEG C oven dry, after testing:
Gas permeability is 245mm/s; Elasticity is 24.6%;
More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; what describe in this description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications; these changes and improvements all fall in the claimed scope of the invention, and application claims protection domain is defined by appending claims and equivalent thereof.
A kind of antibiosis anti-acarien modification bat and preparation method detect Data Comparison
Remarks: before and after experiment be, repeat 10 water loggings, dry front and back, bake out temperature 80-100 DEG C.
As can be seen from the above table, no matter the antibiosis anti-acarien modification bat that the present invention develops is be better than existing common bat all from far away in gas permeability, elasticity, before water logging, the present invention develop bat gas permeability be more than 1.07 times of common bat; After 10 water loggings, the present invention develop bat gas permeability attenuation amplitude be less than or equal to 21mm/s; And the attenuation amplitude of existing common bat is more than or equal to 47mm/s; And its gas permeability is more than 1.2 times of common bat; This describes the environment (as maritime environment, face lacustrine environment, border on the sea environment and tropical rain forest environment) that bat that the present invention develops well can be applicable to high humidity to a certain extent.From flexible angle, before water logging, the present invention develop bat elasticity be more than 2.65 times of common bat, after water logging, its elasticity is also more than 3.45 times of common bat; Reflect that the bulkiness of the bat that the present invention develops is better than the bulkiness of existing common common bat to a certain extent in conjunction with gas permeability and elastic data.In addition, the present invention is owing to adding functional fibre, developed bat is made to have good antibacterial functions, as anticolibacillary efficiency reach more than 96.2%, the efficiency of anti-candida albicans reaches more than 46.33%, the efficiency of anti-Staphylococcus aureus reaches more than 95.28%, the efficiency of anti-pneumobacillus reaches more than 77.3%, anti-mite effect reaches more than 63%; Even if after 10 water loggings, its antibacterial functions is still superior, and every antibacterial index fall is all very little.
Claims (10)
1. an antibiosis anti-acarien modification bat, comprises following component, forms by mass percentage:
Functional fibre 5-40%;
Low-melting fiber 5-20%;
Cotton 35-80%;
Each constituent mass percent and be 100%.
2. a kind of antibiosis anti-acarien modification bat according to claim 1, is characterized in that: described functional fibre is selected from least one in anion anti-mite fiber type, antibacterial health synthetic fibre fiber.
3. a kind of antibiosis anti-acarien modification bat according to claim 2, is characterized in that: described anion anti-mite fiber type fiber number is 0.8D-6.7D, and length is 33-64 millimeter.
4. a kind of antibiosis anti-acarien modification bat according to claim 2, is characterized in that: described antibacterial health synthetic fibre fiber is nanometer metallic silver anti-bacterial fibre, and the fiber number of described nanometer metallic silver anti-bacterial fibre is 3.3-16.5D, and length is 44-61mm.
5. a kind of antibiosis anti-acarien modification bat according to claim 1, is characterized in that: the fusing point of described low-melting fiber is 130-175 DEG C.
6. a kind of antibiosis anti-acarien modification bat according to claim 5, it is characterized in that: described low-melting fiber fiber number is 3D-6.7D, length is 38-64mm.
7. a kind of antibiosis anti-acarien modification bat according to claim 1, is characterized in that: described cotton is more than three grades or three grades state's storage gined cottons, and state's storage gined cotton rank is determined by GB1103--1999 standard.
8. the preparation method of a kind of antibiosis anti-acarien modification bat as described in claim 1-7 any one, comprises the steps:
The first step: take the anti-mite fiber type of anion, health synthetic fibre fiber, low-melting fiber, cotton mixing and stirring respectively by the bat constituent mass proportioning of design, obtain mixed material;
Second step: by mixed material after shredding, removal of impurities, combing in flakes, lamination forms raw cotton flocculus;
3rd step: raw cotton flocculus is sent into baking box, is warming up to 130-180 DEG C, insulation 2-10 minute, outlet, pressurization sizing is to design thickness, and grinding, obtains antibiosis anti-acarien modification bat.
9. the preparation method of a kind of antibiosis anti-acarien modification bat according to claim 8, is characterized in that: after described bat cloth parcel, quilting, trimming, bound edge, obtain antibiosis anti-acarien cotton-wadded quilt.
10. the preparation method of a kind of antibiosis anti-acarien modification bat according to claim 9, is characterized in that: parcel bat cloth is selected from the one in cotton, polyester-mixed cotton cloth, nonwoven fabric; Described trimming adopts synchronous side to cut flat seam machine to carry out car to bat edge and cut process, form fixing sizing edge protection; Described bound edge adopts cloth hypotenuse bar to be wrapped up by synchronous bound edge flat seam machine edge protection of will shaping.