CN202390610U - Composite antibacterial hollow terylene ATY (Airjet Texturing Yarn) - Google Patents
Composite antibacterial hollow terylene ATY (Airjet Texturing Yarn) Download PDFInfo
- Publication number
- CN202390610U CN202390610U CN2011203177804U CN201120317780U CN202390610U CN 202390610 U CN202390610 U CN 202390610U CN 2011203177804 U CN2011203177804 U CN 2011203177804U CN 201120317780 U CN201120317780 U CN 201120317780U CN 202390610 U CN202390610 U CN 202390610U
- Authority
- CN
- China
- Prior art keywords
- aty
- antibacterial
- yarn
- fiber
- hollow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to composite antibacterial hollow terylene ATY (Airjet Texturing Yarn). The composite antibacterial hollow terylene ATY consists of antibacterial outer yarn and core yarn, wherein the antibacterial outer yarn is wound at the periphery of the core yarn in a continuous closed ring shape; and the antibacterial outer yarn is formed by fibers with hollow cross section. The composite antibacterial hollow terylene ATY has the advantages that the ATY has good three-dimensional structure and bulkiness, the weaved fabric has cotton feel, is full and soft to touch and is good in comfort; and since an inorganic antibacterial agent is adopted for blended spinning and an organic antibacterial agent is adopted for finishing the fiber, the antibacterial performance of the fiber can be improved, the antibacterial spectrum is wide, and the lasting antibacterial effect is achieved; and the fiber is hollow and contains a great amount of still air, the density of the fabric is low, and the heat storage is good. The composite antibacterial hollow terylene ATY can be used for western-style clothes, jackets, coats, down-like clothes, woolen cloth and high-grade bat wool and the like, and also can be widely applied in the aspects of decorative cloth for vehicle cushions, laying decorative cloth for furniture, sleeping bags, blankets and the like.
Description
Technical field
The utility model relates to the functional fibre technical field, specifically, is a kind of composite antibiosis hollow polyester ATY.
Background technology
Improving constantly of Along with people's living standard is not only endurable to the requirement of dress, more pays attention to comfortableness, functionalization, differential be the focus of current fiber industry development.
ATY is an air deformation yarn, is fiber is got into nozzle under the overfeeding state, through the jet action of high pressure, high velocity air; Tow is handed over network processing; Form irregular kink wire ring, make tow have the yarn of fluffy looped pile shape, have good 3-D solid structure and bulkiness; The fabric that is made into has cotton feel, and the plentiful softness of sense of touch, comfortableness are good.The precursor that is used for AIRJET TEXTURING YARN has a variety of, comprises terylene, polyamide fibre, polypropylene fibre, viscose, acetate fibre etc., and these long filaments can be fullly drawn yarn (FDY), pre-oriented yarn or low-oriented yarn etc.ATY has overcome shortcomings such as aurora, the sense of wax shape of synthetic fiber, poor, the easy pilling of breathing freely, and is one of main raw material of emulating fabric.
The Nano Silver based inorganic antibacterial agent has good heat resistance, security, and toxicity is low, pollution is little; Organosilicon-quaternary ammonium salt organic antibacterial agent and fiber surface hydroxyl dehydrating condensation, at fiber surface, antibacterial range is wide, price is low with the covalent bond form fix, and the fiber of back arrangement also possesses good water imbibition, flexibility, antistatic behaviour etc.Adopt inorganic and the organic antibacterial agent acting in conjunction, the fiber antibacterial range is wider, persistence is good.
Though normal polyester ATY has outward appearance and feel preferably; But flexibility, comfortableness deficiency show slightly stiffening, thereby through changing the degree of hollowness that cross sectional shape improves fiber; Expand its scope of application; Utilize organosilicon-quaternary ammonium salt organic antibacterial agent that fiber is carried out the back arrangement, make fiber have good accumulation of heat property and comfortableness, possess stronger antibacterial effect simultaneously again.At present, do not see the report of antibiotic hollow polyester ATY.
The utility model content
The purpose of the utility model is to remedy the deficiency of prior art, satisfies and produces and living needs, and a kind of composite antibiosis hollow polyester ATY is provided.
The purpose of the utility model realizes through following technical scheme:
A kind of composite antibiosis hollow polyester ATY is made up of antibiotic skin yarn and heart yarn, and antibiotic skin yarn is wrapped in the heart yarn periphery with the round of continuous sealing; Described antibiotic skin yarn is that the ATY of hollow shape is fibrous by shape of cross section.The monofilament degree of hollowness of the fiber of described antibiotic skin yarn is 30-35%, and fiber number is 0.5-1.5dpf.
Described inorganic antiseptic is the Nano Silver series antibacterial agent, and organic antibacterial agent is organosilicon-quaternary ammonium salt.
As optimized technical scheme: the degree of hollowness of said fiber is 32%.
Compared with prior art, the good effect of the utility model is:
(1) fiber of the utility model preparation is ATY, has good 3-D solid structure and bulkiness, and the fabric that this fiber is made into has cotton feel, and the plentiful softness of sense of touch, comfortableness are good.
(2) finishing fiber behind this practicality employing Nano Silver based inorganic antibacterial agent co-blended spinning and the organosilicon-quaternary ammonium salt organic antibacterial agent.The Nano Silver based inorganic antibacterial agent has good heat resistance, security, and toxicity is low, pollution is little; Organosilicon-quaternary ammonium salt organic antibacterial agent and fiber surface hydroxyl dehydrating condensation, at fiber surface, antibacterial range is wide, price is low with the covalent bond form fix, and fiber also possesses good hygroscopicity, flexibility, static electricity resistance etc.Adopt inorganic and the organic antibacterial agent acting in conjunction, the fiber antibacterial range is wider, persistence is good.
(3) the utility model fibrous inside hollow, degree of hollowness 30-35%, fibrous inside have comprised a large amount of still airs, and Density is little, has good accumulation of heat property.
The purposes of the utility model:
Can be used for western-style clothes, jacket, overcoat, down-like clothes, woollen goods, high-grade cotton for wadding etc., also be widely used with aspects such as shop decorations cloth, sleeping bag, woollen blankets at vehicle seat pad decorations cloth, furniture.
Description of drawings
The fibre section sketch map of Fig. 1 the utility model
The ATY structural representation of Fig. 2 the utility model
The specific embodiment
Below in conjunction with specifically being embodiment, further set forth the utility model.Should be understood that these instances only to be used to the utility model is described and be not used in the restriction the utility model scope, be the preferred implementation of the utility model.Should understand in addition; After the content of having read the utility model instruction; Those skilled in the art can make various changes or modification to the utility model under the prerequisite that does not break away from the utility model design, these equivalent form of values fall within the application's appended claims institute restricted portion equally.
As shown in Figure 2, a kind of composite antibiosis hollow polyester ATY of the utility model is made up of antibiotic skin yarn and heart yarn, and antibiotic skin yarn is wrapped in the heart yarn periphery with the round of continuous sealing; Described antibiotic skin yarn is that the ATY of hollow shape is fibrous by shape of cross section, sees Fig. 1.The monofilament degree of hollowness of the fiber of described antibiotic skin yarn is 30-35%, and fiber number is 0.5-1.5dpf.
Below be the preparation process of a kind of composite antibiosis hollow polyester ATY:
Adopt ECDP section and inorganic antiseptic blend melt-spun, fiber cross section is shaped as hollow shape, utilizes the air-texturing process technology, forms ATY, puts in order behind the employing organic antibacterial agent.
" C " type spinneret orifice of this composite antibiosis hollow ATY employing particular design passes through high-speed spinning process system.Its process route is POY-ATY.Fiber adopts Nano Silver series antibacterial agent and ECDP blend, and the inorganic antiseptic mass fraction is 3%; The wire ring diameter of monofilament is 10-500 μ m in the ATY synnema, and the wire ring number is 10-50/cm, and spinneret orifice inner and outer diameter ratio is 3: 4, makes the degree of hollowness 32% of fiber, and fiber number is 0.5-1.5dpf.
Technological process:
ECDP hybrid slicing → screening → boiled bed drying → hopper → screw extruder → melt distributing pipe → spinning manifold → spinneret assembly → lateral blowing cools off → oils → reels → POY
8 hours → feeding → stretching of POY balance → air-texturing (water-bath dewing) → typing → finish-antiseptic (organosilicon-quaternary ammonium salt) → coiling → ATY
Main technologic parameters is following:
Drying equipment: the continuous BM formula of ebullated bed drying machine;
Spinning temperature: 260-280 ℃;
Spinning speed: 3000-4000m/min;
Side-blown wind speed: 0.45m/min;
Side-blown wind-warm syndrome: 25 ℃;
ATY deformation velocity: 300-500m/min;
Stretching ratio: 1.5-2 doubly;
Overfeeding: 10-15%;
Air pressure: 0.8 ± 0.1MPa;
Confluent: 0.8-1.0L/h;
Setting temperature: 80-120 ℃;
Finish-antiseptic: organosilicon-quaternary ammonium salt (100 ℃ of temperature).
Claims (3)
1. composite antibiosis hollow polyester ATY, it is characterized in that: said composite antibiosis hollow polyester ATY is made up of antibiotic skin yarn and heart yarn, and antibiotic skin yarn is wrapped in the heart yarn periphery with the round of continuous sealing; Described antibiotic skin yarn is to be the fibrous of hollow shape by shape of cross section.
2. a kind of composite antibiosis hollow polyester ATY as claimed in claim 1, it is characterized in that: the degree of hollowness of the fiber of described antibiotic skin yarn is 30-35%.
3. a kind of composite antibiosis hollow polyester ATY as claimed in claim 1, it is characterized in that: the filament number of the fiber of described antibiotic skin yarn is 0.5-1.5dpf.