CN104497793A - Anti-sticking coating - Google Patents
Anti-sticking coating Download PDFInfo
- Publication number
- CN104497793A CN104497793A CN201410831166.8A CN201410831166A CN104497793A CN 104497793 A CN104497793 A CN 104497793A CN 201410831166 A CN201410831166 A CN 201410831166A CN 104497793 A CN104497793 A CN 104497793A
- Authority
- CN
- China
- Prior art keywords
- coating
- acetone
- adds
- water
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-sticking coating. The anti-sticking coating comprises the following components in percentage by weight: 70-80% of waterborne epoxy resin, 8-10% of linseed oil, 5-8% of castor oil, 2-5% of acetone, 2-6% of water and 3-5% of epoxy active diluents. A preparation method of the anti-sticking coating comprises the following steps of adding the epoxy active diluents into the waterborne epoxy resin and uniformly stirring; adding water in the waterborne epoxy resin added with the diluents and uniformly mixing; adding linseed oil into the water-added waterborne epoxy resin and then adding a half amount of acetone to obtain a primary slurry; adding castor oil into the primary slurry prepared in the third step and adding the other half of acetone; placing in normal temperature drying chamber and exposing for 4-6 hours. After the coating is applied on the wall, the inner voids are smaller, the coating layer has the characteristics of higher smoothness and hardness and excellent anti-sticking property, an advertising label is easy to tear off since the advertising label is not tightly stuck and after pigment and coating are applied, and the pigment and coating can be completely wiped with wet cloth.
Description
Technical field
The present invention relates to technical field of chemical products, be specifically related to a kind of paint.
Background technology
Along with the fast development of economy and people are to the continuous increase of information requirement, all kinds of unrest is signposted and is scrawled and continues to bring out, and these disorderly paste small advertisements and not easily tear, and become extremely discordant city " psoriasis ", " scribble ", have a strong impact on city look and feel.Generally adopt at present both at home and abroad non-setting adhesive barrier coating to prevent from disorderly signposting, its weak point adopts organic resin mix with Wax, in material in a large number with an organic solvent, in painting process, meeting work the mischief to environment and human body and pollute.
In order to address these problems, patent of invention CN101712842B discloses " a kind of adhesion and doodling prevention coating ", the patent proposes the technical scheme being better than traditional Antisticking coating, more effectively can solve and paste that small advertisement not easily tears, the problem of coating and drawing at random.But the whole formula scheme of this patent is too complicated, need A, B two component prepare respectively, then with A, B two component be mixed with coating, its preparation process is also more trivial, and cost is higher, is unfavorable for applying.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind ofly prepares simple, anti-paste effective, Antisticking coating that cost is low.
For solving the problems of the technologies described above, the present invention adopts following technical scheme: a kind of Antisticking coating, is characterized in that: fill a prescription by following weight percent composition:
This Antisticking coating is prepared by the following method,
The first step, adds epoxy active diluent in aqueous epoxy resins, divides and adds for three times, add 1/3rd at every turn, often add and once namely stir afterwards;
Second step, adds water toward adding in the aqueous epoxy resins after thinner, carries out fully stirring making it mix;
3rd step, adds the aqueous epoxy resins after adding water, then adds the acetone of half by oleum lini, the just system that obtains that stirs is coated with slip;
4th step, adds the 3rd step and throws in obtained pasting first processed, then add second half acetone by Viscotrol C, be stirred well to Viscotrol C and acetone is completely fused;
5th step, is placed in Air drying room and exposes 4-6 hours, i.e. obtained Antisticking coating.
Preferably, described epoxy active diluent adopts N-butylglycidyl ether.
The present invention is by adopting aqueous epoxy resins as basic raw material, and adopt epoxy active diluent as thinner, enable coating dissolved dilution better, add oleum lini and Viscotrol C, and it is fused to be aided with acetone, after coating wall, internal voids is less, higher, the anti-paste excellent property of slickness and hardness of paint coatings, advertisement tag is sticky tight, is easy to just can tear, and pigment coating is scribbled the rear use cloth that wets and can be cleaned once wiping.
Embodiment
Embodiment 1, described Antisticking coating, formula is by following weight percent composition:
This Antisticking coating is prepared by the following method,
The first step, adds in aqueous epoxy resins by N-butylglycidyl ether, divides and adds for three times, add 1/3rd at every turn, often add and once namely stir afterwards;
Second step, adds water in the aqueous epoxy resins after adding N-butylglycidyl ether, carries out fully stirring making it mix;
3rd step, adds the aqueous epoxy resins after adding water, then adds the acetone of half by oleum lini, the just system that obtains that stirs is coated with slip;
4th step, adds the 3rd step and throws in obtained pasting first processed, then add second half acetone by Viscotrol C, be stirred well to Viscotrol C and acetone is completely fused;
5th step, is placed in Air drying room and exposes 4-6 hours, i.e. obtained Antisticking coating.
Embodiment 2, is by embodiment 1 difference place, described Antisticking coating, and formula is by following weight percent composition:
Embodiment 3, institute's embodiment 1 difference place is, described Antisticking coating, and formula is by following weight percent composition:
Embodiment 4, institute's embodiment 1 difference place is, described Antisticking coating, and formula is by following weight percent composition:
Through repeatedly testing, after advertisement tag, labeling, card etc. are stained with, without the need to by other instrument and solvent, be easy to just to tear with hand; After pigment coating, paintbrush, writing brush etc. are scribbled, even if after drying, as long as can wipe once wiping with wet cloth.
Below the present invention be described in detail, the above, be only the preferred embodiment of the present invention, when not limiting practical range of the present invention, namely allly does impartial change according to the application's scope and modify, all should still belong in covering scope of the present invention.
Claims (2)
1. an Antisticking coating, is characterized in that: fill a prescription by following weight percent composition:
Aqueous epoxy resins 70-80%
Oleum lini 8-10%
Viscotrol C 5-8%
Acetone 2-5%
Water 2-6%
Epoxy active diluent 3-5%
According to claim 1, Antisticking coating, is characterized in that: be prepared by the following method,
The first step, adds epoxy active diluent in aqueous epoxy resins, divides and adds for three times, add 1/3rd at every turn, often add and once namely stir afterwards;
Second step, adds water toward adding in the aqueous epoxy resins after thinner, carries out fully stirring making it mix;
3rd step, adds the aqueous epoxy resins after adding water, then adds the acetone of half by oleum lini, the just system that obtains that stirs is coated with slip;
4th step, adds the 3rd step and throws in obtained pasting first processed, then add second half acetone by Viscotrol C, be stirred well to Viscotrol C and acetone is completely fused;
5th step, is placed in Air drying room and exposes 4-6 hours, i.e. obtained Antisticking coating.
2. Antisticking coating according to claim 2, is characterized in that: described epoxy active diluent adopts N-butylglycidyl ether.