CN104493029A - 一种Fe-Si-B磁性材料的锻造加工工艺 - Google Patents
一种Fe-Si-B磁性材料的锻造加工工艺 Download PDFInfo
- Publication number
- CN104493029A CN104493029A CN201410623788.1A CN201410623788A CN104493029A CN 104493029 A CN104493029 A CN 104493029A CN 201410623788 A CN201410623788 A CN 201410623788A CN 104493029 A CN104493029 A CN 104493029A
- Authority
- CN
- China
- Prior art keywords
- forging
- minute
- heating
- heated
- magnetic material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种Fe-Si-B磁性材料的锻造加工工艺，包括步骤如下：(1)将Fe-Si-B磁性材料毛坯室温装炉；(2)缓慢加热至500℃，升温速度低于100℃/h，在500℃保温40-50分钟；(3)继续第二阶段加热，在30-50分钟内由500℃加热至680℃，在680℃保温40-50分钟。本发明的有益效果：对于这种高硅高硼含量的铁基合金，现在还没有使用锻造工艺生产的报道，在直接使用常规的锻造加热工艺对其进行加热会使合金铸锭发生断裂，本发明通过加热预处理及合理的加热工艺参数，避免了Fe-Si-B磁性材料在锻前加热时发生断裂，使Fe-Si-B磁性材料可以通过锻造工艺加工生产，解决了现有Fe-Si-B磁性材料直接锻造加热发生断裂不能通过锻造生产的问题。
Description
技术领域
本发明涉及一种磁性材料的加工工艺，特别涉及一种Fe-Si-B磁性材料的锻造加工工艺。
背景技术
Fe-Si-B系磁性材料以其高饱和磁感强度低的矫顽力受到青睐，现今主要使用新工艺制备主要使用快速凝固工艺制备合金薄带，这种制备工艺的缺点就是薄带尺寸受限制，带宽和厚度受限制，生产成本比传统工艺高，生产效率较低。
发明内容
针对现有的技术不足，本发明提供一种Fe-Si-B磁性材料的锻造加工工艺。
为了实现上述目的，本发明所采取的技术方案是：一种Fe-Si-B磁性材料的锻造加工工艺，包括步骤如下：
(1)将Fe-Si-B磁性材料毛坯室温装炉；
(2)缓慢加热至500℃，升温速度低于100℃/h，在500℃保温40-50分钟；
(3)继续第二阶段加热，在30-50分钟内由500℃加热至680℃，在680℃保温40-50分钟；
(4)继续第三阶段加热，在50-80分钟内由680℃加热至800℃，在800℃保温30-50分钟；
(5)继续第四阶段加热，在80-110分钟内由800℃加热至900℃，在900℃保温30-50分钟；
(6)继续第五阶段加热，在110-170分钟内由900℃加热至顶温1070℃，在顶温保温110-170分钟；
(7)开始锻造，始锻温度为1060±20℃，终锻温度为1000℃。
所述的Fe-Si-B磁性材料质量百分比组成为：5-8％Si，2-4％B，其余为Fe和不可避免的微量杂质。
本发明的有益效果：对于这种高硅高硼含量的铁基合金，现在还没有使用锻造工艺生产的报道，在直接使用常规的锻造加热工艺对其进行加热会使合金铸锭发生断裂，本发明通过加热预处理及合理的加热工艺参数，避免了Fe-Si-B磁性材料在锻前加热时发生断裂，使Fe-Si-B磁性材料可以通过锻造工艺加工生产，解决了现有Fe-Si-B磁性材料直接锻造加热发生断裂不能通过锻造生产的问题。
附图说明
图1为Fe-Si-B磁性材料锻造加热工艺的加热曲线图。
具体实施方式
实施例；如图1所示，一种Fe-Si-B磁性材料的锻造加工工艺，包括步骤如下：
(1)将Fe-Si-B磁性材料毛坯室温装炉；
(2)缓慢加热至500℃，升温速度低于100℃/h，在500℃保温40-50分钟；
(3)继续第二阶段加热，在30-50分钟内由500℃加热至680℃，在680℃保温40-50分钟；
(4)继续第三阶段加热，在50-80分钟内由680℃加热至800℃，在800℃保温30-50分钟；
(5)继续第四阶段加热，在80-110分钟内由800℃加热至900℃，在900℃保温30-50分钟；
(6)继续第五阶段加热，在110-170分钟内由900℃加热至顶温1070℃，在顶温保温110-170分钟；
(7)开始锻造，始锻温度为1060±20℃，终锻温度为1000℃。
所述的Fe-Si-B磁性材料质量百分比组成为：5-8％Si，2-4％B，其余为Fe和不可避免的微量杂质。
Claims (2)
1.一种Fe-Si-B磁性材料的锻造加工工艺，其特征是，包括步骤如下：
(1)将Fe-Si-B磁性材料毛坯室温装炉；
(2)缓慢加热至500℃，升温速度低于100℃/h，在500℃保温40-50分钟；
(3)继续第二阶段加热，在30-50分钟内由500℃加热至680℃，在680℃保温40-50分钟；
(4)继续第三阶段加热，在50-80分钟内由680℃加热至800℃，在800℃保温30-50分钟；
(5)继续第四阶段加热，在80-110分钟内由800℃加热至900℃，在900℃保温30-50分钟；
(6)继续第五阶段加热，在110-170分钟内由900℃加热至顶温1070℃，在顶温保温110-170分钟；
(7)开始锻造，始锻温度为1060±20℃，终锻温度为1000℃。
2.根据权利要求1所述的Fe-Si-B磁性材料的锻造加工工艺，其特征是，所述的Fe-Si-B磁性材料质量百分比组成为：5-8％Si，2-4％B，其余为Fe和微量杂质。