CN104480353A - 可阳极氧化的压力铸造铝合金配方 - Google Patents

可阳极氧化的压力铸造铝合金配方 Download PDF

Info

Publication number
CN104480353A
CN104480353A CN201410773447.2A CN201410773447A CN104480353A CN 104480353 A CN104480353 A CN 104480353A CN 201410773447 A CN201410773447 A CN 201410773447A CN 104480353 A CN104480353 A CN 104480353A
Authority
CN
China
Prior art keywords
formula
aluminum alloy
aluminium alloy
anodized
die casting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410773447.2A
Other languages
English (en)
Inventor
李树青
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410773447.2A priority Critical patent/CN104480353A/zh
Publication of CN104480353A publication Critical patent/CN104480353A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种可阳极氧化的压力铸造铝合金配方，根据重量百分比，其配方由如下成分组成：硅：0.01％－0.2％；锰：0.01％－5％；钛：0.1％－1％；铁：0.01％－0.2％；铜：0.01％－0.2％；其余为不可避免的杂质和铝：85％－99％。本发明的配方主要用于液态模锻和压铸行业，用以上配方所生产的铝合金铸件经阳极氧化可得到色彩鲜艳，颜色均匀的产品；根据铸件要求，通过配方调整提高铸件的切削加工性能、机械性能和铝合金的抗裂纹能力。

Description

可阳极氧化的压力铸造铝合金配方
技术领域
本发明涉及铝合金铸造的金属材料领域，具体是一种可阳极氧化的压力铸造铝合金配方，适用于液态模锻和压铸等领域。
背景技术
压力铸造铝合金以铝为主体，含其他多种金属元素。随着人们生活水平的提高，对铝合金制品的表面装饰功能和防腐功能的要求越来越高，现有的压力铸造铝合金经阳极氧化处理后有不规则的发灰、发黑、颜色不均现象。且机械性能较差，在压力铸造过程中容易产生粘模、热裂、浇不足等缺陷。
发明内容
为了解决上述技术问题，本发明提供一种铝合金配方，生产出的铸件经阳极氧化后可以得到色彩鲜艳，颜色均匀的产品，且通过调整“有选择性加入元素”还可以提高铸件的切削加工性能、机械性能、铝合金的抗裂纹能力和流动性。
可阳极氧化的压力铸造铝合金配方，根据重量百分比，其配方由如下成分组成：硅：0.01％－0.2％；锰：0.01％－5％；钛：0.1％－1％；铁：0.01％－0.2％；铜：0.01％－0.2％；其余为不可避免的杂质和铝：85％－99％。
进一步：根据重量百分比，其的配方还可以包括以下的一种或多种组合或全部金属元素：
镁：0.1％－3％；钇：0.15％－0.3％；钪：0.1％－0.4％；镍：0.1％－4％；锌：0.5％－10％。
本发明的优点为：
本发明的可阳极氧化的压力铸造铝合金可显著改善铝合金的耐蚀性能，经过适当的着色处理后具有良好的装饰性能、耐光性、耐热性、耐蚀性，同时，可通过有选择性地加入或不加入镁、钇、钪、镍、锌元素的一种或多种组合或全部金属元素可以提高铸合金的强度、切削加工性能、机械性能和铝合金的抗裂纹能力。
具体实施方式
可阳极氧化的压力铸造铝合金配方，根据重量百分比，其的溶液配方由如下成分组成：硅：0.01％－0.2％；锰：0.01％－5％；钛：0.1％－1％；铁：0.01％－0.2％；铜：0.01％－0.2％；其余为不可避免的杂质和铝：85％－99％；进一步：其的配方还可以通过有选择性地加入或不加入以下一种或多种组合或全部金属元素：镁：0.1％－3％；钇：0.15％－0.3％；钪：0.1％－0.4％；镍：0.1％－4％；锌：0.5％－10％。
优选的基本金属元素组合配方例1：
可阳极氧化的压力铸造铝合金配方，根据重量百分比，其配方由如下成分组成：
硅0.08％；锰1.5％；钛0.2％；镁：0.8％；铁：0.2％；铜：0.2％；其余为不可避免的杂质和铝：97.02％。
此配方的铝合金生产的可阳极氧化的压力铸造铝合金铸件色泽鲜艳，加工性能良好。
优选的基本金属元素组合配方例2：
可阳极氧化的压力铸造铝合金配方，根据重量百分比，其配方由如下成分组成：硅：0.18％；锰：2.3％；钛：0.18％；镁：1.3％；铁：0.2％；铜：0.15％；其余为不可避免的杂质和铝：95.69％。
此配方的铝合金生产的可阳极氧化的压力铸造铝合金主要是提高铝合金的硬度等性能。
优选的基本金属元素与有选择性元素组合配方例3：
可阳极氧化的压力铸造铝合金配方，根据重量百分比，其配方由如下成分组成：锰：2.3％；钛：0.2％；镁：2％；镍：0.5％；锌：5％；硅：0.2％；铁：0.2％；铜：0.2％；其余为不可避免的杂质和铝：89.4％。
此配方的生产的铝合金提高了压力铸件的机械性能等。
优选的基本金属元素与有选择性元素组合配方例4：
可阳极氧化的压力铸造铝合金配方，根据重量百分比，其配方由如下成分组成：硅0.1％；锰：2.25％；钛：0.2％；镁：1.9％；钇：0.15％；镍：1％；锌：6％；硅：0.2％；铁：0.2％；铜：0.2％；其余为不可避免的杂质和铝：87.8％。
此配方生产的可阳极氧化的压力铸造铝合金主要是提高铸件机械性能的同时铸件的抗裂纹能力和流动性等也得以提高。
优选的基本金属元素与有选择性元素组合配方例5：
可阳极氧化的压力铸造铝合金配方，根据重量百分比，其配方由如下成分组成：
硅：0.1％；锰：2.3％；钛：0.15％；铁：0.1％；钪：0.2％；钇：0.15％；镍：1.5％；锌：2％；铁：0.2％；铜：0.2％；其余为不可避免的杂质和铝：93.1％。
此配方生产的可阳极氧化的压力铸造铝合金主要是进一步提高铸件的切削加工性能、机械性能和铸造性能，同时也提高了铝合金的抗裂纹等能力，但带来成本的增加。
以上所述仅是本发明的优选实施方案，本发明的保护范围并不仅局限于上述实施例，凡属于本发明思路下的技术方案均属于本发明的保护范围；应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理前提下的若干修改，应视为本发明的保护范围。

Claims (2)

1.可阳极氧化的压力铸造铝合金配方，其特征在于：根据重量百分比，其配方由如下成分组成：硅：0.01％－0.2％；锰：0.01％－5％；钛：0.1％－1％；铁：0.01％－0.2％；铜：0.01％－0.2％；其余为不可避免的杂质和铝：85％－99％。
2.根据权利要求1所述的可阳极氧化的压力铸造铝合金配方，其特征在于：根据重量百分比，其配方还可以包括以下的一种或多种组合或全部金属元素：
镁：0.1％－3％；钇：0.15％－0.3％；钪：0.1％－0.4％；镍：0.1％－4％；锌：0.5％－10％。
CN201410773447.2A 2014-12-12 2014-12-12 可阳极氧化的压力铸造铝合金配方 Pending CN104480353A (zh)