CN104449998A - Protective antirust grease for sealing and preparation method of protective antirust grease - Google Patents
Protective antirust grease for sealing and preparation method of protective antirust grease Download PDFInfo
- Publication number
- CN104449998A CN104449998A CN201410626860.6A CN201410626860A CN104449998A CN 104449998 A CN104449998 A CN 104449998A CN 201410626860 A CN201410626860 A CN 201410626860A CN 104449998 A CN104449998 A CN 104449998A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- protective
- stir
- antirust grease
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses protective antirust grease for sealing. The protective antirust grease is characterized by being prepared from the following raw materials in parts by weight: 8-10 parts of 50# machine oil, 12-15 parts of 20# aviation lubricating oil, 1-2 parts of glycerol monostearate, 35-40 parts of solid paraffin, 21-27 parts of vaseline, 6-8 parts of dodecencylsuccinic acid diethanolamide, 0.5-0.7 part of benzotriazole, 0.7-1 part of tributyl phosphate, 2-3.5 parts of laminar-crystallized sodium disilicate, 1-2 parts of superfine PMMA powder and 2.5-4 parts of a protective agent. The protective antirust grease is scientific and reasonable in formula; by adding a protective agent and such film forming components as the superfine PMMA powder, a firm absorbing film can be formed on the surface of metal, so that rusting caused by corrosion of water and oxygen is prevented, and the high temperature resistance and the fire resistance are achieved; the protective antirust grease is high in oil film strength, does not easily run off or volatilize, is excellent in rusting resistance, can well protect metal parts and is applicable to long-term sealing.
Description
Technical field
The present invention relates to rust protection liquid field, particularly a kind of there is provide protection seal up for safekeeping with rust preventing grease and preparation method thereof.
Background technology
Seal part up for safekeeping at the work in-process of plant produced or supporting warehouse-in, need to smear one deck rust-preventive agent above and prevent part from getting rusty, then wrap with waxed paper.So just can ensure metal non-corrosive over a period to come, existing slushing oil effect is general, the antirust cycle is shorter, the antirust of long term can not be carried out, and complicated operation, need heating during oil sealing, complicated operation and heat-resistant quality and anti-oxidative stability are difficult to reach requirement, and rust-proof life is shorter in the presence of a harsh environment.
The present invention is by research; invent a kind of grease type rust preventing oil; ointment shape; good water-proof effect, adds again the protective material of special development, flame-resistant high-temperature-resistant; heating is smeared or cold painting; quality product can not be caused to change, and rust-proof effect is first-class, has good corrosion protection effect to metal parts, fastening piece, work in-process.
Summary of the invention
The object of this invention is to provide a kind of there is provide protection seal up for safekeeping with rust preventing grease and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
What have a provide protection seals up for safekeeping with a rust preventing grease, is made up of the raw material of following weight part: No. 50 machinery oil 8-10, No. 20 aircraft oil 12-15, single stearic acid glycerine lipoprotein 1-2, solid paraffin 35-40, Vaseline 21-27, dodecenylsuccinic acid diglycollic amide 6-8, benzotriazole 0.5-0.7, tributyl phosphate 0.7-1, laminated crystal of sodium disilicate 2-3.5, ultra-fine PMMA powder 1-2, protective material 2.5-4;
Described protective material is prepared from by the raw material of following weight part: ethene-acetate ethylene copolymer 9-12, methacrylic ester 7-10, polyester emulsion 12-14, linking agent TAIC 1-2, alcohol ester 12 2-3, Terpineol 350 1.5-2.5, oleum lini 2-3, glycerine 5-7, precipitated chalk 3-5, ground silica 1.6-2, super fine magnesium hydroxide 2-3, MALEIC ANHYDRIDE 3-5.5; First preparation method adds oleum lini, glycerine, agitation grinding 60-80 minute by after precipitated chalk, ground silica, super fine magnesium hydroxide mixing, forms dispersion; Then ethene-acetate ethylene copolymer, methacrylic ester, linking agent TAIC are mixed, be heated to 90 DEG C-105 DEG C stirring reaction 2-3 hour, be cooled to 50 DEG C-60 DEG C again, add all the other remaining components, stir 30-40 minute with the speed of 400-500 rev/min; Finally be cooled to room temperature, add dispersion, stir and obtain protective material.
Of the present invention a kind of there is provide protection seal up for safekeeping with rust preventing grease, be made up of following concrete steps:
(1) add laminated crystal of sodium disilicate, solid paraffin by No. 20 aircraft oils, gradation adds Vaseline, fully grinding 2-2.5 hour;
(2) ultra-fine PMMA powder is heated to 90 DEG C-110 DEG C, insulation 40-50 minute, then temperature control is at 60 DEG C-80 DEG C, adds dodecenylsuccinic acid diglycollic amide, single stearic acid glycerine lipoprotein, insulation reaction 30-45 minute;
(3) step (1) is mixed with step (2), add protective material, stir 30-40 minute with the speed of 350-400 rev/min; then all the other remaining components are added; be heated to 55 DEG C-65 DEG C, continue to stir 1.5-2 hour, then namely cold going obtain rust preventing grease of the present invention to room temperature.
Excellent effect of the present invention is: scientific formulation of the present invention is reasonable, add the film forming components such as ultra-fine PMMA powder, the interpolation of mating protection agent, can form firmly adsorption film in metallic surface, the erosion of anti-sealing and oxygen causes getting rusty, and has the effect of fire resistant; Oil film strength of the present invention is high, not easily runs off and volatilizees, high rust resistance, has good provide protection, be applicable to and seal up for safekeeping for a long time metal parts.
Embodiment
Below by specific examples, the present invention is described in detail.
There is sealing up for safekeeping with a rust preventing grease of provide protection, be made up of the raw material of following weight part (kilogram): No. 50 machinery oil 8, No. 20 aircraft oils 12, single stearic acid glycerine lipoprotein 1, solid paraffin 35, Vaseline 21, dodecenylsuccinic acid diglycollic amide 6, benzotriazole 0.5, tributyl phosphate 0.7, laminated crystal of sodium disilicate 2, ultra-fine PMMA powder 1, protective material 2.5;
Described protective material is prepared from by the raw material of following weight part (kilogram): ethene-acetate ethylene copolymer 9, methacrylic ester 7, polyester emulsion 12, linking agent TAIC 1, alcohol ester 12, Terpineol 350 1.5, oleum lini 2, glycerine 5, precipitated chalk 3, ground silica 1.6, super fine magnesium hydroxide 2, MALEIC ANHYDRIDE 3; First preparation method adds oleum lini, glycerine, agitation grinding 60-80 minute by after precipitated chalk, ground silica, super fine magnesium hydroxide mixing, forms dispersion; Then ethene-acetate ethylene copolymer, methacrylic ester, linking agent TAIC are mixed, be heated to 90 DEG C-105 DEG C stirring reaction 2-3 hour, be cooled to 50 DEG C-60 DEG C again, add all the other remaining components, stir 30-40 minute with the speed of 400-500 rev/min; Finally be cooled to room temperature, add dispersion, stir and obtain protective material.
Of the present invention a kind of there is provide protection seal up for safekeeping with rust preventing grease, be made up of following concrete steps:
(1) add laminated crystal of sodium disilicate, solid paraffin by No. 20 aircraft oils, gradation adds Vaseline, fully grinding 2-2.5 hour;
(2) ultra-fine PMMA powder is heated to 90 DEG C-110 DEG C, insulation 40-50 minute, then temperature control is at 60 DEG C-80 DEG C, adds dodecenylsuccinic acid diglycollic amide, single stearic acid glycerine lipoprotein, insulation reaction 30-45 minute;
(3) step (1) is mixed with step (2), add protective material, stir 30-40 minute with the speed of 350-400 rev/min; then all the other remaining components are added; be heated to 55 DEG C-65 DEG C, continue to stir 1.5-2 hour, then namely cold going obtain rust preventing grease of the present invention to room temperature.
The rust preventing grease outward appearance that the present invention makes is the ointment of smooth even, can room temperature coating or heating coating, and salt spray resistance is tested: be 35 DEG C in temperature, and through 150 hours, 45# steel was corrosion-free; Wet-heat resisting is tested: be 50 DEG C in temperature, and through 700 hours, 45# steel was corrosion-free.
Claims (2)
1. one kind there is provide protection seal up for safekeeping with rust preventing grease, it is characterized in that, be made up of the raw material of following weight part: No. 50 machinery oil 8-10, No. 20 aircraft oil 12-15, single stearic acid glycerine lipoprotein 1-2, solid paraffin 35-40, Vaseline 21-27, dodecenylsuccinic acid diglycollic amide 6-8, benzotriazole 0.5-0.7, tributyl phosphate 0.7-1, laminated crystal of sodium disilicate 2-3.5, ultra-fine PMMA powder 1-2, protective material 2.5-4;
Described protective material is prepared from by the raw material of following weight part: ethene-acetate ethylene copolymer 9-12, methacrylic ester 7-10, polyester emulsion 12-14, linking agent TAIC 1-2, alcohol ester 12 2-3, Terpineol 350 1.5-2.5, oleum lini 2-3, glycerine 5-7, precipitated chalk 3-5, ground silica 1.6-2, super fine magnesium hydroxide 2-3, MALEIC ANHYDRIDE 3-5.5; First preparation method adds oleum lini, glycerine, agitation grinding 60-80 minute by after precipitated chalk, ground silica, super fine magnesium hydroxide mixing, forms dispersion; Then ethene-acetate ethylene copolymer, methacrylic ester, linking agent TAIC are mixed, be heated to 90 DEG C-105 DEG C stirring reaction 2-3 hour, be cooled to 50 DEG C-60 DEG C again, add all the other remaining components, stir 30-40 minute with the speed of 400-500 rev/min; Finally be cooled to room temperature, add dispersion, stir and obtain protective material.
2. according to claim 1 a kind of there is provide protection seal up for safekeeping with rust preventing grease, it is characterized in that, be made up of following concrete steps:
(1) add laminated crystal of sodium disilicate, solid paraffin by No. 20 aircraft oils, gradation adds Vaseline, fully grinding 2-2.5 hour;
(2) ultra-fine PMMA powder is heated to 90 DEG C-110 DEG C, insulation 40-50 minute, then temperature control is at 60 DEG C-80 DEG C, adds dodecenylsuccinic acid diglycollic amide, single stearic acid glycerine lipoprotein, insulation reaction 30-45 minute;
(3) step (1) is mixed with step (2), add protective material, stir 30-40 minute with the speed of 350-400 rev/min; then all the other remaining components are added; be heated to 55 DEG C-65 DEG C, continue to stir 1.5-2 hour, then namely cold going obtain rust preventing grease of the present invention to room temperature.