CN104450044A - Multifunctional anti-rust grease for metal processing and preparation method thereof - Google Patents
Multifunctional anti-rust grease for metal processing and preparation method thereof Download PDFInfo
- Publication number
- CN104450044A CN104450044A CN201410626812.7A CN201410626812A CN104450044A CN 104450044 A CN104450044 A CN 104450044A CN 201410626812 A CN201410626812 A CN 201410626812A CN 104450044 A CN104450044 A CN 104450044A
- Authority
- CN
- China
- Prior art keywords
- parts
- grease
- stir
- minute
- rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses multifunctional anti-rust grease for metal processing. The multifunctional anti-rust grease is characterized by being prepared from the following raw materials in parts by weight: 15-20 parts of mechanical oil, 11-15 parts of calcium-base lubricating grease, 3-4 parts of polyurethane, 2-3 parts of butyl acrylate, 1-2 parts of sodium naphthenate, 38-45 parts of lanolin, 24-27 parts of industrial vaseline No.2, 1-2 parts of ethylparaben, 6.5-8 parts of petroleum sodium sulfonate, 1-2 parts of glycerol ester of hydrogenated rosin and 2.5-4 parts of a protective agent. The multifunctional anti-rust grease disclosed by the invention is reasonable in formula, the added sodium naphthenate has an antibacterial effect, and the added film forming components such as the butyl acrylate and the added protective agent are matched with each other to achieve good water preventing and lubricating effects and form a firm hydrophobic film on the surface of metal to protect the metal from erosion of water and oxygen and rusting. The multifunctional anti-rust grease has multiple functions of preventing rust, resisting bacteria and lubricating, thereby being suitable for processing a variety of metals.
Description
Technical field
The present invention relates to rust protection liquid field, particularly a kind of multi-functional rust preventing grease for intermetallic composite coating and preparation method thereof.
Background technology
Current domestic rust preventing grease has dozens of kind, this kind of rust preventing grease is mainly with paraffin or lipid acid soap-type gelling agent, be equipped with sulfonate and other non-ferrous metal inhibiter, be generally used for the packaging of various mechanical component, seal up for safekeeping, high and low temperature performance is all poor, most rust preventing grease oil sealing, play envelope time all need heating, complicated operation and heat-resistant quality and anti-oxidative stability are difficult to reach requirement, and the rust preventing grease containing metal ion can accelerate surface oxidation, rust-proof life is shorter in the presence of a harsh environment.The demand for development rust preventing grease of modern industrial technology will improve antirust ability, increases functional effect, in order to be suitable for economic product for client provides better, the basis now in conjunction with external product advantage is developed a kind of rust preventing grease with multi-efficiency.
The present invention is by reasonably filling a prescription; add the composition of the effects such as antibacterial, film forming; by special technique; make the rust preventing grease that a kind of intermetallic composite coating uses; coordinate and add protective material, add protective material, there is good waterproof lubricant effect; can form firmly hydrophobic membrane in metallic surface, the erosion of anti-sealing and oxygen causes getting rusty.
Summary of the invention
The object of this invention is to provide a kind of multi-functional rust preventing grease for intermetallic composite coating and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
For a multi-functional rust preventing grease for intermetallic composite coating, be made up of the raw material of following weight part: machinery oil 15-20, quicklime grease 11-15, polyurethane(s) 3-4, butyl acrylate 2-3, sodium napthionate 1-2, lanolin 38-45, No. 2 industrial vaseline 24-27, ethylparoben 1-2, petroleum sodium sulfonate 6.5-8, hydrogenated rosin glyceride 1-2, protective material 2.5-4;
Described protective material is prepared from by the raw material of following weight part: poly-hydroxyethyl silicone emulsion 8-11, polyvinyl butyral acetal 3-5, natural rubber latex 5-7, aquadag 3-5, organobentonite 2-4, hydrogenated castor oil 4-6, alkylpolyoxyethylene 2-3, E-12 epoxy resin 19-22, phenylcarbinol 4-6, urea 2-3, Wickenol 111 3-4, linolic acid sodium 1-2; Preparation method adds hydrogenated castor oil, agitation grinding 60-80 minute after first being mixed with organobentonite by aquadag, forms dispersion; Then by E-12 epoxy resin, phenylcarbinol, urea, natural rubber latex mixing, be heated to 85 DEG C-110 DEG C stirring reaction 2-3 hour, then be cooled to 60 DEG C-70 DEG C, add all the other remaining components, stir 20-30 minute with the speed of 300-500 rev/min; Finally be cooled to room temperature, add dispersion, stir and obtain protective material.
A kind of multi-functional rust preventing grease for intermetallic composite coating of the present invention, be made up of following concrete steps:
(1) be placed in mortar by quicklime grease, add lanolin, gradation adds No. 2 industrial vaselines, and grinding evenly forms mashed prod;
(2) polyurethane(s), butyl acrylate, hydrogenated rosin glyceride mixing, be heated to 80 DEG C-100 DEG C, and insulation 20-30 minute, is then cooled to 65 DEG C-75 DEG C, adds ethylparoben, petroleum sodium sulfonate, continues to stir 15-25 minute;
(3) step (1) mashed prod is mixed with step (2), add protective material, stir 30-40 minute with the speed of 200-300 rev/min; then all the other remaining components are added; be heated to 60 DEG C-80 DEG C, continue to stir 1.5-2 hour, then namely cold going obtain rust preventing grease of the present invention to room temperature.
Excellent effect of the present invention is: the present invention fills a prescription rationally, add sodium napthionate and there is antibacterial effect, add the film forming components such as butyl acrylate, coordinate and add protective material, there is good waterproof lubricant effect, can form firmly hydrophobic membrane in metallic surface, the erosion of anti-sealing and oxygen causes getting rusty; Rust preventing grease of the present invention has multi-efficiency, collect anti-embroidery, antibacterial, lubrication with one, be applicable to various metals processing use.
Embodiment
Below by specific examples, the present invention is described in detail.
For a multi-functional rust preventing grease for intermetallic composite coating, be made up of the raw material of following weight part (kilogram): machinery oil 15, quicklime grease 11, polyurethane(s) 3, butyl acrylate 2, sodium napthionate 1, lanolin 38, No. 2 industrial vaselines 24, ethylparoben 1, petroleum sodium sulfonate 6.5, hydrogenated rosin glyceride 1, protective materials 2.5;
Described protective material is prepared from by the raw material of following weight part (kilogram): poly-hydroxyethyl silicone emulsion 8, polyvinyl butyral acetal 3, natural rubber latex 5, aquadag 3, organobentonite 2, hydrogenated castor oil 4, alkylpolyoxyethylene 2, E-12 epoxy resin 19, phenylcarbinol 4, urea 2, Wickenol 111 3, linolic acid sodium 1; Preparation method adds hydrogenated castor oil, agitation grinding 60-80 minute after first being mixed with organobentonite by aquadag, forms dispersion; Then by E-12 epoxy resin, phenylcarbinol, urea, natural rubber latex mixing, be heated to 85 DEG C-110 DEG C stirring reaction 2-3 hour, then be cooled to 60 DEG C-70 DEG C, add all the other remaining components, stir 20-30 minute with the speed of 300-500 rev/min; Finally be cooled to room temperature, add dispersion, stir and obtain protective material.
A kind of multi-functional rust preventing grease for intermetallic composite coating of the present invention, be made up of following concrete steps:
(1) be placed in mortar by quicklime grease, add lanolin, gradation adds No. 2 industrial vaselines, and grinding evenly forms mashed prod;
(2) polyurethane(s), butyl acrylate, hydrogenated rosin glyceride mixing, be heated to 80 DEG C-100 DEG C, and insulation 20-30 minute, is then cooled to 65 DEG C-75 DEG C, adds ethylparoben, petroleum sodium sulfonate, continues to stir 15-25 minute;
(3) step (1) mashed prod is mixed with step (2), add protective material, stir 30-40 minute with the speed of 200-300 rev/min; then all the other remaining components are added; be heated to 60 DEG C-80 DEG C, continue to stir 1.5-2 hour, then namely cold going obtain rust preventing grease of the present invention to room temperature.
The rust preventing grease outward appearance that the present invention makes is the ointment of smooth even, can room temperature coating or heating coating, and salt spray resistance is tested: be 35 DEG C in temperature, and through 150 hours, 45# steel was corrosion-free; Wet-heat resisting is tested: be 50 DEG C in temperature, and through 700 hours, 45# steel was corrosion-free.
Claims (2)
1. the multi-functional rust preventing grease for intermetallic composite coating, it is characterized in that, be made up of the raw material of following weight part: machinery oil 15-20, quicklime grease 11-15, polyurethane(s) 3-4, butyl acrylate 2-3, sodium napthionate 1-2, lanolin 38-45, No. 2 industrial vaseline 24-27, ethylparoben 1-2, petroleum sodium sulfonate 6.5-8, hydrogenated rosin glyceride 1-2, protective material 2.5-4;
Described protective material is prepared from by the raw material of following weight part: poly-hydroxyethyl silicone emulsion 8-11, polyvinyl butyral acetal 3-5, natural rubber latex 5-7, aquadag 3-5, organobentonite 2-4, hydrogenated castor oil 4-6, alkylpolyoxyethylene 2-3, E-12 epoxy resin 19-22, phenylcarbinol 4-6, urea 2-3, Wickenol 111 3-4, linolic acid sodium 1-2; Preparation method adds hydrogenated castor oil, agitation grinding 60-80 minute after first being mixed with organobentonite by aquadag, forms dispersion; Then by E-12 epoxy resin, phenylcarbinol, urea, natural rubber latex mixing, be heated to 85 DEG C-110 DEG C stirring reaction 2-3 hour, then be cooled to 60 DEG C-70 DEG C, add all the other remaining components, stir 20-30 minute with the speed of 300-500 rev/min; Finally be cooled to room temperature, add dispersion, stir and obtain protective material.
2. a kind of multi-functional rust preventing grease for intermetallic composite coating according to claim 1, is characterized in that, be made up of following concrete steps:
(1) be placed in mortar by quicklime grease, add lanolin, gradation adds No. 2 industrial vaselines, and grinding evenly forms mashed prod;
(2) polyurethane(s), butyl acrylate, hydrogenated rosin glyceride mixing, be heated to 80 DEG C-100 DEG C, and insulation 20-30 minute, is then cooled to 65 DEG C-75 DEG C, adds ethylparoben, petroleum sodium sulfonate, continues to stir 15-25 minute;
(3) step (1) mashed prod is mixed with step (2), add protective material, stir 30-40 minute with the speed of 200-300 rev/min; then all the other remaining components are added; be heated to 60 DEG C-80 DEG C, continue to stir 1.5-2 hour, then namely cold going obtain rust preventing grease of the present invention to room temperature.