CN104449035A - 一种防凝结水性油墨 - Google Patents
一种防凝结水性油墨 Download PDFInfo
- Publication number
- CN104449035A CN104449035A CN201410703463.4A CN201410703463A CN104449035A CN 104449035 A CN104449035 A CN 104449035A CN 201410703463 A CN201410703463 A CN 201410703463A CN 104449035 A CN104449035 A CN 104449035A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic resin
- ink
- magnesium oxide
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:丙烯酸树脂乳液:30~33份;水溶性丙烯酸树脂:3.5~4.5份;苯乙烯化丙烯酸分散剂:21~24份;异丙醇:18~24份;滑石粉:5~8份;交联剂:1~4份;氧化镁:26~38份。由于本发明添加了滑石粉和氧化镁,减少了油墨之间的连接性,同时还增加了苯乙烯化丙烯酸分散剂,提高了油墨件的分散性,油墨就不会凝结。
Description
技术领域
本发明涉及一种油墨,尤其涉及一种防凝结水性油墨。
背景技术
油墨,是用于印刷的重要材料,它通过印刷将图案、文字表现在承印物上。油墨中包括主要成分和辅助成分,它们均匀地混合并经反复轧制而成一种黏性胶状流体。由颜料、连结料和助剂和溶剂等组成。用于书刊、包装装潢、建筑装饰等各种印刷。随着社会需求增大,油墨品种和产量也相应扩展和增长。
水性油墨 简称为水墨,柔性版水性墨也称液体油墨,它主要由水溶性树脂、有机颜料、溶剂及相关助剂经复合研磨加工而成。水性油墨特别适用于烟、酒、食品、饮料、药品、儿童玩具等卫生条件要求严格的包装印刷产品。
申请号为CN201110396718.3,申请日为2011年12月5日,公开日为2012年6月27日的中国发明专利申请公开了一种纸张水性油墨,属于柔版水性油墨技术领域,其特征在于按如下重量配比的组份:地沟油20~40份,大豆油5~15份,季荗四醇1~6份,顺丁烯二酸酐8~15份,氧化镁0.01~2份,松香30~45份、交联剂1~3份制备水性合成树脂;按如下重量配比的组份:水性合成树脂45~55份,水30~45份,二甲基乙胺2--5份,氨水3~6份制备水性树脂油;按如下重量配比的组份:水性树脂油50-60份,颜料10-30份,水10-20份、消泡剂0.2~0.5份制得纸张水性油墨产品。本发明用废物地沟油替代相当部分的松香等原料,这既解决了松香短缺的问题,又能将地沟油变废为宝,另外它环保、安全、无毒、无害、不燃不爆,几乎无挥发性有机气体,不污染大气环境。但是该发明专利在印刷时,特别是在冬天,会凝结成块状或者颗粒状,严重影响印刷效果。
发明内容
为了克服上述水性油墨在印刷时出现凝结块的缺陷,本发明提供了一种防凝结水性油墨,该水性油墨及时在冬天也不会凝结成块,印刷效果好。
为了解决上述技术问题,本发明采用的技术方案是:
一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:30~33份;
水溶性丙烯酸树脂:3.5~4.5份;
苯乙烯化丙烯酸分散剂:21~24份;
异丙醇:18~24份;
滑石粉:5~8份;
交联剂:1~4份;
氧化镁:26~38份。
本发明优选成分为:
丙烯酸树脂乳液:30~32份;
水溶性丙烯酸树脂:3.5~4.5份;
苯乙烯化丙烯酸分散剂:21~23份;
异丙醇:18~20份;
滑石粉:5~6份;
交联剂:3~4份;
氧化镁:28~30份。
本发明最优选成分为:
丙烯酸树脂乳液:30份;
水溶性丙烯酸树脂:4份;
苯乙烯化丙烯酸分散剂:22份;
异丙醇:19份;
滑石粉:5份;
交联剂:4份;
氧化镁:30份。
本发明具有以下优点:
本发明印刷适应性好、耐湿摩擦、高光泽、附着力好,可用于不同品种的纸张及塑料薄膜,如出版用纸、包装用纸、瓦楞纸等承印物上印刷,也适用于高速印刷,而且由于本发明添加了滑石粉和氧化镁,减少了油墨之间的连接性,同时还增加了苯乙烯化丙烯酸分散剂,提高了油墨件的分散性,油墨就不会凝结。
具体实施方式
实施例1
一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:30份;
水溶性丙烯酸树脂:3.5份;
苯乙烯化丙烯酸分散剂:21份;
异丙醇:18份;
滑石粉:5份;
交联剂:1份;
氧化镁:26份。
实施例2
一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:33份;
水溶性丙烯酸树脂:34.5份;
苯乙烯化丙烯酸分散剂:24份;
异丙醇:24份;
滑石粉:8份;
交联剂:4份;
氧化镁:38份。
实施例3
一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:30份;
水溶性丙烯酸树脂:4.5份;
苯乙烯化丙烯酸分散剂:21份;
异丙醇:24份;
滑石粉:5份;
交联剂:4份;
氧化镁:38份。
实施例4
一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:30份;
水溶性丙烯酸树脂:3.5份;
苯乙烯化丙烯酸分散剂:24份;
异丙醇:24份;
滑石粉:8份;
交联剂:1份;
氧化镁:38份。
实施例5
一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:32份;
水溶性丙烯酸树脂:4份;
苯乙烯化丙烯酸分散剂:22份;
异丙醇:20份;
滑石粉:6份;
交联剂:3份;
氧化镁:28份。
实施例6
一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:32份;
水溶性丙烯酸树脂:4份;
苯乙烯化丙烯酸分散剂:22份;
异丙醇:20份;
滑石粉:6份;
交联剂:2份;
氧化镁:30份。
实施例7
一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:30份;
水溶性丙烯酸树脂:4.5份;
苯乙烯化丙烯酸分散剂:23份;
异丙醇:20份;
滑石粉:6份;
交联剂:4份;
氧化镁:30份。
实施例8
一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:30份;
水溶性丙烯酸树脂:3.5份;
苯乙烯化丙烯酸分散剂:21份;
异丙醇:18份;
滑石粉:5份;
交联剂:3份;
氧化镁:28份。
实施例9
一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:30份;
水溶性丙烯酸树脂:4份;
苯乙烯化丙烯酸分散剂:22份;
异丙醇:19份;
滑石粉:5份;
交联剂:4份;
氧化镁:30份。
Claims (3)
1.一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:30~33份;
水溶性丙烯酸树脂:3.5~4.5份;
苯乙烯化丙烯酸分散剂:21~24份;
异丙醇:18~24份;
滑石粉:5~8份;
交联剂:1~4份;
氧化镁:26~38份。
2.根据权利要求1所述的一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:30~32份;
水溶性丙烯酸树脂:3.5~4.5份;
苯乙烯化丙烯酸分散剂:21~23份;
异丙醇:18~20份;
滑石粉:5~6份;
交联剂:3~4份;
氧化镁:28~30份。
3.根据权利要求1所述的一种防凝结水性油墨,其特征在于:包括如下以质量份数计的成分:
丙烯酸树脂乳液:30份;
水溶性丙烯酸树脂:4份;
苯乙烯化丙烯酸分散剂:22份;
异丙醇:19份;
滑石粉:5份;
交联剂:4份;
氧化镁:30份。