CN104448516A - Bath ball for children, women and cosmetology and production process thereof - Google Patents
Bath ball for children, women and cosmetology and production process thereof Download PDFInfo
- Publication number
- CN104448516A CN104448516A CN201410621095.9A CN201410621095A CN104448516A CN 104448516 A CN104448516 A CN 104448516A CN 201410621095 A CN201410621095 A CN 201410621095A CN 104448516 A CN104448516 A CN 104448516A
- Authority
- CN
- China
- Prior art keywords
- eva
- children
- weight part
- relative density
- bath balls
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a bath ball for children, women and cosmetology and a production process thereof. The production process specifically comprises the steps: uniformly mixing and stirring 10-70 parts by weight of polyethylene, 30-90 parts by weight of EVA, 0.2-0.7 part by weight of colorant and 0.3-1 part by weight of EVA deodorant, wherein the relative density of the polyethylene is 0.925, and the degree of crystallinity is 55-65%; the relative density of the EVA is 0.93-0.94, the glossiness is 82-85, and the stirring time is 5-10 minutes; and heating to melt the stirred materials, forming a net in a mould, cooling and sizing; sequentially towing, drying, coiling, cutting and rolling the cooled and sized materials to prepare the bath ball. The product prepared by the production process provided by the invention is compact in structure, soft and delicate, good in elasticity, free of deformation, beautiful in appearance, free of peculiar smell, strong in decontamination ability, durable and capable of effectively reducing injury on the skin of children and women, so that the product is suitable for children, women and cosmetology, the production process is simple and easy to operate, and the production energy consumption is low.
Description
Technical field
The present invention relates to daily necessities technical field, is a kind of children, Ms, cosmetically bath balls and production technique thereof specifically.
Background technology
Bath balls is a kind of bath article very conventional in the modern life, steaming Saunas or squeezing a small amount of body wash when having a bath on bath balls, rubs with the hands gently and can produce a large amount of foams, is the best instrument that body wash bubbles.It is not only both artistic and practical, and the weaving structure of its uniqueness is used as the dirt of having a bath and thoroughly can clean skin and skin sweat is greasy, makes skin tender, smooth.What existing bath balls generally adopted is polyethylene material, production technique roughly as shown in Figure 1: polyethylene, tinting material are stirred, then by mixture heat fused, mould goes out net, cooling shaping, traction, the dehydration of heating poach and rolling cutting, roll to obtain finished product by hand.There is following defect in existing bath balls and production technique thereof: 1, product mesh is too thick, and loosely organized not tight, yielding, poor flexibility, can cause skin lesion to children, Ms, cannot be applied to beauty treatment fields; 2, energy waste is large, especially heats poach link, needs the electric energy of at substantial to heat, do not meet the enterprise development demand of current low power consumption and low cost.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, technical problem to be solved by this invention is to provide a kind of product quality is high, production cost is low children, Ms, cosmetically bath balls and production technique thereof.
In order to solve the problems of the technologies described above, the technical solution used in the present invention one is:
A kind of children, Ms, cosmetically bath balls, comprise the component of following weight part:
Described poly relative density is 0.925, and degree of crystallinity is 55 ~ 65%;
The relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85.
Children provided by the invention, Ms, cosmetically bath balls, be different from the quality defects such as thick, loosely organized not tight, yielding, the poor flexibility of mesh existing for existing bath balls, there is following beneficial effect: close structure, soft exquisiteness, good springiness, indeformable, attractive in appearance, free from extraneous odour, the dirty ability of decontamination are strong, durable in use, effectively can reduce the injury to children, Ms's skin, be applicable to children, Ms, beauty treatment use, meet the market requirement of human consumer to high-quality bath balls well.
In order to solve the problems of the technologies described above, the technical solution used in the present invention two is:
A kind of children, Ms, cosmetically bath balls production technique, comprising:
By the EVA deodovization agent mixing and stirring of the EVA of the polyethylene of 10 ~ 70 weight parts, 30 ~ 90 weight parts, the tinting material of 0.2 ~ 0.7 weight part and 0.3 ~ 1 weight part, described poly relative density is 0.925, and degree of crystallinity is 55 ~ 65%; The relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85, and churning time is 5 ~ 10min;
The material be stirred is carried out heat fused, mould goes out net and cooling shaping;
By the material after cooling shaping successively by traction, drying, rolling, cutting, roll after make bath balls.
Children provided by the invention, Ms, cosmetically bath balls production technique, have following beneficial effect:
1, production technique is simple to operation, and production efficiency is high, is very applicable to large-scale industrial production;
2, production energy consumption significantly reduces, and production cost is low, has agreed with modern enterprise well to growth requirement that is energy-saving and cost-reducing and low cost high yield;
3, obtained product structure closely, soft exquisiteness, good springiness, indeformable, attractive in appearance, free from extraneous odour, the dirty ability of decontamination are strong, durable in use, effectively can reduce the injury to children, Ms's skin, be applicable to children, Ms, beauty treatment use, meet the market requirement of human consumer to high-quality bath balls well.
Accompanying drawing explanation
Figure 1 shows that the schematic flow sheet of existing bath balls production technique.
Figure 2 shows that the schematic flow sheet of the bath balls production technique of the embodiment of the present invention.
Embodiment
By describing technology contents of the present invention in detail, realized object and effect, accompanying drawing is coordinated to be explained below in conjunction with embodiment.
The design of most critical of the present invention is: utilize chemical property that EVA material is excellent as high tenacity, high resilience, and coordinate Low Density Polyethylene, tinting material and EVA deodovization agent, the bath balls that production is obtained possesses close structure, soft fine and smooth, good springiness, indeformable, attractive in appearance, free from extraneous odour, decontamination dirt ability is strong, the fine quality such as durable in use, can effectively reduce children, the injury of Ms's skin, be applicable to children, Ms, beauty treatment uses, and when utilizing above-mentioned raw materials to produce bath balls, without the need to product being made to possess enough pliabilitys through heating poach, greatly reduce the production energy consumption of product, agree with modern enterprise well to growth requirement that is energy-saving and cost-reducing and low cost high yield.
Concrete, the children of the embodiment of the present invention, Ms, cosmetically bath balls, comprise the component of following weight part:
Described poly relative density is 0.925, and degree of crystallinity is 55 ~ 65%;
The relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85.
In the above-described embodiments, tinting material to make material manifest the material designing and need color, and tinting material can be divided into powdery, pasty state, paste by its form.Wherein coloured powdery agent is, after tinting material is ground to form fine powder, do not add process and be directly used in painted.The dry mix that coloured powdery agent is applicable to PE, PC, PP, ABS, PC extrude draw mould painted.Pasty state or cream colored agent are dispersed in the volatile liquids such as softening agent makes paste or paste, and it is usually used on the goods such as urethane, ring benzene synthetic glass.Preferably powdered tinting material of the present invention, it comprises the colors such as red, yellow, blue, orange, purple, green, is more preferably the agent of purple coloured powdery.
In the above-described embodiments, described EVA deodovization agent is a kind of special deodovization agent of tasteless close ethylene-vinyl acetate copolymer, for the chemical structure feature of EVA, containing the chemical functional group that various active is extremely strong.To EVA and the various EVA goods various smell small molecules that EVA resin itself and various additive may occur in processing and use, comprise acids, ester class, Ammonia, hydrocarbon polymer and other scent molecules and there is good chemical action ability.EVA deodovization agent, through special processing, so be easy to disperse in EVA or EVA goods and do not change the chemical structure of EVA, has excellent thermotolerance, can use below 400 DEG C.EVA deodovization agent itself is nonpoisonous and tasteless and heavy metal and content of halogen are all less than European Union ROHS standard, has environmental protection usage quantity few, the advantages such as taste removal is effective.
From foregoing description, beneficial effect of the present invention is: close structure, soft exquisiteness, good springiness, indeformable, attractive in appearance, free from extraneous odour, the dirty ability of decontamination are strong, durable in use, effectively can reduce the injury to children, Ms's skin, be applicable to children, Ms, beauty treatment use, meet the market requirement of human consumer to high-quality bath balls well.
Further, the weight part of described tinting material is 0.2 part, and the weight part of described EVA deodovization agent is 0.6 part.
Further, the relative density of described EVA is 0.935, and glossiness is 82.
Concrete, please refer to shown in Fig. 2, the children of the embodiment of the present invention, Ms, cosmetically bath balls production technique, comprising:
By the EVA deodovization agent mixing and stirring of the EVA of the polyethylene of 10 ~ 70 weight parts, 30 ~ 90 weight parts, the tinting material of 0.2 ~ 0.7 weight part and 0.3 ~ 1 weight part, described poly relative density is 0.925, and degree of crystallinity is 55 ~ 65%; The relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85, and churning time is 5 ~ 10min;
The material be stirred is carried out heat fused, mould goes out net and cooling shaping;
By the material after cooling shaping successively by traction, drying, rolling, cutting, roll after make bath balls.
From foregoing description, beneficial effect of the present invention is:
1, production technique is simple to operation, and production efficiency is high, is very applicable to large-scale industrial production;
2, production energy consumption significantly reduces, and production cost is low, has agreed with modern enterprise well to growth requirement that is energy-saving and cost-reducing and low cost high yield;
3, obtained product structure closely, soft exquisiteness, good springiness, indeformable, attractive in appearance, free from extraneous odour, the dirty ability of decontamination are strong, durable in use, effectively can reduce the injury to children, Ms's skin, be applicable to children, Ms, beauty treatment use, meet the market requirement of human consumer to high-quality bath balls well.
Further, described heat fused is carried out in net puller, and net puller is all net pullers being applicable to producing bath balls.Before use can first by main frame heat-flash 1.5 ~ 2 hours.Net puller main frame is divided into five sections to heat, shown in table 1 specific as follows: one section of Heating temperature is 80 ~ 120 DEG C, and heat-up time is 80 ~ 100min; Two sections of Heating temperatures are 120 ~ 140 DEG C, and heat-up time is 80 ~ 100min; Three sections of Heating temperatures are 150 ~ 200 DEG C, and heat-up time is 80 ~ 100min; Four sections of Heating temperatures are 180 ~ 230 DEG C, and heat-up time is 100 ~ 120min; Five sections of Heating temperatures are 200 ~ 240 DEG C, and heat-up time is 100 ~ 120min; After main frame five sections of temperature all reach design temperature, reinstall the material be stirred and carry out heat fused.Time, when reaching 1.5 ~ 2h, is extruded a strip-shaped materials, starts rotating die head.Wherein rotating die head rotating speed is according to the adjustment of guipure sample, can be fast or slow, mainly forms point of crossing, namely make interior external mold rotating, strand material shape is reticulated and enters cooling trough, cooling shaping, take turns traction by one.Wherein an effect taking turns traction is that guipure is drawn from cold rinse bank, take turns traction by two again, wherein two effects taking turns traction mesh bag are entered dehydrate, and after dehydration, guipure is by after plait mill rolling, cutting or with full-automatic cutting machine cutting by hand, then manually or machinery roll and get product.
Table 1
| Each section of main frame | One section | Two sections | Three sections | Four sections | Five sections |
| Heating temperature DEG C | 80～120 | 120～140 | 150～200 | 180～230 | 200～240 |
| Heat-up time min | 80～100 | 80～100 | 80～100 | 100～120 | 100～120 |
Further, the weight part of described tinting material is 0.2 part, and the weight part of described EVA deodovization agent is 0.6 part.
Further, the relative density of described EVA is 0.935, and glossiness is 82.
Embodiment 1
Children, Ms's, a cosmetically bath balls production technique, specifically comprises the following steps:
Step one: stirred by the EVA deodovization agent of the EVA of the polyethylene of 70 weight parts, 30 weight parts, the tinting material of 0.2 weight part and 0.3 weight part, described poly relative density is 0.925, and degree of crystallinity is 55 ~ 65%; The relative density of described EVA is 0.935, and glossiness is 82.
Step 2: the material obtained in described step one is carried out heat fused, mould goes out net and cooling shaping.
Step 3: by the material after cooling shaping in described step 2 successively by traction, rolling, cutting, roll after make bath balls or shower bar.
Embodiment 2
Identical with embodiment 1, difference is: poly weight part is 60 parts, and the weight part of EVA is 40 parts, and the weight part of tinting material is 0.2 part, and the weight part of EVA deodovization agent is 0.6 part.
Embodiment 3
Identical with embodiment 1, difference is: poly weight part is 50 parts, and the weight part of EVA is 50 parts, and the weight part of tinting material is 0.7 part, and the weight part of EVA deodovization agent is 0.6 part.
Embodiment 4
Identical with embodiment 1, difference is: poly weight part is 40 parts, and the weight part of EVA is 60 parts, and the weight part of tinting material is 0.3 part, and the weight part of EVA deodovization agent is 0.6 part.
Embodiment 5
Identical with embodiment 1, difference is: poly weight part is 30 parts, and the weight part of EVA is 70 parts, and the weight part of tinting material is 0.5 part, and the weight part of EVA deodovization agent is 0.6 part.
Embodiment 6
Identical with embodiment 1, difference is: poly weight part is 20 parts, and the weight part of EVA is 80 parts, and the weight part of tinting material is 0.6 part, and the weight part of EVA deodovization agent is 1 part.
Embodiment 7
Identical with embodiment 1, difference is: poly weight part is 10 parts, and the weight part of EVA is 90 parts, and the weight part of tinting material is 0.2 part, and the weight part of EVA deodovization agent is 0.6 part.
The children produced by above-described embodiment 1 ~ 7, Ms, cosmetically bath balls, detect according to company standard Q/SWWR005-2013, and its indices all meets the standard of company standard Q/SWWR005-2013.
To embodiment 1 to 7 finished product pliability, decontamination dirt ability, in shower comfort level and existing bath balls compare, comparative result is as shown in table 2 below.
Table 2
From shown in table 2, embodiment 1 and 2 compares with existing bath balls, in pliability, comfort level, have certain improvement.Embodiment 3, embodiment 4 compare with existing bath balls, improve very large in pliability, comfort level.Embodiment 5, embodiment 6 compare with existing bath balls, improve very large in pliability, comfort level.Embodiment 7 compares with existing bath balls, improves putting in place very much in pliability, comfort level.After use that children take a shower, Ms takes a shower, lady's beauty washes one's face, embodiment 7 is thought that each side all reaches ideal effect.
Therefore embodiment 7 is most preferred embodiment, and the weight part of Low Density Polyethylene is 10 parts, and the weight part of EVA is 90 parts, and the weight part of tinting material is 0.6 part, and the weight part of EVA deodovization agent is 0.6 part.
Illustrate:
Described children's bath balls pliability is: the soft < of general < is very soft
Soil removability is: general < is good
When children, Ms take a shower and old formula do not improve bath balls contrast comfort level: the fine < spy of good < is good
Lady's beauty washes one's face comfort level contrast: the general good < of < is fine.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalents utilizing specification sheets of the present invention and accompanying drawing content to do, or be directly or indirectly used in relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (7)
1. children, Ms, cosmetically a bath balls, is characterized in that, comprises the component of following weight part:
Described poly relative density is 0.925, and degree of crystallinity is 55 ~ 65%;
The relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85.
2. children according to claim 1, Ms, cosmetically bath balls, is characterized in that: the weight part of described tinting material is 0.2 part, and the weight part of described EVA deodovization agent is 0.6 part.
3. children according to claim 1, Ms, cosmetically bath balls, is characterized in that: the relative density of described EVA is 0.935, and glossiness is 82.
4. children, Ms, cosmetically a bath balls production technique, is characterized in that, comprising:
By the EVA deodovization agent mixing and stirring of the EVA of the polyethylene of 10 ~ 70 weight parts, 30 ~ 90 weight parts, the tinting material of 0.2 ~ 0.7 weight part and 0.3 ~ 1 weight part, described poly relative density is 0.925, and degree of crystallinity is 55 ~ 65%; The relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85, and churning time is 5 ~ 10min;
The material be stirred is carried out heat fused, mould goes out net and cooling shaping;
By the material after cooling shaping successively by traction, drying, rolling, cutting, roll after make bath balls.
5. children according to claim 4, Ms, cosmetically bath balls production technique, it is characterized in that: described heat fused is carried out in net puller, net puller main frame is divided into five sections to heat, and one section of Heating temperature is 80 ~ 120 DEG C, and heat-up time is 80 ~ 100min; Two sections of Heating temperatures are 120 ~ 140 DEG C, and heat-up time is 80 ~ 100min; Three sections of Heating temperatures are 150 ~ 200 DEG C, and heat-up time is 80 ~ 100min; Four sections of Heating temperatures are 180 ~ 230 DEG C, and heat-up time is 100 ~ 120min; Five sections of Heating temperatures are 200 ~ 240 DEG C, and heat-up time is 100 ~ 120min; After main frame five sections of temperature all reach design temperature, reinstall the material be stirred and carry out heat fused.
6. children according to claim 4, Ms, cosmetically bath balls production technique, is characterized in that: the weight part of described tinting material is 0.2 part, and the weight part of described EVA deodovization agent is 0.6 part.
7. children according to claim 4, Ms, cosmetically bath balls production technique, is characterized in that: the relative density of described EVA is 0.935, and glossiness is 82.