CN105839224A - Fibers for manufacturing toilet soap string bags and preparation method for fibers - Google Patents
Fibers for manufacturing toilet soap string bags and preparation method for fibers Download PDFInfo
- Publication number
- CN105839224A CN105839224A CN201610446410.8A CN201610446410A CN105839224A CN 105839224 A CN105839224 A CN 105839224A CN 201610446410 A CN201610446410 A CN 201610446410A CN 105839224 A CN105839224 A CN 105839224A
- Authority
- CN
- China
- Prior art keywords
- fiber
- preparation
- density polyethylene
- low density
- follows
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of textile materials and particularly relates to fibers for manufacturing toilet soap string bags. The fibers for the string bags are prepared from the ingredients in percentage by weight: 0 to 100% of low-density polyethylene, 0 to 100% of ethylene-vinyl acetate copolymer, 0 to 100% of linear low-density polyethylene and 0 to 100% of nylon. According to the fibers, the raw materials are wide in source, the preparation cost is low, the required fibers are prepared through carrying out washing, crushing and spinning treatment, the preparation method is simple, convenient and pollution-free and is easy to operate, low in cost, good in wear resistance and high in safety, and no injury to skin is caused.
Description
Technical field
The present invention relates to textile material technical field, particularly to a kind of fiber for manufacturing the perfumed soap string bag and preparation method thereof.
Background technology
At present, the perfumed soap that market is purchased is all to use non-returnable container bag, and the splendid attire of perfumed soap mainly uses soap box, contains with soap box and uses perfumed soap, uses inconvenience when perfumed soap residue is less, often to discard；After moistening due to perfumed soap at ordinary times, the adhesion on soap box all can cause the waste of perfumed soap, is also unfavorable for the cleaning of perfumed soap self.Especially containing with soap box and use perfumed soap, in use operating inconvenience, easy landing etc., extremely inconvenience, consuming excessively of perfumed soap is not only the waste to perfumed soap itself, it is often more important that to the waste of the environment such as water resource, pollutes and destroys.
Application number 201110008615.5 discloses a kind of porous nylon fiber and its production and use, this porous nylon fiber is made up of the housing department of solid core and porous, it is 5% ~ 45% that this porous nylon fiber has porosity, and average pore size is 8 ~ 2nm, and specific surface area is 1.5 ~ 15m2/g.This porous nylon fiber can be used as insulation material；But prepared material preparation complexity, and have heavy-metal residual, it is not suitable for use in the fibrous material of the perfumed soap string bag.
Application number 200610037304.0 discloses a kind of Atnistatic neylon fiber and preparation method thereof, this Atnistatic neylon fiber includes the nylon 6 slice of 89 ~ 96 parts, the polymer type antistatic agent of 3 ~ 10 parts, processing aid in terms of parts by weight, in high-speed stirring mixer, stirring mixing 30 minutes；Under nitrogen protective condition, gains are put in melt spinning machine, at 265 DEG C ~ 275 DEG C, carry out spinning, prepare Atnistatic neylon fiber.But this nylon fiber there is insalubrious auxiliary agent remain, be not suitable for being used as directly and the fibrous material of the perfumed soap string bag of Body contact.
Summary of the invention
In order to solve the problems referred to above, the invention discloses the fiber of a kind of perfumed soap string bag, be made up of low density polyethylene (LDPE), ethylene-vinyl acetate copolymer, linear low density polyethylene (LLDPE), nylon, the percentage by weight of each component is, low density polyethylene (LDPE): 0 ~ 100%；Ethylene-vinyl acetate copolymer: 0 ~ 100%；Linear low density polyethylene (LLDPE): 0 ~ 100%；Nylon: 0 ~ 100%.
Further, the percentage by weight of each component of described fiber is most preferably: low density polyethylene (LDPE): 25%；Ethylene-vinyl acetate copolymer: 25%；Linear low density polyethylene (LLDPE): 25%；Nylon: 25%.
Another object of the present invention is to the preparation method of the open fiber for manufacturing the perfumed soap string bag, its preparation process includes:
Step S01: by low density polyethylene (LDPE), ethylene-vinyl acetate copolymer, linear low density polyethylene (LLDPE), nylon is through cleaning and is dried；
Step S02: material step S01 prepared carries out coarse crushing, obtains little particle；
Step S03: the little particle of step S02 gained is added pure water and is mixed into suspension, broken through fine powder, obtain particulate；
Step S04: by the particulate of step S03 gained under nitrogen protective condition, insert spinning in melt spinning machine, obtain string bag fiber.
Further, in step S01, described cleaning is particularly as follows: under normal temperature and pressure conditions, rinse 15 minutes ~ 30 minutes with giant.
Further, in step S01, described be dried particularly as follows: in atmospheric conditions, be heated to 50 DEG C ~ 60 DEG C forced air dryings 6 hours ~ 8 hours.
Further, in step S02, described little particle is particularly as follows: little particle that length dimension is 600 μm ~ 700 μm.
Further, in step S03, described addition pure water is particularly as follows: addition is little particle weight 10 times of pure water.
Further, described fine powder is broken particularly as follows: pulverize 2 hours ~ 3 hours with ultrasonic grinder.
Further, in step S03, described particulate is particularly as follows: diameter and size are both less than the particulate of 10 μm.
Further, in step S04, described spinning is particularly as follows: under the conditions of 250 DEG C ~ 260 DEG C, be woven into the fiber of a diameter of 0.1mm.
This inorfil filtering paper has the advantage that
Low density polyethylene (LDPE) that perfumed soap string bag fiber prepared by the present invention is used, ethylene-vinyl acetate copolymer, linear low density polyethylene (LLDPE), nylon wide material sources, cheap, process make required fiber through over cleaning, pulverizing, spinning, preparation method is simple and convenient, it is easy to operation, low cost, pollution-free, wearability is good, and security is high, is difficult to damage skin.
Detailed description of the invention
It should be noted that in the case of not conflicting, the embodiment in the application and the feature in embodiment can be mutually combined.The present invention is described in detail below in conjunction with embodiment.
Embodiment
1
A kind of fiber for manufacturing the perfumed soap string bag, its raw material components includes:
Low density polyethylene (LDPE): 25g；Ethylene-vinyl acetate copolymer: 25g；Linear low density polyethylene (LLDPE): 25g；Nylon: 25g.
Its preparation method comprises the following steps:
Step S01: by low density polyethylene (LDPE), ethylene-vinyl acetate copolymer, linear low density polyethylene (LLDPE), nylon under normal temperature and pressure conditions, rinses the cleaning of 20 minutes with giant, and in atmospheric conditions, through 56 DEG C of forced air dryings 6.5 hours.
Step S02: material step S01 prepared carries out coarse crushing, obtains the little particle that length dimension is 670 μm.
Step S03: the little particle of step S02 gained is added 1kg pure water and is mixed into suspension, by ultrasonic grinder fine powder broken 2.5 hours, obtains diameter and size is both less than the particulate of 10 μm；
Step S04: by the particulate of step S03 gained under nitrogen protective condition, insert in melt spinning machine, under the conditions of 256 DEG C, is woven into the fiber of a diameter of 0.1mm.
Embodiment
2
A kind of fiber for manufacturing the perfumed soap string bag, its raw material components includes:
Low density polyethylene (LDPE): 100g.
Its preparation method comprises the following steps:
Step S01: by low density polyethylene (LDPE) under normal temperature and pressure conditions, rinses the cleaning of 15 minutes with giant, and in atmospheric conditions, through 50 DEG C of forced air dryings 6 hours.
Step S02: material step S01 prepared carries out coarse crushing, obtains the little particle that length dimension is 600 μm.
Step S03: the little particle of step S02 gained is added 1kg pure water and is mixed into suspension, by ultrasonic grinder fine powder broken 2 hours, obtains diameter and size is both less than the particulate of 10 μm；
Step S04: by the particulate of step S03 gained under nitrogen protective condition, insert in melt spinning machine, under the conditions of 250 DEG C, is woven into the fiber of a diameter of 0.1mm.
Embodiment
3
A kind of fiber for manufacturing the perfumed soap string bag, its raw material components includes:
Ethylene-vinyl acetate copolymer: 100g.
Its preparation method comprises the following steps:
Step S01: by ethylene-vinyl acetate copolymer under normal temperature and pressure conditions, rinses the cleaning of 30 minutes with giant, and in atmospheric conditions, through 60 DEG C of forced air dryings 8 hours.
Step S02: material step S01 prepared carries out coarse crushing, obtains the little particle that length dimension is 700 μm.
Step S03: the little particle of step S02 gained is added 1kg pure water and is mixed into suspension, by ultrasonic grinder fine powder broken 3 hours, obtains diameter and size is both less than the particulate of 10 μm；
Step S04: by the particulate of step S03 gained under nitrogen protective condition, insert in melt spinning machine, under the conditions of 260 DEG C, is woven into the fiber of a diameter of 0.1mm.
Embodiment
4
A kind of fiber for manufacturing the perfumed soap string bag, its raw material components includes:
Linear low density polyethylene (LLDPE): 100g.
Its preparation method comprises the following steps:
Step S01: by linear low density polyethylene (LLDPE) under normal temperature and pressure conditions, rinses the cleaning of 30 minutes with giant, and in atmospheric conditions, through 55 DEG C of forced air dryings 7 hours.
Step S02: material step S01 prepared carries out coarse crushing, obtains the little particle that length dimension is 650 μm.
Step S03: the little particle of step S02 gained is added 1kg pure water and is mixed into suspension, by ultrasonic grinder fine powder broken 2.5 hours, obtains diameter and size is both less than the particulate of 10 μm；
Step S04: by the particulate of step S03 gained under nitrogen protective condition, insert in melt spinning machine, under the conditions of 255 DEG C, is woven into the fiber of a diameter of 0.1mm.
Embodiment
5
A kind of fiber for manufacturing the perfumed soap string bag, its raw material components includes:
Nylon: 100g.
Its preparation method comprises the following steps:
Step S01: by nylon under normal temperature and pressure conditions, rinses the cleaning of 30 minutes with giant, and in atmospheric conditions, through 54 DEG C of forced air dryings 6.5 hours.
Step S02: material step S01 prepared carries out coarse crushing, obtains the little particle that length dimension is 660 μm.
Step S03: the little particle of step S02 gained is added 1kg pure water and is mixed into suspension, by ultrasonic grinder fine powder broken 2.5 hours, obtains diameter and size is both less than the particulate of 10 μm；
Step S04: by the particulate of step S03 gained under nitrogen protective condition, insert in melt spinning machine, under the conditions of 253 DEG C, is woven into the fiber of a diameter of 0.1mm.
Experimental example
The material using the present embodiment 1 ~ 5 is tested, and performance comparison result is as shown in table 1 below:
Table 1 performance comparison table
The foregoing is only embodiments of the invention and experimental example, be not limited to the present invention, for a person skilled in the art, the present invention can have various modifications and variations.All within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.
Claims (10)
1., for manufacturing a fiber for the perfumed soap string bag, it is made up of low density polyethylene (LDPE), ethylene-vinyl acetate copolymer, linear low density polyethylene (LLDPE), nylon, it is characterised in that the percentage by weight of each component is, low density polyethylene (LDPE): 0 ~ 100%；Ethylene-vinyl acetate copolymer: 0 ~ 100%；Linear low density polyethylene (LLDPE): 0 ~ 100%；Nylon: 0 ~ 100%.
Fiber the most according to claim 1, it is characterised in that the percentage by weight of each component is: low density polyethylene (LDPE): 25%；Ethylene-vinyl acetate copolymer: 25%；Linear low density polyethylene (LLDPE): 25%；Nylon: 25%.
3. the preparation method of a fiber according to claim 1, it is characterised in that its preparation process includes:
Step S01: by low density polyethylene (LDPE), ethylene-vinyl acetate copolymer, linear low density polyethylene (LLDPE), nylon is through cleaning and is dried；
Step S02: material step S01 prepared carries out coarse crushing, obtains little particle；
Step S03: the little particle of step S02 gained is added pure water and is mixed into suspension, broken through fine powder, obtain particulate；
Step S04: by the particulate of step S03 gained under nitrogen protective condition, insert spinning in melt spinning machine, obtain string bag fiber.
The preparation method of fiber the most according to claim 3, it is characterised in that in step S01, described cleaning is particularly as follows: under normal temperature and pressure conditions, rinse 15 minutes ~ 30 minutes with giant.
The preparation method of fiber the most according to claim 3, it is characterised in that in step S01, described be dried particularly as follows: in atmospheric conditions, be heated to 50 DEG C ~ 60 DEG C forced air dryings 6 hours ~ 8 hours.
The preparation method of fiber the most according to claim 3, it is characterised in that in step S02, described little particle is particularly as follows: little particle that length dimension is 600 μm ~ 700 μm.
The preparation method of fiber the most according to claim 3, it is characterised in that in step S03, described addition pure water is particularly as follows: addition is little particle weight 10 times of pure water.
The preparation method of fiber the most according to claim 3, it is characterised in that in step S03, described fine powder is broken particularly as follows: pulverize 2 hours ~ 3 hours with ultrasonic grinder.
The preparation method of fiber the most according to claim 3, it is characterised in that in step S03, described particulate is particularly as follows: diameter and size are both less than the particulate of 10 μm.
The preparation method of fiber the most according to claim 3, it is characterised in that in step S04, described spinning is particularly as follows: under the conditions of 250 DEG C ~ 260 DEG C, be woven into the fiber of a diameter of 0.1mm.