CN104448515A - Bathing ball or strip and production process thereof - Google Patents
Bathing ball or strip and production process thereof Download PDFInfo
- Publication number
- CN104448515A CN104448515A CN201410618021.XA CN201410618021A CN104448515A CN 104448515 A CN104448515 A CN 104448515A CN 201410618021 A CN201410618021 A CN 201410618021A CN 104448515 A CN104448515 A CN 104448515A
- Authority
- CN
- China
- Prior art keywords
- eva
- bar
- bath balls
- heat
- weight part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a bathing ball or strip and a production process thereof. The production process concretely comprises the following steps: uniformly stirring the following raw materials in parts by weight: 100 parts of EVA, 0.2-0.7 part of colorant and 0.3-1 part of EVA smell removal agent, wherein the relative density of the EVA is 0.93-0.94, the glossiness of EVA is 82-85, and the stirring time is 5-10min; carrying out melting by heating, net exiting by a die and setting by cooling on the stirred material; and sequentially carrying out traction, drying, reeling, shearing and rolling on the material after setting by cooling to prepare the bathing ball or strip. The product prepared by using the production process has a compact structure, is soft, fine and smooth, is good in elasticity, beautiful in appearance, strong in fouling removing capability, durable in use, high in product added value, simple in production process, easy in operation of the production process and low in production energy consumption, can not deform and does not have peculiar smell.
Description
Technical field
The present invention relates to daily necessities technical field, is a kind of bath balls, bar and production technique thereof specifically.
Background technology
Bath balls, bar are a kind of bath articles very conventional in the modern life, steaming Saunas or squeezing a small amount of body wash when having a bath on bath balls, bar, rub with the hands gently and can produce a large amount of foams, are the best instruments that body wash bubbles.It is not only both artistic and practical, and the weaving structure of its uniqueness is used as the dirt of having a bath and thoroughly can clean skin and skin sweat is greasy, makes skin tender, smooth.What existing bath balls, bar generally adopted is polyethylene material, production technique roughly as shown in Figure 1: polyethylene, tinting material are stirred, then by mixture heat fused, mould goes out net, cooling shaping, traction, the dehydration of heating poach and rolling cutting, roll to obtain finished product by hand.There is following defect in existing bath balls, bar and production technique thereof: 1, product mesh is too thick, loosely organized not tight, yielding, poor flexibility, and product specification is low, and added value is low; 2, energy waste is large, especially heats poach link, needs the electric energy of at substantial to heat, do not meet the enterprise development demand of current low power consumption and low cost.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, technical problem to be solved by this invention is to provide bath balls, bar and the production technique thereof that a kind of product quality is high, production cost is low.
In order to solve the problems of the technologies described above, the technical solution used in the present invention one is:
A kind of bath balls, bar, comprise the component of following weight part:
EVA 100 parts,
Tinting material 0.2 ~ 0.7 part,
EVA deodovization agent 0.3 ~ 1 part,
The relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85.
Bath balls provided by the invention, bar, be different from mesh existing for existing bath balls, bar thick, loosely organized not tight, yielding, poor flexibility, product specification are low, added value is low waits quality defect, there is following beneficial effect: close structure, soft exquisiteness, good springiness, indeformable, attractive in appearance, free from extraneous odour, the dirty ability of decontamination are strong, durable in use, added value of product is high, meets the market requirement of human consumer to high-quality bath balls, bar well.
In order to solve the problems of the technologies described above, the technical solution used in the present invention two is:
A kind of bath balls, bar production technique, comprising:
By the EVA deodovization agent mixing and stirring of the tinting material of the EVA of 100 weight parts, 0.2 ~ 0.7 weight part and 0.3 ~ 1 weight part, the relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85, and churning time is 5 ~ 10min;
The material be stirred is carried out heat fused, mould goes out net and cooling shaping;
By the material after cooling shaping successively by traction, drying, rolling, cutting, roll after make bath balls or shower bar.
Bath balls provided by the invention, bar production technique, have following beneficial effect:
1, production technique is simple to operation, and production efficiency is high, is very applicable to large-scale industrial production;
2, production energy consumption significantly reduces, and production cost is low, has agreed with modern enterprise well to growth requirement that is energy-saving and cost-reducing and low cost high yield;
3, obtained product structure closely, soft exquisiteness, good springiness, indeformable, attractive in appearance, free from extraneous odour, the dirty ability of decontamination are strong, durable in use, and added value of product is high, meets the market requirement of human consumer to high-quality bath balls, bar well.
Accompanying drawing explanation
Figure 1 shows that the schematic flow sheet of existing bath balls, bar production technique.
Figure 2 shows that the schematic flow sheet of the bath balls of the embodiment of the present invention, bar production technique.
Embodiment
By describing technology contents of the present invention in detail, realized object and effect, accompanying drawing is coordinated to be explained below in conjunction with embodiment.
The design of most critical of the present invention is: utilize chemical property that EVA material is excellent as high tenacity, high resilience, and coordinate special tinting material and EVA deodovization agent, make the bath balls that production obtains, bar possesses close structure, soft fine and smooth, good springiness, indeformable, attractive in appearance, free from extraneous odour, decontamination dirt ability is strong, the fine quality such as durable in use, meet human consumer well to high-quality bath balls, the market requirement of bar, and utilize above-mentioned raw materials to produce bath balls, during bar, without the need to product being made to possess enough pliabilitys through heating poach, greatly reduce the production energy consumption of product, agree with modern enterprise well to growth requirement that is energy-saving and cost-reducing and low cost high yield.
Concrete, the bath balls of the embodiment of the present invention, bar, comprise the component of following weight part:
EVA 100 parts,
Tinting material 0.2 ~ 0.7 part,
EVA deodovization agent 0.3 ~ 1 part,
The relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85.
In the above-described embodiments, tinting material to make material manifest the material designing and need color, and tinting material can be divided into powdery, pasty state, paste by its form.Wherein coloured powdery agent is, after tinting material is ground to form fine powder, do not add process and be directly used in painted.The dry mix that coloured powdery agent is applicable to PE, PC, PP, ABS, PC extrude draw mould painted.Pasty state or cream colored agent are dispersed in the volatile liquids such as softening agent makes paste or paste, and it is usually used on the goods such as urethane, ring benzene synthetic glass.Preferably powdered tinting material of the present invention, it comprises the colors such as red, yellow, blue, orange, purple, green, is more preferably the agent of purple coloured powdery.
In the above-described embodiments, described EVA deodovization agent is a kind of special deodovization agent of tasteless close ethylene-vinyl acetate copolymer, for the chemical structure feature of EVA, containing the chemical functional group that various active is extremely strong.To EVA and the various EVA goods various smell small molecules that EVA resin itself and various additive may occur in processing and use, comprise acids, ester class, Ammonia, hydrocarbon polymer and other scent molecules and there is good chemical action ability.EVA deodovization agent, through special processing, so be easy to disperse in EVA or EVA goods and do not change the chemical structure of EVA, has excellent thermotolerance, can use below 400 DEG C.EVA deodovization agent itself is nonpoisonous and tasteless and heavy metal and content of halogen are all less than European Union ROHS standard, has environmental protection usage quantity few, the advantages such as taste removal is effective.
From foregoing description, beneficial effect of the present invention is: close structure, soft exquisiteness, good springiness, indeformable, attractive in appearance, free from extraneous odour, the dirty ability of decontamination are strong, durable in use, added value of product is high, meets the market requirement of human consumer to high-quality bath balls, bar well.
Further, the weight part of described tinting material is 0.2 part, and the weight part of described EVA deodovization agent is 0.6 part.
Further, the relative density of described EVA is 0.935, and glossiness is 82.
Concrete, please refer to shown in Fig. 2, the bath balls of the embodiment of the present invention, bar production technique, comprising:
By the EVA deodovization agent mixing and stirring of the tinting material of the EVA of 100 weight parts, 0.2 ~ 0.7 weight part and 0.3 ~ 1 weight part, the relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85, and churning time is 5 ~ 10min;
The material be stirred is carried out heat fused, mould goes out net and cooling shaping;
By the material after cooling shaping successively by traction, drying, rolling, cutting, roll after make bath balls or shower bar.
From foregoing description, beneficial effect of the present invention is:
1, production technique is simple to operation, and production efficiency is high, is very applicable to large-scale industrial production;
2, production energy consumption significantly reduces, and production cost is low, has agreed with modern enterprise well to growth requirement that is energy-saving and cost-reducing and low cost high yield;
3, obtained product structure closely, soft exquisiteness, good springiness, indeformable, attractive in appearance, free from extraneous odour, the dirty ability of decontamination are strong, durable in use, and added value of product is high, meets the market requirement of human consumer to high-quality bath balls, bar well.
Further, described heat fused is carried out in net puller, and net puller is all net pullers being applicable to producing bath balls.Before use can first by main frame heat-flash 1.5 ~ 2 hours.Net puller main frame is divided into five sections to heat, shown in table 1 specific as follows: one section of Heating temperature is 80 ~ 120 DEG C, and heat-up time is 80 ~ 100min; Two sections of Heating temperatures are 120 ~ 140 DEG C, and heat-up time is 80 ~ 100min; Three sections of Heating temperatures are 150 ~ 200 DEG C, and heat-up time is 80 ~ 100min; Four sections of Heating temperatures are 180 ~ 230 DEG C, and heat-up time is 100 ~ 120min; Five sections of Heating temperatures are 200 ~ 240 DEG C, and heat-up time is 100 ~ 120min; After main frame five sections of temperature all reach design temperature, reinstall the material be stirred and carry out heat fused.Time, when reaching 1.5 ~ 2h, is extruded a strip-shaped materials, starts rotating die head.Wherein rotating die head rotating speed is according to the adjustment of guipure sample, can be fast or slow, mainly forms point of crossing, namely make interior external mold rotating, strand material shape is reticulated and enters cooling trough, cooling shaping, take turns traction by one.Wherein an effect taking turns traction is that guipure is drawn from cold rinse bank, take turns traction by two again, wherein two effects taking turns traction mesh bag are entered dehydrate, and after dehydration, guipure is by after plait mill rolling, cutting or with full-automatic cutting machine cutting by hand, then manually or machinery roll and get product.
Table 1
| Each section of main frame | One section | Two sections | Three sections | Four sections | Five sections |
| Heating temperature DEG C | 80～120 | 120～140 | 150～200 | 180～230 | 200～240 |
| Heat-up time min | 80～100 | 80～100 | 80～100 | 100～120 | 100～120 |
Further, the weight part of described tinting material is 0.2 part, and the weight part of described EVA deodovization agent is 0.6 part.
Further, the relative density of described EVA is 0.935, and glossiness is 82.
Embodiment 1
A production technique for bath balls, shower bar, specifically comprises the following steps:
Step one: the tinting material of the EVA of 100 weight parts, 0.2 weight part and the EVA deodovization agent of 0.3 weight part are stirred, the relative density of described EVA is 0.935, and glossiness is 82.
Step 2: the material obtained in described step one is carried out heat fused, mould goes out net and cooling shaping.
Step 3: by the material after cooling shaping in described step 2 successively by traction, drying, rolling, cutting, roll after make bath balls or shower bar.
Embodiment 2
A production technique for bath balls, shower bar, specifically comprises the following steps:
Step one: the tinting material of the EVA of 100 weight parts, 0.7 weight part and the EVA deodovization agent of 1 weight part are stirred, the relative density of described EVA is 0.935, and glossiness is 82.
Step 2: the material obtained in described step one is carried out heat fused, mould goes out net and cooling shaping.
Step 3: by the material after cooling shaping in described step 2 successively by traction, drying, rolling, cutting, roll after make bath balls or shower bar.
Embodiment 3
A production technique for bath balls, shower bar, specifically comprises the following steps:
Step one: the tinting material of the EVA of 100 weight parts, 0.2 weight part and the EVA deodovization agent of 0.6 weight part are stirred, the relative density of described EVA is 0.935, and glossiness is 82.
Step 2: the material obtained in described step one is carried out heat fused, mould goes out net and cooling shaping.
Step 3: by the material after cooling shaping in described step 2 successively by traction, drying, rolling, cutting, roll after make bath balls or shower bar.
Bath balls, the shower bar produced by above-described embodiment 1 ~ 3, detect according to company standard Q/SWWR005-2013, and its indices all meets the standard of company standard Q/SWWR005-2013.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalents utilizing specification sheets of the present invention and accompanying drawing content to do, or be directly or indirectly used in relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (7)
1. bath balls, a bar, is characterized in that, comprises the component of following weight part:
EVA 100 parts,
Tinting material 0.2 ~ 0.7 part,
EVA deodovization agent 0.3 ~ 1 part,
The relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85.
2. bath balls according to claim 1, bar, is characterized in that: the weight part of described tinting material is 0.2 part, and the weight part of described deodovization agent is 0.6 part.
3. bath balls according to claim 1, bar, is characterized in that: the relative density of described EVA is 0.935, and glossiness is 82.
4. bath balls, a bar production technique, is characterized in that, comprising:
By the EVA deodovization agent mixing and stirring of the tinting material of the EVA of 100 weight parts, 0.2 ~ 0.7 weight part and 0.3 ~ 1 weight part, the relative density of described EVA is 0.93 ~ 0.94, and glossiness is 82 ~ 85, and churning time is 5 ~ 10min;
The material be stirred is carried out heat fused, mould goes out net and cooling shaping;
By the material after cooling shaping successively by traction, drying, rolling, cutting, roll after make bath balls or shower bar.
5. bath balls according to claim 4, bar production technique, is characterized in that: described heat fused is carried out in net puller, net puller main frame is divided into five sections to heat, and one section of Heating temperature is 80 ~ 120 DEG C, and heat-up time is 80 ~ 100min; Two sections of Heating temperatures are 120 ~ 140 DEG C, and heat-up time is 80 ~ 100min; Three sections of Heating temperatures are 150 ~ 200 DEG C, and heat-up time is 80 ~ 100min; Four sections of Heating temperatures are 180 ~ 230 DEG C, and heat-up time is 100 ~ 120min; Five sections of Heating temperatures are 200 ~ 240 DEG C, and heat-up time is 100 ~ 120min; After main frame five sections of temperature all reach design temperature, reinstall the material be stirred and carry out heat fused.
6. bath balls according to claim 4, bar production technique, is characterized in that: the weight part of described tinting material is 0.2 part, and the weight part of described EVA deodovization agent is 0.6 part.
7. bath balls according to claim 4, bar production technique, is characterized in that: the relative density of described EVA is 0.935, and glossiness is 82.