CN104446639A - 一种矩形孔轻质烧结页岩砖 - Google Patents
一种矩形孔轻质烧结页岩砖 Download PDFInfo
- Publication number
- CN104446639A CN104446639A CN201410761968.6A CN201410761968A CN104446639A CN 104446639 A CN104446639 A CN 104446639A CN 201410761968 A CN201410761968 A CN 201410761968A CN 104446639 A CN104446639 A CN 104446639A
- Authority
- CN
- China
- Prior art keywords
- shale brick
- brick
- parts
- rectangular openings
- shale
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种矩形孔轻质烧结页岩砖，其中，包括：该矩形孔轻质烧结页岩砖组成原料的重量分数组成为：木屑20-30份、添加剂5-12份、页岩55-65份。本发明所述矩形孔轻质烧结页岩砖由于原材料添加了适量的木屑，减轻了矩形孔页岩多孔砖的自重，最低强度为5MPa，满足规范的强度要求，可应用于非承重墙，由于砖坯中木屑有机质纤维的抗拉作用，所以比普通矩形孔烧结页岩砖的裂缝长度小、裂缝数量少、保温隔热、隔声性能好、耐久性良好、经济效益高，具有良好广阔的应用前景。
Description
技术领域
本发明涉及新型墙体材料，特别地，涉及一种矩形孔轻质烧结页岩砖。
背景技术
目前现有的新型墙体材料主要是向着环保、节能、绿色建筑材料方向发展，主要包括砌块、砖、板这三个方向。目前市面上的现有的新型墙体材料包括加气混凝土砌块、混凝土多孔砖、普通混凝土小型空心砌块以及砖新型墙板等。
其中，加气混凝土砌块存在空袭率高，吸水性大，其表面容易生成粉末，不能与砂浆很好的粘结，而且其表面强度低，容易出现缺角和裂缝，加大运输的困难等缺点。普通混凝土小型空心砌块还具有易变形、易断裂、易出现漏和热的建筑质量问题、不能进行砍削、对施工技术要求较高等缺点。
混凝土多孔砖其混凝土的裂缝问题、自重大、水泥用量大、热工性能较差等诸多缺点。
新型墙板具有单位面积质量小、表面平整、抗震性能好等优点，并且施工过程中基本是干燥的环境操作，使得施工现场干净卫生，效率高。但是墙板的种类较多，性能差异大，施工技术差异较大，对新型墙板进行二次施工比较困难，所以新型墙板的发展比较缓慢，在市场的占有率较低。
发明内容
本发明目的在于提供一种矩形孔轻质烧结页岩砖，以解决现有技术中现有的新型墙体材料包括加气混凝土砌块、混凝土多孔砖、普通混凝土小型空心砌块以及砖新型墙板等易变形、易断裂、容易出现缺角和裂缝、对施工技术要求较高等的问题。
为实现上述目的，本发明提供一种矩形孔轻质烧结页岩砖，其中，包括：该矩形孔轻质烧结页岩砖组成原料的重量分数组成为：木屑20-30份、添加剂5-12份、页岩55-65份。
进一步地，本发明提供一种矩形孔轻质烧结页岩砖，其中，该矩形孔轻质烧结页岩砖组成原料的重量分数组成为：木屑30份、添加剂8份、页岩62份。
进一步地，本发明提供一种矩形孔轻质烧结页岩砖，其中，所述添加剂是内燃煤。
本发明具有以下有益效果：所述矩形孔轻质烧结页岩砖由于原材料添加了适量的木屑，减轻了矩形孔页岩多孔砖的自重，最低强度为5MPa，满足规范的强度要求，可应用于非承重墙，由于砖坯中木屑有机质纤维的抗拉作用，所以比普通矩形孔烧结页岩砖的裂缝长度小、裂缝数量少、保温隔热、隔声性能好、耐久性良好、经济效益高、既可具有非烧结类墙材中加气混凝土砌块的保温性好、容重低、强度满足隔墙要求等优点，又可具有烧结类墙材中实心粘土砖的经高温烧结后的热稳定性好、热胀冷缩率较低、抗风化性好、吸水率低、保温效果及隔音效果好、墙体不开裂等优点，具有良好广阔的应用前景。
具体实施方式
其中，本发明所述矩形孔轻质烧结页岩砖包括：该矩形孔轻质烧结页岩砖组成原料的重量分数组成为：木屑20-30份、添加剂5-12份、页岩55-65份。
本优选实施例提供的矩形孔轻质烧结页岩砖，其具体实现过程如下，其中，该矩形孔轻质烧结页岩砖组成原料最优配比的重量分数组成为：木屑30份、添加剂8份、页岩62份。木屑占原材料的掺比量为30份，经试验证明木屑占原材料的最佳掺比量为30份时，使得矩形孔轻质烧结页岩砖可以达到非承重墙的强度，抗压强度较高，受力性能好。
又，于上述实施例中，所述添加剂是内燃煤或者含铁和铝元素高的原料。
从以上的描述中，可以看出，本发明上述的实施例实现了如下技术效果：
本发明提供了一种矩形孔轻质烧结页岩砖，不仅具有非烧结类墙材中加气混凝土砌块的保温性好、容重低、强度满足隔墙要求等优点，还具有烧结类墙材中实心粘土砖的经高温烧结后的热稳定性好、热胀冷缩率较低、抗风化性好、吸水率低、保温效果及隔音效果好、墙体不开裂等优点，具有良好广阔的应用前景。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明；对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (3)
1.一种矩形孔轻质烧结页岩砖，其特征在于，包括：该矩形孔轻质烧结页岩砖组成原料的重量分数组成为：木屑20-30份、添加剂5-12份、页岩55-65份。
2.根据权利要求1所述的矩形孔轻质烧结页岩砖，其特征在于，该矩形孔轻质烧结页岩砖组成原料的重量分数组成为：木屑30份、添加剂8份、页岩62份。
3.根据权利要求1或2所述的矩形孔轻质烧结页岩砖，其特征在于，所述添加剂是内燃煤。