CN104446354A - Sericite ceramic wine bottle - Google Patents
Sericite ceramic wine bottle Download PDFInfo
- Publication number
- CN104446354A CN104446354A CN201410742268.2A CN201410742268A CN104446354A CN 104446354 A CN104446354 A CN 104446354A CN 201410742268 A CN201410742268 A CN 201410742268A CN 104446354 A CN104446354 A CN 104446354A
- Authority
- CN
- China
- Prior art keywords
- parts
- sericite
- wine bottle
- ceramic wine
- stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a sericite ceramic wine bottle. The sericite ceramic wine bottle is prepared from the following components in parts by weight: 25-34 parts of china stones, 15-24 parts of kaolin, 35-49 parts of sericite, 12-17 parts of quartz, 5-10 parts of illite, 4-9 parts of aventurine quartz and 1-3 parts of epidote. The rigidity of the prepared ceramic wine bottle is higher than that of common ceramic so that the sericite ceramic wine bottle is suitable for large-batch production.
Description
Technical field
The present invention relates to ceramic wine bottle field, more specifically, relate to a kind of sericite matter ceramic wine bottle.
Background technology
Sericite china is one of traditional daily porcelain of China, is a kind of hard-paste.This porcelain utilizes the character forming high-viscosity glass in porcelain stone after contained sericite melting, with itself containing quartzy feature, it has the general aspects of feldspathic china, and have transparency high and white in the characteristic of micro-general green grass or young crops, become the traditional style of hard paste porcelain and exclusive feature.
Summary of the invention
The object of this invention is to provide a kind of sericite matter ceramic wine bottle, its hardness comparatively conventional ceramic is higher, is applicable to produce in enormous quantities.
The object of the invention is achieved by the following technical programs:
A kind of sericite matter ceramic wine bottle is provided, is made up of each component of following weight fraction: porcelain stone 25 ~ 34 parts, kaolin 15 ~ 24 parts, sericite 35 ~ 49 parts, 12 ~ 17 parts, quartz, illite 5 ~ 10 parts, 4 ~ 9 parts, Dongling stone, pistacite 1 ~ 3 part.
Preferably, described sericite matter ceramic wine bottle is made up of each component of following weight fraction: porcelain stone 28 parts, kaolin 19 parts, sericite 42 parts, 14 parts, quartz, illite 8 parts, 7 parts, Dongling stone, pistacite 2 parts.
Sericite matter ceramic wine bottle of the present invention can traditionally be prepared.
Compared with prior art, the present invention has following beneficial effect:
The invention provides a kind of sericite matter ceramic wine bottle, hardness comparatively conventional ceramic is higher, is applicable to produce in enormous quantities.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of sericite matter ceramic wine bottle, be made up of each component of following weight fraction: porcelain stone 28 parts, kaolin 19 parts, sericite 42 parts, 14 parts, quartz, illite 8 parts, 7 parts, Dongling stone, pistacite 2 parts.
Embodiment 2
Present embodiment discloses a kind of sericite matter ceramic wine bottle, be made up of each component of following weight fraction: porcelain stone 25 parts, kaolin 15 parts, sericite 49 parts, 12 parts, quartz, illite 10 parts, 9 parts, Dongling stone, pistacite 1 part.
Embodiment 3
Present embodiment discloses a kind of sericite matter ceramic wine bottle, be made up of each component of following weight fraction: porcelain stone 34 parts, kaolin 24 parts, sericite 35 parts, 17 parts, quartz, illite 5 parts, 4 parts, Dongling stone, pistacite 3 parts.
Embodiment 4
Present embodiment discloses a kind of sericite matter ceramic wine bottle, be made up of each component of following weight fraction: porcelain stone 30 parts, kaolin 20 parts, sericite 39 parts, 15 parts, quartz, illite 6 parts, 6 parts, Dongling stone, pistacite 2 parts.
Embodiment 5
Present embodiment discloses a kind of sericite matter ceramic wine bottle, its preparation method comprises the following steps:
(1) by the arbitrary formula weighing of embodiment 1 ~ 4, through ball milling, sieving obtains mud, adopts traditional slip-casting shaping process to make bottle base substrate;
(2) base substrate obtained for step (1) is sent into kiln 1300 DEG C and fire 10 hours, obtain sericite matter ceramic wine bottle.
Comparatively conventional ceramic is higher for gained ceramic wine bottle hardness, and porcelain is pure white, and water-intake rate is low, transparence and thermally-stabilised good, is applicable to produce in enormous quantities.
Claims (2)
1. a sericite matter ceramic wine bottle, is characterized in that, is made up of each component of following weight fraction: porcelain stone 25 ~ 34 parts, kaolin 15 ~ 24 parts, sericite 35 ~ 49 parts, 12 ~ 17 parts, quartz, illite 5 ~ 10 parts, 4 ~ 9 parts, Dongling stone, pistacite 1 ~ 3 part.
2. sericite matter ceramic wine bottle according to claim 1, is characterized in that, is made up of each component of following weight fraction: porcelain stone 28 parts, kaolin 19 parts, sericite 42 parts, 14 parts, quartz, illite 8 parts, 7 parts, Dongling stone, pistacite 2 parts.