CN104388771A - 一种防开裂空调散热器铝合金片及其制备方法 - Google Patents

一种防开裂空调散热器铝合金片及其制备方法 Download PDF

Info

Publication number
CN104388771A
CN104388771A CN201410684166.XA CN201410684166A CN104388771A CN 104388771 A CN104388771 A CN 104388771A CN 201410684166 A CN201410684166 A CN 201410684166A CN 104388771 A CN104388771 A CN 104388771A
Authority
CN
China
Prior art keywords
aluminum alloy
temperature
alloy sheet
air conditioner
conditioner heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410684166.XA
Other languages
English (en)
Inventor
骆宣佐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd
Original Assignee
ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd filed Critical ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd
Priority to CN201410684166.XA priority Critical patent/CN104388771A/zh
Publication of CN104388771A publication Critical patent/CN104388771A/zh
Pending legal-status Critical Current

Abstract

一种防开裂空调散热器铝合金片，其含有的化学元素成分及其质量百分比为：Si0.8-1.4、Ti0.04-0.10、Fe0.10-0.15、Cu0.11-0.35、Mn0.58-0.95、P≤0.01、Ni0.02-0.05、Cr0.13-0.28、Pb0.02-0.05、剩余为Al。本发明铝合金片韧性好，能够有效防开裂，强度高，可以制作轻薄的散热片，成本低，散热效果好；本发明生产方法减少了铝合金成层、起皮、气泡、裂纹的现象，提高了成品率；本发明精炼剂精炼效果好，明显降低了气孔和夹渣现象。

Description

一种防开裂空调散热器铝合金片及其制备方法
技术领域
本发明涉及铝合金散热材料领域，尤其涉及一种防开裂空调散热器铝合金片及其制备方法。
背景技术
空调散热器是空调的关键部件，关系到空调的工作效率和使用寿命。而且随着家用空调小型化和降低制造成本的要求，空调箔翅片的厚度越来越薄，向着减薄、趋硬、高精的方向发展，要求有新的合金、新的加工技术和新的质量高度。空调箔翅片的加工精度要求高，要求铝箔具有良好的塑性和较高的强度。目前空调散热器铝箔主要存在机械性能差，如抗拉强度(140Rm/MPa)、屈服强度（100R0.2/MPa）、硬度（9-12度）较弱，导电性能差，导热性差，可塑性差等缺点。
铝合金散热片经常出现成层、起皮、气泡、裂纹的质量问题，取决于熔铸、挤压温度、挤压速度等加工工艺，因此需要改进散热片的生产工艺，来改善散热片的性能。
发明内容
本发明的目的在于提供一种防开裂空调散热器铝合金片及其制备方法，该铝合金片韧性好，能够有效防开裂，强度高，可以制作轻薄的散热片，成本低，散热效果好。
本发明的技术方案如下：
一种防开裂空调散热器铝合金片，其特征在于：其含有的化学元素成分及其质量百分比为：Si0.8-1.4、Ti0.04-0.10、Fe0.10-0.15、Cu0.11-0.35、Mn0.58-0.95、P≤0.01、Ni0.02-0.05、Cr0.13-0.28、Pb0.02-0.05、剩余为Al。
所述的防开裂空调散热器铝合金片的生产方法，其特征在于：
（1）配料，熔炼，温度为740-755℃，熔炼时间3.5-4个小时；
（2）精炼，温度为740-755℃，精炼剂用量为铝合金液重量的1.6%，精炼时间为26-30分钟，静置15-20分钟；
（3）铸造，采用50目高温陶瓷过滤板过滤铝液，再进行铸造，铝液温度为700-710℃，铸造后用20-25℃的水冷却和水温一致，送入均匀化炉内，在570-580℃下处理6-7个小时；
（4）挤压成型，挤压速度为2.0-3.7m/min，铸棒温度为495-520℃，模具温度为495-520℃，挤压筒温度为450-460℃；
（5）挤压成型后进行风冷淬火，冷却速度控制在4-6℃/S；
（6）拉伸矫直，拉伸率保持在0.8-1.4%；
（7）时效处理，时效温度为160-168℃，时间为8-9个小时，即得。
所述的防开裂空调散热器铝合金片的生产方法，其特征在于：所述精炼剂由下列重量份的原料制成：氟硼酸钾1-1.3、氟铝酸钾20-25、KCl22-27、SiCl4 1.5-3、CaF2 2-3、Na3AlF6 3.5-5.5、活性炭1-2、CCl4 0.5-1.3、CaO0.3-0.6、MgO0.6-0.8、纳米铝粉0.3-0.6、稀土0.2-0.3、乙醇15-20；制备方法为：将CaO、MgO、稀土、活性炭粉碎，过100目筛，与氟硼酸钾、氟铝酸钾、KCl、CaF2、Na3AlF6、乙醇混合，研磨20-30分钟，在150-170℃下烘干至绝干，喷雾干燥，再与其他剩余成分混合，研磨分散均匀，即得。
本发明的有益效果
本发明铝合金片韧性好，能够有效防开裂，强度高，可以制作轻薄的散热片，成本低，散热效果好；本发明生产方法减少了铝合金成层、起皮、气泡、裂纹的现象，提高了成品率；本发明精炼剂精炼效果好，明显降低了气孔和夹渣现象。
具体实施方式
一种防开裂空调散热器铝合金片，其含有的化学元素成分及其质量百分比为：Si0.8-1.4、Ti0.04-0.10、Fe0.10-0.15、Cu0.11-0.35、Mn0.58-0.95、P≤0.01、Ni0.02-0.05、Cr0.13-0.28、Pb0.02-0.05、剩余为Al。
所述的防开裂空调散热器铝合金片的生产方法：
（1）配料，熔炼，温度为748℃，熔炼时间3.8个小时；
（2）精炼，温度为748℃，精炼剂用量为铝合金液重量的1.6%，精炼时间为28分钟，静置18分钟；
（3）铸造，采用50目高温陶瓷过滤板过滤铝液，再进行铸造，铝液温度为705℃，铸造后用23℃的水冷却和水温一致，送入均匀化炉内，在575℃下处理6.5个小时；
（4）挤压成型，挤压速度为3m/min，铸棒温度为510℃，模具温度为510℃，挤压筒温度为455℃；
（5）挤压成型后进行风冷淬火，冷却速度控制在5℃/S；
（6）拉伸矫直，拉伸率保持在1.2%；
（7）时效处理，时效温度为165℃，时间为8.5个小时，即得。
所述精炼剂由下列重量份的原料制成：
实验数据
按照YS/T95.1标准，1122状态铝箔的抗拉强度为129MPa，伸长率20%，杯突值5.7mm。

Claims (3)

1.一种防开裂空调散热器铝合金片，其特征在于：其含有的化学元素成分及其质量百分比为：Si0.8-1.4、Ti0.04-0.10、Fe0.10-0.15、Cu0.11-0.35、Mn0.58-0.95、P≤0.01、Ni0.02-0.05、Cr0.13-0.28、Pb0.02-0.05、剩余为Al。
2.根据权利要求1所述的防开裂空调散热器铝合金片的生产方法，其特征在于：
（1）配料，熔炼，温度为740-755℃，熔炼时间3.5-4个小时；
（2）精炼，温度为740-755℃，精炼剂用量为铝合金液重量的1.6%，精炼时间为26-30分钟，静置15-20分钟；
（3）铸造，采用50目高温陶瓷过滤板过滤铝液，再进行铸造，铝液温度为700-710℃，铸造后用20-25℃的水冷却和水温一致，送入均匀化炉内，在570-580℃下处理6-7个小时；
（4）挤压成型，挤压速度为2.0-3.7m/min，铸棒温度为495-520℃，模具温度为495-520℃，挤压筒温度为450-460℃；
（5）挤压成型后进行风冷淬火，冷却速度控制在4-6℃/S；
（6）拉伸矫直，拉伸率保持在0.8-1.4%；
（7）时效处理，时效温度为160-168℃，时间为8-9个小时，即得。
3.根据权利要求2所述的防开裂空调散热器铝合金片的生产方法，其特征在于：所述精炼剂由下列重量份的原料制成：氟硼酸钾1-1.3、氟铝酸钾20-25、KCl22-27、SiCl4 1.5-3、CaF2 2-3、Na3AlF6 3.5-5.5、活性炭1-2、CCl4 0.5-1.3、CaO0.3-0.6、MgO0.6-0.8、纳米铝粉0.3-0.6、稀土0.2-0.3、乙醇15-20；制备方法为：将CaO、MgO、稀土、活性炭粉碎，过100目筛，与氟硼酸钾、氟铝酸钾、KCl、CaF2、Na3AlF6、乙醇混合，研磨20-30分钟，在150-170℃下烘干至绝干，喷雾干燥，再与其他剩余成分混合，研磨分散均匀，即得。
CN201410684166.XA 2014-11-25 2014-11-25 一种防开裂空调散热器铝合金片及其制备方法 Pending CN104388771A (zh)