CN104387830A - Architectural putty powder and preparation method thereof - Google Patents
Architectural putty powder and preparation method thereof Download PDFInfo
- Publication number
- CN104387830A CN104387830A CN201410633042.9A CN201410633042A CN104387830A CN 104387830 A CN104387830 A CN 104387830A CN 201410633042 A CN201410633042 A CN 201410633042A CN 104387830 A CN104387830 A CN 104387830A
- Authority
- CN
- China
- Prior art keywords
- parts
- putty powder
- raw material
- initiator
- building putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an architectural putty powder and a preparation method thereof, relating to the technical field of chemical raw materials. The preparation method comprises the following steps: reasonably proportioning calcium oxide, magnesium oxide, kieselguhr, talcum powder, methyl cellulose, an initiator, a surfactant and an assistant, carrying out mix processing, drying and pulverizing. The method has the advantages of convenient and simple preparation process, environmental protection, no pollution, accessible raw materials and low equipment investment, and is convenient for operation; and the prepared architectural putty powder has the advantages of favorable use effect, favorable derusting capacity, no toxic or side effect and high safety and reliability.
Description
Technical field
The present invention relates to industrial chemicals technical field, be specifically related to a kind of building putty powder and preparation method thereof.
Background technology
Putty powder is before the construction of paint class, the surperficial levelling powder material of pretreated one is carried out to construction surface, main purpose is filled the hole of construction surface and corrects the curve deviation of construction surface, lay a solid foundation for obtaining even, level and smooth lacquer painting, but the putty powder product existed on the market is at present a feast for the eyes, but what a kind of building putty powder can be inreal plays obvious effect, but also corresponding toxicity can be there is, affect HUMAN HEALTH.
Summary of the invention
It is high that technical problem to be solved by this invention is to provide a kind of intensity, and condense fast building putty powder and preparation method thereof.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of building putty powder, is characterized in that: the raw material composition comprising following weight part,
Calcium oxide 4-6 part, magnesium oxide 3-5 part, diatomite 10-20 part, talcum powder 10-20 part, methylcellulose gum 1-3, initiator 1-3 part, tensio-active agent 2-4 part, auxiliary agent 1-3 part.
Preferred weight part of each raw material is: 5 parts, calcium oxide, 4 parts, magnesium oxide, 15 parts, diatomite, talcum powder 15 parts, methylcellulose gum 2, initiator 2 parts, 3 parts, tensio-active agent, auxiliary agent 2 parts.
Described initiator is ammonium persulphate or Potassium Persulphate.
Described tensio-active agent is polyoxyethylene octylphenol ether, sulfo-succinic acid Soxylat A 25-7 nonyl phenol sodium salt, alkylphenol polyoxyethylene phosphoric acid ester and alkylphenol polyoxyethylene ammonium sulfate one wherein.
Described auxiliary agent is ripe rubber powder or ether of cellulose, or is both mixture.
Another object of the present invention prepares the method for building putty powder in the present invention, it is characterized in that: comprise the following steps:
A, select a stirred autoclave, the calcium oxide in raw material, diatomite, talcum powder, methylcellulose gum are added wherein, add and open stirring at low speed 20min
B, until step a stir terminate after, the magnesium oxide in raw material, initiator, tensio-active agent and auxiliary agent are all added in reactor, high-speed stirring is until solution mixes;
C, the raw material in step b poured out and puts into pulverizer, pulverize, then carry out being sieved into appointment fineness.
The invention has the beneficial effects as follows: the present invention is simply easy to prepare, environment friendly and pollution-free, raw material is easy to get, and facility investment is few, convenient operation, and the building putty powder result of use of preparation is good, and result of use is good, and no side effects is safe and reliable.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of building putty powder, comprises the raw material composition of following weight part,
Calcium oxide 4kg, magnesium oxide 3kg, diatomite 10kg, talcum powder 10kg, methylcellulose gum 1kg, ammonium sulfate 1kg, polyoxyethylene octylphenol ether 2kg, ripe rubber powder 1kg.
Another object of the present invention prepares the method for building putty powder in the present invention, it is characterized in that: comprise the following steps:
A, select a stirred autoclave, the calcium oxide in raw material, diatomite, talcum powder, methylcellulose gum are added wherein, add and open stirring at low speed 20min
B, until step a stir terminate after, the magnesium oxide in raw material, ammonium sulfate, polyoxyethylene octylphenol ether and ripe rubber powder are all added in reactor, high-speed stirring is until solution mixes;
C, the raw material in step b poured out and puts into pulverizer, pulverize, then carry out being sieved into appointment fineness.
Embodiment 2
A kind of building putty powder, comprises the raw material composition of following weight part,
Calcium oxide 5kg, magnesium oxide 4kg, diatomite 15kg, talcum powder 15kg, methylcellulose gum 2kg, Potassium Persulphate 2kg, sulfo-succinic acid Soxylat A 25-7 nonyl phenol sodium salt 3kg, ether of cellulose 2kg.
Another object of the present invention prepares the method for building putty powder in the present invention, it is characterized in that: comprise the following steps:
A, select a stirred autoclave, the calcium oxide in raw material, diatomite, talcum powder, methylcellulose gum are added wherein, add and open stirring at low speed 20min
B, until step a stir terminate after, the magnesium oxide in raw material, Potassium Persulphate, sulfo-succinic acid Soxylat A 25-7 nonyl phenol sodium salt and ether of cellulose are all added in reactor, high-speed stirring is until solution mixes;
C, the raw material in step b poured out and puts into pulverizer, pulverize, then carry out being sieved into appointment fineness.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (6)
1. a building putty powder, is characterized in that: the raw material composition comprising following weight part,
Calcium oxide 4-6 part, magnesium oxide 3-5 part, diatomite 10-20 part, talcum powder 10-20 part, methylcellulose gum 1-3, initiator 1-3 part, tensio-active agent 2-4 part, auxiliary agent 1-3 part.
2. a kind of building putty powder according to claim 1, is characterized in that: preferred weight part of each raw material is: 5 parts, calcium oxide, 4 parts, magnesium oxide, 15 parts, diatomite, talcum powder 15 parts, methylcellulose gum 2, initiator 2 parts, 3 parts, tensio-active agent, auxiliary agent 2 parts.
3. a kind of building putty powder according to claim 1, is characterized in that: described initiator is ammonium persulphate or Potassium Persulphate.
4. a kind of building putty powder according to claim 1, is characterized in that: described tensio-active agent is polyoxyethylene octylphenol ether, sulfo-succinic acid Soxylat A 25-7 nonyl phenol sodium salt, alkylphenol polyoxyethylene phosphoric acid ester and alkylphenol polyoxyethylene ammonium sulfate one wherein.
5. a kind of building putty powder according to claim 1, is characterized in that: described auxiliary agent is ripe rubber powder or ether of cellulose, or is both mixture.
6. prepare the method for building putty powder described in claim 1 or 2, it is characterized in that, comprise the following steps:
A, select a stirred autoclave, the calcium oxide in raw material, diatomite, talcum powder, methylcellulose gum are added wherein, add and open stirring at low speed 20min
B, until step a stir terminate after, the magnesium oxide in raw material, initiator, tensio-active agent and auxiliary agent are all added in reactor, high-speed stirring is until solution mixes;
C, the raw material in step b poured out and puts into pulverizer, pulverize, then carry out being sieved into appointment fineness.