CN104382430A - Ramie and paper straw mix-woven mat and processing technology thereof - Google Patents
Ramie and paper straw mix-woven mat and processing technology thereof Download PDFInfo
- Publication number
- CN104382430A CN104382430A CN201410588360.8A CN201410588360A CN104382430A CN 104382430 A CN104382430 A CN 104382430A CN 201410588360 A CN201410588360 A CN 201410588360A CN 104382430 A CN104382430 A CN 104382430A
- Authority
- CN
- China
- Prior art keywords
- mat
- ramie
- processing technology
- paper
- grass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a mat and a processing technology thereof, in particular to a ramie and paper straw mix-woven mat and the processing technology thereof. The ramie and paper straw mix-woven mat is formed by weaving ramie and paper straws in a mixed way. The processing technology of the ramie and paper straw mix-woven mat comprises the following steps of firstly manufacturing the paper straws into paper, cutting the paper into pieces according to the specification of the ramie and paper straw mix-woven mat, then taking the pieces as weft threads by rolling the pieces into rope shapes or core-spun cotton threads in the pieces to form the rope shapes, obtaining ramie fiber by carrying out chemical degumming on the ramie, soaking the ramie fiber by nano-silver antibiotic finishing agent solution of which the PH is 5.0-6.5, and taking the ramie fiber as warp threads for weaving after the ramie fiber is dried, so as to obtain a mat main body; obtaining a mat semi-finished product by carrying out water spraying, heating, press polishing and shrinkage treatment on the mat main body by a press atomizer; finally, drying the mat semi-finished product after soaking the mat semi-finished product is soaked in a waterproof agent of which the PH is 4.3-6.2 for 5-10 minutes, and obtaining a mat finished product by carrying out edge covering treatment. According to the ramie and paper straw mix-woven mat and the processing technology, disclosed by the invention, the processing technology is simple, and the ramie and paper straw mix-woven mat which is obtained through the processing technology not only has excellent performance of moisture-absorption air permeability, anti-bacterial deodorization performance, health and environment protection performance and the like, but also is comfortable in hand feeling, is washable and foldable and is long in service life.
Description
Technical field
The present invention relates to a kind of mat and processing technology thereof, particularly relate to mat and the processing technology thereof of a kind of ramie and Asia grass shuffling.
Background technology
During the broiling summer, mat has become the necessity in people's daily life naturally.Along with the development of society, the pursuit of people to quality of the life improves along with growth in the living standard, so the requirement of people to mat is also more and more higher.Therefore, mat kind in the market, also in continuous increase, comprises straw mat, bamboo mat, cow leather mat, linolenic summer sleeping mat, ice silk seat, sub-straw mat, rattan seat etc.Although bamboo mat is felt nice and cool, but easily makes people suffer from cold, be not suitable for old man, child uses; Although rattan seat is more durable, process more complicated, and expend the resources such as rattan material, welding; Although sub-straw mat, linen mat and ice silk seat quality are soft, selection is natural not, easily produces harm to human body.
Ramie, have another name called wild flax, siam falsenettle herb, family fiber crops, piemarker and hemp, its fiber is a kind of natural environmental-protective fiber, and hat has the good reputation of " king of natural fiber ".Ramee structure is cavity-like, containing giving repeated exhortations, the element such as pyrimidine, has the performance such as very superior gas permeability, hydrofuge, salubrious property, uvioresistant, static electricity resistance and natural bacteriostatic effect, is widely used in the aspects such as medicine, weaving, ecology.
Chinese invention patent application file (publication number: CN103415086A) discloses processing technology of a kind of ice silk and the dual-purpose seat of bamboo mat compound and products thereof, although the processing technology of this invention is simple, obtained mat has the good performance such as ventilative, wear-resisting, antistatic, and there are good feel, aesthetic feeling etc., but this mat selection consumes resources, and mat can not reach the objects such as antibacterial, anti-peculiar smell and uvioresistant.
Summary of the invention
The object of the invention is for the above-mentioned problems in the prior art, propose a kind of processing technology by the careless shuffling mat of ramie and Asia, make the mat obtained have excellent sucting wet air permeability, bacteriostatic deodorizing and uviolresistance.
Above-mentioned purpose of the present invention is achieved through the following technical solutions, the processing technology of the mat of a kind of ramie and Asia grass shuffling, and described processing technology comprises the following steps:
Parallel process done by S1, sub-grass: first Asia grass is made paper through paper technology, then the paper that sub-grass is made is cut into sheet, become the paper of rope form to make parallel, or become the paper of rope form to make parallel cotton thread cored with the paper of sheet with the paper roll of sheet;
S2, ramie do warp process: ramie obtains ramee through chemical Degumming, and ramee twisted filament becomes line, then it are soaked through the nano-silver antibacterial finishing agent solution that PH is 5.0-6.5, weave, obtain mat main body after oven dry as warp and Asia grass parallel;
S3, the process of mat main body: mat main body is obtained mat semi-finished product by press atomized water spray, heating, press polish and shrink process;
S4, post processing: mat semi-finished product being immersed in pH is in the waterproofing agent of 4.3-6.2, soak 5-10min, finally dries, bound edge process obtains ramie and the mat finished product of Asia grass shuffling.
Mat of the present invention adopt various aspects of performance excellent and the ramie of environmental protection after treatment as warp, form as parallel shuffling with sub-grass.Compared with other fiber, ramee has following special performance, and one, due to the cavity structure of ramee uniqueness and the many spaces of tube wall, so its sucting wet air permeability and be loosely moistly far longer than other fiber, 3 times more than to be exceeded than general cotton fiber; Two, ramee inside have special ultrafine micropore structure and be rich in give repeated exhortations, the multiple natural antibacterial trace element such as purine, pyrimidine, not only make it have very strong adsorption capacity, the harmful substance such as formaldehyde in air, benzene can be absorbed to eliminate bad smell, can also the growth of anti-bacteria, reach the object of bacteriostatic deodorizing; And through antibacterial detection, after washing 50 times, antibacterial effect still reaches 99%; Three, ramee is very tough and tensile, is not subject to mold corrosion, then have superpower mildew-resistant wear-resisting functions; Four, ramie anti-uv-ray is extremely strong, is cotton 41.7 times, and has natural static electricity resistance.And sub-grass a kind of to be pulverized by natural grass wood plant, dries, and through mildew-resistant, sterilization processing, then the material be prepared from by string, there is the two-fold advantage of flax and door screen grass, the strong and good permeability of wettability power.Therefore, mat of the present invention adopts ramie and Asia grass shuffling, the excellent performances such as the sucting wet air permeability of the mat obtained, loose moist, bacteriostatic deodorizing, mildew resistance, wearability, uvioresistant, antistatic performance, and security improves greatly, thus improve the market competitiveness of mat.
In the processing technology of the mat of the careless shuffling of above-mentioned a kind of ramie and Asia, paper technology described in step S1 is for first obtaining paper pulp by Asia grass through semichemical pulping legal system, starching by faling apart, pulling an oar and adding the modulation treatment such as glue and filling, then being manufactured paper with pulp through dehydration, drying, press polish etc. by the paper pulp after modulation treatment processes obtained paper product.Wherein, the semichemical pulping method in described paper technology, modulation treatment, process of manufacturing paper with pulp are the common technological process in this area.Sub-grass is first made paper by the present invention, then becomes the paper of rope form after as parallel as parallel or paper using using cotton thread cored using paper, not only makes the mat that obtains more solid, and plays more abundant by the excellent properties of sub-grass.In addition, in pulping process, also can add water and oil repellent agent as organofluoro surfactants, make final paper product have good waterproof and oilproof performance, apply it in mat of the present invention and make mat have more excellent waterproof and oilproof performance.
In the processing technology of the mat of the careless shuffling of above-mentioned a kind of ramie and Asia, nano-silver antibacterial finishing agent described in step S2 is that 1:700-750 is obtained by mixing by nano silver particles and butyl polyacrylate emulsion with mass ratio, wherein the particle diameter of nano silver particles is 25-45nm, mixing temperature is 60-65 DEG C, and incorporation time is 50-60min.Nano silver antimicrobials is a kind of novel antiseptic, because its particle is extremely small, surface area is larger, make it have significant skin effect, quantum size effect and quantum tunneling effect, Nano Silver is then made to have superpower activity and permeability, there is powerful antibacterial and bactericidal action, and without the property of medicine, security is high.In the processing technology of mat of the present invention, compositely on the basis of Nano Silver add butyl polyacrylate emulsion, Nano Silver can be wrapped in butyl polyacrylate, and be dispersed in wherein uniformly, better antibacterial effect can be obtained.For nanometer silver antiseptic, the particle diameter of nano silver particles is less, and its antibacterial effect is better, so the present invention selects the particle diameter of 25-45nm.And the mixing quality ratio of Nano Silver and butyl polyacrylate emulsion, the time of mixing and temperature all have impact to the antibacterial effect of final nano-silver antibacterial finishing agent, the consumption of butyl polyacrylate emulsion is too high or too low, overlong time, the temperature of the mixing time that is too high or mixing is too short, temperature is too low etc. all can reduce the antibacterial effect of nano-silver antibacterial finishing agent, selects suitable mixing quality ratio, incorporation time and mixing temperature in the processing technology of therefore mat of the present invention.In addition, in the processing technology of mat of the present invention, be the conventional chemical degumming technique in this area for the extraction process of ramee in step S2.
In the processing technology of the mat of above-mentioned a kind of ramie and Asia grass shuffling, as preferably, in the solution of nano-silver antibacterial finishing agent described in step S2, the concentration of nano-silver antibacterial finishing agent is 4.0%-6.0%.The concentration of nano-silver antibacterial finishing agent is too low, and antibacterial effect can be very poor, too highly can reduce antibacterial effect on the contrary, and therefore the present invention selects the concentration of suitable nano-silver antibacterial finishing agent.
In the processing technology of the mat of above-mentioned a kind of ramie and Asia grass shuffling, as preferably, the bake out temperature of drying course described in step S2 is 110-125 DEG C, and drying time is 1.0-1.5min.In order to the surface making nano-silver antibacterial finishing agent more firmly can anchor at fiber, to make ramee have more lasting anti-microbial property, and reach laundry-resistant requirement, the fiber soaked through nano-silver antibacterial finishing agent solution will be dried.And temperature and time the having the greatest impact to whole drying course of drying, oven dry too high or too low for temperature, all can not reach the requirement of antibacterial finishing agent; And the long meeting of drying time causes ramee yellowing, powerful lower degradation, drying time is too short, causes ramee insecure, wash durability difference etc.
In the processing technology of the mat of the careless shuffling of above-mentioned a kind of ramie and Asia, the water-jet velocity of the atomizer of press described in step S3 is 0.3-0.5kg/min, and water is vaporific; Employing water smoke is sprayed water, and not only can increase the area of water spray, and can reduce water consumption.The speed of water spray is moderate, and mat body surfaces all can not clean up by too fast or mistake slowly; And the heat time of heating is moderate, heating-up temperature is too low, then do not reach expected effect; Heating-up temperature is too high, can damage the material of mat.Therefore, the heating-up temperature during the present invention heats is 75-85 DEG C, and the heat time is 1.2-2.5min.
In the processing technology of the mat of the careless shuffling of above-mentioned a kind of ramie and Asia, the calendering pressure in the process of press polish described in step S3 is 100-160kgf/cm
2, calendering temperature is 120-160 DEG C, and the press polish time is 0.2-1.0min, and mat main body operates with 1.0-1.2m/min speed in press.Mat after press polish process, can form the light top layer of one deck densification, this not only adds mat glossiness and aesthetic feeling, also improve the toughness of mat, make mat more durable on its surface.
In the processing technology of the mat of the careless shuffling of above-mentioned a kind of ramie and Asia, waterproofing agent described in step S4 becomes to be grouped into primarily of following parts by weight: LZ-706 waterproofing agent: 5-9 part, AG-710 waterproofing agent: 1-2 part, organosilicon: 0.5-1.5 part, HTUV100:0.5-1 part, water: 45-60 part.And for the consumption of waterproofing agent, control just can play waterproof effect in suitable scope.Waterproofing agent consumption is too high, and mat surface can form waterproof membrane thus affect aesthetics and the comfort level of mat; Waterproofing agent consumption is too low, then do not reach the effect of waterproof.Therefore, in the processing technology of mat of the present invention, the consumption of waterproofing agent controls suitable scope 0.2-0.3kg/m
2.
Waterproofing agent in the processing technology of mat of the present invention adopts LZ-706 waterproofing agent and the composite use of AG-710 waterproofing agent.LZ-706 waterproofing agent is a kind of water and oil repellent agent being applicable to each fiber, its environmental protection, to human body without illeffects, and the compatibility of AG-710 waterproofing agent and other auxiliary agent is good, can give the waterproof oil-proof result that various fiber is excellent, stable.The basis of LZ-706 waterproofing agent adds AG-710 waterproofing agent can make mat have better waterproof, grease proofing, soil resistant and antibacterial ability.The basis of LZ-706 waterproofing agent and the composite use of AG-710 waterproofing agent adds a small amount of silicone softening agent and HTUV100 uvioresistant finishing agent, HTUV100 is a kind of safety non-toxic, the uvioresistant finishing agent non-stimulated to skin, it add the anti-ultraviolet property that obviously can improve mat, adding of silicone softening agent, feel and the smoothness of mat can be improved, make mat in use more comfortable.Therefore, in the processing technology of mat of the present invention, adopt waterproofing agent of the present invention to fill a prescription, on the one hand meet environmental requirement, not only make mat wash on the other hand, and there is the performances such as good antibacterial, wear-resisting, soil resistant, and feel soft comfortable more, extend the service life of mat.
In the processing technology of the mat of the careless shuffling of above-mentioned a kind of ramie and Asia, the bake out temperature in baking oven described in step S4 is 115-125 DEG C, and mat semi-finished product operate with 1-1.2m/min speed in an oven.With this understanding, waterproofing agent can be attached to mat surface of semi-finished well and even penetrate between the half-finished space of mat and form waterproofing membrane, makes mat have the washable effect of better waterproof.
Another object of the present invention is the mat providing a kind of ramie and Asia grass shuffling, and described mat comprises mat main body, and mat main body adopts ramie to form as parallel shuffling as warp, sub-grass.
Mat of the present invention adopts ramie and Asia grass shuffling, and the mat quality obtained is very soft, and comfortable feel is cool in summer and warm in winter, suitable for four seasons, and because of attractive in appearance beautiful with decorative pattern.And mat of the present invention has protection human body, regulate the natural performances such as temperature, human body room temperature-sensitive degree under normal temperature, can be made to decline 4 to 8 degrees Celsius, be called as ' natural air conditioner ', be especially applicable to the family's Long-Time Service having old man, women, children.
In addition, the quality of mat of the present invention is soft, can fold as sheet, easy to carry, and maximum specification can reach 2.5 × 2.5m, is applicable to the bed of any size, substantially increases the practicality of mat, very has the market competitiveness.
Compared with prior art, the present invention has following advantage:
1, mat main body of the present invention adopts ramie to form as weft knit as warp, sub-grass, there is the dual property of ramie and Asia grass, particularly the various aspects of performance of ramie is excellent, the mat obtained not only sucting wet air permeability, loose moist, bacteriostatic deodorizing, mildew resistance, wearability, uvioresistant, antistatic performance are good, and comfortable feel, long service life.
2, mat of the present invention do manual work fine and smooth, quality gloss is beautiful, flat smooth, and cool in summer and warm in winter, suitable for four seasons, its maximum specification can reach 2.5 × 2.5m, collapsible use, easy to carry, economical and practical, has the very strong market competitiveness.
3, the processing technology of mat of the present invention is simple to operate, for adopting nano-silver antibacterial finishing agent solution to soak in the process of ramee, makes the antibacterial ability of the mat obtained stronger; And after heating, press polish, mat is dipped in waterproofing agent, make mat have fabulous waterproof effect, reach the object that can wash, and the waterproofing agent adopted is composite effective, environmental protection, also can improve the wearability of mat and anti-tear properties.
Detailed description of the invention
Be below specific embodiments of the invention, technical scheme of the present invention is further described, but the present invention is not limited to these embodiments.
Table 1: the main constituent of embodiment of the present invention 1-3 waterproofing agent and parts by weight thereof
Embodiment 1:
Parallel process done by sub-grass: first Asia grass is obtained paper pulp through semichemical pulping legal system, starching by faling apart again, pulling an oar and adding the modulation treatment such as glue and filling, then the paper pulp after modulation treatment is manufactured paper with pulp through dehydration, drying, press polish etc. and process obtained paper product, again the paper that sub-grass is made is cut into sheet, finally becomes the paper of rope form to make parallel with the paper roll of sheet.
Ramie does warp process: first ramie is obtained ramee through chemical Degumming, ramee twisted filament becomes line, again by its through PH be 5.0, concentration be 4.0% nano-silver antibacterial finishing agent solution soak, weave as warp dry 1.0min at 110 DEG C after, obtain mat main body; Wherein by particle diameter, to be the nano silver particles of 25nm and butyl polyacrylate emulsion with mass ratio be nano-silver antibacterial finishing agent that 1:700 carries out mixing 50min at 60 DEG C obtains.
Mat main body process: mat main body is obtained mat semi-finished product by press atomized water spray, heating, press polish and shrink process; Wherein, press atomizer caliber is Φ 2cm, and the water-jet velocity controlling press is 0.3kg/min, and water is vaporific; Heating-up temperature is 75 DEG C, and the heat time is 1.2min; Calendering pressure is 100kgf/cm
2, calendering temperature is 120 DEG C, and the press polish time is 0.2min; Shrink for common shrink PROCESS FOR TREATMENT; Mat main body operates with 1.0m/min speed in press.
Post processing: take raw material by the main constituent of waterproofing agent in embodiment in table 11 and parts by weight thereof, preparing waterproofing agent and it is adjusted pH value with acetic acid is 4.3, then 5min is soaked through waterproofing agent in above-mentioned mat semi-finished product two sides, then drying, bound edge process obtain the mat finished product of ramie and Asia grass shuffling; Wherein waterproofing agent consumption is 0.2kg/m
2, mat semi-finished product bake out temperature is in an oven 115 DEG C, and mat semi-finished product operate with 1.0m/min speed in an oven.
Embodiment 2:
Parallel process done by sub-grass: first Asia grass is obtained paper pulp through semichemical pulping legal system, wherein in the process of slurrying, add organofluoro surfactants, starching by faling apart again, pulling an oar and adding the modulation treatment such as glue and filling, then the paper pulp after modulation treatment is manufactured paper with pulp through dehydration, drying, press polish etc. and process obtained paper product, again the paper that sub-grass is made is cut into sheet, finally becomes the paper of rope form to make parallel cotton thread cored with the paper of sheet.
Ramie does warp process: first ramie is obtained ramee through chemical Degumming, ramee twisted filament becomes line, again by its through PH be 5.5, concentration be 5.0% nano-silver antibacterial finishing agent solution soak, weave as warp dry 1.2min at 120 DEG C after, obtain mat main body; Wherein by particle diameter, to be the nano silver particles of 35nm and butyl polyacrylate emulsion with mass ratio be nano-silver antibacterial finishing agent that 1:720 carries out mixing 55min at 63 DEG C obtains.
Mat main body process: mat main body is obtained mat semi-finished product by press atomized water spray, heating, press polish and shrink process; Wherein, press atomizer caliber is Φ 2cm, and the water-jet velocity controlling press is 0.4kg/min, and water is vaporific; Heating-up temperature is 80 DEG C, and the heat time is 1.8min; Calendering pressure is 130kgf/cm
2, calendering temperature is 130 DEG C, and the press polish time is 0.8min; Shrink for common shrink PROCESS FOR TREATMENT; Mat main body operates with 1.1m/min speed in press.
Post processing: take raw material by the main constituent of waterproofing agent in embodiment in table 12 and parts by weight thereof, preparing waterproofing agent and it is adjusted pH value with acetic acid is 5.0, then 8min is soaked through waterproofing agent in above-mentioned mat semi-finished product two sides, then drying, bound edge process obtain the mat finished product of ramie and Asia grass shuffling; Wherein waterproofing agent consumption is 0.25kg/m
2, mat semi-finished product bake out temperature is in an oven 120 DEG C, and mat semi-finished product operate with 1.1m/min speed in an oven.
Embodiment 3:
Parallel process done by sub-grass: first Asia grass is obtained paper pulp through semichemical pulping legal system, wherein in the process of slurrying, add organofluoro surfactants, starching by faling apart again, pulling an oar and adding the modulation treatment such as glue and filling, then the paper pulp after modulation treatment is manufactured paper with pulp through dehydration, drying, press polish etc. and process obtained paper product, again the paper that sub-grass is made is cut into sheet, finally becomes the paper of rope form to make parallel with the paper roll of sheet.
Ramie does warp process: first ramie is obtained ramee through chemical Degumming, ramee twisted filament becomes line, again by its through PH be 6.5, concentration be 6.0% nano-silver antibacterial finishing agent solution soak, weave as warp dry 1.5min at 125 DEG C after, obtain mat main body; Wherein by particle diameter, to be the nano silver particles of 40nm and butyl polyacrylate emulsion with mass ratio be nano-silver antibacterial finishing agent that 1:750 carries out mixing 60min at 65 DEG C obtains.
Mat main body process: mat main body is obtained mat semi-finished product by press atomized water spray, heating, press polish and shrink process; Wherein, press atomizer caliber is Φ 2cm, and the water-jet velocity controlling press is 0.5kg/min, and water is vaporific; Heating-up temperature is 85 DEG C, and the heat time is 2.3min; Calendering pressure is 160kgf/cm
2, calendering temperature is 160 DEG C, and the press polish time is 1.0min; Shrink for common shrink PROCESS FOR TREATMENT; Mat main body operates with 1.2m/min speed in press.
Post processing: take raw material by the main constituent of waterproofing agent in embodiment in table 13 and parts by weight thereof, preparing waterproofing agent and it is adjusted pH value with acetic acid is 6.0, then 10min is soaked through waterproofing agent in above-mentioned mat semi-finished product two sides, then drying, bound edge process obtain the mat finished product of ramie and Asia grass shuffling; Wherein waterproofing agent consumption is 0.3kg/m
2, mat semi-finished product bake out temperature is in an oven 125 DEG C, and mat semi-finished product operate with 1.2m/min speed in an oven.
The mat obtained by embodiment of the present invention 1-3 and the mat of comparative example carry out performance test, and test result is as shown in table 2.
The performance test results of the mat of table 2: embodiment of the present invention 1-3 and comparative example
Comparative example is commercially available common bamboo mat.
In sum, mat of the present invention adopts the ramie of excellent performance and Asia grass shuffling to form, weaving is simple, and selects the waterproofing agent formula of environmental protection, and obtained mat is compared with common commercially available common bamboo mat, gas permeability, comfortableness, wearability, antibiotic property, uvioresistant, static electricity resistance etc. are all significantly improved, but also can wash, can use be folded, improve the practicality of mat, extend the service life of mat, improve the market competitiveness of mat.
Specific embodiment described herein is only to the explanation for example of the present invention's spirit.Those skilled in the art can make various amendment or supplement or adopt similar mode to substitute to described specific embodiment, but can't depart from spirit of the present invention or surmount the scope that appended claims defines.
Although made a detailed description the present invention and quoted some specific embodiments as proof, to those skilled in the art, only otherwise it is obvious for leaving that the spirit and scope of the present invention can make various changes or revise.
Claims (10)
1. a processing technology for the mat of ramie and Asia grass shuffling, it is characterized in that, this processing technology comprises the steps:
Parallel process done by S1, sub-grass: first Asia grass is made paper through paper technology, then the paper that sub-grass is made is cut into sheet, become the paper of rope form to make parallel, or become the paper of rope form to make parallel cotton thread cored with the paper of sheet with the paper roll of sheet;
S2, ramie do warp process: ramie obtains ramee through chemical Degumming, and ramee twisted filament becomes line, then it are soaked through the nano-silver antibacterial finishing agent solution that PH is 5.0-6.5, weave, obtain mat main body after oven dry as warp and Asia grass parallel;
S3, the process of mat main body: mat main body is obtained mat semi-finished product by press atomized water spray, heating, press polish and shrink process;
S4, post processing: mat semi-finished product being immersed in pH is in the waterproofing agent of 4.3-6.2, soak 5-10min, finally dries, bound edge process obtains ramie and the mat finished product of Asia grass shuffling.
2. the processing technology of the mat of ramie according to claim 1 and Asia grass shuffling, it is characterized in that, nano-silver antibacterial finishing agent described in step S2 is that 1:700-750 mixes by nano silver particles and butyl polyacrylate emulsion with mass ratio, wherein the particle diameter of nano silver particles is 25-45nm, mixing temperature is 60-65 DEG C, and incorporation time is 50-60min.
3. the processing technology of the mat of ramie according to claim 1 and 2 and Asia grass shuffling, it is characterized in that, in the solution of nano-silver antibacterial finishing agent described in step S2, the concentration of nano-silver antibacterial finishing agent is 4.0%-6.0%.
4. the processing technology of the mat of ramie according to claim 1 and Asia grass shuffling, it is characterized in that, the bake out temperature of drying course described in step S2 is 110-125 DEG C, and drying time is 1.0-1.5min.
5. the processing technology of the mat of ramie according to claim 1 and Asia grass shuffling, it is characterized in that, the water-jet velocity of the atomizer of press described in step S3 is 0.3-0.5kg/min, and water is vaporific; Heating-up temperature in described heating is 75-85 DEG C, and the heat time is 1.2-2.5min.
6. the processing technology of the mat of ramie according to claim 1 and Asia grass shuffling, it is characterized in that, the calendering pressure in the process of press polish described in step S3 is 100-160kgf/cm
2, calendering temperature is 120-160 DEG C, and the press polish time is 0.2-1.0min, and mat main body operates with 1.0-1.2m/min speed in press.
7. the processing technology of the mat of ramie according to claim 1 and Asia grass shuffling, it is characterized in that, the consumption of waterproofing agent described in step S4 is 0.2-0.3kg/m
2
8. the processing technology of the mat of the ramie according to claim 1 or 7 and Asia grass shuffling, it is characterized in that, waterproofing agent described in step S4 becomes to be grouped into primarily of following parts by weight: LZ-706 waterproofing agent: 5-9 part, AG-710 waterproofing agent: 1-2 part, organosilicon: 0.5-1.5 part, HTUV100:0.5-1 part, water: 45-60 part.
9. the processing technology of the mat of ramie according to claim 1 and Asia grass shuffling, it is characterized in that, the bake out temperature in baking oven described in step S4 is 115-125 DEG C, and mat semi-finished product operate with 1-1.2m/min speed in an oven.
10. a mat for ramie and Asia grass shuffling, it is characterized in that, described mat comprises mat main body, and mat main body adopts ramie to form as parallel shuffling as warp, sub-grass.