CN104371602A - High-temperature-resistant adhesive - Google Patents
High-temperature-resistant adhesive Download PDFInfo
- Publication number
- CN104371602A CN104371602A CN201410597996.9A CN201410597996A CN104371602A CN 104371602 A CN104371602 A CN 104371602A CN 201410597996 A CN201410597996 A CN 201410597996A CN 104371602 A CN104371602 A CN 104371602A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- alcohol resin
- resistant adhesive
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a high-temperature-resistant adhesive which is prepared from the following raw materials in parts by weight: 5-10 parts of maleimide, 3-9 parts of N-methylpyrrolidone, 4-8 parts of di-tert-butyl peroxide, 5-10 parts of acetone, 2-8 parts of aluminum powder, 4-11 parts of epoxypropane phenyl ether, 5-9 parts of epoxy resin, 5-7 parts of filler, 6-10 parts of polyvinyl alcohol resin, 4-6 parts of triisopropanolamine, 1-5 parts of fly ash, 3-6 parts of titanium white, 5-10 parts of furfuryl alcohol resin and 2-8 parts of curing agent. The high-temperature-resistant adhesive has the advantages of favorable high-temperature resistance, favorable binding property and favorable binding effect, and can be normally used at high temperature.
Description
Technical field
The present invention relates to a kind of resistant to elevated temperatures sizing agent.
Background technology
Glued joint and refer to the technology that homogeneity or heterogeneous body surface sizing agent link together, there is stress distribution continuous, lightweight, or sealing, the features such as most technological temperature is low.Glued joint the connection being specially adapted to unlike material, different thickness, ultra-thin specification and complex component.Tackiness agent has a very wide range of applications in real life, plays very important effect.But existing sizing agent at high temperature generally all ruckbildung can occur, and cohesiveness reduces greatly, can not meet service requirements, even can have an accident, cause casualties and huge financial loss.
Summary of the invention
For the deficiencies in the prior art, the technical problem to be solved in the present invention is, provide a kind of resistant to elevated temperatures sizing agent, have good resistance to elevated temperatures, at high temperature can normally use, have good cohesiveness simultaneously, bond effect is good.
For solving the deficiencies in the prior art, the technical scheme that the present invention takes is: a kind of resistant to elevated temperatures sizing agent, is made up of the raw material of following parts by weight:
Maleimide 5-10 part, N-Methyl pyrrolidone 3-9 part, ditertiary butyl peroxide 4-8 part, acetone 5-10 part, aluminium powder 2-8 part, propylene oxide phenyl ether 4-11 part, epoxy resin 5-9 part, filler 5-7 part, polyvinyl alcohol resin 6-10 part, tri-isopropanolamine 4-6 part, flyash 1-5 part, titanium dioxide 3-6 part, furfuryl alcohol resin 5-10 part, solidifying agent 2-8 part.
The invention has the beneficial effects as follows, resistant to elevated temperatures sizing agent of the present invention, has good resistance to elevated temperatures, at high temperature can normally use, and has good cohesiveness simultaneously, and bond effect is good.
Embodiment
embodiment 1
A kind of resistant to elevated temperatures sizing agent, be made up of the raw material of following parts by weight:
Maleimide 5 parts, N-Methyl pyrrolidone 3 parts, ditertiary butyl peroxide 4 parts, 5 parts, acetone, aluminium powder 2 parts, propylene oxide phenyl ether 4 parts, epoxy resin 5 parts, filler 5 parts, polyvinyl alcohol resin 6 parts, tri-isopropanolamine 4 parts, 1 part, flyash, titanium dioxide 3 parts, furfuryl alcohol resin 5 parts, 2 parts, solidifying agent.
embodiment 2
A kind of resistant to elevated temperatures sizing agent, be made up of the raw material of following parts by weight:
Maleimide 10 parts, N-Methyl pyrrolidone 9 parts, ditertiary butyl peroxide 8 parts, 10 parts, acetone, aluminium powder 8 parts, propylene oxide phenyl ether 11 parts, epoxy resin 9 parts, filler 7 parts, polyvinyl alcohol resin 10 parts, tri-isopropanolamine 6 parts, 5 parts, flyash, titanium dioxide 6 parts, furfuryl alcohol resin 10 parts, 8 parts, solidifying agent.
Claims (1)
1. a resistant to elevated temperatures sizing agent, is characterized in that: be made up of the raw material of following parts by weight:
Maleimide 5-10 part, N-Methyl pyrrolidone 3-9 part, ditertiary butyl peroxide 4-8 part, acetone 5-10 part, aluminium powder 2-8 part, propylene oxide phenyl ether 4-11 part, epoxy resin 5-9 part, filler 5-7 part, polyvinyl alcohol resin 6-10 part, tri-isopropanolamine 4-6 part, flyash 1-5 part, titanium dioxide 3-6 part, furfuryl alcohol resin 5-10 part, solidifying agent 2-8 part.