CN103666329A - Modified nitrile rubber adhesive - Google Patents
Modified nitrile rubber adhesive Download PDFInfo
- Publication number
- CN103666329A CN103666329A CN201310618733.7A CN201310618733A CN103666329A CN 103666329 A CN103666329 A CN 103666329A CN 201310618733 A CN201310618733 A CN 201310618733A CN 103666329 A CN103666329 A CN 103666329A
- Authority
- CN
- China
- Prior art keywords
- parts
- acetone
- nitrile rubber
- epoxy resin
- carboxyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a modified nitrile rubber adhesive which comprises components in parts by mass as follows: 280-320 parts of carboxyl nitrile rubber, 40-62 parts of resorcinol formaldehyde resin, 85-100 parts of E-51 epoxy resin, 290-310 parts of acetone, 70-75 parts of phenolic resin and 5-10 parts of dicyandiamide. The modified nitrile rubber adhesive is made from carboxyl nitrile rubber, resorcinol formaldehyde resin, E-51 epoxy resin, acetone, phenolic resin and dicyandiamide in certain proportion, and has the advantages of light weight, energy saving, sealing, leakage proofing, warming keeping, poisonousness reduction, contamination prevention and durability.
Description
Technical field
The present invention relates to a kind of tackiness agent, especially a kind of modified butadiene acrylonitrile rubber tackiness agent.
Background technology
Tackiness agent is all indispensable in modern industry and daily life.In structure, connecting, assemble the aspects such as reinforcing, damping antidetonation, loss of weight speedup, decorations, water-tight corrosion-proof, emergent reparation is all widely used.
Summary of the invention
Technical problem to be solved by this invention is just to provide a kind of modified butadiene acrylonitrile rubber tackiness agent, plays under construction lightweight, energy-conservation, sealing, leakproof, warming, attenuation, antifouling, durable effect.
For achieving the above object, the present invention adopts following technical scheme: a kind of modified butadiene acrylonitrile rubber tackiness agent, and composed of the following components and each constituent mass umber scope is: the western nitrile rubber 280-320 of carboxyl part; Resorcinol formaldehyde resin 40-62 part; E-51 epoxy resin 85-100 part; Acetone 290-310 part; Resol 70-75 part; Dyhard RU 100 5-10 part.
As preferably, each constituent mass umber is: 300 parts of the western nitrile rubbers of carboxyl; 60 parts of resorcinol formaldehyde resins; 96 parts of E-51 epoxy resin; 300 parts, acetone; 72 parts, resol; 7 parts of Dyhard RU 100s.
As preferably, each constituent mass umber is: 305 parts of the western nitrile rubbers of carboxyl; 50 parts of resorcinol formaldehyde resins; 93 parts of E-51 epoxy resin; 290 parts, acetone; 73 parts, resol; 9 parts of Dyhard RU 100s.
As preferably, each constituent mass umber is: 300 parts of the western nitrile rubbers of carboxyl; 49 parts of resorcinol formaldehyde resins; 88 parts of E-51 epoxy resin; 300 parts, acetone; 75 parts, resol; 10 parts of Dyhard RU 100s.
The present invention makes the western nitrile rubber of carboxyl, resorcinol formaldehyde resin, E-51 epoxy resin, acetone, resol, Dyhard RU 100 by a certain percentage, the modified butadiene acrylonitrile rubber tackiness agent obtaining, has advantages of lightweight, energy-conservation, sealing, leakproof, warming, attenuation, antifouling, durable.
Embodiment
Modified butadiene acrylonitrile rubber tackiness agent of the present invention, a kind of modified butadiene acrylonitrile rubber tackiness agent, composed of the following components and each constituent mass umber scope is: the western nitrile rubber 280-320 of carboxyl part; Resorcinol formaldehyde resin 40-62 part; E-51 epoxy resin 85-100 part; Acetone 290-310 part; Resol 70-75 part; Dyhard RU 100 5-10 part.
Described in embodiment 1, each constituent mass umber is: 300 parts of the western nitrile rubbers of carboxyl; 60 parts of resorcinol formaldehyde resins; 96 parts of E-51 epoxy resin; 300 parts, acetone; 72 parts, resol; 7 parts of Dyhard RU 100s.
Embodiment 2, differently from embodiment 1 are that each constituent mass umber is: each constituent mass umber is: 305 parts of the western nitrile rubbers of carboxyl; 50 parts of resorcinol formaldehyde resins; 93 parts of E-51 epoxy resin; 290 parts, acetone; 73 parts, resol; 9 parts of Dyhard RU 100s.
Embodiment 3, differently from embodiment 1 are that each constituent mass umber is: each constituent mass umber is: 300 parts of the western nitrile rubbers of carboxyl; 49 parts of resorcinol formaldehyde resins; 88 parts of E-51 epoxy resin; 300 parts, acetone; 75 parts, resol; 10 parts of Dyhard RU 100s.
The modified butadiene acrylonitrile rubber tackiness agent that the present invention obtains has good bonding characteristic and environmental protection through evidence, has advantages of lightweight, energy-conservation, sealing, leakproof, warming, attenuation, antifouling, durable.
Above-described embodiment is to explanation of the present invention, is not limitation of the invention, any scheme after simple transformation of the present invention is all belonged to protection scope of the present invention.
Claims (4)
1. a modified butadiene acrylonitrile rubber tackiness agent, is characterized in that: composed of the following components and each constituent mass umber scope is: the western nitrile rubber 280-320 of carboxyl part; Resorcinol formaldehyde resin 40-62 part; E-51 epoxy resin 85-100 part; Acetone 290-310 part; Resol 70-75 part; Dyhard RU 100 5-10 part.
2. modified butadiene acrylonitrile rubber tackiness agent according to claim 1, is characterized in that: each constituent mass umber is: 300 parts of the western nitrile rubbers of carboxyl; 60 parts of resorcinol formaldehyde resins; 96 parts of E-51 epoxy resin; 300 parts, acetone; 72 parts, resol; 7 parts of Dyhard RU 100s.
3. modified butadiene acrylonitrile rubber tackiness agent according to claim 1, is characterized in that: each constituent mass umber is: 305 parts of the western nitrile rubbers of carboxyl; 50 parts of resorcinol formaldehyde resins; 93 parts of E-51 epoxy resin; 290 parts, acetone; 73 parts, resol; 9 parts of Dyhard RU 100s.
4. modified butadiene acrylonitrile rubber tackiness agent according to claim 1, is characterized in that: each constituent mass umber is: 300 parts of the western nitrile rubbers of carboxyl; 49 parts of resorcinol formaldehyde resins; 88 parts of E-51 epoxy resin; 300 parts, acetone; 75 parts, resol; 10 parts of Dyhard RU 100s.