CN104817957A - Durable agricultural mechanical coating - Google Patents
Durable agricultural mechanical coating Download PDFInfo
- Publication number
- CN104817957A CN104817957A CN201510196081.1A CN201510196081A CN104817957A CN 104817957 A CN104817957 A CN 104817957A CN 201510196081 A CN201510196081 A CN 201510196081A CN 104817957 A CN104817957 A CN 104817957A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- agricultural machine
- hexabromocyclododecane
- agricultural mechanical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a durable agricultural mechanical coating which is made of raw materials including, by weight, 30-50 parts of aluminum powder, 0.1-0.5 part of silane coupling agents A-151, 0.5-2 parts of hydroxyethyl cellulose, 0.2-1 part of ethylene diamine tetraacetic acid, 0.5-0.8 part of calcium stearate, 0.1-0.5 part of polysorbate-80, 20-25 parts of rosin resin, 10-20 parts of CAB (cellulose acetate butyrate) liquid resin, 6-15 parts of talcum powder and 7-18 parts of hexabromocyclododecane. The agricultural mechanical coating is fine in corrosion resistance and durability, so that the mechanical performance of an agricultural mechanical component is effectively enhanced.
Description
Technical field
The present invention relates to technical field of coatings, especially, relate to a kind of durable type agricultural machine coating.
Background technology
Agricultural machine coating just refers to the coating of application on agricultural machine surface and all kinds of element part.
Existing agricultural machine coating, Main Function falls to prevent from agricultural machine parts to be isolated from the outside coming, and avoids that agricultural machine parts are oxidized, corrosion.But, existing agricultural machine coating due to durability inadequate, have a strong impact on the mechanical property of agricultural machine parts.
Summary of the invention
The object of the invention is to provide a kind of durable type agricultural machine coating, with solve agricultural machine coating in prior art due to durability inadequate, have a strong impact on the problem of the mechanical property of agricultural machine parts.
For achieving the above object, the invention provides a kind of durable type agricultural machine coating, wherein, this coating is made up of the raw material of following massfraction:
Aluminium powder 30-50 part;
Silane coupling A-151 0.1-0.5 part;
Natvosol 0.5-2 part;
Disodium ethylene diamine tetraacetate 0.2-1 part;
Calcium stearate 0.5-0.8 part;
Tween-80 0.1-0.5 part;
Gum Rosin 20-25 part;
CAB resin liquid 10-20 part;
Talcum powder 6-15 part; And
Hexabromocyclododecane 7-18 part.
Further, the invention provides a kind of durable type agricultural machine coating, wherein, this coating is made up of the raw material of following massfraction: aluminium powder 30 parts; Silane coupling A-151 0.2 parts; Natvosol 0.5 part; Disodium ethylene diamine tetraacetate 0.5 part; Calcium stearate 0.7 part; Tween-80 0.3 part; Gum Rosin 20 parts; CAB resin liquid 12 parts; Talcum powder 8 parts; And hexabromocyclododecane 10 parts.
Further, the invention provides a kind of durable type agricultural machine coating, wherein, this coating is made up of the raw material of following massfraction: aluminium powder 50 parts; Silane coupling A-151 0.3 parts; Natvosol 2 parts; Disodium ethylene diamine tetraacetate 1 part; Calcium stearate 0.8 part; Tween-80 0.5 part; Gum Rosin 23 parts; CAB resin liquid 18 parts; Talcum powder 15 parts; And hexabromocyclododecane 15 parts.
The present invention has following beneficial effect: the invention provides a kind of agricultural machine coating, and its corrosion-resistant durability is good, thus effectively enhances the mechanical property of agricultural machine parts.
Embodiment
A kind of agricultural machine coating that this preferred embodiment provides, its specific implementation process is as follows:
Wherein, this coating is made up of the raw material of following massfraction:
Aluminium powder 30-50 part;
Silane coupling A-151 0.1-0.5 part;
Natvosol 0.5-2 part;
Disodium ethylene diamine tetraacetate 0.2-1 part;
Calcium stearate 0.5-0.8 part;
Tween-80 0.1-0.5 part;
Gum Rosin 20-25 part;
CAB resin liquid 10-20 part;
Talcum powder 6-15 part; And
Hexabromocyclododecane 7-18 part.
Embodiment 1:
Wherein, this coating is made up of the raw material of following massfraction: aluminium powder 30 parts; Silane coupling A-151 0.2 parts; Natvosol 0.5 part; Disodium ethylene diamine tetraacetate 0.5 part; Calcium stearate 0.7 part; Tween-80 0.3 part; Gum Rosin 20 parts; CAB resin liquid 12 parts; Talcum powder 8 parts; And hexabromocyclododecane 10 parts.
Embodiment 2:
Wherein, this coating is made up of the raw material of following massfraction: aluminium powder 50 parts; Silane coupling A-151 0.3 parts; Natvosol 2 parts; Disodium ethylene diamine tetraacetate 1 part; Calcium stearate 0.8 part; Tween-80 0.5 part; Gum Rosin 23 parts; CAB resin liquid 18 parts; Talcum powder 15 parts; And hexabromocyclododecane 15 parts.
As can be seen from the above description, the above embodiments of the present invention achieve following technique effect:
The invention provides a kind of agricultural machine coating, its corrosion-resistant durability is good, thus effectively enhances the mechanical property of agricultural machine parts.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention; For a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. a durable type agricultural machine coating, is characterized in that, this coating is made up of the raw material of following massfraction:
Aluminium powder 30-50 part;
Silane coupling A-151 0.1-0.5 part;
Natvosol 0.5-2 part;
Disodium ethylene diamine tetraacetate 0.2-1 part;
Calcium stearate 0.5-0.8 part;
Tween-80 0.1-0.5 part;
Gum Rosin 20-25 part;
CAB resin liquid 10-20 part;
Talcum powder 6-15 part; And
Hexabromocyclododecane 7-18 part.
2. durable type agricultural machine coating according to claim 1, it is characterized in that, this coating is made up of the raw material of following massfraction: aluminium powder 30 parts; Silane coupling A-151 0.2 parts; Natvosol 0.5 part; Disodium ethylene diamine tetraacetate 0.5 part; Calcium stearate 0.7 part; Tween-80 0.3 part; Gum Rosin 20 parts; CAB resin liquid 12 parts; Talcum powder 8 parts; And hexabromocyclododecane 10 parts.
3. durable type agricultural machine coating according to claim 1, it is characterized in that, this coating is made up of the raw material of following massfraction: aluminium powder 50 parts; Silane coupling A-151 0.3 parts; Natvosol 2 parts; Disodium ethylene diamine tetraacetate 1 part; Calcium stearate 0.8 part; Tween-80 0.5 part; Gum Rosin 23 parts; CAB resin liquid 18 parts; Talcum powder 15 parts; And hexabromocyclododecane 15 parts.