CN104371514A - Anti-corrosion mould-proof moth-proof paint - Google Patents
Anti-corrosion mould-proof moth-proof paint Download PDFInfo
- Publication number
- CN104371514A CN104371514A CN201410539696.5A CN201410539696A CN104371514A CN 104371514 A CN104371514 A CN 104371514A CN 201410539696 A CN201410539696 A CN 201410539696A CN 104371514 A CN104371514 A CN 104371514A
- Authority
- CN
- China
- Prior art keywords
- paint
- leaf
- proof
- parts
- cortex cinnamomi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-corrosion mould-proof moth-proof paint prepared by mixing the following components in parts by weight: 10-15 parts of xylene, 25-29 parts of butyl acetate, 10-15 parts of ethyl acetate, 30-34 parts of alkyd resin, 10-15 parts of a curing agent, 0.5-3 parts of a mould-proof agent or 2-5 parts of a cinnamomum camphora leaf extract, 0.1-1 part of a defoaming agent, and 0.1-0.8 part of a levelling agent. The anti-corrosion mould-proof moth-proof paint has excellent anti-corrosion mould-proof performance, and does not contain benzene, formaldehyde, low-free TDI and other harmful substances and heavy metals.
Description
Technical field
The present invention relates to a kind of coating, particularly the mothproof paint of a kind of anticorrosive mildewproof.
Background technology
Paint is mainly the coating in order to decorate and to protect article that raw material is made with resin, adds material modified according to different purposes, as: ferric oxide, oxidisability etc.The origin of paint there is no final conclusion.B.C. 6000, China with mineral compound and pigment dyestuff baking mixed to paint improved.B.C. 1500, in France and Hispanic cavern, paint was for drawing and decoration.B.C. 1500, Egyptian's dyestuff such as indigo and madder manufactured blue and red pigment, but this paint is still far from perfect.In 18th century, due to the exploitation to Semen Lini oil and zinc oxide, paint industry is developed rapidly.20th century, painting technology has had significant development, having occurred that clinging power paint that is larger, higher, fire-retardant, the anticorrosive shades of colour high with thermostability of glossiness paints large is in early days main raw material mainly with vegetables oil, therefore is called " paint ", as the boiled wood oil of health environment-friendly ecosystem.No matter the coating products of to be traditional with crude substance be raw material, or in modern development to synthesize the coating products that Chemicals are raw material, all belong to organic chemical industry's macromolecular material, the film formed belongs to macromolecular compound type.The classification of the Chemicals of passing through according to the modern times, coating belongs to fine chemical product.Modern coating is progressively becoming the polyfunctional engineering materials of a class, is an important industry in chemical industry.
At present, there is the defect that anticorrosive mildewproof performance is not good, therefore, need to develop a kind of anticorrosive mildewproof performance preferably paint in conventional bamboo woodenware paint under high humidity environment.
Summary of the invention
The object of the present invention is to provide the mothproof paint of a kind of anticorrosive mildewproof, anticorrosive mildewproof excellent performance, not containing objectionable impurities and heavy metals such as benzene, formaldehyde, low-free TDIs.
The technical solution adopted for the present invention to solve the technical problems is:
The mothproof paint of a kind of anticorrosive mildewproof, by weight, is mixed by following component:
The feature of the mothproof paint of anticorrosive mildewproof of the present invention is:
1, belong to two component, air drying type, have easy to use, the advantage that rate of drying is adjustable.
2, wide spectrum, long-acting kill various bacteria, fungi and yeasts, have special efficacy to mould, nontoxic.
3, be the dry film fungus-proof antisepsis being specifically designed to bamboo woodenware.
4, not containing objectionable impurities and heavy metals such as benzene, formaldehyde, low-free TDIs.
In formula of the present invention, this natural plant milk extract of leaf of Yellow cinnamon extract can be adopted to replace chemical anti mildew agent, to reduce the use of chemical assistant, better environmental protection, leaf of Yellow cinnamon extract has the effect of mildew-resistant, mothproof, sterilization, delicate fragrance, and also there is auxiliary light effect, there is the performance more excellent than mould inhibitor.
As preferably, described solidifying agent is isocyanate curing agent.
As preferably, the preparation method of described leaf of Cortex cinnamomi camphorae extract is: leaf of Cortex cinnamomi camphorae is dried to water ratio below 10%, pulverizes, and adds dehydrated alcohol mixing by the solid-liquid ratio of 1g:10-15ml, 20-40min is extracted at 40-50 DEG C, filter, filter residue adds dehydrated alcohol by the solid-liquid ratio of 1g:8-12ml, extracts 40-60min at 40-50 DEG C, filter, merging filtrate, concentrating under reduced pressure reclaims ethanol, obtains leaf of Cortex cinnamomi camphorae extract.Leaf of Cortex cinnamomi camphorae extract adopts preparation method of the present invention, and extraction yield is high, and result of use is good.
As preferably, described defoamer model is BYK-A530.
As preferably, described flow agent model is BYK-358N.
The invention has the beneficial effects as follows:
1, can manually or electrostatic automatic coating.
2, paint film flexibility is good, anti-scratch, strong adhesion, hardness are high.
3, paint film is plentiful tough and tensile, and be smooth to the touch exquisiteness, and ageing resistance is good, good decorative property.
4, resistance toheat is good, acid and alkali-resistance, and wear resistance is good, anti-scouring.
5, anticorrosive mildewproof insect protected excellent performance, not containing objectionable impurities and heavy metals such as benzene, formaldehyde, low-free TDIs.
Embodiment
Below by specific embodiment, technical scheme of the present invention is described in further detail.
In the present invention, if not refer in particular to, the raw material adopted and equipment etc. all can be buied from market or this area is conventional.Method in following embodiment, if no special instructions, is the ordinary method of this area.
The defoamer model used in the present invention is BYK-A530, commercially available; Flow agent model is BYK-358N, commercially available.Solidifying agent is isocyanate curing agent, commercially available.Dimethylbenzene, N-BUTYL ACETATE, ethyl acetate, Synolac are commercially available prod.
Embodiment 1:
The mothproof paint of a kind of anticorrosive mildewproof, by weight, is mixed (preparation method is existing ordinary method) by following component:
Embodiment 2:
The mothproof paint of a kind of anticorrosive mildewproof, by weight, is mixed by following component:
Embodiment 3:
The mothproof paint of a kind of anticorrosive mildewproof, by weight, is mixed by following component:
Embodiment 4:
The difference of the present embodiment and embodiment 1 is to replace mould inhibitor to use with leaf of Cortex cinnamomi camphorae extract, and leaf of Cortex cinnamomi camphorae extract consumption is 2 parts, the other the same as in Example 1.
The preparation method of leaf of Cortex cinnamomi camphorae extract is: leaf of Cortex cinnamomi camphorae is dried to water ratio below 10%, pulverize, add dehydrated alcohol mixing by the solid-liquid ratio of 1g:10ml, at 40 DEG C, extract 40min, filter, filter residue adds dehydrated alcohol by the solid-liquid ratio of 1g:8ml, extract 60min at 40 DEG C, filter, merging filtrate, concentrating under reduced pressure reclaims ethanol, obtains leaf of Cortex cinnamomi camphorae extract.
Embodiment 5:
The difference of the present embodiment and embodiment 2 is to replace mould inhibitor to use with leaf of Cortex cinnamomi camphorae extract, and leaf of Cortex cinnamomi camphorae extract consumption is 5 parts, the other the same as in Example 2.
The preparation method of leaf of Cortex cinnamomi camphorae extract is: leaf of Cortex cinnamomi camphorae is dried to water ratio below 10%, pulverize, add dehydrated alcohol mixing by the solid-liquid ratio of 1g:15ml, at 50 DEG C, extract 20min, filter, filter residue adds dehydrated alcohol by the solid-liquid ratio of 1g:12ml, extract 40min at 50 DEG C, filter, merging filtrate, concentrating under reduced pressure reclaims ethanol, obtains leaf of Cortex cinnamomi camphorae extract.
Embodiment 6:
The difference of the present embodiment and embodiment 3 is to replace mould inhibitor to use with leaf of Cortex cinnamomi camphorae extract, and leaf of Cortex cinnamomi camphorae extract consumption is 4 parts, the other the same as in Example 3.
The preparation method of leaf of Cortex cinnamomi camphorae extract is: leaf of Cortex cinnamomi camphorae is dried to water ratio below 10%, pulverize, add dehydrated alcohol mixing by the solid-liquid ratio of 1g:12ml, at 45 DEG C, extract 30min, filter, filter residue adds dehydrated alcohol by the solid-liquid ratio of 1g:10ml, extract 50min at 45 DEG C, filter, merging filtrate, concentrating under reduced pressure reclaims ethanol, obtains leaf of Cortex cinnamomi camphorae extract.
Product of the present invention, performance test is as follows:
| Project | Index | Detection method |
| Paint film appearance and color | Colors, paint film flat smooth | GB/T1729 |
| Time of drying | Surface drying: 1h, does solid work: 24h | GB/T1728 |
| Sticking power (drawing compartment apart from 1mm) | ≤ 1 grade | GB/T9286 |
| Pencil hardness | ≥H | GB/T6739 |
| Shock resistance | ≥50cm | GB/T1732 |
| Snappiness | ≤1mm | GB/T1731 |
| Mildew resistance (mixed strains 120 days) | 0 grade | GB/T1741 |
| Abrasion resistance (200g counterweight pressed by wet cloth) | >=1500 times | GB/T9266 |
| Acid and alkali-resistance (saturated calcium hydroxide, 5% sulphur | Not bubble, does not come off | GB/T9274 |
[0048]
| Acid), 24h | ||
| Wet-heat resisting (80 DEG C, 95% humidity), 7 days | Not bubble, does not come off | GB/T1740 |
The paint film flexibility of product formation of the present invention is good, anti-scratch, strong adhesion, hardness are high; Paint film is plentiful tough and tensile, and be smooth to the touch exquisiteness, and ageing resistance is good, good decorative property; Resistance toheat is good, acid and alkali-resistance, and wear resistance is good, anti-scouring; Anticorrosive mildewproof insect protected excellent performance, not containing objectionable impurities and heavy metals such as benzene, formaldehyde, low-free TDIs.
Above-described embodiment is one of the present invention preferably scheme, not does any pro forma restriction to the present invention, also has other variant and remodeling under the prerequisite not exceeding the technical scheme described in claim.
Claims (5)
1. the mothproof paint of anticorrosive mildewproof, is characterized in that: by weight, is mixed by following component:
Mould inhibitor 0.5-3 part or leaf of Yellow cinnamon extract 2-5 part,
Defoamer 0.1-1 part,
Flow agent 0.1-0.8 part.
2. the mothproof paint of a kind of anticorrosive mildewproof according to claim 1, is characterized in that: described solidifying agent is isocyanate curing agent.
3. the mothproof paint of a kind of anticorrosive mildewproof according to claim 1 and 2, it is characterized in that: the preparation method of described leaf of Cortex cinnamomi camphorae extract is: leaf of Cortex cinnamomi camphorae is dried to water ratio below 10%, pulverize, add dehydrated alcohol mixing by the solid-liquid ratio of 1g:10-15ml, 20-40min is extracted at 40-50 DEG C, filter, filter residue adds dehydrated alcohol by the solid-liquid ratio of 1g:8-12ml, extracts 40-60min at 40-50 DEG C, filter, merging filtrate, concentrating under reduced pressure reclaims ethanol, obtains leaf of Cortex cinnamomi camphorae extract.
4. the mothproof paint of a kind of anticorrosive mildewproof according to claim 1 and 2, is characterized in that: described defoamer model is BYK-A530.
5. the mothproof paint of a kind of anticorrosive mildewproof according to claim 1 and 2, is characterized in that: described flow agent model is BYK-358N.