CN1603373A - Colored polyurethane (PU polyester) antibacterial wood paint - Google Patents
Colored polyurethane (PU polyester) antibacterial wood paint Download PDFInfo
- Publication number
- CN1603373A CN1603373A CN 03151429 CN03151429A CN1603373A CN 1603373 A CN1603373 A CN 1603373A CN 03151429 CN03151429 CN 03151429 CN 03151429 A CN03151429 A CN 03151429A CN 1603373 A CN1603373 A CN 1603373A
- Authority
- CN
- China
- Prior art keywords
- mixture
- polyester
- colored polyurethane
- wooden article
- article coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention involves a kind of colored polyurethane antibacterial wooden article coating, its characteristic lies in: By A, the B two components constitutions, the A component is composed for following constituent and the per cent by weight: Toluene two isocyanogens diethylene glycol dinitrate (TDI) and three methylol propane addition compound either TDI tripolymer or their mixture 25%~65%, ethyl acetate, xylene solvent or their mixture 35%~75%, B component for following constituent and per cent by weight composition: The alkyd resin or the modified alkyd resin, or their mixture 49.88%~69.88%, the cutyl acetate or the ethyl acetate, the xylene solvent or their mixture 10.19%~30.19%, the defoamer 0.16%~0.36%, flows the even medicinal preparation 0.20%~0.50%, the pigment or the fuel 3.50%~30.50%, antibiotics 0.10%~5.0%, the dispersing agent 0.10%~0.30%, guards against sinks medicinal preparation 0.04%~1.0%, the anti- yellow stain helps medicinal preparation 0.79%~0.99%, the deadening agent 0%~12.50%, armor component and second grade component according to 0.3~1: 1 proportion mix. The invention merit is can kill extinguishes wooden woodware surface the and so on the furniture, wood floor bacterium.
Description
Technical field
The present invention relates to a kind of woodwork coating, particularly a kind of colored polyurethane antibacterial wooden article coating.
Background technology
Wood product surfaces such as wooden furniture, timber floor exist harmful bacterium at present, in order to keep the health of product surface, adopt outside measure usually, as spraying medicine, medicine wiping etc.Its defective is that medicine easily runs off, and bacterium easily regenerates, and antibiotic timeliness is short, and antimicrobial efficiency is low, the cost height.
Summary of the invention
The objective of the invention is to solve the existing problem of woodwork coating in the prior art, a kind of application of woodworks such as wooden furniture, timber floor and colored polyurethane antibacterial wooden article coating of decoration design for residence of can be used for is provided.The present invention designs a kind of colored polyurethane (PU polyester) antibacterial wooden article coating, it is characterized in that: constitute by A, B two components,
The A component is that following constituent and weight percent are formed:
The affixture of tolylene diisocyanate (TDI) and TriMethylolPropane(TMP) or the tripolymer of TDI or their mixture 25%~65%, N-BUTYL ACETATE or vinyl acetic monomer, xylene solvent or their mixture 35%~75%, the B component is that following constituent and weight percent are formed: Synolac or modified alkyd resin, or their mixture 49.88%~69.88%, N-BUTYL ACETATE or vinyl acetic monomer, xylene solvent or their mixture 10.19%~30.19%, defoamer 0.16%~0.36%, flow agent 0.20%~0.50%, pigment or dyestuff 3.50%~30.50%, antiseptic-germicide 0.10%~5.0%, dispersion agent 0.10%~0.30%, anti-settling agent 0.04%~1.0%, anti-yellowing additive 0.79%~0.99%, matting agent 0%~12.50%, first component and component B are in 0.3~1: 1 ratio is mixed.Defoamer is CFC-151, BYK 066, moral modest 5100 or their mixture.Flow agent is KEPER-150, BYK 310, HX-3130 or their mixture.Pigment or dyestuff are titanium dioxide, permanent yellow, light-resistant dye or their mixture.Antiseptic-germicide is mineral-type nano titania antiseptic-germicide, organic class isothiazolinone antiseptic-germicide or their mixture.Dispersion agent is KEPER-602, BYK-110 or their mixture.Anti-settling agent is 6901-20X, BYK 410, efka-, 4500 or their mixture.Anti-yellowing additive is KH-10,1130 or their mixture.Matting agent is ED30, mute light powder or their mixture.Advantage of the present invention is to kill the bacterium of wood product surfaces such as wooden furniture, timber floor.
Below in conjunction with embodiment the present invention is elaborated,
Embodiment
Can add proper amount of diluting during construction as the case may be and regulate viscosity.
The present invention mainly utilizes filmogen (Synolac, modified alkyd resin or cellulose nitrate ester etc.) in the prescription, antiseptic-germicide, matting agent, N-BUTYL ACETATE, pigment (dyestuff), flow agent, defoamer etc., in the coating process of woodworks such as wooden furniture, timber floor, form antibacterial film, kill the bacterium that grows on its surface thereby press down.Have advantages such as antimicrobial efficiency height, decorative effect are good, easy construction, can be used as the application and the decoration design for residence of modern wooden furniture.
After testing, antimicrobial efficiency is 99.9%.
After testing, harmful substance contents is as follows:
Volatile organic compounds (VOC) 648g/L
Benzene does not detect
Toluene and dimethylbenzene summation 28.5%
Free toluene diisocyanate 0.5%
After testing, main quality and technical index is as follows:
Appearance of film surfacing, smooth
Time of drying (25 ℃)
Surface drying 15min
Do solid work≤24h
Sticking power≤3 grade
Hardness (the pencil method, 72h) 〉=H
Water tolerance (25 ℃, 18h) no change
Thermotolerance (60 ℃, 2h) no change
Example 1 is got 40 kilograms of the affixtures of tolylene diisocyanate (TDI) and TriMethylolPropane(TMP), 60 kilograms of N-BUTYL ACETATEs, get 50 kilograms of Synolac again, 20 kilograms of N-BUTYL ACETATEs, 0.2 kilogram of defoamer (CFC-151), 0.20 kilogram of flow agent (KEPER-150), 20 kilograms of pigment or dyestuffs (titanium dioxide), 0.2 kilogram of dispersion agent (KEPER-602), 0.2 kilogram of anti-settling agent (6901-20X), 0.8 kilogram of anti-yellowing additive (KH-10), 5.40 kilograms of matting agents (mute light powder) add 3 kilograms of antiseptic-germicides (nano titania antiseptic-germicide) after fully disperseing.
Example 2 is got 40 kilograms of the affixtures of tolylene diisocyanate (TDI) and TriMethylolPropane(TMP), 60 kilograms of N-BUTYL ACETATEs, get 55.4 kilograms of Synolac again, 20 kilograms of N-BUTYL ACETATEs, 0.2 kilogram of defoamer (moral modest 5100), 0.20 kilogram of flow agent (HX-3130), 20 kilograms of pigment (titanium dioxide), 0.2 kilogram of dispersion agent (KEPER-602), 0.2 kilogram of anti-settling agent (6901-20X), 0.8 kilogram of anti-yellowing additive (KH-10) adds 3 kilograms of antiseptic-germicides (isothiazolinone antiseptic-germicide) after fully disperseing.
Coating process of the present invention requires, and mixes up this product, with the method for brushing and spray woodworks such as wooden furniture, timber floor is carried out application, gets final product.
Claims (9)
1, a kind of colored polyurethane (PU polyester) antibacterial wooden article coating is characterized in that: constitutes by A, B two components,
The A component is that following constituent and weight percent are formed:
The affixture of tolylene diisocyanate (TDI) and TriMethylolPropane(TMP) or the tripolymer of TDI or their mixture
25%~65%,
N-BUTYL ACETATE or vinyl acetic monomer, xylene solvent or their mixture 35%~75%,
The B component is that following constituent and weight percent are formed:
Synolac or modified alkyd resin or their mixture 49.88%~69.88%,
N-BUTYL ACETATE or vinyl acetic monomer, xylene solvent or their mixture 10.19%~30.19%,
Defoamer 0.16%~0.36%,
Flow agent 0.20%~0.50%,
Pigment or dyestuff 3.50%~30.50%,
Antiseptic-germicide 0.10%~5.0%,
Dispersion agent 0.10%~0.30%,
Anti-settling agent 0.04%~1.0%,
Anti-yellowing additive 0.79%~0.99%,
Matting agent 0%~12.50%,
First component and component B are in 0.3~1: 1 ratio is mixed.
2, the described a kind of colored polyurethane of claim 1 (PU polyester) antibacterial wooden article coating is characterized in that: defoamer is CFC-151, BYK 066, moral modest 5100 or their mixture.
3, the described a kind of colored polyurethane of claim 1 (PU polyester) antibacterial wooden article coating, it is characterized in that: flow agent is KEPER-150, BYK 310, HX-3130 or their mixture.
4, the described a kind of colored polyurethane of claim 1 (PU polyester) antibacterial wooden article coating, it is characterized in that: pigment or dyestuff are titanium dioxide, permanent yellow, light-resistant dye or their mixture.
5, the described a kind of colored polyurethane of claim 1 (PU polyester) antibacterial wooden article coating is characterized in that: antiseptic-germicide is mineral-type nano titania antiseptic-germicide, organic class isothiazolinone antiseptic-germicide or their mixture.
6, the described a kind of colored polyurethane of claim 1 (PU polyester) antibacterial wooden article coating, it is characterized in that: dispersion agent is KEPER-602, BYK-110 or their mixture.
7, the described a kind of colored polyurethane of claim 1 (PU polyester) antibacterial wooden article coating, it is characterized in that: anti-settling agent is 6901-20X, BYK 410, efka-4500 or their mixture.
8, the described a kind of colored polyurethane of claim 1 (PU polyester) antibacterial wooden article coating is characterized in that: anti-yellowing additive is KH-10,1130 or their mixture.
9, the described a kind of colored polyurethane of claim 1 (PU polyester) antibacterial wooden article coating is characterized in that: matting agent is ED30, mute light powder or their mixture.