CN104358183A - 一种纸板用高硬度涂料及其制备方法 - Google Patents

一种纸板用高硬度涂料及其制备方法 Download PDF

Info

Publication number
CN104358183A
CN104358183A CN201410479710.7A CN201410479710A CN104358183A CN 104358183 A CN104358183 A CN 104358183A CN 201410479710 A CN201410479710 A CN 201410479710A CN 104358183 A CN104358183 A CN 104358183A
Authority
CN
China
Prior art keywords
parts
coating
stock
itaconate
acrylonitrile
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410479710.7A
Other languages
English (en)
Other versions
CN104358183B (zh
Inventor
费金华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Ruize Chuangyi New Material Co ltd
Original Assignee
Suzhou Shengpula New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Shengpula New Material Technology Co Ltd filed Critical Suzhou Shengpula New Material Technology Co Ltd
Priority to CN201410479710.7A priority Critical patent/CN104358183B/zh
Publication of CN104358183A publication Critical patent/CN104358183A/zh
Application granted granted Critical
Publication of CN104358183B publication Critical patent/CN104358183B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种纸板用高硬度涂料及其制备方法，该涂料以质量份计含有以下成分：丙烯酸正丁酯15～35份，三羟甲基丙烷三丙烯酸酯10～20份，苯乙烯6～15份，丙烯腈2.8～4.6份，胶体二氧化硅0.6～1.6份，衣康酸酯0.2～0.4份，乙二胺0.07～0.13份，正十二烷基硫醇0.05～0.15份，二苯甲酮0.7～1.2份，去离子水48～65份。本发明提供的涂料具有很强的硬度，同时涂层的耐水、耐沸水、耐碱性都很高，对纸板具有很好的保护和装饰作用。

Description

一种纸板用高硬度涂料及其制备方法
技术领域
本发明涉及涂料领域，尤其涉及一种纸板用高硬度涂料及其制备方法。
背景技术
纸板存在于人们生活的各个角落，如箱纸板、电绝缘纸板、石膏纸板、封面纸板等。纸板一般采用涂覆涂料的方法增加美观度。市场上纸板专用涂料的种类很少，并且硬度、弹性、耐水、耐碱性能都不高，不能很好地起到保护和装饰纸板的作用。
发明内容
解决的技术问题：针对市场上纸板专用涂料种类少，涂料硬度、弹性、耐水、耐碱性能不高的缺点，本发明提供一种纸板用高硬度涂料及其制备方法。
技术方案：一种纸板用高硬度涂料，以质量份计含有以下成分：丙烯酸正丁酯15～35份，三羟甲基丙烷三丙烯酸酯10～20份，苯乙烯6～15份，丙烯腈2.8～4.6份，胶体二氧化硅0.6～1.6份，衣康酸酯0.2～0.4份，乙二胺0.07～0.13份，正十二烷基硫醇0.05～0.15份，二苯甲酮0.7～1.2份，去离子水48～65份。
上述所述的一种纸板用高硬度涂料，以质量份计含有以下成分：丙烯酸正丁酯25份，三羟甲基丙烷三丙烯酸酯15份，苯乙烯10份，丙烯腈3.7份，胶体二氧化硅1.1份，衣康酸酯0.3份，乙二胺0.1份，正十二烷基硫醇0.1份，二苯甲酮1份，去离子水56份。
上述所述的一种纸板用高硬度涂料的制备步骤如下：将丙烯酸正丁酯、三羟甲基丙烷三丙烯酸酯、苯乙烯、丙烯腈、胶体二氧化硅、衣康酸酯、乙二胺、正十二烷基硫醇、二苯甲酮和去离子水混合均匀，在温度为70～80℃下保温1～2h，接着用浓度为25％的氨水调节pH值至7～8，即得成品。
有益效果：本发明提供的一种纸板用高硬度涂料及其制备方法，该涂料具有很强的硬度，同时涂层的耐水、耐沸水、耐碱性都很高，对纸板具有很好的保护和装饰作用。
具体实施方式
实施例1
本实施例提供一种纸板用高硬度涂料，以质量份计含有以下成分：丙烯酸正丁酯15份，三羟甲基丙烷三丙烯酸酯10份，苯乙烯6份，丙烯腈2.8份，胶体二氧化硅0.6份，衣康酸酯0.2份，乙二胺0.07份，正十二烷基硫醇0.05份，二苯甲酮0.7份，去离子水48份。
一种纸板用高硬度涂料的制备步骤如下：将丙烯酸正丁酯、三羟甲基丙烷三丙烯酸酯、苯乙烯、丙烯腈、胶体二氧化硅、衣康酸酯、乙二胺、正十二烷基硫醇、二苯甲酮和去离子水混合均匀，在温度为70℃下保温1h，接着用浓度为25％的氨水调节pH值至7，即得成品。
实施例2
本实施例提供一种纸板用高硬度涂料，以质量份计含有以下成分：丙烯酸正丁酯35份，三羟甲基丙烷三丙烯酸酯20份，苯乙烯15份，丙烯腈4.6份，胶体二氧化硅1.6份，衣康酸酯0.4份，乙二胺0.13份，正十二烷基硫醇0.15份，二苯甲酮1.2份，去离子水65份。
一种纸板用高硬度涂料的制备步骤如下：将丙烯酸正丁酯、三羟甲基丙烷三丙烯酸酯、苯乙烯、丙烯腈、胶体二氧化硅、衣康酸酯、乙二胺、正十二烷基硫醇、二苯甲酮和去离子水混合均匀，在温度为80℃下保温2h，接着用浓度为25％的氨水调节pH值至8，即得成品。
实施例3
本实施例提供一种纸板用高硬度涂料，以质量份计含有以下成分：丙烯酸正丁酯25份，三羟甲基丙烷三丙烯酸酯15份，苯乙烯10份，丙烯腈3.7份，胶体二氧化硅1.1份，衣康酸酯0.3份，乙二胺0.1份，正十二烷基硫醇0.1份，二苯甲酮1份，去离子水56份。
一种纸板用高硬度涂料的制备步骤如下：将丙烯酸正丁酯、三羟甲基丙烷三丙烯酸酯、苯乙烯、丙烯腈、胶体二氧化硅、衣康酸酯、乙二胺、正十二烷基硫醇、二苯甲酮和去离子水混合均匀，在温度为75℃下保温1.5h，接着用浓度为25％的氨水调节pH值至7，即得成品。
上述实施例1～实施例3的一种纸板用高硬度涂料的技术性能指标，其检测结果如下：
检测结果
检测项目 测试指标 实施例1 实施例2 实施例3
铅笔硬度(7d) GB/T6739 ≥2H ≥2H ≥2H
耐碱性15d·.h≥ GB/T1763-89 32 35 38
以上对本发明实施例进行了详细介绍，对于本领域的一般技术人员，依据本发明实施例的思想，在具体实施方式及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (3)

1.一种纸板用高硬度涂料，其特征在于以质量份计含有以下成分：丙烯酸正丁酯15～35份，三羟甲基丙烷三丙烯酸酯10～20份，苯乙烯6～15份，丙烯腈2.8～4.6份，胶体二氧化硅0.6～1.6份，衣康酸酯0.2～0.4份，乙二胺0.07～0.13份，正十二烷基硫醇0.05～0.15份，二苯甲酮0.7～1.2份，去离子水48～65份。
2.根据权利要求1所述的一种纸板用高硬度涂料，其特征在于以质量份计含有以下成分：丙烯酸正丁酯25份，三羟甲基丙烷三丙烯酸酯15份，苯乙烯10份，丙烯腈3.7份，胶体二氧化硅1.1份，衣康酸酯0.3份，乙二胺0.1份，正十二烷基硫醇0.1份，二苯甲酮1份，去离子水56份。
3.如权利要求1所述的一种纸板用高硬度涂料的制备方法，其特征在于该方法的制备步骤如下：将丙烯酸正丁酯、三羟甲基丙烷三丙烯酸酯、苯乙烯、丙烯腈、胶体二氧化硅、衣康酸酯、乙二胺、正十二烷基硫醇、二苯甲酮和去离子水混合均匀，在温度为70～80℃下保温1～2h，接着用浓度为25％的氨水调节pH值至7～8，即得成品。
CN201410479710.7A 2014-09-18 2014-09-18 一种纸板用高硬度涂料及其制备方法 Active CN104358183B (zh)