CN104358114A - 一种海藻纤维高弹丝变形油剂 - Google Patents
一种海藻纤维高弹丝变形油剂 Download PDFInfo
- Publication number
- CN104358114A CN104358114A CN201410694727.4A CN201410694727A CN104358114A CN 104358114 A CN104358114 A CN 104358114A CN 201410694727 A CN201410694727 A CN 201410694727A CN 104358114 A CN104358114 A CN 104358114A
- Authority
- CN
- China
- Prior art keywords
- parts
- deformation
- oiling agent
- stretch yarn
- alginate fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种海藻纤维高弹丝变形油剂，其组分按重量份计，乙醇100份、松油30-40份、天然椰子油30-40份、玻尿酸5-17份、棕榈酸酯聚氧乙烯醚5-9份、淀粉酶2-6份、三羟甲基丙烷三C5-9酸酯2-5份、氯化钠0.5-2份、硫酸镁0.01-1份。本发明所提供的海藻纤维高弹丝变形油剂，在高弹丝变形油剂的配方基础上，得到一款针对性强的变形油剂，所得海藻纤维高弹丝弹性收缩率大，且弹力均匀，拓展了海藻纤维的应用范围。
Description
技术领域
本发明涉及一种纺织染整助剂。
背景技术
对纺织材料(纤维、纱线和织物)进行以化学处理为主的工艺过程，现代也通称为印染。染整同纺纱、机织或针织生产一起，形成纺织物生产的全过程。染整包括预处理、染色、印花和整理。染整质量的优劣对纺织品的使用价值有重要的影响。预处理亦称练漂，其主要目的在于去除纺织材料上的杂质，使后续的染色、印花、整理加工得以顺利进行，获得预期的加工效果。染色是通过染料和纤维发生物理的或化学的结合而使纺织材料具有一定的颜色。印花是用色浆在纺织物上获得彩色花纹图案。整理是通过物理作用或使用化学药剂改进织物的光泽、形态等外观；提高织物的服用性能或使织物具有拒水、拒油等特性。大多数整理加工是在织物染整的后阶段进行的。在毛纺织物染整中往往把许多预处理过程归入整理范畴，并把整理划分为湿整理和干整理。目前，用于制作高弹织物或纤维丝的助剂，只能应用于毛纤维、棉纤维和粘胶纤维，对于其它的一些纤维，效果不好。海藻纤维作为一种有机纤维，很难做成高弹丝。
发明内容
本发明要解决的技术问题是克服现有的缺陷，提供了一种海藻纤维高弹丝变形油剂。
本发明的目的通过以下技术方案来具体实现：
一种海藻纤维高弹丝变形油剂，其组分按重量份计，乙醇100份、松油30-40份、天然椰子油30-40份、玻尿酸5-17份、棕榈酸酯聚氧乙烯醚5-9份、淀粉酶2-6份、三羟甲基丙烷三C5-9酸酯2-5份、氯化钠0.5-2份、硫酸镁0.01-1份。
作为优选方案，上述的海藻纤维高弹丝变形油剂，其组分按重量份计，乙醇100份、松油35份、天然椰子油35份、玻尿酸12.5份、棕榈酸酯聚氧乙烯醚7.5份、淀粉酶5份、三羟甲基丙烷三C5-9酸酯2.5份、氯化钠1份、硫酸镁0.08份。
本发明的有益效果：
本发明所提供的海藻纤维高弹丝变形油剂，在高弹丝变形油剂的配方基础上，得到一款针对性强的变形油剂，所得海藻纤维高弹丝弹性收缩率大，且弹力均匀，拓展了海藻纤维的应用范围。
具体实施方式
以下对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例1：
一种海藻纤维高弹丝变形油剂，其组分按重量份计，乙醇100份、松油35份、天然椰子油35份、玻尿酸12.5份、棕榈酸酯聚氧乙烯醚7.5份、淀粉酶5份、三羟甲基丙烷三C5-9酸酯2.5份、氯化钠1份、硫酸镁0.08份。
实施例2：
一种海藻纤维高弹丝变形油剂，其组分按重量份计，乙醇100份、松油30份、天然椰子油40份、玻尿酸5份、棕榈酸酯聚氧乙烯醚9份、淀粉酶2份、三羟甲基丙烷三C5-9酸酯5份、氯化钠0.5份、硫酸镁1份。
实施例3：
一种海藻纤维高弹丝变形油剂，其组分按重量份计，乙醇100份、松油40份、天然椰子油30份、玻尿酸17份、棕榈酸酯聚氧乙烯醚5份、淀粉酶6份、三羟甲基丙烷三C5-9酸酯2份、氯化钠2份、硫酸镁0.01份。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (2)
1.一种海藻纤维高弹丝变形油剂，其特征在于：其组分按重量份计，乙醇100份、松油30-40份、天然椰子油30-40份、玻尿酸5-17份、棕榈酸酯聚氧乙烯醚5-9份、淀粉酶2-6份、三羟甲基丙烷三C5-9酸酯2-5份、氯化钠0.5-2份、硫酸镁0.01-1份。
2. 根据权利要求1所述的海藻纤维高弹丝变形油剂，其特征在于：其组分按重量份计，乙醇100份、松油35份、天然椰子油35份、玻尿酸12.5份、棕榈酸酯聚氧乙烯醚7.5份、淀粉酶5份、三羟甲基丙烷三C5-9酸酯2.5份、氯化钠1份、硫酸镁0.08份。