CN104341129A - Concrete pavement brick with water permeability and preparation method thereof - Google Patents
Concrete pavement brick with water permeability and preparation method thereof Download PDFInfo
- Publication number
- CN104341129A CN104341129A CN201410554124.4A CN201410554124A CN104341129A CN 104341129 A CN104341129 A CN 104341129A CN 201410554124 A CN201410554124 A CN 201410554124A CN 104341129 A CN104341129 A CN 104341129A
- Authority
- CN
- China
- Prior art keywords
- water
- weight parts
- fabric
- bed material
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a concrete pavement brick with water permeability. The concrete pavement brick comprises a fabric layer and a base layer, wherein the base layer is prepared from the following raw materials in parts by weight: 200 parts of 42.5# cement, 100 parts of 0.5cm pebbles or ore, 850 parts of 200-mesh pebble flour, 850 parts of 200-mesh ore flour and 110 parts of water. Compared with the prior art, the concrete pavement brick with water permeability disclosed by the invention is high in compression strength, good in fracture resistance, good in waterproof function, standard in physical dimension, skidproof, and free of radioactivity.
Description
Technical field
The present invention's municipal administration field, particularly a kind of concrete road pavement brick with water-permeable and preparation method thereof.
Background technology
The manual Water milled brick that existing Route for pedestrians pavior brick adopts manual mode to utilize mold box to produce, intensity is low, became uneven, aberration greatly, not anti-skidding, waterproof and water mill can cause water pollutions.
Common water-permeable brick intensity is low, easily fade.Utilize the natural granite intensity of infrared rays or semiautomatic equipment cutting high, waterproof but generally there is radioactivity.
The vitrified brick obtained through mechanical pressing and high-temperature roasting be waterproof, compare conference spoiled soil mountain forest and arable land to the demand of clay.
Summary of the invention
An object of the present invention is just to provide a kind of concrete road pavement brick with water-permeable, and this has, and the concrete road pavement brick compressive strength of water-permeable is high, flexural capacity good, have pervious function, geometrical dimension standard, anti-skidding, and does not have radioactivity.
Technical scheme is: a kind of concrete road pavement brick with water-permeable, comprise precoat and initial bed, described initial bed bed material is made up of No. 42.5 cement, 0.5cm cobble or ore, 200 order cobble flours, 200 order ore flours and water, and described No. 42.5 cement are 200 weight parts, 0.5cm cobble or ore are 100 weight parts, 200 order cobble flours are 850 weight parts, 200 order ore flours are 850 weight parts, water is 110 weight parts.
As preferably, described precoat thickness is 5-10mm, and initial bed thickness is 50-55mm.
As preferably, described precoat fabric is made up of No. 42.5 cement, quartz sand, pigment and water, and described No. 42.5 cement are 100 weight parts, quartz sand is 300 weight parts, pigment is 4 weight parts, water is 25 weight parts.
As preferably, described precoat fabric is made up of No. 42.5 cement, quartz sand, granite, pigment and water, and described No. 42.5 cement are 100 weight parts, quartz sand is 210 weight parts, granite is 90 weight parts, pigment is weight part, water is 25 weight parts.
As preferably, described precoat fabric is made up of No. 42.5 cement, river sand, pigment and water, and described No. 42.5 cement are 100 weight parts, river sand is 300 weight parts, pigment is 4 weight parts, water is 25 weight parts.
Two of the object of the invention is that providing a kind of prepares the above-mentioned method with the concrete road pavement brick of water-permeable.
Technical scheme is: a kind ofly prepare the above-mentioned method with the concrete road pavement brick of water-permeable, comprises the following steps:
1. fabric and bed material is taken by formula and backing material formula respectively;
2. respectively to having taken fabric and bed material mixes;
3. respectively mixed fabric and bed material are stirred;
4. formed product; This step is being exempted to carry out in supporting brick machine;
5. product is obtained after surface treatment.
Compared with prior art, beneficial effect of the present invention is:
The concrete road pavement brick compressive strength with water-permeable of the present invention is high, and flexural capacity is good, and has pervious function.
The concrete road pavement brick with water-permeable of the present invention and traditional-handwork brickmaking technology, without compared with pressurization, can reduce cement about 30%.
The concrete road pavement brick with water-permeable of the present invention solves that manual Water milled brick intensity is low, geometrical dimension is nonstandard, not anti-skidding, waterproof, easily pollute, common water-permeable brick intensity is low, fugitive color, natural granite is waterproof, have radioactivity, and vitrified brick is waterproof, can the shortcoming in spoiled soil mountain forest and arable land.
The concrete road pavement brick geometrical dimension standard with water-permeable of the present invention, can do airport, harbour, parking lot; Anti-skidding; The texture with lithotome makes up again lithotome, the fluid-tight defect of diaphragm capsule Water milled brick.
The present invention adopts dry type rubbing down, and rubbing down powder can be recycled.And traditional brickmaking technology adopts water mill technology, produce water mill mud, can not reuse, contaminate environment.
It is product within 600 that present invention process can do specification.
Embodiment
The invention will be further described below.
The preparation of embodiment 1 pitted skin concrete road pavement brick
1. fabric and bed material is taken.
No. 42.5 cement 100 weight parts, quartz sand 300 weight part, pigment 4 weight part and water 25 weight part is claimed to mix, as fabric.
No. 42.5 cement 200 weight parts, 0.5cm cobble or ore 100 weight part, 200 order cobble flour 850 weight parts, 200 order ore flour 850 weight parts and water 110 weight part is claimed to mix, as bed material.
2. respectively fabric and bed material are stirred.
3. formed product and the demoulding.Formed product and the demoulding exempt from U18-15 to carry out in supporting brick machine.
Formed product: framed decline, pressure head are risen, then open bed material door, bed material car is sent into bed material and is carried out cloth, shakes the framed bed material that makes smooth, then bed material car return, pressure head pressure bed material, after compressing, pressure head returns, and then opens fabric door, fabric car is sent into fabric and is carried out cloth, the even cloth of fabric is on bed material, and then fabric car return, pressure head presses down and exciting vibratory compaction becomes brick.Exciting force is 60--240KN, and vibrational frequency is 8 ~ 55Hz, and time of vibration is 4-5S.
The demoulding: move forward to lifting table position with brick framed and brick is placed on after after on lifting table returns original position.
4. surface treatment.Surface treatment is dry type rubbing down, and abrasive material is shot.
5. obtain product 600mm × 600mm × 60mm pitted skin concrete road pavement brick, precoat thickness is 6mm, and joint thickness is 450 microns.
The preparation of embodiment 2 artificial grantie surface concrete pavior brick
1. fabric and bed material is taken.
No. 42.5 cement 100 weight parts, quartz sand 210 weight part, granite 90 weight part, pigment weight part, water 25 weight part is claimed to mix, as fabric.
No. 42.5 cement 200 weight parts, 0.5cm cobble or ore 100 weight part, 200 order cobble flour 850 weight parts, 200 order ore flour 850 weight parts and water 110 weight part is claimed to mix, as bed material.
2. respectively fabric and bed material are stirred.
3. formed product and the demoulding.Formed product and the demoulding exempt from U18-15 to carry out in supporting brick machine.
Formed product: framed decline, pressure head are risen, then open bed material door, bed material car is sent into bed material and is carried out cloth, shakes the framed bed material that makes smooth, then bed material car return, pressure head pressure bed material, after compressing, pressure head returns, and then opens fabric door, fabric car is sent into fabric and is carried out cloth, the even cloth of fabric is on bed material, and then fabric car return, pressure head presses down and exciting vibratory compaction becomes brick.Exciting force is 240KN, and vibrational frequency is 8 ~ 55Hz, and time of vibration is 4-5S.
The demoulding: move forward to lifting table position with brick framed and brick is placed on after after on lifting table returns original position.
4. surface treatment.Surface treatment is dry type rubbing down, and abrasive material is shot.
5. obtain product 600mm × 600mm × 60mm artificial grantie surface concrete pavior brick, precoat thickness is 8mm, and joint thickness is 450 microns.
The preparation of embodiment 3 days Shamian Island concrete road pavement bricks
1. fabric and bed material is taken.
No. 42.5 cement 100 weight parts, river sand 300 weight part, pigment 4 weight part, water 25 weight part is claimed to mix, as fabric.
No. 42.5 cement 200 weight parts, 0.5cm cobble or ore 100 weight part, 200 order cobble flour 850 weight parts, 200 order ore flour 850 weight parts and water 110 weight part is claimed to mix, as bed material.
2. respectively fabric and bed material are stirred.
3. formed product and the demoulding.Formed product and the demoulding exempt from U18-15 to carry out in supporting brick machine.
Formed product: framed decline, pressure head are risen, then open bed material door, bed material car is sent into bed material and is carried out cloth, shakes the framed bed material that makes smooth, then bed material car return, pressure head pressure bed material, after compressing, pressure head returns, and then opens fabric door, fabric car is sent into fabric and is carried out cloth, the even cloth of fabric is on bed material, and then fabric car return, pressure head presses down and exciting vibratory compaction becomes brick.Exciting force is 240KN, and vibrational frequency is 8 ~ 55Hz, and time of vibration is 4-5S.
The demoulding: move forward to lifting table position with brick framed and brick is placed on after after on lifting table returns original position.
4. surface treatment.Surface treatment is dry type rubbing down, and abrasive material is shot.
5. obtain product 300mm × 300mm × 60mm days Shamian Island concrete road pavement bricks, precoat thickness is 9mm, and joint thickness is 450 microns.
Embodiment 4
The concrete road pavement brick that enforcement 1-3 produces out is respectively got 30 pieces detect by the detection method in JC/T 446-2000 (concrete road pavement brick), detected result sees the following form one.
Table one
Embodiment 5
The concrete road pavement brick produced out by embodiment 1-3 is respectively got 30 pieces and is carried out coefficient of permeability detection by the method in JC/T 945-2005 (water-permeable brick), and detected result sees the following form two.
Table two
Claims (9)
1. one kind has the concrete road pavement brick of water-permeable, comprise precoat and initial bed, described initial bed bed material is made up of No. 42.5 cement, 0.5cm cobble or ore, 200 order cobble flours, 200 order ore flours and water, and described No. 42.5 cement are 200 weight parts, 0.5cm cobble or ore are 100 weight parts, 200 order cobble flours are 850 weight parts, 200 order ore flours are 850 weight parts, water is 110 weight parts.
2. the concrete road pavement brick with water-permeable according to claim 1, is characterized in that: described precoat thickness is 5-10mm, and initial bed thickness is 50-55mm.
3. the concrete road pavement brick with water-permeable according to claim 1 and 2, it is characterized in that: described precoat fabric is made up of No. 42.5 cement, quartz sand, pigment and water, described No. 42.5 cement are 100 weight parts, quartz sand is 300 weight parts, pigment is 4 weight parts, water is 25 weight parts.
4. the concrete road pavement brick with water-permeable according to claim 1 and 2, it is characterized in that: described precoat fabric is made up of No. 42.5 cement, quartz sand, granite, pigment and water, described No. 42.5 cement are 100 weight parts, quartz sand is 210 weight parts, granite is 90 weight parts, pigment is 4 weight parts, water is 25 weight parts.
5. the concrete road pavement brick with water-permeable according to claim 1 and 2, it is characterized in that: described precoat fabric is made up of No. 42.5 cement, river sand, pigment and water, described No. 42.5 cement are 100 weight parts, river sand is 300 weight parts, pigment is 4 weight parts, water is 25 weight parts.
6. prepare the method with the concrete road pavement brick of water-permeable described in the arbitrary claim of claim 1-5, comprise the following steps:
1. fabric and bed material is taken by formula and backing material formula respectively;
2. respectively to having taken fabric and bed material mixes;
3. respectively mixed fabric and bed material are stirred;
4. formed product and the demoulding; This step is being exempted to carry out in supporting brick machine;
5. product is obtained after surface treatment.
7. preparation according to claim 6 has the method for the concrete road pavement brick of water-permeable, it is characterized in that: described formed product and demoulding step are carried out in the following order:
Formed product: framed decline, pressure head are risen, then open bed material door, bed material car is sent into bed material and is carried out cloth, shakes the framed bed material that makes smooth, then bed material car return, pressure head pressure bed material, after compressing, pressure head returns, and then opens fabric door, fabric car is sent into fabric and is carried out cloth, the even cloth of fabric on bed material, then fabric car return, pressure head press down and exciting vibratory compaction become brick;
The demoulding: move forward to lifting table position with brick framed and brick is placed on after after on lifting table returns original position.
8. preparation according to claim 7 has the method for the concrete road pavement brick of water-permeable, it is characterized in that: in described exciting vibration, exciting force is 60-240KN, and vibrational frequency is 8 ~ 55Hz, and time of vibration is 4-5S.
9. preparation according to claim 6 has the method for the concrete road pavement brick of water-permeable, it is characterized in that: described surface treatment is dry type rubbing down, and abrasive material is shot.