CN104311133A - 一种氮化硅、碳化硅结合硼化二钼泡沫陶瓷的制备方法 - Google Patents

一种氮化硅、碳化硅结合硼化二钼泡沫陶瓷的制备方法 Download PDF

Info

Publication number
CN104311133A
CN104311133A CN201410563151.8A CN201410563151A CN104311133A CN 104311133 A CN104311133 A CN 104311133A CN 201410563151 A CN201410563151 A CN 201410563151A CN 104311133 A CN104311133 A CN 104311133A
Authority
CN
China
Prior art keywords
silicon
silicon nitride
foamed ceramics
silicon carbide
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410563151.8A
Other languages
English (en)
Other versions
CN104311133B (zh
Inventor
唐竹兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong University of Technology
Original Assignee
Shandong University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong University of Technology filed Critical Shandong University of Technology
Priority to CN201410563151.8A priority Critical patent/CN104311133B/zh
Publication of CN104311133A publication Critical patent/CN104311133A/zh
Application granted granted Critical
Publication of CN104311133B publication Critical patent/CN104311133B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种氮化硅、碳化硅结合硼化二钼泡沫陶瓷的制备方法，其特征在于：将Mo2B、硅微粉、酚醛树脂外加羟丙基甲基纤维素溶液均匀混合制成陶瓷浆料，然后将陶瓷浆料浸渍在聚氨酯泡沫上，干燥后在氮气气氛中烧制成氮化硅、碳化硅结合硼化二钼泡沫陶瓷。本发明制备的氮化硅、碳化硅结合硼化二钼泡沫陶瓷显微结构均匀，强度高，孔大小均匀，避免炭和游离硅的残留，使其强度、耐高温、抗热冲击性能得到大幅度提高。

Description

一种氮化硅、碳化硅结合硼化二钼泡沫陶瓷的制备方法
技术领域
本发明涉及一种氮化硅、碳化硅结合硼化二钼泡沫陶瓷，属于多孔陶瓷制备技术领域。
背景技术
氮化硅、碳化硅结合硼化二钼复合陶瓷是一种低膨胀、耐腐蚀、高强度、耐高温的结构陶瓷材料。氮化硅、碳化硅结合硼化二钼泡沫陶瓷主要作为钢水过滤元件应用于大型特种钢铸件的钢铁铸造等行业。目前使用的氧化铝泡沫陶瓷、硼化二钼泡沫陶瓷普遍存在使用温度低、抗热冲击性能差等问题，已无法满足大型特种钢铸件连续铸造的需要。
发明内容
本发明的目的在于提供一种氮化硅、碳化硅结合硼化二钼泡沫陶瓷的制备方法，其技术方案为：
一种氮化硅、碳化硅结合硼化二钼泡沫陶瓷的制备方法，将Mo2B、硅微粉、酚醛树脂以重量比为40~88:10~40:2~20的比例并外加浓度为0.1~0.3wt%羟丙基甲基纤维素溶液40~60wt%均匀混合制成陶瓷浆料，然后将陶瓷浆料浸渍在聚氨酯泡沫上，干燥后在氮气气氛中、在温度为300℃~1450℃缓慢升温20~100小时，在1450℃保温5~10小时，然后在真空或氩气气氛、温度为1700~1750℃保温20~120分钟制成氮化硅、碳化硅结合硼化二钼泡沫陶瓷。
本发明与现有技术相比，其优点为：
1、本发明制备的氮化硅、碳化硅结合硼化二钼泡沫陶瓷显微结构均匀，强度高，孔大小均匀；
2、本发明采用的酚醛树脂、聚氨酯泡沫以及羟丙基甲基纤维素炭化后形成的炭与硅粉完全反应形成碳化硅，避免了炭的残留，而剩余的硅粉在高温下与氮气反应生成氮化硅将硼化二钼结合起来，新生成的氮化硅、碳化硅结合硼化二钼制成氮化硅、碳化硅结合硼化二钼泡沫陶瓷，避免了游离的残留，硅使其强度大幅度提高；
3、该氮化硅、碳化硅结合硼化二钼泡沫陶瓷重量轻、耐高温、抗热冲击性能优良。
具体实施方式
实施例1
将Mo2B、硅微粉、酚醛树脂以重量比为40:40:20的比例并外加浓度为0.1wt%羟丙基甲基纤维素溶液40wt%均匀混合制成陶瓷浆料，然后将陶瓷浆料浸渍在聚氨酯泡沫上，经干燥后在氮气气氛中、在温度为300℃~1450℃缓慢升温20小时，在1450℃保温5小时，然后在真空或氩气气氛、温度为1700℃保温20分钟制成氮化硅、碳化硅结合硼化二钼泡沫陶瓷。
实验所用的配料原料的纯度均为工业纯。
实施例2
将Mo2B、硅微粉、酚醛树脂以重量比为60:25:15的比例并外加浓度为0.2wt%羟丙基甲基纤维素溶液50wt%均匀混合制成陶瓷浆料，然后将陶瓷浆料浸渍在聚氨酯泡沫上，经干燥后在氮气气氛中、在温度为300℃~1450℃缓慢升温60小时，在1450℃保温8小时，然后在真空或氩气气氛、温度为1730℃保温70分钟制成氮化硅、碳化硅结合硼化二钼泡沫陶瓷。
实验所用的配料原料的纯度均为工业纯。
实施例3
将Mo2B、硅微粉、酚醛树脂以重量比为88:10:2的比例并外加浓度为0.3wt%羟丙基甲基纤维素溶液60wt%均匀混合制成陶瓷浆料，然后将陶瓷浆料浸渍在聚氨酯泡沫上，干燥后在氮气气氛中、在温度为300℃~1450℃缓慢升温100小时，在1450℃保温10小时，然后在真空或氩气气氛、温度为1750℃保温120分钟制成氮化硅、碳化硅结合硼化二钼泡沫陶瓷。
实验所用的配料原料的纯度均为工业纯。

Claims (1)

1.一种氮化硅、碳化硅结合硼化二钼泡沫陶瓷的制备方法，其特征在于：将Mo2B、硅微粉、酚醛树脂以重量比为40~88:10~40:2~20的比例并外加浓度为0.1~0.3wt%羟丙基甲基纤维素溶液40~60wt%均匀混合制成陶瓷浆料，然后将陶瓷浆料浸渍在聚氨酯泡沫上，干燥后在氮气气氛中、在温度为300℃~1450℃缓慢升温20~100小时，在1450℃保温5~10小时，然后在真空或氩气气氛、温度为1700~1750℃保温20~120分钟制成氮化硅、碳化硅结合硼化二钼泡沫陶瓷。
CN201410563151.8A 2014-10-22 2014-10-22 一种氮化硅、碳化硅结合硼化二钼泡沫陶瓷的制备方法 Expired - Fee Related CN104311133B (zh)