CN104310908A - 混凝土 - Google Patents

混凝土 Download PDF

Info

Publication number
CN104310908A
CN104310908A CN201410555971.2A CN201410555971A CN104310908A CN 104310908 A CN104310908 A CN 104310908A CN 201410555971 A CN201410555971 A CN 201410555971A CN 104310908 A CN104310908 A CN 104310908A
Authority
CN
China
Prior art keywords
parts
concrete
stone
admixture
medium sand
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201410555971.2A
Other languages
English (en)
Inventor
刘权
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HAIAN COUNTY EAST SPECIAL BUILDING MATERIAL CO Ltd
Original Assignee
HAIAN COUNTY EAST SPECIAL BUILDING MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HAIAN COUNTY EAST SPECIAL BUILDING MATERIAL CO Ltd filed Critical HAIAN COUNTY EAST SPECIAL BUILDING MATERIAL CO Ltd
Priority to CN201410555971.2A priority Critical patent/CN104310908A/zh
Publication of CN104310908A publication Critical patent/CN104310908A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种混凝土，属于建筑材料领域。其由水泥、中砂、骨料、加强纤维、外加剂和水混合而成，所述各组份质量份如下：水泥300-450份；中砂650-800份；骨料780-900份；加强纤维10-20份；外加剂4-8份；水180份-200份。本发明混凝土通过加强纤维在其中杂乱无章分布，协助混凝土承担拉应力、传递拉应力，阻止宏观裂缝的扩展，从而提高混凝土抗折强度和韧性；通过外加剂的加入可以增加混凝土的强度，降低泥土对混凝土的影响，改善混凝土的抗拉、抗折强度。

Description

混凝土
 
技术领域
    本发明涉及一种混凝土，具体讲是一种抗拉、抗裂性能好的混凝土，属于建筑材料领域。
背景技术
混凝土，简称为“砼”，通常是指用水泥作胶凝材料，砂、石作集料，与水按一定比例配合，经搅拌所得。混凝土具有原料丰富，价格低廉，生产工艺简单的特点，使其使用范围十分广泛，不仅在各种土木工程中使用，就是造船业、机械工业、海洋的开发、地热工程等，混凝土也是重要的材料。
现有的混凝土材料普遍存在抗拉、抗折强度低，抗冲击性能差，无法满足某些特殊建设领域的需求；同时，现有的混凝土材料在大体积混凝土施工过程中，混凝土裂缝较为普遍，影响了工程质量。
发明内容
本发明所要解决的技术问题在于克服现有技术缺陷，提供一种抗拉、抗折、抗裂性能好的混凝土。
为了解决上述技术问题，本发明提供的混凝土，其由水泥、中砂、骨料、加强纤维、外加剂和水混合而成，所述各组份质量份如下：水泥300-450份；中砂650-800份；骨料780-900份；加强纤维10-20份；外加剂4-8份；水180份-200份。
本发明中，所述外加剂由聚羧酸系减水剂35份、硅烷偶联剂6份、聚乙烯吡咯烷酮3份、碳化硅2份、二氧化硅包覆二氧化钛8份、明胶粉5份、膨润土12份、纳米碳粉10份、葡萄糖酸钠4份、醋酸酯苯酚4份混合而成。
本发明中，所述加强纤维为钢纤维、玻璃纤维和碳纤维，其长度均为9-30mm。
本发明中，所述中砂的细度模数大于2.7。
本发明中，所述骨料为石子，所述石子的粒径为8mm-18mm。
本发明中，所述的石子的含粉量为5.1%-5.4%，石子的细度模数为1.6-1.8。
本发明中，所述的水泥为32.5或42.5硅酸盐水泥。
本发明的有益效果在于：(1)、本发明混凝土通过加强纤维在其中杂乱无章分布，协助混凝土承担拉应力、传递拉应力，阻止宏观裂缝的扩展，从而提高混凝土抗折强度和韧性；通过外加剂的加入可以增加混凝土的强度，降低泥土对混凝土的影响，改善混凝土的抗拉、抗折强度；此外，外加剂具有一定的粘结性，凝胶吸收后会形成网络结构，可以使各成分在较少水的情况下结合良好，减少离析、泌水情况的发生，确保混凝土施工质量；(2)、本发明混凝土能有效降低水泥基材料早期水化和减缓慢水化放热速率，以改善界面结构状态，抵抗混凝土表面龟裂；(3)、本发明可大大降低了水泥用量，节约了能耗，混凝土制作成本大幅降低，减少了污染，符合国家能源发展战略。
具体实施方式
下面结合具体实施例对本发明作进一步详细说明。
实施例1
本例中各组份质量份如下：42.5硅酸盐水泥375份；中砂725份；8mm-18mm石子840份；9-30mm玻璃纤维15份；外加剂6份；水190份。
上述中砂的细度模数为2.72；石子的含粉量为5.1%，石子的细度模数为1.6；外加剂由聚羧酸系减水剂35份、硅烷偶联剂6份、聚乙烯吡咯烷酮3份、碳化硅2份、二氧化硅包覆二氧化钛8份、明胶粉5份、膨润土12份、纳米碳粉10份、葡萄糖酸钠4份、醋酸酯苯酚4份混合而成。
将上述质量份的水泥、中砂、石子、玻璃纤维投入搅拌机搅拌均匀后，加入上述质量份的外加剂和水进行搅拌，得到该混凝土。
实施例2
本例中各组份质量份如下：32.5硅酸盐水泥300份；中砂800份；8mm-18mm石子800份；9-30mm炭纤维20份；外加剂4份；水180份。
上述中砂的细度模数为2.76；石子的含粉量为5.4%，石子的细度模数为1.8；外加剂由聚羧酸系减水剂35份、硅烷偶联剂6份、聚乙烯吡咯烷酮3份、碳化硅2份、二氧化硅包覆二氧化钛8份、明胶粉5份、膨润土12份、纳米碳粉10份、葡萄糖酸钠4份、醋酸酯苯酚4份混合而成。
将上述质量份的水泥、中砂、石子、炭纤维投入搅拌机搅拌均匀后，加入上述质量份的外加剂和水进行搅拌，得到该混凝土。
实施例3
本例中各组份质量份如下：32.5硅酸盐水泥450份；中砂690份；8mm-18mm石子780份；9-30mm钢纤维10份；外加剂5份；水185份。
上述中砂的细度模数为2.74；石子的含粉量为5.4%，石子的细度模数为1.7；外加剂由聚羧酸系减水剂35份、硅烷偶联剂6份、聚乙烯吡咯烷酮3份、碳化硅2份、二氧化硅包覆二氧化钛8份、明胶粉5份、膨润土12份、纳米碳粉10份、葡萄糖酸钠4份、醋酸酯苯酚4份混合而成。
将上述质量份的水泥、中砂、石子、钢纤维投入搅拌机搅拌均匀后，加入上述质量份的外加剂和水进行搅拌，得到该混凝土。
实施例4
本例中各组份质量份如下：42.5硅酸盐水泥420份；中砂770份；8mm-18mm石子900份；9-30mm玻璃纤维18份；外加剂8份；水200份。
上述中砂的细度模数为2.76；石子的含粉量为5.3%，石子的细度模数为1.7；外加剂由聚羧酸系减水剂35份、硅烷偶联剂6份、聚乙烯吡咯烷酮3份、碳化硅2份、二氧化硅包覆二氧化钛8份、明胶粉5份、膨润土12份、纳米碳粉10份、葡萄糖酸钠4份、醋酸酯苯酚4份混合而成。
将上述质量份的水泥、中砂、石子、玻璃纤维投入搅拌机搅拌均匀后，加入上述质量份的外加剂和水进行搅拌，得到该混凝土。
实施例5
本例中各组份质量份如下：32.5硅酸盐水泥375份；中砂725份；8mm-18mm石子840份；9-30mm钢纤维15份；外加剂6份；水190份。
上述中砂的细度模数为2.72；石子的含粉量为5.2%，石子的细度模数为1.6；外加剂由聚羧酸系减水剂35份、硅烷偶联剂6份、聚乙烯吡咯烷酮3份、碳化硅2份、二氧化硅包覆二氧化钛8份、明胶粉5份、膨润土12份、纳米碳粉10份、葡萄糖酸钠4份、醋酸酯苯酚4份混合而成。
将上述质量份的水泥、中砂、石子、钢纤维投入搅拌机搅拌均匀后，加入上述质量份的外加剂和水进行搅拌，得到该混凝土。
以上所述的具体实施例，对本发明解决的技术问题、技术方案和有益效果进行了进一步详细说明，所应理解的是，以上所述仅为本发明的具体实施例而已，并不用于限制本发明，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (7)

1.一种混凝土，其特征在于：由水泥、中砂、骨料、加强纤维、外加剂和水混合而成，所述各组份质量份如下：
水泥300-450份；   
中砂650-800份；
骨料780-900份；
加强纤维10-20份；
外加剂4-8份；
水180份-200份。
2.根据权利要求1所述的混凝土，其特征在于：所述外加剂由聚羧酸系减水剂35份、硅烷偶联剂6份、聚乙烯吡咯烷酮3份、碳化硅2份、二氧化硅包覆二氧化钛8份、明胶粉5份、膨润土12份、纳米碳粉10份、葡萄糖酸钠4份、醋酸酯苯酚4份混合而成。
3.根据权利要求1或2所述的混凝土，其特征在于：所述加强纤维为钢纤维、玻璃纤维和碳纤维，其长度均为9-30mm。
4.根据权利要求3所述的混凝土，其特征在于：所述中砂的细度模数大于2.7。
5.根据权利要求4所述的混凝土，其特征在于：所述骨料为石子，所述石子的粒径为8mm-18mm。
6.根据权利要求5 所述的纤维混凝土，其特征在于：所述的石子的含粉量为5.1%-5.4%，石子的细度模数为1.6-1.8。
7.根据权利要求4所述的混凝土，其特征在于：所述的水泥为32.5或42.5硅酸盐水泥。
CN201410555971.2A 2014-10-20 2014-10-20 混凝土 Withdrawn CN104310908A (zh)