CN104293056A - 一种水性多彩真石型仿石涂料及其生产工艺 - Google Patents

一种水性多彩真石型仿石涂料及其生产工艺 Download PDF

Info

Publication number
CN104293056A
CN104293056A CN201410525231.4A CN201410525231A CN104293056A CN 104293056 A CN104293056 A CN 104293056A CN 201410525231 A CN201410525231 A CN 201410525231A CN 104293056 A CN104293056 A CN 104293056A
Authority
CN
China
Prior art keywords
stone
coating
water
add
formula ratio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410525231.4A
Other languages
English (en)
Other versions
CN104293056B (zh
Inventor
胡建钢
吴文峰
殷智峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HANGZHOU CHAOTOU BUILDING MATERIALS CO Ltd
Original Assignee
HANGZHOU CHAOTOU BUILDING MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANGZHOU CHAOTOU BUILDING MATERIALS CO Ltd filed Critical HANGZHOU CHAOTOU BUILDING MATERIALS CO Ltd
Priority to CN201410525231.4A priority Critical patent/CN104293056B/zh
Priority claimed from CN201410525231.4A external-priority patent/CN104293056B/zh
Publication of CN104293056A publication Critical patent/CN104293056A/zh
Application granted granted Critical
Publication of CN104293056B publication Critical patent/CN104293056B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种水性多彩真石型仿石涂料及生产工艺。现有的一些多彩真石型仿石涂料，抗开裂性好，仿真度高，耐候性好；但是生产工艺复杂，对生产人员要求高；粒子很容易被搅碎；储存稳定性差。本发明水性多彩真石型仿石涂料的质量百分含量如下：去离子水25-40％，基础漆10-30％，第一水性消泡剂0.1-0.3％，AMP-950.1-0.3％，乙二醇0.5-2.5％，Texanol成膜助剂0.5-2.5％，陶砂20-40％，第一杀菌剂0.1-0.3％，第一保护胶0.5-1.5％，硅丙乳液15-25％，稳定剂0.1-0.4％，碱溶胀增稠剂0.3-0.5％。本发明的涂料储存稳定性好，粒子不容易被搅碎。

Description

一种水性多彩真石型仿石涂料及其生产工艺
技术领域
本发明涉及建材涂料领域，具体地说是一种水性多彩真石型仿石涂料及生产工艺。
背景技术
随着我国经济迅速蓬勃发展，居民生活水平不断得到改善，对生活质量的要求也越来越高，对自身房屋的品质要求也越来越严格。人们不再满足简单的装饰，更多关心的是房屋的装饰高雅大方美观、装饰材料的节能环保。因此对在房屋装饰中扮演重要角色的涂料，人们对其的性能要求也是非常严格。我国住建部也考虑到这个发展方向，为此在十一五涂料科技规划中一再强调涂料品种的发展方向是“三高一低”，即高装饰性、高耐候性、高功能性和低污染的涂料品种，此已在我国涂料工业发展中得到了具体体现，也是今后我国涂料工业继续发展的方向。
中国的外墙建筑涂料装饰经过几十年的发展也是按照这个方向不断推出新的产品：从普通外墙涂料到弹性涂料、真石漆、岩片质感漆、水性仿花岗岩涂料发展。水性仿花岗岩涂料作为新一代涂料产品，具有优异的节能环保性能、美观性能。但是该涂料本身仍存在一些问题，由于其只是简单在普通外墙涂料上面喷涂水性仿花岗岩涂料。导致其厚度较低，耐候性、抗开裂性等性能较差。也由于其形成的点子只是简单漂浮在外墙涂料上，点子的灵活生动性较差，导致其仿真度较差。为此，国内许多公司提出在真石漆上喷涂水性仿花岗岩涂料，这样能够提高耐候性，耐水性等问题。但这样也同样也有一些缺点，主要表现在两个方向：(一)多彩和真石漆两道喷涂，导致施工费用增大；(二)多彩还是简单漂浮在真石漆上，点子的灵活生动性较差，仿真度降低。
为此，国内开始有一些厂家尝试开发新型产品—多彩真石型仿石涂料，该涂料结合了真石漆和水包水的优点，抗开裂性好，仿真度高，耐候性好。但是在技术上还是存在缺陷，主要表现在以下几个方面：(一)生产工艺复杂，对生产人员要求高；(二)粒子很容易被搅碎；(三)储存稳定性差。
发明内容
本发明所要解决的技术问题是克服上述现有技术存在的不足，提供一种储存稳定性好、粒子不容易被搅碎的水性多彩真石型仿石涂料。
为此，本发明采用如下的技术方案：一种水性多彩真石型仿石涂料，其各组分的质量百分含量如下：去离子水25-40％，基础漆10-30％，第一水性消泡剂0.1-0.3％，AMP-950.1-0.3％，乙二醇0.5-2.5％，Texanol成膜助剂0.5-2.5％，陶砂20-40％，第一杀菌剂0.1-0.3％，第一保护胶0.5-1.5％，硅丙乳液15-25％，稳定剂0.1-0.4％，碱溶胀增稠剂0.3-0.5％；
其中的基础漆由以下质量百分含量的各组分组成：去离子水20-38％，第二水性消泡剂0.3-0.6％，分散剂0.3-0.5％，木质素0.1-0.3％，AMP-950.1-0.3％，水性防霉剂0.2-0.4％，第二杀菌剂0.1-0.3％，羟乙基纤维素0.5-1％，疏水改性羟乙基纤维素0-0.5％，白砂35-50％，弹性乳液25-35％，色浆0-4％，钛白粉0.2-3％，第二保护胶0.3-0.7％，玻璃微珠0.2-0.5％。
进一步，所述的第一保护胶和第二保护胶均为S482保护胶，如BYK公司生产的LAPONITE S482。
进一步，所述陶砂的粒径选用20-40目、40-80目、80-120目中的一种或多种。
进一步，所述的白砂选用雪花白或/和汉白玉，其粒径选用80-120目、200目中的一种或多种。
进一步，所述的钛白粉选用金红石型，本发明的颜料由白度高、耐粉化、易分散的白色颜料和色浆组成，如白色颜料选用美国杜邦公司的钛白粉R-706或R-902，色浆选用科莱恩和希必思等公司的高品质水性色浆；所述的分散剂选用聚羧酸铵盐，能有效地分散无机颜、填料，并吸附在颜、填料表面，对亲水的颜、填料进行表面疏水改性，如上海海川公司的1124、科莱恩公司的740W或诺普科公司的SN-5027；所述的第一水性消泡剂和第二水性消泡剂均选用矿物油类或有机硅改性矿物油类消泡剂，如亚什兰公司的AM1512、诺普科公司的NXZ或者巴斯夫公司的A10消泡剂；所述的第一杀菌剂和第二杀菌剂均选用卡松防腐剂或1，2-苯并异噻唑啉-3-酮，如TOR公司MV杀菌剂或陶氏公司的LXE杀菌剂；所述的稳定剂选用25％、50％或99％固含量的聚乙烯亚胺，如BASF公司的聚乙烯亚胺。
进一步，所述的碱溶胀增稠剂选用疏水改性碱溶性乳液增稠剂，如陶氏化学的TT-935。
进一步，所述的玻璃微珠选用0.2-10um粒径的一种或多种，如上海汇精亚纳米材料有限公司的AS6。
本发明的水性防霉剂采用TOR公司的AM146防霉剂；所述的羟乙基纤维素采用亚什兰公司的HBR250，所述的疏水改性羟乙基纤维素采用亚什兰公司的HE-10K，所述的木质素采用尼恩化学的N-300或N-500。所述的弹性乳液为高弹性高耐水白性乳液，如上海居宁公司的GP-400或者昭日公司的SLX1048-3。所述的硅丙乳液为高耐水白性乳液，如上海巴德富公司的RS-996AD或者上海日出公司的TD-661B。
本发明的另一目的在于提供上述水性多彩真石型仿石涂料的生产工艺，其步骤如下：
第一步，制备白色分散相：
1)用去离子水和配方量的第二保护胶制备质量浓度为7％的第二保护胶溶液，待用；
2)在300-500rpm的转速搅拌下，往去离子水中依次加入配方量的羟乙基纤维素、疏水改性羟乙基纤维素搅拌，然后依次加入基础漆中配方量的分散剂、第二杀菌剂、水性防霉剂、1/2的第二水性消泡剂，搅拌3-5分钟；
3)依次加入配方量的钛白粉以及白砂，转速调整到1000-1200rpm，分散20-30分钟；
4)将转速调整到600-800rpm，依次加入基础漆中配方量的弹性乳液、1/2第二水性消泡剂、AMP-95、前述配置好的第二保护胶溶液、木质素，搅拌20-30分钟；
5)将转速调整到500-600rpm，加入玻璃微珠，分散5-10分钟；
第二步，基础漆(即调色漆)的制备：将上述制备好的白色分散相，在600-800rpm搅拌下，加入配方量的色浆，搅拌10-15分钟，根据花岗岩石头确定所需要的花纹种类，制备所需要的不同颜色的单色漆；
第三步，涂料(即连续相)的制备：
1)用去离子水和配方量的第一保护胶制备质量浓度为7％的第一保护胶溶液，待用；
2)制备陶砂溶液，将上述配置好的第一保护胶溶液取出10％，在转速500-600rpm搅拌下，加入其重量10倍的去离子水，加入配方量1/2的碱溶胀增稠剂，加入配方量的陶砂，搅拌待用；
3)在上述剩余的第一保护胶溶液中加入稳定剂，搅拌后投入单色漆，每投入一种单色漆，转速50-150rpm搅拌达到花纹要求后，再投入另一种颜色的单色漆；
4)在转速50-150rpm的搅拌下，在第3)步得到的基础漆中加入配方量的硅丙乳液、第一杀菌剂、第一水性消泡剂、Texanol成膜助剂、剩余的去离子水、乙二醇、剩余的碱溶胀增稠剂和AMP-95；
5)最后加入已制备好的陶砂溶液，搅拌混合均匀，即制得本发明的水性多彩真石型仿石涂料。
本发明水性多彩真石型仿石涂料通过利用保护胶和增稠剂对陶砂进行防沉处理，保证了陶砂加入时候不容易下沉，在底部不形成堆积，易混合均匀；同时也解决了由于陶砂加入时因摩擦大导致单色粒子易碎的后果。
同时，本发明通过添加稳定剂聚乙烯亚胺，聚乙烯亚胺对保护胶表面进行包覆，有助于降低保护胶和助剂反应所造成的粒子变硬、变老现象及储存不稳定的现象。其次，通过聚乙烯亚胺对重金属离子的吸附作用，减少重金属离子含量，减少由于重金属离子和保护胶反应导致的后稠现象。
本发明通过添加木质素解决了多彩普遍存在的问题，即喷涂形成的多彩由于挥发不均匀导致的皱缩现象。由于纤维结构的毛细管作用，将系统内部的水分迅速地传输到浆料表面和界面，使得浆料内部的水分均匀分布，明显减少结皮现象；并使得粘结强度和表面强度明显提高，这个机理也由于干燥过程中张力的减少而明显起到抗裂的作用。
本发明选用陶砂，是由于陶砂为煅烧砂，其批次稳定；而天然彩砂由于其批次不稳定，容易导致色差，使喷涂的多彩会出现发花等现象。
本发明具有的有益效果为：(1)通过加入陶砂和白砂，增加了单位平方的厚度，解决了常规多彩仿花岗岩石漆的耐水性、抗裂性。(2)通过多彩点子内外均含砂的包裹效果，使形成的多彩仿石漆比较生动，仿真度逼真。(3)通过一次成型解决了真石漆加水性多彩仿花岗岩石漆的施工复杂性，以及降低了因真石漆掉砂而导致的自然资源浪费现象。
具体实施方式
下面结合具体实施方式对本发明作进一步说明。
实施例1
本发明水性多彩真石型仿石漆的配方为：
(1)分散相(白色)：233g去离子水、8g HBR250、2g HE-10K、3.0g分散剂740W、2.0g多功能助剂AMP-95、3.0g消泡剂A10、2.0g卡松杀菌剂LXE、3.0g水性防霉剂AM146、9.0g金红石型钛白粉R-902、300gSLX1048-3乳液、350g雪花白、7％S482水溶液80g、N-3002g、AS63g。分散相(黑色)：233g去离子水、8g HBR250、2g HE-10K、3.0g分散剂740W、2.0g多功能助剂AMP-95、3.0g消泡剂A10、2.0g卡松杀菌剂LXE、3.0g水性防霉剂AM146、6.0g金红石型钛白粉R-902、300g SLX1048-3乳液、350g雪花白、7％S482水溶液80g、N-3002g、3g炭黑、AS63g。分散相(黄色)：232g去离子水、8g HBR250、2g HE-10K、3.0g分散剂740W、2.0g多功能助剂AMP-95、3.0g消泡剂A10、2.0g卡松杀菌剂LXE、3.0g水性防霉剂AM146、4.0g金红石型钛白粉R-902、300g SLX1048-3乳液、350g雪花白、7％S482水溶液80g、N-3002g、6g铁黄、AS63g。
(2)连续相：分散相(白色)90g，分散相(黄色)55g，分散相(黑色)5g，去离子水233g，消泡剂NXZ 3g，AMP-952g，乙二醇15g，Texanol20g，陶砂220g，7％S-482150g，硅丙乳液TD-661B 200g，杀菌剂MV 2g，TT-9354g，稳定剂1g。
实施例2
本发明水性多彩真石型仿石漆的配方为：
(1)分散相(白色)：227g去离子水、6g HBR250、4g HE-10K、4.0g分散剂1124、2.0g多功能助剂AMP-95、1.5g消泡剂A10、1.5g消泡剂NXZ、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、5g金红石型钛白粉R-706、250g SLX1048-3乳液、415g雪花白、7％S482水溶液70g、N-3003g、AS65g。分散相(深黄)227g去离子水、6g HBR250、4g HE-10K、4.0g分散剂1124、2.0g多功能助剂AMP-95、1.5g消泡剂A10、1.5g消泡剂NXZ、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、5g金红石型钛白粉R-706、250g SLX1048-3乳液、405g雪花白、7％S482水溶液70g、N-3003g、AS65g、铁黄10g。分散相(浅黄)197g去离子水、6g HBR250、4g HE-10K、4.0g分散剂1124、2.0g多功能助剂AMP-95、1.5g消泡剂A10、1.5g消泡剂NXZ、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、5g金红石型钛白粉R-706、280g SLX1048-3乳液、411g雪花白、7％S482水溶液70g、N-3003g、铁黄4g、AS65g。分散相(黑色)227g去离子水、6g HBR250、4g HE-10K、4.0g分散剂1124、2.0g多功能助剂AMP-95、1.5g消泡剂A10、1.5g消泡剂NXZ、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、5g金红石型钛白粉R-706、250g SLX1048-3乳液、413g雪花白、7％S482水溶液70g、N-3003g、炭黑2g、AS65g。
(2)连续相：分散相(白色)60g，分散相(深黄)50g，分散相(浅黄)35g，分散相(黑色)5g，去离子水221g，消泡剂AM15123g，AMP-952g，乙二醇15g，Texanol 22g，陶砂180g，7％S-482150g，硅丙乳液RS-996AD 250g，TT-9354g，杀菌剂MV 1.5g，稳定剂1.5g。
实施例3
本发明水性多彩真石型仿石漆的配方为：
(1)分散相(白色)：160g去离子水、5g HBR250、5g HE-10K、4.0g分散剂5027、2.0g多功能助剂AMP-95、3g消泡剂AM1512、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、12g金红石型钛白粉R-706、320g SLX1048-3乳液、416g雪花白、7％S482水溶液60g、N-3003g、AS64g。分散相(黄色)：160g去离子水、5g HBR250、5g HE-10K、4.0g分散剂5027、2.0g多功能助剂AMP-95、3g消泡剂AM1512、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、8g金红石型钛白粉R-706、320g SLX1048-3乳液、416g雪花白、7％S482水溶液60g、N-3003g、AS64g、铁黄4g。分散相(黑色)：160g去离子水、5g HBR250、5g HE-10K、4.0g分散剂5027、2.0g多功能助剂AMP-95、3g消泡剂AM1512、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、8g金红石型钛白粉R-706、320g SLX1048-3乳液、418g雪花白、7％S482水溶液60g、N-3003g、AS64g、炭黑2g。
(2)连续相：分散相(白色)122g，分散相(黄色)85g，分散相(黑色)3g，去离子水201g，消泡剂AM15123g，AMP-952g，乙二醇13.5g，Texanol 23g，陶砂160g，7％S-482180g，硅丙乳液RS-996AD 200g，TT-9354g，杀菌剂MV 1.5g，稳定剂2g。
实施例4
本发明水性多彩真石型仿石漆的配方为：
(1)分散相(白色)：160g去离子水、8g HBR250、2g HE-10K、6.0g分散剂5027、2.0g多功能助剂AMP-95、3g消泡剂AM1512、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、10g金红石型钛白粉R-706、310gSLX1048-3乳液、416g雪花白、7％S482水溶液70g、N-3003g、AS64g。分散相(黄色)：160g去离子水、8g HBR250、2g HE-10K、6.0g分散剂5027、2.0g多功能助剂AMP-95、3g消泡剂AM1512、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、6g金红石型钛白粉R-706、310g SLX1048-3乳液、416g雪花白、7％S482水溶液70g、N-3003g、AS64g、铁黄4g。分散相(黑色)：160g去离子水、8g HBR250、2g HE-10K、6.0g分散剂5027、2.0g多功能助剂AMP-95、3g消泡剂AM1512、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、6g金红石型钛白粉R-706、310g SLX1048-3乳液、418g雪花白、7％S482水溶液70g、N-3003g、AS64g、炭黑2g。
(2)连续相：分散相(白色)156g，分散相(黄色)87g，分散相(黑色)7g，去离子水161g，消泡剂AM15122.5g，AMP-952g，乙二醇14g，Texanol 23.5g，陶砂160g，7％S-482180g，硅丙乳液RS-996AD 200g，TT-9354g，稳定剂1.5g，杀菌剂MV 1.5g。
实施例5
本发明水性多彩真石型仿石漆的配方为：
(1)分散相(白色)：160g去离子水、7g HBR250、3g HE-10K、4.0g分散剂1124、2.0g多功能助剂AMP-95、3g消泡剂NXZ、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、12g金红石型钛白粉R-706、350g SLX1048-3乳液、386g雪花白、7％S482水溶液60g、N-3003g、AS64g。分散相(黄色)：160g去离子水、7g HBR250、3g HE-10K、4.0g分散剂1124、2.0g多功能助剂AMP-95、3g消泡剂NXZ、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、8g金红石型钛白粉R-706、350g SLX1048-3乳液、386g雪花白、7％S482水溶液60g、N-3003g、AS64g、铁黄4g。分散相(黑色)：160g去离子水、7g HBR250、3g HE-10K、4.0g分散剂1124、2.0g多功能助剂AMP-95、3g消泡剂NXZ、2.0g卡松杀菌剂LXE、4.0g水性防霉剂AM146、8g金红石型钛白粉R-706、350g SLX1048-3乳液、388g雪花白、7％S482水溶液60g、N-3003g、AS64g、炭黑2g。
(2)连续相：分散相(白色)120g，分散相(黄色)60g，分散相(黑色)10g，去离子水221g，消泡剂AM15123g，AMP-952g，乙二醇12.5g，Texanol 22g，陶砂190g，7％S-482150g，硅丙乳液RS-996AD 200g，TT-9354g，杀菌剂MV 2.5g，稳定剂3g。
实施例1-5所述涂料的制备方法，工艺步骤具体如下：
1)在分散机中加入去离子水，在500-600rpm的转速搅拌下按照水的重量份数的93/7倍数加入S482，加入完毕后，调整转速为1000-1200rpm，搅拌30分钟后待用。
2)在高速分散机中加入上述重量份数剩余的水，在300-500rpm的转速搅拌下依次加入上述重量份数的羟乙基纤维素、疏水改性羟乙基纤维素搅拌15分钟，然后依次加入上述重量份数的分散剂、第二杀菌剂、水性防霉剂、1/2的消泡剂，搅拌3-5分钟。
3)依次加入上述重量份数的钛白粉以及白砂，转速调整到1000-1200rpm，分散20-30分钟。
4)将转速调整到600-800rpm，依次加入上述重量份数的弹性乳液、1/2第二水性消泡剂，AMP-95，已配置好的7％S482溶液，木质素，搅拌20-30分钟。
5)将转速调整到500-600rpm，加入玻璃微珠，低速分散5-10分钟。
6)将上述制备好的白色分散相，在600-800rpm搅拌下，加入重量份数的色浆，搅拌10-15分钟。根据花岗岩石头确定所需要的花纹种类，制备所需要的不同颜色的单色漆，制备好待用。
7)制作连续相中的7％S482溶液。即按照上述重量份数的S482计算出需要水的份数，然后在500-600rpm的转速搅拌下加入上述重量份数的S482，加入完毕后，调整转速为1000-1200rpm，搅拌30分钟待用。
8)制备陶砂溶液，将上述配置好的7％S482溶液取出10％，在转速500-600rpm搅拌下，加入其重量份数10倍的水，加入上述重量份数1/2的增稠剂，加入上述重量份数的陶砂，搅拌10分钟待用。
9)在上述已制备好的7％S472溶液中低速搅拌加入稳定剂，搅拌5分钟，投入单色漆，50-150rpm，每投入一种单色漆，低速搅拌达到花纹要求后，再投入另一种颜色的单色漆。上述要求所需要的花纹颜色加入相应的单色漆。
10)按重量份数在50-150rpm加入硅丙乳液，第一杀菌剂，第一水性消泡剂，成膜助剂，剩余的水，乙二醇，剩余的增稠剂和和AMP-95。
11)最后加入已制备好的陶砂溶液，低速(50-150rpm)混合均匀，即制得本发明的水性多彩真石型仿石涂料。
上述的五个实施例根据JG/T 4342-2012水性多彩建筑涂料(非弹性)、JG/T 24-2000合成树脂砂壁状建筑涂料(W型(外用))的技术要求，其测试结果如下：
从上表可知，本发明水性真石型仿石涂料具有耐水性，耐碱性好，以及优异的耐候性能和粘结性能。
以上所述，仅是本发明的较佳实施例而已，并非对本发明的技术方案作任何形式上的限制。凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均落入本发明的保护范围内。

Claims (10)

1.一种水性多彩真石型仿石涂料，其各组分的质量百分含量如下：
其中的基础漆由以下质量百分含量的各组分组成：
2.根据权利要求1所述的水性多彩真石型仿石涂料，其特征在于，所述的第一保护胶和第二保护胶均为S482保护胶。
3.根据权利要求1所述的水性多彩真石型仿石涂料，其特征在于，所述陶砂的粒径选用20-40目、40-80目、80-120目中的一种或多种。
4.根据权利要求1所述的水性多彩真石型仿石涂料，其特征在于，所述的白砂选用雪花白或/和汉白玉，其粒径选用80-120目、200目中的一种或多种。
5.根据权利要求1所述的水性多彩真石型仿石涂料，其特征在于，所述的钛白粉选用金红石型，所述的分散剂选用聚羧酸铵盐。
6.根据权利要求1所述的水性多彩真石型仿石涂料，其特征在于，所述的第一水性消泡剂和第二水性消泡剂均选用矿物油类或有机硅改性矿物油类消泡剂，所述的第一杀菌剂和第二杀菌剂均选用卡松防腐剂或1，2-苯并异噻唑啉-3-酮。
7.根据权利要求1所述的水性多彩真石型仿石涂料，其特征在于，所述的稳定剂选用25％、50％或99％固含量的聚乙烯亚胺聚乙烯亚胺。
8.根据权利要求1所述的水性多彩真石型仿石涂料，其特征在于，所述的碱溶胀增稠剂选用疏水改性碱溶性乳液增稠剂。
9.根据权利要求1所述的水性多彩真石型仿石涂料，其特征在于，所述的玻璃微珠选用0.2-10um粒径的一种或多种。
10.权利要求1-9任一项所述水性多彩真石型仿石涂料的生产工艺，其步骤如下：
第一步，制备白色分散相：
1)用去离子水和配方量的第二保护胶制备质量浓度为7％的第二保护胶溶液，待用；
2)在300-500rpm的转速搅拌下，往去离子水中依次加入配方量的羟乙基纤维素、疏水改性羟乙基纤维素搅拌，然后依次加入基础漆中配方量的分散剂、第二杀菌剂、水性防霉剂、1/2的第二水性消泡剂，搅拌3-5分钟；
3)依次加入配方量的钛白粉以及白砂，转速调整到1000-1200rpm，分散20-30分钟；
4)将转速调整到600-800rpm，依次加入基础漆中配方量的弹性乳液、1/2第二水性消泡剂、AMP-95、前述配置好的第二保护胶溶液、木质素，搅拌20-30分钟；
5)将转速调整到500-600rpm，加入玻璃微珠，分散5-10分钟；
第二步，基础漆的制备：将上述制备好的白色分散相，在600-800rpm搅拌下，加入配方量的色浆，搅拌10-15分钟，根据花岗岩石头确定所需要的花纹种类，制备所需要的不同颜色的单色漆；
第三步，涂料的制备：
1)用去离子水和配方量的第一保护胶制备质量浓度为7％的第一保护胶溶液，待用；
2)制备陶砂溶液，将上述配置好的第一保护胶溶液取出10％，在转速500-600rpm搅拌下，加入其重量10倍的去离子水，加入配方量1/2的碱溶胀增稠剂，加入配方量的陶砂，搅拌待用；
3)在上述剩余的第一保护胶溶液中加入稳定剂，搅拌后投入单色漆，每投入一种单色漆，转速50-150rpm搅拌达到花纹要求后，再投入另一种颜色的单色漆；
4)在转速50-150rpm的搅拌下，在第3)步得到的基础漆中加入配方量的硅丙乳液、第一杀菌剂、第一水性消泡剂、Texanol成膜助剂、剩余的去离子水、乙二醇、剩余的碱溶胀增稠剂和AMP-95；
5)最后加入已制备好的陶砂溶液，搅拌混合均匀，即制得水性多彩真石型仿石涂料。
CN201410525231.4A 2014-10-08 一种水性多彩真石型仿石涂料及其生产工艺 Active CN104293056B (zh)