CN104278176A - 一种高质量Al-5Ti-1B中间合金的制备方法 - Google Patents

一种高质量Al-5Ti-1B中间合金的制备方法 Download PDF

Info

Publication number
CN104278176A
CN104278176A CN201310275375.4A CN201310275375A CN104278176A CN 104278176 A CN104278176 A CN 104278176A CN 201310275375 A CN201310275375 A CN 201310275375A CN 104278176 A CN104278176 A CN 104278176A
Authority
CN
China
Prior art keywords
alloy
villiaumite
intermediate alloy
high quality
melt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310275375.4A
Other languages
English (en)
Other versions
CN104278176B (zh
Inventor
赵九洲
江鸿翔
杨雪村
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI CHAOSHAN NEW MATERIAL CO LTD
Institute of Metal Research of CAS
Original Assignee
ANHUI CHAOSHAN NEW MATERIAL CO LTD
Institute of Metal Research of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI CHAOSHAN NEW MATERIAL CO LTD, Institute of Metal Research of CAS filed Critical ANHUI CHAOSHAN NEW MATERIAL CO LTD
Priority to CN201310275375.4A priority Critical patent/CN104278176B/zh
Publication of CN104278176A publication Critical patent/CN104278176A/zh
Application granted granted Critical
Publication of CN104278176B publication Critical patent/CN104278176B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高质量Al-5Ti-1B中间合金的制备方法，属于铝基中间合金的制备技术领域。该方法采用双级反应-熔炼技术，即：用K2TiF6、KBF4、Na3AlF6、CaF2、MgF2混合物与Al熔体反应的方法获得初级Al-5Ti-1B熔体，进而在电阻炉内对熔体进行熔炼，达到精炼与调整中间合金中Al3Ti粒子尺寸与分布的目的，制备高质量Al-5Ti-1B中间合金。该方法制备的Al-5Ti-1B中间合金质量高、对铝合金的变质效果好，满足工业生产需求。

Description

一种高质量Al-5Ti-1B中间合金的制备方法
技术领域
本发明涉及铝基中间合金的制备技术领域，具体涉及一种高质量Al-5Ti-1B中间合金的制备方法。
背景技术
Al-Ti-B合金是工业上广泛使用的铝合金晶粒细化剂，对提高铝合金的质量和性能极为重要。随着工业技术的不断发展，对Al-Ti-B合金质量与变质性能的要求日益提高。通常在生产Al-Ti-B合金时易于出现合金中TiAl3相尺寸过大或过小、合金含渣量较高、纯净度较低的问题。研制Al-Ti-1B中间合金的生产技术，以提高Al-Ti-B中间合金的质量，满足铝合金生产行业对高质量Al-Ti-B中间合金的需求，具有重要的意义。
发明内容
本发明的目的在于提供一种高质量Al-5Ti-1B中间合金的制备方法，满足工业生产需求。
本发明的技术方案是：
一种高质量Al-5Ti-1B中间合金的制备方法，该方法采用氟盐混合物与铝熔体进行化学反应获取Al-5Ti-1B中间合金；其中：按照氟盐混合物中各组分占所述铝熔体的质量百分比计，所述氟盐混合物由22～30%的K2TiF6、10～14%的KBF4、3.5～4.1%的Na3AlF6、0.015～0.035%的CaF2和0.015～0.035%的MgF2组成；
该方法具体包括如下步骤：
（1）所述的高质量Al-5Ti-1B中间合金的制备方法，首先用中频感应炉将纯铝熔化，获得铝熔体；然后将熔体升温至775～825℃；将所述氟盐混合物全部覆盖于铝熔体表面，并在775～825℃保温反应30min（以获得Al3Ti粒子细小的中间合金熔体），获得Al-5Ti-1B中间合金熔体及氟盐。
（2）将步骤（1）所得Al-5Ti-1B中间合金熔体及氟盐转入电阻炉内，在775～825℃静置保温20～40min，以调整Al-5Ti-1B中间合金熔体中Al3Ti粒子尺寸与分布，并去除夹渣物，提高合金熔体纯度。
（3）将Al-5Ti-1B中间合金熔体表面的氟盐倒出，对合金熔体进行搅拌后，将其浇入金属模，获得Al-5Ti-1B中间合金。
本发明具有以下有益效果：
1、本发明方法制备的中间合金中，Al3Ti颗粒分布弥散，尺寸适中，形状为块状，对铝及合金的变质效果好。
2、本发明方法制备的中间合金其含渣量低、纯净度高，能够满足铝合金生产行业对高质量Al-Ti-B中间合金的需求。
附图说明
图1为实施例1中Al-5Ti-1B合金组织形貌；其中：图(a)：标尺50μm；图(b)：标尺2μm。
图2为实施例2中Al-5Ti-1B合金组织形貌；其中：图(a)：标尺100μm；图(b)：标尺2μm。
图3为细化实验用不锈钢模。
图4为经本发明制备的Al-5Ti-1B合金细化处理后工业纯铝的晶粒组织。
图5为经用某商用Al-5Ti-1B合金细化处理后工业纯铝的晶粒组织。
具体实施方式
以下结合附图及实施例详述本发明。
实施例1
将1.3公斤纯铝在感应坩埚内熔化并加热至810℃，将312克K2TiF6、145克KBF4、48.4克Na3AlF6、0.3克CaF2和0.3克MgF2粉（粒度160目-300目）混合均匀后覆盖于铝熔体表面，在810℃下保温27min，将上述合金熔体及氟盐转入电阻炉内在810℃静置保温26min，将合金熔体表面氟盐倒出，对合金熔体进行搅拌后，将其浇入金属模，形成中间合金锭。
图1为Al-5Ti-1B合金组织形貌。分析表明，本实施例所研制的Al-5Ti-1B合金中TiAl3颗粒尺寸在4.0～81.3之间，平均尺寸为20.4μm，TiB2颗粒尺寸在0.16～0.50μm之间，平均尺寸为0.33μm，合金中夹渣物含量很低。
实施例2
将1.3公斤纯铝在感应坩埚内熔化并加热至800℃，将338克K2TiF6、156克KBF4、49.4克Na3AlF6、0.3克CaF2和0.3克MgF2粉（粒度160目-300目）混合均匀后覆盖于铝熔体表面，在800℃下保温30min，将上述合金熔体及氟盐转入电阻炉内在800℃静置保温30min，将合金熔体表面氟盐倒出，对合金熔体进行搅拌后，将其浇入金属模，形成中间合金锭。
图2为Al-5Ti-1B合金组织形貌。分析表明，本实施例所研制的Al-5Ti-1B合金中TiAl3颗粒尺寸在4.08～81.8之间，平均尺寸为20.7μm，TiB2颗粒尺寸在0.18～0.51μm之间，平均尺寸为0.34μm，合金中夹渣物含量很低。
实施例3
采用实施例2制备的Al-5Ti-1B中间合金对纯铝进行细化处理，过程如下：
晶粒细化试验材料为工业纯铝。试验设备为井式电阻炉和刚玉坩埚。将纯铝置于坩埚内加热熔化，待铝熔体升至710℃～730℃后精炼、搅拌和扒渣，加入质量分数为0.4%的Al-5Ti-1B合金料，加入后搅拌30s左右，然后进行保温，在保温不同时间后，浇注于不锈钢模内，不锈钢模形状如图3所示。凝固后将试样从距钢模底部20mm处切，经磨制、抛光并用0.5%的HF腐蚀后观察试样宏观晶粒组织，并测量晶粒的平均直径。
图4为经实施例3细化处理后工业纯铝的晶粒组织，分析表明，细化后的晶粒尺寸几乎都在50μm以下。图5为经用某商用Al-5Ti-1B合金细化处理后工业纯铝的晶粒组织，分析表明，细化后晶粒尺寸大约在100-150μm之间。可见，本专利技术制备的Al-5Ti-1B合金具有很强的晶粒细化作用。

Claims (2)

1.一种高质量Al-5Ti-1B中间合金的双级反应-熔炼制备方法，其特征在于：该方法采用氟盐混合物与铝熔体进行化学反应获取Al-5Ti-1B中间合金；其中：按照氟盐混合物中各组分占所述铝熔体的质量百分比计，所述氟盐混合物由22～30%的K2TiF6、10～14%的KBF4、3.5～4.1%的Na3AlF6、0.015～0.035%的CaF2和0.015～0.035%的MgF2组成；
2.根据权利要求1所述的Al-5Ti-1B中间合金的制备方法，其特征在于：该方法具体包括如下步骤：
（1）所述的高质量Al-5Ti-1B中间合金的制备方法，首先用中频感应炉将纯铝熔化，获得铝熔体，然后升温至775～825℃，将所述氟盐混合物全部覆盖于铝熔体表面，并在775～825℃下保温反应30min，获得Al-5Ti-1B中间合金熔体及氟盐；
（2）将步骤（1）所得Al-5Ti-1B中间合金熔体及氟盐转入电阻炉内，在775～825℃静置保温20～40min；
（3）将Al-5Ti-1B中间合金熔体表面的氟盐倒出，对Al-5Ti-1B中间合金熔体进行搅拌后，并将其浇入金属模，获得Al-5Ti-1B中间合金。
CN201310275375.4A 2013-07-01 2013-07-01 一种高质量Al-5Ti-1B中间合金的制备方法 Expired - Fee Related CN104278176B (zh)