CN104277739A - Corrugated carton adhesive - Google Patents
Corrugated carton adhesive Download PDFInfo
- Publication number
- CN104277739A CN104277739A CN201410509655.1A CN201410509655A CN104277739A CN 104277739 A CN104277739 A CN 104277739A CN 201410509655 A CN201410509655 A CN 201410509655A CN 104277739 A CN104277739 A CN 104277739A
- Authority
- CN
- China
- Prior art keywords
- parts
- tackiness agent
- corrugated box
- water
- agent according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a corrugated carton adhesive which is prepared from the following raw materials in parts by weight: 45-55 parts of water, 28-34 parts of sweet potato powder, 12-16 parts of calcium carbonate, 2-3 parts of hydrochloric acid, 3-4 parts of meerschaum powder, 0.12-0.16 part of naphthalene sulfonate formaldehyde condensate, 0.15-0.18 part of sodium carboxymethyl cellulose and 0.10-0.12 part of white granulated sugar. The corrugated carton adhesive is prepared from the following steps: pouring water into a container, and regulating the water temperature to 56-64 DEG C; adding the sweet potato powder, and stirring to a viscous state; adding the calcium carbonate, and stirring for 15-18 minutes; adding the hydrochloric acid, and stirring for 6-8 minutes; and adding the meerschaum powder, naphthalene sulfonate formaldehyde condensate, sodium carboxymethyl cellulose and white granulated sugar, stirring uniformly, standing and cooling. The corrugated carton adhesive has the advantages of high adhesive capacity, high safety and environmental protection.
Description
Technical field
The invention belongs to technical field of adhesive, particularly relate to a kind of Corrugated Box tackiness agent.
Background technology
Tackiness agent is the requisite material of Carbon enterprise, and it is mainly used on the compound working procedure of face Paper or cardboard.At present, the bonding for cardboard mainly adopts amylan.But because this type of adhesives power is weak, crushing resistance, moisture protection are poor, and the quality product therefore produced can not be guaranteed.In prior art, exist and in amylan, add other one-tenth assign to improve its performance, but this type of added ingredients often containing to human body composition excitatory, adds chemical pollution, needs to improve.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, provide a kind of Corrugated Box tackiness agent, its adhesive capacity is strong, and safety and environmental protection.
The present invention proposes a kind of Corrugated Box tackiness agent, be made up of the raw material of following weight part: water: 45-55 part; Sweet potato powder: 28-34 part; Calcium carbonate: 12-16 part; Hydrochloric acid: 2-3 part; Sepiolite powder: 3-4 part; Naphthalenesulfonate formaldehyde condensation compound: 0.12-0.16 part; Xylo-Mucine: 0.15-0.18 part; White sugar: 0.10-0.12 part;
According to above-mentioned raw materials proportioning, prepare described Corrugated Box tackiness agent according to the following steps:
S1: the water of proportioning is poured in container, and to adjust water temperature be 56-64 DEG C;
S2: add sweet potato powder in water in S1, and be stirred to thick, obtain latex A;
S3: add calcium carbonate in the latex A in S2, and carry out stirring and obtain emulsion B, wherein, churning time is 15-18min;
S4: add hydrochloric acid in the emulsion B in S3, and carry out stirring and obtain emulsion C, wherein, churning time is 6-8min;
S5: add sepiolite powder, naphthalenesulfonate formaldehyde condensation compound, Xylo-Mucine, white sugar in S4 gained emulsion C, after stirring, leave standstill, cooling after obtain described Corrugated Box tackiness agent.
Preferably, be made up of the raw material of following weight part: water: 48-52 part; Sweet potato powder: 29-32 part; Calcium carbonate: 13-15 part; Hydrochloric acid: 2.3-2.7 part; Sepiolite powder: 3.2-3.8 part; Naphthalenesulfonate formaldehyde condensation compound: 0.14-0.15 part; Xylo-Mucine: 0.16-0.17 part; White sugar: 0.11-0.12 part.
Preferably, be made up of the raw material of following weight part: water: 50 parts; Sweet potato powder: 30 parts; Calcium carbonate: 14 parts; Hydrochloric acid: 2.6 parts; Sepiolite powder: 3.8 parts; Naphthalenesulfonate formaldehyde condensation compound: 0.14 part; Xylo-Mucine: 0.16 part; White sugar: 0.11 part.
Preferably, in S1, adjustment water temperature is 58-62 DEG C.
Preferably, in S1, adjustment water temperature is 60 DEG C.
Preferably, in S3, churning time is 15.6-17min.
Preferably, in S3, churning time is 16min.
Preferably, in S4, churning time is 6.5-7.5min.
Preferably, in S4, churning time is 7min.
In the present invention, by carrying out choose reasonable to the components by weight percent of Corrugated Box tackiness agent, and adopting proper step to allocate, making the cohesive strength of tackiness agent high; Meanwhile, obtained tackiness agent is nontoxic, not easily occurs the phenomenon that glue is separated, and in whole allocation process, to stir, technique is simple, and processing condition are low, product with stable quality, and the cardboard compressive resistance obtained after bonding is large, and the resistance to power of exposing is strong.
Embodiment
Below in conjunction with specific examples, the present invention is described in detail; should understand; embodiment is only for illustration of the present invention, instead of for limiting the present invention, any amendment, equivalent replacement etc. made on basis of the present invention is all in protection scope of the present invention.
Embodiment 1
A kind of Corrugated Box tackiness agent, is made up of the raw material of following weight part: water: 50 parts; Sweet potato powder: 30 parts; Calcium carbonate: 14 parts; Hydrochloric acid: 2.6 parts; Sepiolite powder: 3.8 parts; Naphthalenesulfonate formaldehyde condensation compound: 0.14 part; Xylo-Mucine: 0.16 part; White sugar: 0.11 part;
According to above-mentioned raw materials proportioning, prepare described Corrugated Box tackiness agent according to the following steps:
S1: the water of proportioning is poured in container, and to adjust water temperature be 60 DEG C;
S2: add sweet potato powder in water in S1, and be stirred to thick, obtain latex A;
S3: add calcium carbonate in the latex A in S2, and carry out stirring and obtain emulsion B, wherein, churning time is 16min;
S4: add hydrochloric acid in the emulsion B in S3, and carry out stirring and obtain emulsion C, wherein, churning time is 7min;
S5: add sepiolite powder, naphthalenesulfonate formaldehyde condensation compound, Xylo-Mucine, white sugar in S4 gained emulsion C, after stirring, leave standstill, cooling after obtain described Corrugated Box tackiness agent.
Embodiment 2
A kind of Corrugated Box tackiness agent, is made up of the raw material of following weight part: water: 45 parts; Sweet potato powder: 34 parts; Calcium carbonate: 12 parts; Hydrochloric acid: 3 parts; Sepiolite powder: 3 parts; Naphthalenesulfonate formaldehyde condensation compound: 0.16 part; Xylo-Mucine: 0.15 part; White sugar: 0.12 part;
According to above-mentioned raw materials proportioning, prepare described Corrugated Box tackiness agent according to the following steps:
S1: the water of proportioning is poured in container, and to adjust water temperature be 56 DEG C;
S2: add sweet potato powder in water in S1, and be stirred to thick, obtain latex A;
S3: add calcium carbonate in the latex A in S2, and carry out stirring and obtain emulsion B, wherein, churning time is 18min;
S4: add hydrochloric acid in the emulsion B in S3, and carry out stirring and obtain emulsion C, wherein, churning time is 6min;
S5: add sepiolite powder, naphthalenesulfonate formaldehyde condensation compound, Xylo-Mucine, white sugar in S4 gained emulsion C, after stirring, leave standstill, cooling after obtain described Corrugated Box tackiness agent.
Embodiment 3
A kind of Corrugated Box tackiness agent, is made up of the raw material of following weight part: water: 55 parts; Sweet potato powder: 28 parts; Calcium carbonate: 16 parts; Hydrochloric acid 2 parts; Sepiolite powder: 4 parts; Naphthalenesulfonate formaldehyde condensation compound: 0.12 part; Xylo-Mucine: 0.18 part; White sugar: 0.10 part;
According to above-mentioned raw materials proportioning, prepare described Corrugated Box tackiness agent according to the following steps:
S1: the water of proportioning is poured in container, and to adjust water temperature be 64 DEG C;
S2: add sweet potato powder in water in S1, and be stirred to thick, obtain latex A;
S3: add calcium carbonate in the latex A in S2, and carry out stirring and obtain emulsion B, wherein, churning time is 15min;
S4: add hydrochloric acid in the emulsion B in S3, and carry out stirring and obtain emulsion C, wherein, churning time is 8min;
S5: add sepiolite powder, naphthalenesulfonate formaldehyde condensation compound, Xylo-Mucine, white sugar in S4 gained emulsion C, after stirring, leave standstill, cooling after obtain described Corrugated Box tackiness agent.
Embodiment 4
A kind of Corrugated Box tackiness agent, is made up of the raw material of following weight part: water: 46 parts; Sweet potato powder: 28.9 parts; Calcium carbonate: 14.3 parts; Hydrochloric acid: 2.6 parts; Sepiolite powder: 3.7 parts; Naphthalenesulfonate formaldehyde condensation compound: 0.129 part; Xylo-Mucine: 0.157 part; White sugar: 0.115 part;
According to above-mentioned raw materials proportioning, prepare described Corrugated Box tackiness agent according to the following steps:
S1: the water of proportioning is poured in container, and to adjust water temperature be 57 DEG C;
S2: add sweet potato powder in water in S1, and be stirred to thick, obtain latex A;
S3: add calcium carbonate in the latex A in S2, and carry out stirring and obtain emulsion B, wherein, churning time is 17.3min;
S4: add hydrochloric acid in the emulsion B in S3, and carry out stirring and obtain emulsion C, wherein, churning time is 7.3min;
S5: add sepiolite powder, naphthalenesulfonate formaldehyde condensation compound, Xylo-Mucine, white sugar in S4 gained emulsion C, after stirring, leave standstill, cooling after obtain described Corrugated Box tackiness agent.
Embodiment 5
A kind of Corrugated Box tackiness agent, is made up of the raw material of following weight part: water: 51.4 parts; Sweet potato powder: 32.3 parts; Calcium carbonate: 15.4 parts; Hydrochloric acid: 2.2 parts; Sepiolite powder: 3.15 parts; Naphthalenesulfonate formaldehyde condensation compound: 0.16 part; Xylo-Mucine: 0.16 part; White sugar: 0.11 part;
According to above-mentioned raw materials proportioning, prepare described Corrugated Box tackiness agent according to the following steps:
S1: the water of proportioning is poured in container, and to adjust water temperature be 62 DEG C;
S2: add sweet potato powder in water in S1, and be stirred to thick, obtain latex A;
S3: add calcium carbonate in the latex A in S2, and carry out stirring and obtain emulsion B, wherein, churning time is 16.4min;
S4: add hydrochloric acid in the emulsion B in S3, and carry out stirring and obtain emulsion C, wherein, churning time is 7.6min;
S5: add sepiolite powder, naphthalenesulfonate formaldehyde condensation compound, Xylo-Mucine, white sugar in S4 gained emulsion C, after stirring, leave standstill, cooling after obtain described Corrugated Box tackiness agent.
Claims (9)
1. a Corrugated Box tackiness agent, is characterized in that, is made up: water of the raw material of following weight part: 45-55 part; Sweet potato powder: 28-34 part; Calcium carbonate: 12-16 part; Hydrochloric acid: 2-3 part; Sepiolite powder: 3-4 part; Naphthalenesulfonate formaldehyde condensation compound: 0.12-0.16 part; Xylo-Mucine: 0.15-0.18 part; White sugar: 0.10-0.12 part;
According to above-mentioned raw materials proportioning, prepare described Corrugated Box tackiness agent according to the following steps:
S1: the water of proportioning is poured in container, and to adjust water temperature be 56-64 DEG C;
S2: add sweet potato powder in water in S1, and be stirred to thick, obtain latex A;
S3: add calcium carbonate in the latex A in S2, and carry out stirring and obtain emulsion B, wherein, churning time is 15-18min;
S4: add hydrochloric acid in the emulsion B in S3, and carry out stirring and obtain emulsion C, wherein, churning time is 6-8min;
S5: add sepiolite powder, naphthalenesulfonate formaldehyde condensation compound, Xylo-Mucine, white sugar in S4 gained emulsion C, after stirring, leave standstill, cooling after obtain described Corrugated Box tackiness agent.
2. Corrugated Box tackiness agent according to claim 1, is characterized in that, is made up: water of the raw material of following weight part: 48-52 part; Sweet potato powder: 29-32 part; Calcium carbonate: 13-15 part; Hydrochloric acid: 2.3-2.7 part; Sepiolite powder: 3.2-3.8 part; Naphthalenesulfonate formaldehyde condensation compound: 0.14-0.15 part; Xylo-Mucine: 0.16-0.17 part; White sugar: 0.11-0.12 part.
3. Corrugated Box tackiness agent according to claim 1 and 2, is characterized in that, is made up: water of the raw material of following weight part: 50 parts; Sweet potato powder: 30 parts; Calcium carbonate: 14 parts; Hydrochloric acid: 2.6 parts; Sepiolite powder: 3.8 parts; Naphthalenesulfonate formaldehyde condensation compound: 0.14 part; Xylo-Mucine: 0.16 part; White sugar: 0.11 part.
4. the Corrugated Box tackiness agent according to any one of claim 1-3, is characterized in that, in S1, adjustment water temperature is 58-62 DEG C.
5. the Corrugated Box tackiness agent according to any one of claim 1-4, is characterized in that, in S1, adjustment water temperature is 60 DEG C.
6. the Corrugated Box tackiness agent according to any one of claim 1-5, is characterized in that, in S3, churning time is 15.6-17min.
7. the Corrugated Box tackiness agent according to any one of claim 1-6, is characterized in that, in S3, churning time is 16min.
8. the Corrugated Box tackiness agent according to any one of claim 1-7, is characterized in that, in S4, churning time is 6.5-7.5min.
9. the Corrugated Box tackiness agent according to any one of claim 1-8, is characterized in that, in S4, churning time is 7min.