CN103725251A - Formula for producing paper tube adhesive by taking bean flour as raw material - Google Patents
Formula for producing paper tube adhesive by taking bean flour as raw material Download PDFInfo
- Publication number
- CN103725251A CN103725251A CN201310690803.XA CN201310690803A CN103725251A CN 103725251 A CN103725251 A CN 103725251A CN 201310690803 A CN201310690803 A CN 201310690803A CN 103725251 A CN103725251 A CN 103725251A
- Authority
- CN
- China
- Prior art keywords
- raw material
- paper tube
- bean powder
- tube adhesive
- take
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a formula for producing a paper tube adhesive for taking bean flour as a raw material. The paper tube adhesive is prepared from the following main raw materials in parts by weight: 30 parts of defatted soybean flour, 60 to 170 parts of water, 6 to 12 parts of water glass, 1 to 3 parts of calcium hydroxide, 0 to 1 part of guar gum and 0.15 to 0.3 part of BIT sterilization preservative. The paper tube adhesive is prepared by the following main steps of mixing and heating the soybean flour and water, sequentially adding the calcium hydroxide, the water glass and the guar gum, performing reaction while stirring for 30 to 60 minutes, adding the BIT sterilization preservative for uniform mixing, and storing a product. The formula has such advantages that a production process is simple; the volatilization of harmful substances such as formaldehyde in production and using processes is avoided; the product is environment-friendly, degradable, low in cost and wide in application range.
Description
Technical field
The present invention relates to a kind of production technique of paper tube adhesive, especially a kind of production formula of take the paper tube adhesive that bean powder is raw material.
Background technology
Existing market mainly contains starch paper tube adhesive, white glue with vinyl, three kinds of sizing agents of producing for the paper tube that spins of albumen paper tube adhesive.Wherein starch paper tube adhesive has not humidity, even runs into the shortcoming that water will come unglued, and has greatly limited his use; White glue with vinyl water-tolerant, but formaldehyde contained, there is the shortcoming of polluting Working environment; The albumen paper tube adhesive water-tolerant that market is used in addition, is mainly raw material by protein isolate (soybean bean powder refined product), has expensive shortcoming.
Summary of the invention
The object of this invention is to provide a kind of production formula of take the paper tube adhesive that bean powder is raw material.
The technical solution adopted in the present invention is:
A production formula for the paper tube adhesive that the bean powder of take is raw material, the proportioning of raw material is (weight part):
Defatted soyflour: 30 parts
Water: 60-170 part
Water glass: 6-12 part
Calcium hydroxide or sodium hydroxide or both mixtures: 1-3 part (solid)
Guar gum: 0-1 part
BIT fungicidal preservative: 0.15-0.3 part.
Described defatted soyflour is low-temperature defatted bean powder, by low temperature soy meal, pulverizes and forms, or the byproduct for producing in low temperature soy meal production process; Described water glass, modulus is 3.2-3.4, concentration is 40%; Described sodium hydroxide, calcium hydroxide are solids, can be also the liquid that alkalinity reaches solid weight mark; Described guar gum viscosity is 5000-10000 centipoise.
Comprise following step in sequence:
(1) to the water that adds 60-170 part in reactor;
(2), under room temperature, to the bean powder that adds 30 parts in reactor, make slurries while stirring;
(3) be heated to 45-55 degree Celsius;
(4) add calcium hydroxide or sodium hydroxide or both mixtures of 1-3 part;
(5) to the water glass that adds 6-12 part in reactor;
(6) add the guar gum of 0-1 part;
(7) raw material add complete, under the temperature condition of 45-55 ℃, stirring reaction 30-60 minute.
The granularity of the bean powder adding in described (2) is 100-200 order.
Heating means in described (3) can, for indirect steam or open steam heating, can be also indirect heating in water bath.
While adding calcium hydroxide in described (4), first by its dispersed with stirring in water.
In described (6), guar gum, before adding reactor, with the water soaking of 30 times, and carries out colloidal mill homogenization treatment.
During described product needed long storage time, preparation finishes in reactor, to add 0.15-0.3 part BIT fungicidal preservative, mixes, and deposits.
Before depositing, use colloidal mill homogeneous one time.
Compared with prior art, advantage of the present invention is: be that to take cheap soybean defatted soy flour be raw material, have that raw material (soybean) is renewable, cheap, cohesive strength is large, water-tolerant, free of contamination advantage, and facility investment is few, production technique is simple.
Embodiment
A production formula for the paper tube adhesive that the bean powder of take is raw material, the proportioning of raw material is (weight part):
Defatted soyflour: 30 parts
Water: 60-170 part
Water glass: 6-12 part
Calcium hydroxide or sodium hydroxide or both mixtures: 1-3 part (solid)
Guar gum: 0-1 part
BIT fungicidal preservative: 0.15-0.3 part.
Described defatted soyflour is low-temperature defatted bean powder, by low temperature soy meal, pulverizes and forms, or the byproduct for producing in low temperature soy meal production process; Described water glass, modulus is 3.2-3.4, concentration is 40%; Described sodium hydroxide, calcium hydroxide are solids, can be also the liquid that alkalinity reaches solid weight mark; Described guar gum viscosity is 5000-10000 centipoise.
Comprise following step in sequence:
(1) to the water that adds 60-170 part in reactor;
(2), under room temperature, to the bean powder that adds 30 parts in reactor, make slurries while stirring;
(3) be heated to 45-55 degree Celsius;
(4) add calcium hydroxide or sodium hydroxide or both mixtures of 1-3 part;
(5) to the water glass that adds 6-12 part in reactor;
(6) add the guar gum of 0-1 part;
(7) raw material add complete, under the temperature condition of 45-55 ℃, stirring reaction 30-60 minute.
The granularity of the bean powder adding in described (2) is 100-200 order.
Heating means in described (3) can, for indirect steam or open steam heating, can be also indirect heating in water bath.
While adding calcium hydroxide in described (4), first by its dispersed with stirring in water.
In described (6), guar gum, before adding reactor, with the water soaking of 30 times, and carries out colloidal mill homogenization treatment.
During described product needed long storage time, preparation finishes in reactor, to add 0.15-0.3 part BIT fungicidal preservative, mixes, and deposits.
Before depositing, use colloidal mill homogeneous one time.
Claims (9)
1. a production formula for the paper tube adhesive that the bean powder of take is raw material, the proportioning that it is characterized in that raw material is (weight part):
Defatted soyflour: 30 parts
Water: 60-170 part
Water glass: 6-12 part
Calcium hydroxide or sodium hydroxide or both mixtures: 1-3 part (solid)
Guar gum: 0-1 part
BIT fungicidal preservative: 0.15-0.3 part.
2. a kind of production formula of take the paper tube adhesive that bean powder is raw material as claimed in claim 1, is characterized in that described defatted soyflour is low-temperature defatted bean powder, by low temperature soy meal, pulverize and form, or the byproduct for producing in low temperature soy meal production process; Described water glass, modulus is 3.2-3.4, concentration is 40%; Described sodium hydroxide, calcium hydroxide are solids, can be also the liquid that alkalinity reaches solid weight mark; Described guar gum viscosity is 5000-10000 centipoise.
3. a kind of production formula of take the paper tube adhesive that bean powder is raw material according to claim 1, is characterized in that comprising following step in sequence:
(1) to the water that adds 60-170 part in reactor;
(2), under room temperature, to the bean powder that adds 30 parts in reactor, make slurries while stirring;
(3) be heated to 45-55 degree Celsius;
(4) add calcium hydroxide or sodium hydroxide or both mixtures of 1-3 part;
(5) to the water glass that adds 6-12 part in reactor;
(6) add the guar gum of 0-1 part;
(7) raw material add complete, under the temperature condition of 45-55 ℃, stirring reaction 30-60 minute.
4. a kind of production formula of take the paper tube adhesive that bean powder is raw material according to claim 3, is characterized in that the granularity of the bean powder that adds in described (2) is 100-200 order.
5. a kind of production formula of take the paper tube adhesive that bean powder is raw material according to claim 3, is characterized in that the heating means in described (3) can, for indirect steam or open steam heating, can be also indirect heating in water bath.
6. a kind of production formula of take the paper tube adhesive that bean powder is raw material according to claim 3, while it is characterized in that adding calcium hydroxide in described (4), first by its dispersed with stirring in water.
7. a kind of production formula of take the paper tube adhesive that bean powder is raw material according to claim 3, is characterized in that in described (6), guar gum, before adding reactor, with the water soaking of 30 times, and carries out colloidal mill homogenization treatment.
8. a kind of production formula of take the paper tube adhesive that bean powder is raw material according to claim 3, while it is characterized in that described product needed long storage time, preparation finishes in reactor, to add 0.15-0.3 part BIT fungicidal preservative, mixes, and deposits.
9. according to a kind of described in claim 3 or 8, take the production formula of the paper tube adhesive that bean powder is raw material, before it is characterized in that depositing, with colloidal mill homogeneous one time.