CN101054501A - Cardboard starch gum activating agent and cardboard starch gum - Google Patents
Cardboard starch gum activating agent and cardboard starch gum Download PDFInfo
- Publication number
- CN101054501A CN101054501A CN 200710110787 CN200710110787A CN101054501A CN 101054501 A CN101054501 A CN 101054501A CN 200710110787 CN200710110787 CN 200710110787 CN 200710110787 A CN200710110787 A CN 200710110787A CN 101054501 A CN101054501 A CN 101054501A
- Authority
- CN
- China
- Prior art keywords
- cardboard
- starch gum
- promoting agent
- cardboard starch
- activating agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a cardboard starch glue activating agent and cardboard starch glue. Said activating agent includes following matters by weight (wt.%): 65-75% of sepiolite powder, 10-20% of light calcium powder, 1-5% of sand pulp plasticizer, 3-6% of sodium carboxymethylcellulose, 1-5% of custer sugar. Said starch glue has 1-6% of activating agent. The starch glue produced by inventive activating agent is non-poisonous and harmless and is not tending to the phenomenon of water gel separation, and has a good bonding capacity, a simple producing craft, a stable product quality, a small pollution. The cardboard has a big pressure resistance, a fast car speed, a powerful puncturing resistance.
Description
Technical field
The present invention relates to a kind of promoting agent of tackiness agent and adopt the tackiness agent of this promoting agent, specifically, the present invention relates to a kind of cardboard starch gum promoting agent and cardboard starch gum.
Background technology
Current, for bonding amylans that adopt of cardboard, as the starch bonded adhesives that all uses mostly in the production of corrugated cardboard, honeycomb cardboard more.But because a little less than this kind adhesives power, crushing resistance, moistureproof ability, therefore the quality product of producing can not get guaranteeing.So occurred in this amylan, adding the method that other one-tenth assign to improve its performance in the prior art.
Yet, often containing in this type of added ingredients human body composition excitatory, the phenomenon of glue precipitation separation appears easily, both caused waste, had a strong impact on bonding force again.What have then needs mechanical disintegration or secondary glue, both complicated, has increased man-hour, pollution again, and product also is difficult to stablize.
Summary of the invention
Therefore, the object of the present invention is to provide a kind of cardboard starch gum promoting agent and cardboard starch gum, this promoting agent is nontoxic, and the cardboard starch gum bond properties that makes by force, is not prone to glue to be separated, and makes simple.
In order to realize purpose of the present invention, a kind of cardboard starch gum promoting agent is provided, it is characterized in that described promoting agent comprises the material of following weight percent:
Sepiolite powder 65-75%, light calcium carbonate powder 10-20%, mortar plasticizer 1-5%, cellulose sodium carboxymethyl 3-6%, white sugar 1-5%.Wherein any mortar plasticizer of mortar plasticizer for buying on the market starched agent as " solid wound " board WF molding sand that pear tree garden New Building Materials factory produces.
Preferred, described promoting agent comprises the material of following weight percent:
Sepiolite powder 68-72%, light calcium carbonate powder 15-20%, mortar plasticizer 2-4%, cellulose sodium carboxymethyl 4-5%, white sugar 1.5-4%.
The present invention uses the sepiolite powder of selling on the market, and wherein the sepiolite composition generally accounts for 40-85%, and the weight of preferred sepiolite composition is greater than 80% sepiolite powder.
The granularity of sepiolite powder of the present invention and described light calcium carbonate powder can be used the above powder of 200 common orders, preferably is the 800-1200 order.
Mortar plasticizer of the present invention more preferably comprises a kind of mortar plasticizer in naphthalenesulfonate formaldehyde condensation compound or melamine resin or the aliphatic sulfonate in its composition, can reach water-reducing effect more efficiently.
In order to realize purpose of the present invention, a kind of cardboard starch gum is provided, it is characterized in that described cardboard starch gum stirs after adding cardboard starch gum promoting agent of the present invention, the add-on of this promoting agent is the 1-6% of this cardboard starch gum weight
Beneficial effect of the present invention is: the amylan that adopts the cardboard starch gum promoting agent of composition of the present invention and proportioning to make is nontoxic, be not prone to the isolating phenomenon of glue, and the adhesive capacity of this amylan is strong, manufacturing process is simple, product with stable quality, the speed of a motor vehicle is fast, and the bonding cardboard compressive resistance that obtains is big, and the anti-power of exposing is strong.
Embodiment
Embodiment 1
The promoting agent of present embodiment is that the material uniform mixing with following weight percent forms:
Sepiolite powder 70%, wherein sepiolite content is 85%, granularity is 800 orders;
Light calcium carbonate powder 20%, granularity are 1200 orders;
Mortar plasticizer 2.5%, " solid wound " board WF molding sand slurry agent that pear tree garden New Building Materials factory produces;
Cellulose sodium carboxymethyl 5%, technical grade;
White sugar 2.5%, civilian level;
The promoting agent of present embodiment will promptly be obtained behind the mentioned component uniform mixing.It being joined stirs in the commercially available common cardboard starch gum again gets final product, and the add-on of promoting agent is 1% of an amylan weight
Embodiment 2
The promoting agent of present embodiment is that the material uniform mixing with following weight percent forms:
Sepiolite powder 75%, wherein sepiolite content is 70%, granularity is 1200 orders;
Light calcium carbonate powder 10%, granularity are 1000 orders;
Mortar plasticizer 5% is received the mortar plasticizer of formaldehyde condensation products for containing naphthene sulfonic acid;
Cellulose sodium carboxymethyl 6%, technical grade;
White sugar 1%, civilian level;
Flyash 3%;
The promoting agent of present embodiment will promptly be obtained behind the mentioned component uniform mixing.It being joined stirs in the commercially available common cardboard starch gum again gets final product, and the add-on of promoting agent is 3% of an amylan weight
Embodiment 3
The promoting agent of present embodiment is that the material uniform mixing with following weight percent forms:
Sepiolite powder 65%, wherein sepiolite content is 78%, granularity is 1000 orders;
Light calcium carbonate powder 15%, granularity are 800 orders;
Mortar plasticizer 1%, dimension contains the mortar plasticizer that dodecyl sodium sulfonate is received;
Cellulose sodium carboxymethyl 3%, technical grade;
White sugar 5%, civilian level;
Wilkinite 11%;
The promoting agent of present embodiment will promptly be obtained behind the mentioned component uniform mixing.It being joined stirs in the commercially available common cardboard starch gum again gets final product, and the add-on of promoting agent is 6% of an amylan weight
Claims (6)
1. a cardboard starch gum promoting agent is characterized in that, described promoting agent comprises the material of following weight percent:
Sepiolite powder 65-75%, light calcium carbonate powder 10-20%, mortar plasticizer 1-5%, cellulose sodium carboxymethyl 3-6%, white sugar 1-5%.
2. cardboard starch gum promoting agent according to claim 1 is characterized in that, described promoting agent comprises the material of following weight percent:
Sepiolite powder 68-72%, light calcium carbonate powder 15-20%, mortar plasticizer 2-4%, cellulose sodium carboxymethyl 4-5%, white sugar 1.5-4%.
3. cardboard starch gum promoting agent according to claim 1 and 2 is characterized in that the weight of sepiolite composition is greater than 80% in the described sepiolite powder.
4. cardboard starch gum promoting agent according to claim 1 and 2 is characterized in that the granularity of described sepiolite powder and described light calcium carbonate powder is the 800-1200 order.
5. cardboard starch gum promoting agent according to claim 1 and 2 is characterized in that, comprises a kind of in naphthalenesulfonate formaldehyde condensation compound or melamine resin or the aliphatic sulfonate in the composition of described mortar plasticizer.
6. a cardboard starch gum is characterized in that, described cardboard starch gum stirs after adding cardboard starch gum promoting agent as claimed in claim 1 or 2, and the add-on of this promoting agent is the 1-6% of this cardboard starch gum weight.