CN104277484A - 一种特种耐腐蚀土工格栅及制备方法 - Google Patents
一种特种耐腐蚀土工格栅及制备方法 Download PDFInfo
- Publication number
- CN104277484A CN104277484A CN201410575573.7A CN201410575573A CN104277484A CN 104277484 A CN104277484 A CN 104277484A CN 201410575573 A CN201410575573 A CN 201410575573A CN 104277484 A CN104277484 A CN 104277484A
- Authority
- CN
- China
- Prior art keywords
- resin
- carbon black
- grid
- resistant
- speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种特种耐腐蚀土工格栅,由下列重量份的组份原料加工而得:TPE树脂20-30,PP树脂30-40,SEBS树脂6-8,抗氧剂BHT0.5-0.8,松节油0.2-0.4,硅油0.4-0.6,抗氧剂2150.1~0.2,UV吸收剂0.1~0.2,光稳定剂7440.1-0.2,改性炭黑母料4-6。特种耐腐蚀土工格栅,将配方材料混炼,挤出,熔体通过三辊压光机成型板材,板材经过冲压机进行冲孔,孔板经过升温后拉伸,即制得土工格栅。本发明的加工出的改性土工格栅具有耐高温、耐酸碱性能。
Description
技术领域
本发明涉及土工格栅的制造,具体涉及一种特种耐腐蚀土工格栅及制备方法。
背景技术
随着土工合成材料行业的发展,越来越多的土工格栅产品推向了市场,土工格栅的主要竞争就是产品性能和价格成本竞争。由于聚丙烯土工格栅领域和使用区域广泛,因此对土工格栅要求其具有多种性能。但是只靠一种聚合物来实现这些性能是很难实现的,因此需要对土工格栅配方进行改性成为这个行业的必然趋势。 在制备高性能材料方面纤维增强是一种普遍而有效的方法,增强所用的纤维一般为玻璃纤维、碳纤维等。由这些纤维填充得到的树脂增强效果明显,能够使得相同规格的土工格栅更薄。但是使用玻璃纤维和碳纤维后,聚合物的拉伸伸长率又会有很大下降,导致土工格栅拉伸很短,产品单位面积重量上升,使得生产成本反而增加,不利于达到低成本化的目的。
在土工格栅中加入改性炭黑等填料,可使其具有较好的耐酸、耐碱、耐腐蚀和抗老化性能,提高抗冲击强度和拉伸强度。
发明内容
本发明提供了一种特种耐腐蚀土工格栅及制备方法。本发明通过配方原材料的改性,从而得到具有耐高温、耐酸碱性能良的土工格栅。
本发明所采用技术方案如下:
一种特种耐腐蚀土工格栅,其特征在于,由下列重量份的组份原料加工而得:TPE树脂60-70,PP树脂20-30,SEBS树脂6-8,抗氧剂BHT 0.5-0.8,松节油0.2-0.4,硅油0.4-0.6,抗氧剂215 0.1~0.2,UV吸收剂0.1~0.2,光稳定剂7440.1-0.2,改性炭黑母料 4-6,
所述的改性炭黑母料的制备方法:(1)按重量份称取聚乙烯30-40、聚丙烯10-20、炭黑 40-50、丙烯酸酯 0.2-1.5、氧化锌0.1-0.4、抗氧剂168 0.1-0.3、防老化剂 0.1-0.3、煤油 0.5-1.0、粉煤灰1-3、 聚甘油辛癸酸酯3-5、滑石粉 4-6;(2)将称量好的炭黑、丙烯酸酯、氧化锌加入搅拌机中,在60℃-180℃的温度下充分混合,得到混合物料A;(3)将聚乙烯、聚丙烯、滑石粉、抗氧剂1010 、防老化剂 、白油、粉煤灰、 聚甘油辛癸酸酯等其余原料组分依次投入高速搅拌机中高速搅拌3-5分钟,得到混合物物料B;(4)将A和B混合均匀后得到共混物加入到双螺杆挤出机中,螺杆转速为80-130 rpm,加热机筒温度180-200℃熔融挤出,冷却,造粒即可。
所述的特种耐腐蚀土工格栅的制备方法,其特征在于,包括以下步骤:
(1)按配方比例称取各组分原料,将TPE树脂、PP树脂、SEBS树脂、抗氧剂BHT加入高速混合机中,高速混合10-15min后,再向混合机中加入硅油、抗氧剂215、UV吸收剂和松节油,高速混合10-20min后将物料放出,与改性炭黑母料混合均匀;
(2)将混合好的物料送入双螺杆挤出机中挤出,控制挤出机螺杆的转速为200~300r/min,控制挤出机料筒的温度为195-235℃,熔体通过三辊压光机成型板材,板材经过冲压机使用模具进行冲孔,孔板经过升温到85℃ -105℃后拉伸,即制得特种耐腐蚀土工格栅。
本发明取得的有益效果在于:
本发明在配方中将TPE树脂,PP树脂,SEBS树脂混合改性,再添加自制的改性填料,复合助剂,调整适当的工艺参数,加工出的改性土工格栅具有耐高温、耐低寒、抗老化、耐腐蚀等优良性能。广泛应用于沥青路面、水泥路面及路基的增强和铁路路基、堤坝护坡、机场跑道、防沙治沙等工程项目。
具体实施方式
以下结合实施例对本发明作进一步说明,
一种特种耐腐蚀土工格栅,由下列重量(kg)的组份原料加工而得:TPE树脂65,PP树脂65,SEBS树脂7,抗氧剂BHT 0.7,松节油0.3,硅油0.5,抗氧剂215 0.1,UV吸收剂0.15,光稳定剂744 0.15,改性炭黑母料 5,
其中,改性炭黑母料的制备方法:(1)按重量(kg)称取聚乙烯35、聚丙烯15、炭黑 45、丙烯酸酯 0.8、氧化锌0.3、抗氧剂168 0.2、防老化剂 0.2、煤油 0.6、粉煤灰2、 聚甘油辛癸酸酯4、滑石粉5;(2)将称量好的炭黑、丙烯酸酯、氧化锌加入搅拌机中,在60℃-180℃的温度下充分混合,得到混合物料A; (3)将聚乙烯、聚丙烯、滑石粉、抗氧剂1010 、防老化剂 、白油、粉煤灰、 聚甘油辛癸酸酯等其余原料组分依次投入高速搅拌机中高速搅拌3-5分钟,得到混合物物料B;(4)将A和B混合均匀后得到共混物加入到双螺杆挤出机中,螺杆转速为80-130 rpm,加热机筒温度180-200℃熔融挤出,冷却,造粒即可。
特种耐腐蚀土工格栅的制备方法,包括以下步骤:
(1)按配方比例称取各组分原料,将TPE树脂、PP树脂、SEBS树脂、抗氧剂BHT加入高速混合机中,高速混合10-15min后,再向混合机中加入硅油、抗氧剂215、UV吸收剂和松节油,高速混合10-20min后将物料放出,与改性炭黑母料混合均匀;
(2)将混合好的物料送入双螺杆挤出机中挤出,控制挤出机螺杆的转速为200~300r/min,控制挤出机料筒的温度为195-235℃,熔体通过三辊压光机成型板材,板材经过冲压机使用模具进行冲孔,孔板经过升温到85℃ -105℃后拉伸,即制得特种耐腐蚀土工格栅。
本发明的土工格栅不同规格的性能检测值如下表:
Claims (2)
1.一种特种耐腐蚀土工格栅,其特征在于,由下列重量份的组份原料加工而得:TPE树脂60-70,PP树脂20-30,SEBS树脂6-8,抗氧剂BHT 0.5-0.8,松节油0.2-0.4,硅油0.4-0.6,抗氧剂215 0.1~0.2,UV吸收剂0.1~0.2,光稳定剂7440.1-0.2,改性炭黑母料 4-6,
所述的改性炭黑母料的制备方法:(1)按重量份称取聚乙烯30-40、聚丙烯10-20、炭黑 40-50、丙烯酸酯 0.2-1.5、氧化锌0.1-0.4、抗氧剂168 0.1-0.3、防老化剂 0.1-0.3、煤油 0.5-1.0、粉煤灰1-3、 聚甘油辛癸酸酯3-5、滑石粉 4-6;(2)将称量好的炭黑、丙烯酸酯、氧化锌加入搅拌机中,在60℃-180℃的温度下充分混合,得到混合物料A;(3)将聚乙烯、聚丙烯、滑石粉、抗氧剂1010 、防老化剂 、白油、粉煤灰、 聚甘油辛癸酸酯等其余原料组分依次投入高速搅拌机中高速搅拌3-5分钟,得到混合物物料B;(4)将A和B混合均匀后得到共混物加入到双螺杆挤出机中,螺杆转速为80-130 rpm,加热机筒温度180-200℃熔融挤出,冷却,造粒即可。
2.根据权利要求1所述的特种耐腐蚀土工格栅的制备方法,其特征在于,包括以下步骤:
(1)按配方比例称取各组分原料,将TPE树脂、PP树脂、SEBS树脂、抗氧剂BHT加入高速混合机中,高速混合10-15min后,再向混合机中加入硅油、抗氧剂215、UV吸收剂和松节油,高速混合10-20min后将物料放出,与改性炭黑母料混合均匀;
(2)将混合好的物料送入双螺杆挤出机中挤出,控制挤出机螺杆的转速为200~300r/min,控制挤出机料筒的温度为195-235℃,熔体通过三辊压光机成型板材,板材经过冲压机使用模具进行冲孔,孔板经过升温到85℃ -105℃后拉伸,即制得特种耐腐蚀土工格栅。