CN104263071A - Water-based gravure ink and preparation method thereof - Google Patents
Water-based gravure ink and preparation method thereof Download PDFInfo
- Publication number
- CN104263071A CN104263071A CN201410454511.0A CN201410454511A CN104263071A CN 104263071 A CN104263071 A CN 104263071A CN 201410454511 A CN201410454511 A CN 201410454511A CN 104263071 A CN104263071 A CN 104263071A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic resin
- pigment
- hydroxylated acrylic
- printing ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-based gravure ink. The water-based gravure ink comprises the following components: hydroxyl acrylic resin solution, hydroxyl acrylic resin emulsion, a monoalcoxyl pyrophosphate type coupling agent, tributyl phosphate, pigment, isopropyl alcohol and deionized water. The water-based gravure ink has the advantages that breeding of microorganisms in printing ink can be controlled, the service life of the water-based gravure ink can be prolonged, the stability of the water-based gravure ink is high, and the preparation method of the water-based gravure ink is simple and easy to realize.
Description
Technical field
The present invention relates to a kind of ink, be specifically related to a kind of aquosity intaglio printing ink and preparation method thereof.
Background technology
The stability of traditional aquosity intaglio printing ink, colour strength and gloss all have corresponding defect.
Summary of the invention
Goal of the invention: the object of the invention is to solve deficiency of the prior art, a kind of aquosity intaglio printing ink and preparation method thereof is provided.
Technical scheme: a kind of aquosity intaglio printing ink of the present invention, following component is comprised: Hydroxylated acrylic resin solution 70 ~ 80 parts, Hydroxylated acrylic resin emulsion 5 ~ 10 parts, monoalkoxy tetra-sodium ester type coupling agent 0.5 ~ 1 part, tributyl phosphate 0.5 ~ 1.5 part, pigment 20 ~ 25 parts, Virahol 5 ~ 10 parts and deionized water 10 ~ 15 parts according to parts by weight.
Wherein, acrylic resin soln can improve colour strength and the glossiness of ink.
Further, described Hydroxylated acrylic resin solution 72 ~ 79 parts, Hydroxylated acrylic resin emulsion 5.5 ~ 8 parts, monoalkoxy tetra-sodium ester type coupling agent 0.59 ~ 0.95 part, tributyl phosphate 0.65 ~ 1.3 part, pigment 21 ~ 24.5 parts, Virahol 5.8 ~ 9.2 parts and deionized water 11 ~ 14 parts.
Further, described pigment be that iron oxide black, lithopone, phthalein are blue or green blue, aniline yellow and pink in one or more.
The invention also discloses a kind of preparation method of aquosity intaglio printing ink, comprise the following steps:
(1) Virahol and deionized water are put into agitator to stir, temperature is controlled in 48 ~ 58 DEG C, slowly adds during stirring: Hydroxylated acrylic resin solution and Hydroxylated acrylic resin emulsion, stirs 30min, then adds pigment and continues to stir 30min;
(2) add monoalkoxy tetra-sodium ester type coupling agent, tributyl phosphate successively in the pigment slurry of gained in step (1), be uniformly mixed, stirring velocity is now 25m/s, and temperature is controlled in 20 ~ 30 DEG C.
Beneficial effect: the present invention can control growing and breeding of microorganism in ink, be conducive to the work-ing life extending aquosity intaglio printing ink, ink stability of the present invention is high, and preparation method of the present invention is simple and easy to realize.
Embodiment
Below technical solution of the present invention is described in detail, but protection scope of the present invention is not limited to described embodiment.
embodiment 1:
A kind of aquosity intaglio printing ink of the present invention, following component is comprised: Hydroxylated acrylic resin solution 70 parts, Hydroxylated acrylic resin emulsion 5 parts, monoalkoxy tetra-sodium ester type coupling agent 0.5 part, tributyl phosphate 0.5 part, pigment 20 parts, Virahol 5 parts and deionized water 10 parts according to parts by weight.
Above-mentioned pigment is that iron oxide black, lithopone, phthalein are blue or green blue, aniline yellow and pink in one or more.
The invention also discloses a kind of preparation method of aquosity intaglio printing ink, comprise the following steps:
(1) Virahol and deionized water are put into agitator to stir, temperature is controlled in 48 ~ 58 DEG C, slowly adds during stirring: Hydroxylated acrylic resin solution and Hydroxylated acrylic resin emulsion, stirs 30min, then adds pigment and continues to stir 30min;
(2) add monoalkoxy tetra-sodium ester type coupling agent, tributyl phosphate successively in the pigment slurry of gained in step (1), be uniformly mixed, stirring velocity is now 25m/s, and temperature is controlled in 20 ~ 30 DEG C.
embodiment 2:
A kind of aquosity intaglio printing ink of the present invention, following component is comprised: Hydroxylated acrylic resin solution 80 parts, Hydroxylated acrylic resin emulsion 10 parts, monoalkoxy tetra-sodium ester type coupling agent 1 part, tributyl phosphate 1.5 parts, pigment 25 parts, Virahol 10 parts and deionized water 15 parts according to parts by weight.
Above-mentioned pigment is that iron oxide black, lithopone, phthalein are blue or green blue, aniline yellow and pink in one or more.
The invention also discloses a kind of preparation method of aquosity intaglio printing ink, comprise the following steps:
(1) Virahol and deionized water are put into agitator to stir, temperature is controlled in 48 ~ 58 DEG C, slowly adds during stirring: Hydroxylated acrylic resin solution and Hydroxylated acrylic resin emulsion, stirs 30min, then adds pigment and continues to stir 30min;
(2) add monoalkoxy tetra-sodium ester type coupling agent, tributyl phosphate successively in the pigment slurry of gained in step (1), be uniformly mixed, stirring velocity is now 25m/s, and temperature is controlled in 20 ~ 30 DEG C.
embodiment 3:
A kind of aquosity intaglio printing ink of the present invention, following component is comprised: Hydroxylated acrylic resin solution 72 parts, Hydroxylated acrylic resin emulsion 5.5 parts, monoalkoxy tetra-sodium ester type coupling agent 0.59 part, tributyl phosphate 0.65 part, pigment 21 parts, Virahol 5.8 parts and deionized water 11 parts according to parts by weight.
Above-mentioned pigment is that iron oxide black, lithopone, phthalein are blue or green blue, aniline yellow and pink in one or more.
The invention also discloses a kind of preparation method of aquosity intaglio printing ink, comprise the following steps:
(1) Virahol and deionized water are put into agitator to stir, temperature is controlled in 48 ~ 58 DEG C, slowly adds during stirring: Hydroxylated acrylic resin solution and Hydroxylated acrylic resin emulsion, stirs 30min, then adds pigment and continues to stir 30min;
(2) add monoalkoxy tetra-sodium ester type coupling agent, tributyl phosphate successively in the pigment slurry of gained in step (1), be uniformly mixed, stirring velocity is now 25m/s, and temperature is controlled in 20 ~ 30 DEG C.
embodiment 4:
A kind of aquosity intaglio printing ink of the present invention, following component is comprised: Hydroxylated acrylic resin solution 79 parts, Hydroxylated acrylic resin emulsion 8 parts, monoalkoxy tetra-sodium ester type coupling agent 0.95 part, tributyl phosphate 1.3 parts, pigment 24.5 parts, Virahol 9.2 parts and deionized water 14 parts according to parts by weight.
Above-mentioned pigment is that iron oxide black, lithopone, phthalein are blue or green blue, aniline yellow and pink in one or more.
The invention also discloses a kind of preparation method of aquosity intaglio printing ink, comprise the following steps:
(1) Virahol and deionized water are put into agitator to stir, temperature is controlled in 48 ~ 58 DEG C, slowly adds during stirring: Hydroxylated acrylic resin solution and Hydroxylated acrylic resin emulsion, stirs 30min, then adds pigment and continues to stir 30min;
(2) add monoalkoxy tetra-sodium ester type coupling agent, tributyl phosphate successively in the pigment slurry of gained in step (1), be uniformly mixed, stirring velocity is now 25m/s, and temperature is controlled in 20 ~ 30 DEG C.
Claims (4)
1. an aquosity intaglio printing ink, it is characterized in that: comprise following component according to parts by weight: Hydroxylated acrylic resin solution 70 ~ 80 parts, Hydroxylated acrylic resin emulsion 5 ~ 10 parts, monoalkoxy tetra-sodium ester type coupling agent 0.5 ~ 1 part, tributyl phosphate 0.5 ~ 1.5 part, pigment 20 ~ 25 parts, Virahol 5 ~ 10 parts and deionized water 10 ~ 15 parts.
2. aquosity intaglio printing ink according to claim 1, it is characterized in that: described Hydroxylated acrylic resin solution 72 ~ 79 parts, Hydroxylated acrylic resin emulsion 5.5 ~ 8 parts, monoalkoxy tetra-sodium ester type coupling agent 0.59 ~ 0.95 part, tributyl phosphate 0.65 ~ 1.3 part, pigment 21 ~ 24.5 parts, Virahol 5.8 ~ 9.2 parts and deionized water 11 ~ 14 parts.
3. aquosity intaglio printing ink according to claim 1, is characterized in that: described pigment is that iron oxide black, lithopone, phthalein are blue or green blue, aniline yellow and pink in one or more.
4. a preparation method for the aquosity intaglio printing ink according to claims 1 to 3 any one, is characterized in that: comprise the following steps:
(1) Virahol and deionized water are put into agitator to stir, temperature is controlled in 48 ~ 58 DEG C, slowly adds during stirring: Hydroxylated acrylic resin solution and Hydroxylated acrylic resin emulsion, stirs 30min, then adds pigment and continues to stir 30min;
(2) add monoalkoxy tetra-sodium ester type coupling agent, tributyl phosphate successively in the pigment slurry of gained in step (1), be uniformly mixed, stirring velocity is now 25m/s, and temperature is controlled in 20 ~ 30 DEG C.