CN104250489A - Weather-resisting light reflection road mark coating - Google Patents
Weather-resisting light reflection road mark coating Download PDFInfo
- Publication number
- CN104250489A CN104250489A CN201410480633.7A CN201410480633A CN104250489A CN 104250489 A CN104250489 A CN 104250489A CN 201410480633 A CN201410480633 A CN 201410480633A CN 104250489 A CN104250489 A CN 104250489A
- Authority
- CN
- China
- Prior art keywords
- parts
- weather
- light reflection
- road mark
- mark coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a weather-resisting light reflection road mark coating, and belongs to the technical field of coatings. The coating comprises the following components in parts by weight: 100-120 parts of acrylic emulsion, 50-70 parts of fluorocarbon emulsion, 10-25 parts of hollow glass beads, 1-3 parts of zinc stearate, 2-5 parts of a dispersing agent, 1-2 parts of a defoaming agent, 5-8 parts of nanometer titania, 0.1-0.2 part of hydroxyethyl cellulose, 0.1-0.3 part of dibutyltin dilaurate and 0-6 parts of pigment. The weather-resisting light reflection road mark coating provided by the invention is high in adhesion property, rapid to dry, relatively high in weather resistance, high in wearing resistance and compression resistance, convenient to construct and friendly to the environment. In addition, the weather-resisting light reflection road mark coating is relatively wide in use application and is applicable to various places needing light reflection coatings.
Description
Technical field
The invention belongs to technical field of coatings, be specifically related to a kind of weather-proof reflector marker coating.
Background technology
In the last few years, along with the development of China's economy, drive the fast development of the construction of the highway of China.The pavement marker lines such as highway mid-line, line of delimitation and securing band are the important symbols relieving traffic congestion, command vehicle operating, pedestrains safety and judge break in traffic rules and regulations accident.Nowadays the requirement of people's road pavement marking material is more and more higher, requires that coating has the performances such as good sticking power, wear resistance and reflective, and therefore reflective coating becomes the study hotspot of increasing research and development scholar.
At present, the reflective coating weathering resistance on domestic market is poor, and resistance to pressure is inadequate, and be difficult to the requirement meeting life-time service, therefore how overcoming the deficiencies in the prior art is problems that current technical field of coatings needs solution badly.
Summary of the invention
The object of the invention is to solve the deficiencies in the prior art, providing a kind of weather-proof reflector marker coating, this paint adhesion is strong, rapidly dry, easy construction.
The technical solution used in the present invention is as follows:
A kind of weather-proof reflector marker coating, comprises the following component according to weight parts: ACRYLIC EMULSION 100 ~ 120 parts, fluorine carbon emulsion 50 ~ 70 parts, hollow glass micropearl 10 ~ 25 parts, Zinic stearas 1 ~ 3 part, dispersion agent 2 ~ 5 parts, defoamer 1 ~ 2 part, nano titanium oxide 5 ~ 8 parts, Natvosol 0.1 ~ 0.2 part, dibutyl tin laurate 0.1 ~ 0.3 part, pigment 0 ~ 6 part.
Further preferably described dispersion agent is metasilicate pentahydrate sodium.
Further preferably described defoamer is silicone oil.
The preparation method of the present invention's weather-proof reflector marker coating be the ACRYLIC EMULSION of above-mentioned weight fraction, fluorine carbon emulsion, hollow glass micropearl are joined together with dispersion agent carry out in homogenizer dispersed, and then add Zinic stearas, defoamer, nano titanium oxide, Natvosol, dibutyl tin laurate and pigment wherein, continue to be stirred to and mix, control viscosity is 85 ~ 95UK.
Compared with prior art, its beneficial effect is in the present invention: (1) weather-proof reflector marker paint adhesion of the present invention is strong, rapidly dry, and weathering resistance is comparatively strong, has strong wear-resisting withstand voltage properties; (2) easy construction, and environmentally friendly; (3) product use range of the present invention is comparatively wide, is applicable to the various occasion needing reflective coating.
Specific embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
A kind of weather-proof reflector marker coating, comprises the following component according to weight parts: ACRYLIC EMULSION 100 parts, fluorine carbon emulsion 50 parts, hollow glass micropearl 10 parts, Zinic stearas 1 part, metasilicate pentahydrate sodium 2 parts, silicone oil 1 part, nano titanium oxide 5 parts, Natvosol 0.1 part, dibutyl tin laurate 0.1 part.
The preparation method of the present embodiment weather-proof reflector marker coating be the ACRYLIC EMULSION of above-mentioned weight fraction, fluorine carbon emulsion, hollow glass micropearl are joined together with metasilicate pentahydrate sodium carry out in homogenizer dispersed, and then add Zinic stearas, silicone oil, nano titanium oxide, Natvosol and dibutyl tin laurate wherein, continue to be stirred to and mix, control viscosity is 85 ~ 95UK, obtains the present embodiment product.
Embodiment 2
A kind of weather-proof reflector marker coating, comprises the following component according to weight parts: ACRYLIC EMULSION 120 parts, fluorine carbon emulsion 70 parts, hollow glass micropearl 25 parts, Zinic stearas 3 parts, metasilicate pentahydrate sodium 5 parts, silicone oil 2 parts, nano titanium oxide 8 parts, Natvosol 0.2 part, dibutyl tin laurate 0.1 ~ 0.3 part, pigment 6 parts.
The preparation method of the present embodiment weather-proof reflector marker coating be the ACRYLIC EMULSION of above-mentioned weight fraction, fluorine carbon emulsion, hollow glass micropearl are joined together with metasilicate pentahydrate sodium carry out in homogenizer dispersed, and then add Zinic stearas, silicone oil, nano titanium oxide, Natvosol, dibutyl tin laurate and pigment wherein, continue to be stirred to and mix, control viscosity is 85 ~ 95UK, obtains the present embodiment product.
Embodiment 3
A kind of weather-proof reflector marker coating, comprises the following component according to weight parts: ACRYLIC EMULSION 110 parts, fluorine carbon emulsion 60 parts, hollow glass micropearl 15 parts, Zinic stearas 2 parts, metasilicate pentahydrate sodium 4 parts, silicone oil 1.5 parts, nano titanium oxide 7 parts, Natvosol 0.18 part, dibutyl tin laurate 0.23 part, pigment 3 parts.
The preparation method of the present embodiment weather-proof reflector marker coating be the ACRYLIC EMULSION of above-mentioned weight fraction, fluorine carbon emulsion, hollow glass micropearl are joined together with metasilicate pentahydrate sodium carry out in homogenizer dispersed, and then add Zinic stearas, silicone oil, nano titanium oxide, Natvosol, dibutyl tin laurate and pigment wherein, continue to be stirred to and mix, control viscosity is 85 ~ 95UK, obtains the present embodiment product.
Product performance of the present invention detect as shown in table 1.
Table 1 embodiment of the present invention product performance detect data
Above the embodiment of the present invention is described in detail, for one of ordinary skill in the art, according to the thought of the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (3)
1. a weather-proof reflector marker coating, it is characterized in that, comprise the following component according to weight parts: ACRYLIC EMULSION 100 ~ 120 parts, fluorine carbon emulsion 50 ~ 70 parts, hollow glass micropearl 10 ~ 25 parts, Zinic stearas 1 ~ 3 part, dispersion agent 2 ~ 5 parts, defoamer 1 ~ 2 part, nano titanium oxide 5 ~ 8 parts, Natvosol 0.1 ~ 0.2 part, dibutyl tin laurate 0.1 ~ 0.3 part, pigment 0 ~ 6 part.
2. weather-proof reflector marker coating according to claim 1, is characterized in that, described dispersion agent is metasilicate pentahydrate sodium.
3. weather-proof reflector marker coating according to claim 1, is characterized in that, described defoamer is silicone oil.