CN105001687A - Environment-friendly water-based inorganic coating - Google Patents
Environment-friendly water-based inorganic coating Download PDFInfo
- Publication number
- CN105001687A CN105001687A CN201510515280.4A CN201510515280A CN105001687A CN 105001687 A CN105001687 A CN 105001687A CN 201510515280 A CN201510515280 A CN 201510515280A CN 105001687 A CN105001687 A CN 105001687A
- Authority
- CN
- China
- Prior art keywords
- parts
- inorganic paint
- environmental protection
- trichroite
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly water-based inorganic coating. The environment-friendly water-based inorganic coating comprises the following raw materials in parts by weight: 32-45 parts of cordierite, 2-5 parts of activated carbon/graphene, 18-24 parts of attapulgite and 13-25 parts of water. All of the adopted raw materials are environment-friendly; the coating adopts cordierite which is low in expansion coefficient, high in chemical stability and excellent in weatherability as a main raw material, and the cordierite is cooperated with an auxiliary material comprising activated carbon/grapheme which is light in weight and attapulgite which is high in water absorbability and excellent in dispersivity to prepare the environment-friendly water-based inorganic coating. A coat prepared by the environment-friendly water-based inorganic coating has excellent chemical resistance and weatherability, and the possibility of falling off of the coat is low under the repeated exposure, wind and rain environment.
Description
Technical field
The present invention relates to technical field of coatings, the aqueous inorganic paint of specifically a kind of environmental protection.
Background technology
Inorganic paint is the high durable exterior coating be composited by multiple inorganic materials, and has the advantages such as low smell, low VOC, take inorganic materials as the coating of main film forming substance.Coating conventional in construction work is the aqueous dispersions of alkali metal silicate aqueous solution and colloid silica.With above two kinds of film forming matters or continue to add pigment, filler and various auxiliary agent, can be made into silicate and silicon sol inorganic paint, there is good water-fast, alkaline-resisting, anti-pollution, gasproof performance.
The inorganic polymer coating that inorganic paint is made up of inorganic polymer and the metal activated through dispersion, metal oxide nano-material, rare earth ultrafine powder; can with the rapid reaction of steel structure surface iron atom; generation has physics, chemical double protection; by the inorganic polymer corrosion protection coating of chemical bond and matrix mortise; environmentally safe; long service life, antiseptic property is reached advanced world standards, and is the regeneration product meeting environmental requirement.
Due to the raising gradually of people's living standard, also more and more stricter to the requirement of coating quality.When selecting coating products, price is no longer the determinative of purchasing power, and human consumer's more attention is its environment protection health.Water-borne coatings arises at the historic moment as a kind of energy-saving and environmental protection coating, development.
Summary of the invention
The object of the present invention is to provide a kind of aqueous inorganic paint of environmental protection, the coating obtained has good chemical resistance and weathering resistance, though repeatedly be exposed to the sun and wind and weather environment under, also not easily there is coming off of coating.
For achieving the above object, the invention provides following technical scheme:
An aqueous inorganic paint for environmental protection, according to mass fraction meter, is made up of trichroite 32-45 part, gac 2-5 part, attapulgite 18-24 part and water 13-25 part.
As the further scheme of the present invention: the particle diameter of described trichroite is 10-50 μm.
As the further scheme of the present invention: adopt the gac in Graphene replacement component.
As the further scheme of the present invention: according to mass fraction meter, be made up of trichroite 42 parts, gac 3 parts, attapulgite 21 parts and 22 parts, water.
As the further scheme of the present invention: also comprise defoamer 0.5-0.8 part.
As the further scheme of the present invention: described defoamer is aqueous medium versatility mineral oil defoaming agent.
Compared with prior art, the invention has the beneficial effects as follows:
Raw material of the present invention is environmental protection raw material, its with the good trichroite of low-expansion coefficient, high chemical stability, weathering resistance for main raw material, gac/the Graphene, water-absorbent is strong and dispersing property the is excellent attapulgite that coordinate light weight are auxiliary material, the aqueous inorganic paint of obtained a kind of environmental protection, the coating obtained by the aqueous inorganic paint of this environmental protection has good chemical resistance and weathering resistance, even if being exposed to the sun with under wind and weather environment repeatedly, also not easily there is coming off of coating.
Embodiment
Below in conjunction with the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 32 parts, gac 2 parts, attapulgite 18 parts and 13 parts, water.The particle diameter of trichroite is 10-50 μm.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite and water mixing and ball milling to particle diameter are less than 20 μm, then add gac and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 2
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 42 parts, gac 3 parts, attapulgite 21 parts and 22 parts, water.The particle diameter of trichroite is 10-50 μm.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite and water mixing and ball milling to particle diameter are less than 20 μm, then add gac and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 3
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 45 parts, gac 5 parts, attapulgite 24 parts and 25 parts, water.The particle diameter of trichroite is 10-50 μm.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite and water mixing and ball milling to particle diameter are less than 20 μm, then add gac and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 4
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 32 parts, Graphene 2 parts, attapulgite 18 parts and 13 parts, water.The particle diameter of trichroite is 10-50 μm.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite and water mixing and ball milling to particle diameter are less than 20 μm, then add Graphene and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 5
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 42 parts, Graphene 3 parts, attapulgite 21 parts and 22 parts, water.The particle diameter of trichroite is 10-50 μm.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite and water mixing and ball milling to particle diameter are less than 20 μm, then add Graphene and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 6
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 45 parts, Graphene 5 parts, attapulgite 24 parts and 25 parts, water.The particle diameter of trichroite is 10-50 μm.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite and water mixing and ball milling to particle diameter are less than 20 μm, then add Graphene and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 7
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 32 parts, gac 2 parts, attapulgite 18 parts, 13 parts, water and defoamer 0.5 part.The particle diameter of trichroite is 10-50 μm.Defoamer is aqueous medium versatility mineral oil defoaming agent.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite, water and defoamer mixing and ball milling to particle diameter are less than 20 μm, then add gac and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 8
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 42 parts, gac 3 parts, attapulgite 21 parts, 22 parts, water and defoamer 0.6 part.The particle diameter of trichroite is 10-50 μm.Defoamer is aqueous medium versatility mineral oil defoaming agent.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite, water and defoamer mixing and ball milling to particle diameter are less than 20 μm, then add gac and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 9
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 45 parts, gac 5 parts, attapulgite 24 parts, 25 parts, water and defoamer 0.8 part.The particle diameter of trichroite is 10-50 μm.Defoamer is aqueous medium versatility mineral oil defoaming agent.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite, water and defoamer mixing and ball milling to particle diameter are less than 20 μm, then add gac and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 10
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 32 parts, Graphene 2 parts, attapulgite 18 parts, 13 parts, water and defoamer 0.5 part.The particle diameter of trichroite is 10-50 μm.Defoamer is aqueous medium versatility mineral oil defoaming agent.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite, water and defoamer mixing and ball milling to particle diameter are less than 20 μm, then add Graphene and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 11
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 42 parts, Graphene 3 parts, attapulgite 21 parts, 22 parts, water and defoamer 0.7 part.The particle diameter of trichroite is 10-50 μm.Defoamer is aqueous medium versatility mineral oil defoaming agent.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite, water and defoamer mixing and ball milling to particle diameter are less than 20 μm, then add Graphene and continue to stir, mix, obtain required aqueous inorganic paint.
Embodiment 12
In the embodiment of the present invention, a kind of aqueous inorganic paint of environmental protection, according to mass fraction meter, is made up of trichroite 45 parts, Graphene 5 parts, attapulgite 24 parts, 25 parts, water and defoamer 0.8 part.The particle diameter of trichroite is 10-50 μm.Defoamer is aqueous medium versatility mineral oil defoaming agent.
The preparation method of the aqueous inorganic paint of described environmental protection, comprises the following steps:
By above-mentioned mass fraction, trichroite, attapulgite, water and defoamer mixing and ball milling to particle diameter are less than 20 μm, then add Graphene and continue to stir, mix, obtain required aqueous inorganic paint.
Raw material of the present invention is environmental protection raw material, its with the good trichroite of low-expansion coefficient, high chemical stability, weathering resistance for main raw material, gac/the Graphene, water-absorbent is strong and dispersing property the is excellent attapulgite that coordinate light weight are auxiliary material, the aqueous inorganic paint of obtained a kind of environmental protection, the coating obtained by the aqueous inorganic paint of this environmental protection has good chemical resistance and weathering resistance, even if being exposed to the sun with under wind and weather environment repeatedly, also not easily there is coming off of coating.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when not deviating from spirit of the present invention or essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from which point, all should embodiment be regarded as exemplary, and be nonrestrictive, scope of the present invention is limited by claims instead of above-mentioned explanation, and all changes be therefore intended in the implication of the equivalency by dropping on claim and scope are included in the present invention.
In addition, be to be understood that, although this specification sheets is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of specification sheets is only for clarity sake, those skilled in the art should by specification sheets integrally, and the technical scheme in each embodiment also through appropriately combined, can form other embodiments that it will be appreciated by those skilled in the art that.
Claims (6)
1. an aqueous inorganic paint for environmental protection, is characterized in that, according to mass fraction meter, is made up of trichroite 32-45 part, gac 2-5 part, attapulgite 18-24 part and water 13-25 part.
2. the aqueous inorganic paint of environmental protection according to claim 1, is characterized in that, the particle diameter of described trichroite is 10-50 μm.
3. the aqueous inorganic paint of environmental protection according to claim 1, is characterized in that, adopts the gac in Graphene replacement component.
4., according to the aqueous inorganic paint of the arbitrary described environmental protection of claim 1-3, it is characterized in that, according to mass fraction meter, be made up of trichroite 42 parts, gac 3 parts, attapulgite 21 parts and 22 parts, water.
5., according to the aqueous inorganic paint of the arbitrary described environmental protection of claim 1-3, it is characterized in that, also comprise defoamer 0.5-0.8 part.
6. the aqueous inorganic paint of environmental protection according to claim 5, is characterized in that, described defoamer is aqueous medium versatility mineral oil defoaming agent.