CN1042351C - 用刚玉渣制磷铁的方法 - Google Patents

用刚玉渣制磷铁的方法 Download PDF

Info

Publication number
CN1042351C
CN1042351C CN95118506A CN95118506A CN1042351C CN 1042351 C CN1042351 C CN 1042351C CN 95118506 A CN95118506 A CN 95118506A CN 95118506 A CN95118506 A CN 95118506A CN 1042351 C CN1042351 C CN 1042351C
Authority
CN
China
Prior art keywords
phosphorus
corundum slag
slag
production cost
corundum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN95118506A
Other languages
English (en)
Other versions
CN1149631A (zh
Inventor
朱培基
李正辉
赵伟毅
陈国兴
张南荪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN95118506A priority Critical patent/CN1042351C/zh
Publication of CN1149631A publication Critical patent/CN1149631A/zh
Application granted granted Critical
Publication of CN1042351C publication Critical patent/CN1042351C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种用刚玉渣制备磷铁的方法，它是以刚玉渣、磷矿石为原料，加入熔剂，采用冶金高温炉用常规冶炼方法进行冶炼。本发明与现有技术相比，具有操作简单、易于控制，生产成本低，充分利用了工业废渣等优点，其生产成本较传统工艺降低20%～30%，具有极大的实用价值。

Description

用刚玉渣制磷铁的方法
本发明属于一种用含铁废渣生产磷铁矿的方法。
传统的磷铁生产方法是采用铁或铁矿石在电炉或高炉中溶炼而得到磷铁，这种工艺技术难度大，且生产成本高。而刚玉渣作为一种工业废渣，一般都作为废渣倒掉。
本发明的目的在于：提供一种利用工业废渣来生产磷铁产品的方法，从而大大降低产品成本，且又充分利用了工业废渣，变废为宝。
本发明是这样构成的：它是以刚玉渣、磷矿石为原料，加入硅石、粘土，并以焦碳为燃料，采用冶金高温炉用常规冶炼方法在1400℃以上进行冶炼。
本发明与现有技术相比，具有操作简单、易于控制，生产成本低，充分利用了工业废渣等优点，其生产成本较传统工艺降低20％～30％，具有极大的实用价值。
本发明的实施例1：采用小型化铁炉熔炼，主要原料成分(％)；刚玉渣Fe 72.1、Si 15.6、Al 5.8、Ti 4.2、P 0.7；硅石SiO2 98.6，当炉温升至1400℃以上时，开始加料，其顺序和批料为：焦炭10公斤，磷矿10公斤，刚玉渣5公斤，硅石4公斤，共加料10批，产出磷铁45.3公斤，磷铁成份(％)：P 22.8、Si 2.3、C 0.9、S 0.2、Mn 0.1，磷回收率：76.3％。
实施例2：采用坩埚炉处理，用刚玉渣200克，磷矿石400克、硅石120克、粘土80克，将料混匀后放入石墨坩埚内，于1450℃反应2小时，出炉冷却、渣铁分离后，得磷铁168.6克，磷铁成份(％):P 22.3、Si 0.5、C 1.0、S 0.1、Mn 0.05，磷回收率：88.06％。

Claims (1)

1、一种用刚玉渣制备磷铁的方法，其特征在于：它是以刚玉渣、磷矿石为原料，加入硅石、粘土，并以焦碳为燃料，采用冶金高温炉用常规冶炼方法在1400℃以上进行冶炼。
CN95118506A 1995-11-03 1995-11-03 用刚玉渣制磷铁的方法 Expired - Fee Related CN1042351C (zh)