CN104229711A - Down-drilling-preventive textile and production method thereof - Google Patents

Down-drilling-preventive textile and production method thereof Download PDF

Info

Publication number
CN104229711A
CN104229711A CN201310253281.7A CN201310253281A CN104229711A CN 104229711 A CN104229711 A CN 104229711A CN 201310253281 A CN201310253281 A CN 201310253281A CN 104229711 A CN104229711 A CN 104229711A
Authority
CN
China
Prior art keywords
textiles
production method
chiseling
fabric
filament
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310253281.7A
Other languages
Chinese (zh)
Other versions
CN104229711B (en
Inventor
张恩杰
康慧珠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUNZETAL (SHANGHAI) Ltd
Original Assignee
GUNZETAL (SHANGHAI) Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUNZETAL (SHANGHAI) Ltd filed Critical GUNZETAL (SHANGHAI) Ltd
Priority to CN201310253281.7A priority Critical patent/CN104229711B/en
Publication of CN104229711A publication Critical patent/CN104229711A/en
Application granted granted Critical
Publication of CN104229711B publication Critical patent/CN104229711B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses down-drilling-preventive textile and a production method thereof. The down-drilling-preventive textile comprises two or more layers of fabric. The production method includes adopting filaments as facial sutures; adopting another type of sewing threads, except for the filaments, as bottom sutures, sewing the fabric forming the textile to form a cavity, and filling a filler in the cavity. By improving the sewing facial sutures and the sewing bottom sutures, the sewing sutures are enabled to be less prone to causing down drilling in the process of sewing; the sewn position of the textile produced by the method is less prone to sliding during use, so that probability that the filler drills down through a needle hole channel is lowered effectively, and effect of down drilling prevention is realized.

Description

A kind of textiles of anti-chiseling down and production method thereof
Technical field
The present invention relates to a kind of production method of textiles, particularly relating to is that one adopts long filament as upper thread, adopts the production method of sewing thread as the textiles of the anti-chiseling down of bottom line of the another kind of type except long filament.
Background technology
Society, filling class textiles has become popular, and down products (comprising down jackets, eiderdown quilt etc.) becomes daily necessities indispensable in people's daily life especially, and it is deeply loved by the public with features such as its soft comfortable, warmth retention property are good, light.But at present, because many reasons causes such textiles producing and there will be the problem of boring suede in use procedure.By the anti-chiseling down process of fabric, weighting material (plumage, suede) can be avoided to get out from fabric.But because textiles needs the design style being reached textiles by the process of making, use current method of sewing, weighting material (plumage, suede) can easily get out from seam, cause occurring boring suede problem in production and use procedure.
In the art, in order to ensure to make with in use procedure, the powerful optimization of colluding with of seam bottom line and upper thread is arranged in pairs or groups, and current known method of sewing uses long filament as bottom line and upper thread, or short fiber sewing thread is as bottom line and upper thread.The principle of colluding with powerful optimization collocation is two one threads acted in collusion, if wherein an one thread to collude with brute force more weak, then to collude with brute force more weak for entirety; If two one threads are colluded with quite powerful, then entirety is colluded with powerful is optimization collocation.Usually select bottom line, upper thread to be homogeneous raw material, or select bottom line, upper thread not homogeneous raw material but collude with powerful quite, then what can ensure seam colludes with brute force.In addition, long filament refers to continuous print fiber, and as the continuous tow sprayed when silk and chemical fibre throwing, be usually combined make long filament line with tens or tens of one filament, line surface is smooth, and gloss is stronger.Short fiber line refers to by chopped fiber through spinning process, forms continuous print yarn after making to twist obvolvent between fiber, then threads is formed short fiber line after also closing.But, when using common long filament sewing thread as upper thread and bottom line, due to long filament sewing thread smoother, when such textiles is subject to external forces, sewing thread can be made to produce certain slippage at the place of making of fabric, the weighting substance be attached to around sewing thread is taken out of with the slip of sewing thread, causes and bore suede phenomenon, then there will be in textiles use procedure and bore suede problem.And when using short fiber sewing thread as upper thread and bottom line, in the process of making, needle is after forming coil with rotating shuttle, in the process upwards returned, weighting material is easily taken out of fabric face by the chopped fiber as upper thread, thus causes brill suede phenomenon.
Also there are at present some to solve process of making and produce the method for boring suede, such as before filling plumage, suede, first fabric is carried out cut-parts, then sews up, form the cavity structure of an openings at one side, then plumage, suede are filled with, finally sew up opening again; But in order to fixing weighting material, cavity structure also can be sewed up in centre after sewing up again, in this procedure, can there is the problem of boring suede in the process of making in weighting material.
Occur boring suede phenomenon in the process of making, current known method also has in the process of making, use common long filament sewing thread as upper thread and bottom line, but due to long filament sewing thread smoother, when such textiles is subject to external forces, sewing thread can be made to produce certain slippage at the place of making of fabric, the weighting substance be attached to around sewing thread is taken out of with the slip of sewing thread, cause and bore suede phenomenon, there will be in textiles use procedure and bore suede problem.
Fig. 1 is the schematic diagram of the patent No. 201220007497.6 down-proof fabric, shown in Figure 1.This down-proof fabric adopts warp thread 11 and weft yarn 12 to work out, and the total number of the warp thread 11 comprised in fabric per square inch and weft yarn 12 is between 250 to 500.But when reality uses, because plumage, suede are thinner, the brill suede problem of part fabric still can be there is.
Fig. 2 is the schematic diagram that the patent No. 201120400812.7 anti-chiseling down prevents pushing away the down jackets of suede, shown in Figure 2.The down jackets that this anti-chiseling down prevents pushing away suede comprise the inner bag be folded between fabric 21 and lining 22, and inner bag is made up of several chamber 23 spaced apart from each other, is filled with eider down 24 in each chamber 23; The inner side of fabric 21 and the outside of lining 22 are all compounded with air-permeable elastic film 25.But this kind of scheme, owing to need form some chambers by suture in inner bag, causes the trouble of suture operation.Meanwhile, plumage, suede outwards can bore suede between thread.
Summary of the invention
The object of the invention is to reduce and fill class textiles in the brill suede phenomenon of producing and occur in use procedure, to provide a kind of method of sewing of filling class textiles, this textiles is filled with plumage, suede or its compound, and the method effectively can reduce such textiles in the brill suede problem of producing and produce in use procedure.
Concrete technical scheme is as follows:
A production method for the textiles of anti-chiseling down, textiles comprises two-layer or two-layer above fabric; Wherein, also comprise: adopt long filament as upper thread; Adopt the sewing thread of the another kind of type except long filament as bottom line, the described fabric of composition textiles is sewed up, forms a cavity, and be filled with weighting material in described cavity.
According to another embodiment of the invention, provide a kind of production method of textiles of anti-chiseling down, comprise two-layer or two-layer above fabric; Wherein, also comprise: adopt long filament as upper thread, the described long filament as upper thread is through water-proofing treatment; Adopt the sewing thread of the another kind of type except long filament as bottom line, the described fabric of composition textiles is sewed up, forms a cavity, and be filled with weighting material in described cavity.
According to another embodiment of the invention, provide a kind of production method of textiles of anti-chiseling down, comprise two-layer or two-layer above fabric; Wherein, also comprise: adopt long filament as upper thread, the described long filament as upper thread is through fluent movement agent process; Adopt the sewing thread of the another kind of type except long filament as bottom line, the described fabric of composition textiles is sewed up, forms a cavity, and be filled with weighting material in described cavity.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described long filament is the continuous filament yarn that one or more synthetic polymers are formed.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described long filament is nylon, polyester, rayon, polyethylene, polypropylene, aramid fiber, meta-aramid or its any several compound.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described long filament is by the continuous filament yarn of continuous print PFY through single thread twisting, plying, doubling twisting.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described bottom line contains sewing thread or the textured filament of chopped fiber.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, the chopped fiber that described bottom line contains is cotton, nylon, polyester, rayon, polyethylene, polypropylene, aramid fiber, meta-aramid or its any several compound.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, the chopped fiber that described bottom line contains is made up of cotton fiber or is made up of polyester staple fiber or is made up of the compound of cotton fiber and polyester staple fiber.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described bottom line is core-spun yarn, and described core-spun yarn adopts long filament as heart yarn, and coated chopped fiber outside long filament, coated chopped fiber is made up of cotton fiber or poly-ester fibres.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described textured filament is nylon, polyester, rayon, polyethylene, polypropylene, aramid fiber, meta-aramid or its any several compound.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described textured filament is the continuous polycondensation textured filament through twisting.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described textured filament is the continuous polycondensation air textured yarn through twisting.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described textured filament has high-elastic and that height is bulk continuous polycondensation textured filament.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described fabric is two-layer or multilayer, is filled with weighting material in the middle of described fabric.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described weighting material is the compound that feather or eider down or feather and eider down mix with various ratio.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described fabric is woven fabric or knitted fabric fabric or non-woven fabric fabric.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, described long filament has less friction force and friction force difference, friction force under the speed of 5m/min is less than 200cN, and test 5m length internal friction extreme difference is less than 50cN, make the sewing process smooth to described fabric, avoid weighting material described in sewing process to get out.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, three edges after the described fabric overlap of composition textiles are sewed up by described upper thread and described bottom line, formed and there is one end open and the textiles with cavity, meanwhile, described opening is connected with described cavity.
According to the production method of the textiles of any one above-mentioned anti-chiseling down, wherein, the quantity of described cavity is multiple, and is parallel to each other between multiple described cavity.
A textiles for anti-chiseling down, wherein, is obtained by above-mentioned production method.
A kind of textile garment, wherein, adopts the textiles of the anti-chiseling down obtained by said method to make.
This method uses long filament line as upper thread, and the sewing thread containing chopped fiber or high-elastic, high bulk distortion silk thread are made as bottom line.Wherein textured filament (being also textured fibre) refers to the feature utilizing syntheticfibres be out of shape by thermoplastification, under machinery and hot effect, makes the fiber that the fiber stretched becomes curling.Textured filament is divided into two classes.One class is based on bulkiness, and apparent volume is fluffy.Take acrylic fibers as the textured filament of primary raw material, be called bulked yarn, for the production of knitting wool and knitted underwear and coat.Another kind of based on elasticity, be called elastic filament.Elastic filament divides two kinds, high-elastic and low bullet.False-twist textured yarn, based on polyamide fibre, is used for producing stretch shirt trousers, stretch socks etc.Low stretch yarn based on terylene, mainly for the production of coat and upholstery cloth.
Through the long filament sewing thread of fluent movement agent post-processing in the present invention, due to surperficial smoother, and friction coefficient between institute's sewing fabric and weighting material is smaller, therefore can reduce as far as possible and bore suede phenomenon.Because bottom line adopts containing the sewing thread of chopped fiber or the distortion silk thread of high-elastic, high bulk type, these two kinds of sewing threads, compared with common long filament line, when the function himself had can avoid filling class textiles to be subject to ambient pressure or friction, produce and bore suede phenomenon.Cardinal principle is: (1) selects ganoid long filament line as upper thread, can avoid make with use procedure in be attached to long wire surface and the brill suede phenomenon produced with the displacement of long filament line due to weighting material.(2) to use containing the sewing thread of chopped fiber as bottom line, compare with common long filament line, the filoplume that its chopped fiber is formed can interlock at pin hole place with weighting material and block pin hole to a certain extent; Meanwhile, because the sewing thread surface friction coefficient containing short fiber is large, can be formed at the intersection with long filament line to lock and tie, the free displacement of restriction long filament, reduce with this and bore suede phenomenon.(3) use the textured filament of high-elastic, high bulk type as bottom line, because this line has higher bulkiness, after sewing terminates, this bottom line reduces due to suffered tension force, this line bulkiness is recovered, and blocks pin hole after expansion, reduces with this brill suede phenomenon that textiles in use produces.
Accompanying drawing explanation
In order to be illustrated more clearly in the embodiment of the present invention or technical scheme of the prior art, be briefly described to the accompanying drawing used required in embodiment or description of the prior art below, apparently, accompanying drawing in the following describes is only some embodiments of the present invention, for those of ordinary skill in the art, under the prerequisite not paying creative work, other accompanying drawing can also be obtained according to these accompanying drawings.
Fig. 1 is the schematic diagram of the patent No. 201220007497.6 down-proof fabric;
Fig. 2 is the schematic diagram that the patent No. 201120400812.7 anti-chiseling down prevents pushing away the down jackets of suede;
Fig. 3 is the schematic diagram of suture stitching in the textiles of a kind of anti-chiseling down of the present invention and production method thereof;
Fig. 4 is the schematic diagram of upper thread and bottom line in the textiles of a kind of anti-chiseling down of the present invention and production method thereof;
Fig. 5 is the schematic diagram of fabric trellis method of sewing in the textiles of a kind of anti-chiseling down of the present invention and production method thereof;
Fig. 6 is the schematic diagram that trellis makes that sample A, sample B and sample C get out eider down number;
Fig. 7 is the schematic diagram of fabric strip method of sewing in the textiles of a kind of anti-chiseling down of the present invention and production method thereof;
Fig. 8 is the schematic diagram that strip makes that sample A, sample B and sample C get out eider down number.
Detailed description of the invention
Below in conjunction with the drawings and specific embodiments, the invention will be further described, but should be understood that these embodiments are only not used in for illustration of the present invention and limit the scope of the invention.In addition should be understood that those skilled in the art can make various changes or modifications the present invention, and these equivalent form of values fall within the application's appended claims limited range equally after the content of having read the present invention's instruction.
Fig. 3 is the schematic diagram of suture stitching in the textiles of a kind of anti-chiseling down of the present invention and production method thereof, Fig. 4 is the schematic diagram of upper thread and bottom line in the textiles of a kind of anti-chiseling down of the present invention and production method thereof, Fig. 5 is the schematic diagram of fabric trellis method of sewing in the textiles of a kind of anti-chiseling down of the present invention and production method thereof, Fig. 7 is the schematic diagram of fabric strip method of sewing in the textiles of a kind of anti-chiseling down of the present invention and production method thereof, refers to shown in Fig. 3 to Fig. 5 and Fig. 7.The textiles of a kind of anti-chiseling down of the present invention and the first embodiment of production method thereof, comprise two-layer or two-layer above fabric 3, at this fabric 3 surface coating coatings.Also comprise: adopt long filament as upper thread 4, the another kind of sewing thread of employing except long filament is as bottom line 5, and by this upper thread 4 and this bottom line 5, the fabric 3 to composition textiles is sewed up, and forms a cavity.Concrete, first that fabric 3 is overlapping, and three edges of fabric 3 after overlap are sewed up by upper thread 4 and bottom line 5, be sewed together by fabric 3, formed and have one end open and have the textiles of cavity, meanwhile, this opening is connected with this cavity.Finally in this cavity, insert weighting material.
The textiles of a kind of anti-chiseling down of the present invention and the second embodiment of production method thereof, comprise two-layer or two-layer above fabric 3, at the surface coating coatings of this fabric 3.Also comprise: adopt long filament as upper thread 4, and this long filament as upper thread 4 is through water-proofing treatment, the another kind of sewing thread of employing except long filament is as bottom line 5, and by this upper thread 4 and this bottom line 5, the fabric 3 to composition textiles is sewed up, and forms a cavity.Concrete, first that fabric 3 is overlapping, and three edges of fabric 3 after overlap are sewed up by upper thread 4 and bottom line 5, formed and have one end open and have the textiles of cavity, meanwhile, this opening is connected with this cavity.Finally in this cavity, insert weighting material.
The textiles of a kind of anti-chiseling down of the present invention and the 3rd embodiment of production method thereof, comprise two-layer or two-layer above fabric 3, at the surface coating coatings of this fabric 3.Also comprise: adopt long filament as upper thread 4, and this long filament as upper thread 4 is through fluent movement agent process, the another kind of sewing thread of employing except long filament is as bottom line 5, and by this upper thread 4 and this bottom line 5, the fabric 3 to composition textiles is sewed up, and forms a cavity.Concrete, first that fabric 3 is overlapping, and three edges of fabric 3 after overlap are sewed up by upper thread 4 and bottom line 5, formed and have one end open and have the textiles of cavity, meanwhile, this opening is connected with this cavity.Finally in this cavity, insert weighting material.
The present invention also has following embodiment on the basis of the above:
In further embodiment of the present invention, the quantity of above-mentioned cavity is multiple, and is parallel to each other between multiple cavity.
In further embodiment of the present invention, above-mentioned long filament is the continuous filament yarn that one or more synthetic polymers are formed.
In further embodiment of the present invention, long filament is nylon, polyester, rayon, polyethylene, polypropylene, aramid fiber, meta-aramid or its any several compound.
In further embodiment of the present invention, long filament is polyester.
In further embodiment of the present invention, long filament is twisted through single thread by continuous print PFY, the continuous filament yarn of plying, doubling twisting.
In further embodiment of the present invention, above-mentioned bottom line 5 contains sewing thread or the textured filament of chopped fiber.
In further embodiment of the present invention, the chopped fiber that bottom line 5 contains is cotton, nylon, polyester, rayon, polyethylene, polypropylene, aramid fiber, meta-aramid or its any several compound.
In further embodiment of the present invention, the chopped fiber that bottom line 5 contains is made up of cotton fiber or is made up of polyester staple fiber or is made up of the compound of cotton fiber and polyester staple fiber.
In further embodiment of the present invention, bottom line 5 is core-spun yarn, and this core-spun yarn uses long filament as heart yarn, and the coated chopped fiber in outside of long filament, coated chopped fiber is made up of cotton fiber or poly-ester fibres.
In further embodiment of the present invention, above-mentioned textured filament is nylon, polyester, rayon, polyethylene, polypropylene, aramid fiber, meta-aramid or its any several compound.
In further embodiment of the present invention, textured filament is polyester.
In further embodiment of the present invention, textured filament is the continuous polycondensation textured filament through twisting.
In further embodiment of the present invention, textured filament is the continuous polycondensation air textured yarn through twisting.
In further embodiment of the present invention, textured filament has high-elastic and that height is bulk continuous polycondensation textured filament.
In further embodiment of the present invention, above-mentioned fabric 3 is two-layer or multilayer, in the cavity in the middle of fabric 3, be filled with weighting material.
In further embodiment of the present invention, above-mentioned weighting material is the compound that feather or eider down or feather and eider down mix with various ratio.
In further embodiment of the present invention, fabric 3 is woven fabric or knitted fabric fabric or non-woven fabric fabric.
In further embodiment of the present invention, long filament has less friction force and friction force difference, friction force under the speed of 5m/min is less than 200cN, and test 5m length internal friction extreme difference is less than 50cN, make the sewing process smooth to fabric 3, avoid sewing process to cause weighting material to get out.
In further embodiment of the present invention, it is used for textiles in textile garment that fabric 3 forms.
In further embodiment of the present invention, obtained a kind of textiles of anti-chiseling down by the production method of the textiles of above-mentioned anti-chiseling down.
The present invention can adopt as the long filament sewing thread of upper thread the continuous filament yarn sewing thread be made up of 100% polyester, and the sewing thread as bottom line can adopt 100% polyester, the textured filament sewing thread of high-elastic, high loft.
These two kinds of sewing threads can be buied from Jin Taixian industry (Shanghai) Co., Ltd., and its commodity are called LoDown Tkt121 and Flexo Plus Tkt140.
In order to compare, use 3 kinds of at present conventional production methods to make other 3 textile samples, and compare fabric trellis respectively and make the brill suede number made from strip.
Evaluate the method for each test sample: with reference to using National Standard of the People's Republic of China GB/T12705.2-2009 " textile fabric anti-chiseling down test method part 2: turn case method ".
The test philosophy of the method is placed in the revolution case of experimental apparatus by test sample, rotated by the constant speed of turning round case, rubber sphere in revolution casing is brought to certain height, test sample in impingement box, reach the in use suffered various extruding of simulation textiles, rub, the effect such as collision, the quantity of the weighting material got out from test sample interior by counting carrys out the anti-chiseling down performance of evaluation test sample; The weighting material quantity that test sample gets out is fewer, then the anti-chiseling down effect of testing sample is better.
The setting of testing tool: revolution case rotating speed 45r/min; That tests sample fills suede amount: be 28g
Test sample is:
Fig. 6 is the schematic diagram that trellis makes that sample A, sample B and sample C get out eider down number, and Fig. 8 is the schematic diagram that strip makes that sample A, sample B and sample C get out eider down number, please continue see shown in Fig. 3 to Fig. 8.
Sample A uses two panels 42cm × 42cm woven fabric, and this web surface has carried out coating process; Jin Taixian industry (Shanghai) Co., Ltd. anti-chiseling down sewing thread specification is adopted to be that the anti-chiseling down polyester filament sewing thread of Tex24 is as upper thread, Flexo Plus is called with Jin Taixian industry (Shanghai) Co., Ltd. brand, specification is that the sewing thread of Tkt140 is as bottom line, two panels fabric three edges are sewed up, form a bag-shaped textiles, then 100% white duck down is filled in bag-shaped textiles inside, after filling, uses same upper thread and bottom line to sew up this bag-shaped textiles opening part.
Sample B uses two panels 42cm × 42cm woven fabric, and this web surface has carried out coating process; Jin Taixian industry (Shanghai) Co., Ltd. brand is used to be called MITON, specification is that the polyester filament sewing thread of Tkt120 is as upper thread, MITON is called with Jin Taixian industry (Shanghai) Co., Ltd. brand, specification is that the long filament sewing thread of Tkt120 is as bottom line, sewed up at two panels fabric three edges, form a bag-shaped textiles, then 100% white duck down is filled in bag-shaped textiles inside, after filling, same upper thread and bottom line is used to sew up this bag-shaped textiles opening part.
Sample C uses two panels 42cm × 42cm woven fabric, and this web surface has carried out coating process; Jin Taixian industry (Shanghai) Co., Ltd. brand is used to be called Zabre, specification is that the terylene short fiber sewing thread of Tkt122 is as upper thread, Zabre is called with Jin Taixian industry (Shanghai) Co., Ltd. brand, specification is that the terylene short fiber sewing thread of Tkt122 is as bottom line, sewed up in two panels fabric three face, form a bag-shaped textiles, then 100% white duck down is filled in bag-shaped textiles inside, after filling, same upper thread and bottom line is used to sew up this bag-shaped textiles opening part.
The stitching of three kinds of above-mentioned samples uses eedle to be No. 9 eedles; Pin is close is 13 pins/inch; Stitch types is crosspointer flush joint.
Can be drawn by test, when fabric trellis is made, the brill suede number of sample A is minimum, is 5; When material strip shape is made face to face, the suede number of sample A is minimum, is 3.Therefore, the effect of the anti-chiseling down of sample A is best.
In sum, use textiles and the production method thereof of a kind of anti-chiseling down of the present invention, improved by needle thread and sewing bottom line, make this sewing thread in sewing process, not easily cause the textiles place of making of boring suede and the method production in use not easily to be slided, effectively reduce weighting material bores suede possibility by pin hole passage, thus reach the effect of anti-chiseling down.
The foregoing is only preferred embodiment of the present invention, not thereby limit claim of the present invention, so all utilizations specification sheets of the present invention and the change of the equivalent structure done by diagramatic content, be all included in protection scope of the present invention.

Claims (22)

1. a production method for the textiles of anti-chiseling down, described textiles comprises two-layer or two-layer above fabric; It is characterized in that, also comprise:
Adopt long filament as upper thread; Adopt the sewing thread of the another kind of type except long filament as bottom line, the described fabric of composition textiles is sewed up, forms a cavity, and be filled with weighting material in described cavity.
2. the production method of the textiles of anti-chiseling down according to claim 1, is characterized in that, the described long filament as upper thread is through water-proofing treatment.
3. the production method of the textiles of anti-chiseling down according to claim 1, is characterized in that, the described long filament as upper thread is through fluent movement agent process.
4. the production method of the textiles of anti-chiseling down as claimed in any of claims 1 to 3, is characterized in that, described long filament is the continuous filament yarn that one or more synthetic polymers are formed.
5. the production method of the textiles of anti-chiseling down as claimed in any of claims 1 to 3, is characterized in that, described long filament is nylon, polyester, rayon, polyethylene, polypropylene, aramid fiber, meta-aramid or its any several compound.
6. the production method of the textiles of anti-chiseling down as claimed in any of claims 1 to 3, is characterized in that, described long filament is twisted through single thread by continuous print PFY, the continuous filament yarn of plying, doubling twisting.
7. the production method of the textiles of anti-chiseling down as claimed in any of claims 1 to 3, is characterized in that, described bottom line contains sewing thread or the textured filament of chopped fiber.
8. the production method of the textiles of anti-chiseling down as claimed in any of claims 1 to 3, it is characterized in that, the chopped fiber that described bottom line contains is cotton, nylon, polyester, rayon, polyethylene, polypropylene, aramid fiber, meta-aramid or its any several compound.
9. the production method of the textiles of anti-chiseling down as claimed in any of claims 1 to 3, it is characterized in that, the chopped fiber that described bottom line contains is made up of cotton fiber or is made up of polyester staple fiber or is made up of the compound of cotton fiber and polyester staple fiber.
10. the production method of the textiles of anti-chiseling down as claimed in any of claims 1 to 3, it is characterized in that, described bottom line is core-spun yarn, and described core-spun yarn adopts long filament as heart yarn, coated chopped fiber outside long filament, coated chopped fiber is made up of cotton fiber or poly-ester fibres.
The production method of the textiles of 11. anti-chiseling downs according to claim 7, is characterized in that, described textured filament is nylon, polyester, rayon, polyethylene, polypropylene, aramid fiber, meta-aramid or its any several compound.
The production method of the textiles of 12. anti-chiseling downs according to claim 7, is characterized in that, described textured filament is the continuous polycondensation textured filament through twisting.
The production method of the textiles of 13. anti-chiseling downs according to claim 7, is characterized in that, described textured filament is the continuous polycondensation air textured yarn through twisting.
The production method of the textiles of 14. anti-chiseling downs according to claim 7, is characterized in that, described textured filament has high-elastic and that height is bulk continuous polycondensation textured filament.
The production method of the textiles of 15. anti-chiseling downs as claimed in any of claims 1 to 3, is characterized in that, described fabric is two-layer or multilayer, is filled with weighting material in the middle of described fabric.
The production method of the textiles of 16. anti-chiseling downs as claimed in any of claims 1 to 3, is characterized in that, described weighting material is the compound that feather or eider down or feather and eider down mix with various ratio.
The production method of the textiles of 17. anti-chiseling downs as claimed in any of claims 1 to 3, is characterized in that, described fabric is woven fabric or knitted fabric fabric or non-woven fabric fabric.
The production method of the textiles of 18. anti-chiseling downs according to claim 3, it is characterized in that, described long filament has less friction force and friction force difference, friction force under the speed of 5m/min is less than 200cN, and test 5m length internal friction extreme difference is less than 50cN, make the sewing process smooth to described fabric, avoid weighting material described in sewing process to get out.
The production method of the textiles of 19. anti-chiseling downs as claimed in any of claims 1 to 3, it is characterized in that, three edges after the described fabric overlap of composition textiles are sewed up by described upper thread and described bottom line, formed and there is one end open and the textiles with cavity, meanwhile, described opening is connected with described cavity.
The production method of the textiles of 20. anti-chiseling downs according to claim 19, is characterized in that, the quantity of described cavity is multiple, and is parallel to each other between multiple described cavity.
The textiles of 21. 1 kinds of anti-chiseling downs, is characterized in that, is obtained by the production method described in claim 1-20.
The textiles of 22. anti-chiseling downs according to claim 21, is characterized in that, a kind of textile garment, the textiles that described textile garment adopts described fabric to form.
CN201310253281.7A 2013-06-21 2013-06-21 The textile of a kind of anti-chiseling down and production method thereof Expired - Fee Related CN104229711B (en)