CN104212214A - 一种耐低温聚氯乙烯粉末涂料及其制备方法 - Google Patents
一种耐低温聚氯乙烯粉末涂料及其制备方法 Download PDFInfo
- Publication number
- CN104212214A CN104212214A CN201410456377.8A CN201410456377A CN104212214A CN 104212214 A CN104212214 A CN 104212214A CN 201410456377 A CN201410456377 A CN 201410456377A CN 104212214 A CN104212214 A CN 104212214A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyvinyl chloride
- low
- temperature
- chloride powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐低温聚氯乙烯粉末涂料及其制备方法，耐低温聚氯乙烯粉末涂料包括按照质量份数计的如下原料：聚氯乙烯树脂89-95份、环氧树脂5-10份、钡锌复合稳定剂1-3份、顺丁烯二酸酐5-7份、滑石粉4-6份、季戊四醇四-（2,2-二乙基丙烯酸）1-3份。本发明涂料具有良好的耐低温性，在低温寒冷环境中仍可保持良好的综合性能。
Description
技术领域
本发明属于涂料领域，具体涉及一种耐低温聚氯乙烯粉末涂料及其制备方法。
背景技术
涂料在中国传统的叫法为油漆，涂料可以涂覆在被涂物件上以起到保护和装饰的效果。涂料不论品种或形态如何，都是由成膜物质、次要成膜物质和辅助成膜物质三种基本物质组成，涂料的性能主要由成膜物质决定。而现有的聚氯乙烯粉末涂料的耐低温性较差，在低温环境下性能不佳。
综上所述，如何克服现有技术的不足已成为现有领域亟待解决的问题。
发明内容
本发明的目的是克服现有技术的不足而提出一种耐低温聚氯乙烯粉末涂料及其制备方法，本发明涂料具有良好的耐低温性，在低温环境中仍可保持良好的综合性能。
本发明的技术方案如下：
一种耐低温聚氯乙烯粉末涂料，包括按照质量份数计的如下原料：聚氯乙烯树脂89-95份、环氧树脂5-10份、钡锌复合稳定剂1-3份、顺丁烯二酸酐5-7份、滑石粉4-6份、季戊四醇四-（2,2-二乙基丙烯酸）1-3份。
作为优选，所述的耐低温聚氯乙烯粉末涂料，包括按照质量份数计的如下原料：聚氯乙烯树脂91份、环氧树脂7份、钡锌复合稳定剂2份、顺丁烯二酸酐6份、滑石粉5份、季戊四醇四-（2,2-二乙基丙烯酸）2份。
一种耐低温聚氯乙烯粉末涂料的制备方法，包括以下步骤：按照质量配比称取各原料，于90-110℃下置于高速混合机中混合搅拌均匀，自然冷却后过60目筛即得。
有益效果：本发明涂料具有良好的耐低温性，在低温寒冷环境中仍可保持良好的综合性能。
具体实施方式
下面结合具体实施方式对本发明作进一步详细说明。
实施例1
一种耐低温聚氯乙烯粉末涂料，包括按照质量份数计的如下原料：聚氯乙烯树脂89份、环氧树脂5份、钡锌复合稳定剂1份、顺丁烯二酸酐5份、滑石粉4份、季戊四醇四-（2,2-二乙基丙烯酸）1份。
本实施例的制备方法，包括以下步骤：按照质量配比称取各原料，于90℃下置于高速混合机中混合搅拌均匀，自然冷却后过60目筛即得。
实施例2
一种耐低温聚氯乙烯粉末涂料，包括按照质量份数计的如下原料：聚氯乙烯树脂95份、环氧树脂10份、钡锌复合稳定剂3份、顺丁烯二酸酐7份、滑石粉6份、季戊四醇四-（2,2-二乙基丙烯酸）3份。
本实施例的制备方法，包括以下步骤：按照质量配比称取各原料，于110℃下置于高速混合机中混合搅拌均匀，自然冷却后过60目筛即得。
实施例3
一种耐低温聚氯乙烯粉末涂料，包括按照质量份数计的如下原料：聚氯乙烯树脂91份、环氧树脂7份、钡锌复合稳定剂2份、顺丁烯二酸酐6份、滑石粉5份、季戊四醇四-（2,2-二乙基丙烯酸）2份。
本实施例的制备方法，包括以下步骤：按照质量配比称取各原料，于100℃下置于高速混合机中混合搅拌均匀，自然冷却后过60目筛即得。
将实施例1-3所得成品于进行下表各项性能测试，结果见表1：
| 性能 | 实施例1 | 实施例2 | 实施例3 |
| 附着力（划圈法），级 | 2 | 1 | 1 |
| 铅笔硬度，H | 2 | 2 | 2 |
| 耐低温，℃ | -30 | -30 | -25 |
将实施例3的涂料形成的涂层进行耐腐蚀性能测试（25℃，5d，质量浓度为20%的稀硫酸），涂层未出现裂纹、剥落和起泡现象。
上述实施例仅是对本发明产品的说明，并非对本发明做出任何形式上的限制，在不脱离本发明的技术方案范围之内，任何利用上述揭示的技术内容作出简单变换的等同方案，均属本发明的保护范围。
Claims (3)
1.一种耐低温聚氯乙烯粉末涂料，其特征在于，包括按照质量份数计的如下原料：聚氯乙烯树脂89-95份、环氧树脂5-10份、钡锌复合稳定剂1-3份、顺丁烯二酸酐5-7份、滑石粉4-6份、季戊四醇四-（2,2-二乙基丙烯酸）1-3份。
2.根据权利要求1所述的耐低温聚氯乙烯粉末涂料，其特征在于，包括按照质量份数计的如下原料：聚氯乙烯树脂91份、环氧树脂7份、钡锌复合稳定剂2份、顺丁烯二酸酐6份、滑石粉5份、季戊四醇四-（2,2-二乙基丙烯酸）2份。
3.一种耐低温聚氯乙烯粉末涂料的制备方法，其特征在于，包括以下步骤：按照质量配比称取各原料，于90-110℃下置于高速混合机中混合搅拌均匀，自然冷却后过60目筛即得。