CN104211378B - The inner tube of water bowl of a kind of ceramic, its preparation method and preparation and water dispenser - Google Patents
The inner tube of water bowl of a kind of ceramic, its preparation method and preparation and water dispenser Download PDFInfo
- Publication number
- CN104211378B CN104211378B CN201410475666.2A CN201410475666A CN104211378B CN 104211378 B CN104211378 B CN 104211378B CN 201410475666 A CN201410475666 A CN 201410475666A CN 104211378 B CN104211378 B CN 104211378B
- Authority
- CN
- China
- Prior art keywords
- water
- stone
- ceramic
- heating chamber
- inner tube
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of ceramic, the inner tube of water bowl of its preparation method and preparation and water dispenser, the material of ceramic is made up of the raw material of following ratio of weight and number: feldspar 10-25 part, boccaro stone 10-20 part, excellent native 10-15 part, quartzy 15-30 part, clay 10-25 part, stone needle 10-20 part, medical stone 15-30 part and Nishan stone 10-30 part.The invention has the beneficial effects as follows: the present invention with the multiple ore factory such as boccaro and medical stone flour for raw material, boccaro stone, medical stone, stone needle and Nishan stone are containing the trace element useful to human body, the peculiar smell in tap water, poor-quality water can be adsorbed, tap water can also be made, poor-quality water activates Viability mineralized water, water oxygen level is enriched, generate pH value 7.3--8.0 alkalescent water, the acid base equilibrium of human body can be reconciled, free radical rubbish unnecessary in anti-oxidant removing human body, long-term drinking can make people absorb more mineral substance, adjustment metabolism.
Description
Technical field
The present invention relates to ceramic technology field, the inner tube of water bowl of particularly a kind of ceramic, its preparation method and preparation and water dispenser.
Background technology
Along with growth in the living standard, and the pollution of environment is serious gradually, and the requirement of people to water quality is more and more higher.The pure water nutritive substance that present people quote is more single.Also there is mineral substance water dispenser or alkaline water water dispenser in the market.But existing water dispenser is all adopt filter core, if need to have several mineral materials in water or want that quoting alkaline water needs to allow water through multiple tracks filter core, and need often more renew cartridge, cleaning and use inconvenience.
Summary of the invention
In order to meet demand easy to use, embodiments provide a kind of ceramic can make water through, make simultaneously through water become alkaline water, be rich in the multiple mineral substance useful to human body.
In order to realize foregoing invention object, the invention provides a kind of ceramic, the material of described ceramic is made up of the raw material of following ratio of weight and number: feldspar 10-25 part, boccaro stone 10-20 part, excellent native 10-15 part, quartzy 15-30 part, clay 10-25 part, stone needle 10-20 part, medical stone 15-30 part and Nishan stone 10-30 part.
The material of described ceramic is made up of the raw material of following ratio of weight and number: feldspar 15-20 part, boccaro stone 10-15 part, excellent native 10-15 part, quartzy 15-25 part, clay 15-20 part, stone needle 10-15 part, medical stone 15-25 part and Nishan stone 15-25 part.
A preparation method for ceramic, comprises the following steps:
(1) get each raw material in described ratio, add ball milling slurrying in ball mill and within 18-22 hour, reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected the gypsum mold manufactured, place shaping rear continuation in 1-2 hour at 35 degree and place 3-5 days;
(3) by dried base substrate removing mould, moisturizing 3-5 time, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, be warming up to 1200-1300 degree in 3 hours, fire 8-10 hour altogether, after having fired, naturally cool to room temperature, obtain finished product.
The inner tube of water bowl that pottery is made, comprises a round shape inner lining, and the below of described inner lining is provided with three feets.
Comprise a water dispenser for inner tube of water bowl, comprise from top to bottom the ceramic cap 1 of snapping successively, water purifying chamber 2 and heating chamber 3, it is characterized in that, in described water purifying chamber 2 hollow structure, be provided with inner tube of water bowl 4.
Be provided with the base 5 with filter screen bottom described water purifying chamber 2, described base 5 is for supporting described inner tube of water bowl 4.
The bottom of described heating chamber 3 is provided with well heater 31, the outside of described heating chamber 3, has been arranged side by side cold water faucet 32 and hot water effluent's mouth 33 respectively.
Described heating chamber 3 side is provided with power switch 34, is provided with the plug be connected with described well heater 31 wire bottom described heating chamber 3.
Described water purifying chamber 2 and heating chamber 3 are all be made up of ceramic material.
The outline of described ceramic cap 1, described water purifying chamber 2 and described heating chamber 3 forms a calabash shaped.
The beneficial effect that the technical scheme that the embodiment of the present invention provides is brought is:
(1) the present invention is with the multiple ore factory such as boccaro and medical stone flour for raw material, and material environmental protection, waste product utilizes.Boccaro stone, medical stone, stone needle and Nishan stone are containing the trace element useful to human body, the peculiar smell in tap water, poor-quality water can be adsorbed, tap water can also be made, poor-quality water activates Viability mineralized water, water oxygen level is enriched, generate pH value 7.3-8.0 alkalescent water, the acid base equilibrium of human body can be reconciled, free radical rubbish unnecessary in anti-oxidant removing human body, long-term drinking can make people absorb more mineral substance, adjustment metabolism.
(2) natural permeate under External Force Acting can there is no.
And the prepared using local resources of preparation (3), raw material sources are easy, and save freight charges, cost is low,
Productivity effect is high, makes purple sand ceramics product, have local characteristic with " Nishan, Qufu stone, stone needle ".
Accompanying drawing explanation
The structural representation of Fig. 1 embodiment of the present invention 5.
Wherein, 1, ceramic cap; 2, water purifying chamber; 3, heating chamber; 31, well heater; 32, cold water faucet, 33, hot water effluent's mouth; 34, power switch; 4, inner tube of water bowl; 5, base; 6, plug.
Embodiment
For the problem of prior art, the invention provides a kind of ceramic can make water through, make simultaneously through water become alkaline water, be rich in the multiple mineral substance useful to human body.
In order to realize foregoing invention object, the invention provides a kind of ceramic, the material of ceramic is made up of the raw material of following ratio of weight and number: feldspar 10-25 part, boccaro stone 10-20 part, excellent native 10-15 part, quartzy 15-30 part, clay 10-25 part, stone needle 10-20 part, medical stone 15-30 part and Nishan stone 10-30 part.
The material of ceramic is made up of the raw material of following ratio of weight and number: feldspar 15-20 part, boccaro stone 10-15 part, excellent native 10-15 part, quartzy 15-25 part, clay 15-20 part, stone needle 10-15 part, medical stone 15-25 part and Nishan stone 15-25 part.
A preparation method for ceramic, comprises the following steps:
(1) get each raw material in described ratio, add ball milling slurrying in ball mill and within 18-22 hour, reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected the gypsum mold manufactured, place shaping rear continuation in 1-2 hour at 35 degree and place 3-5 days;
(3) by dried base substrate removing mould, moisturizing 3-5 time, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, be warming up to 1200-1300 degree in 3 hours, fire 8-10 hour altogether, after having fired, naturally cool to room temperature, obtain finished product.
Fill water with finished product and leave standstill 1-2 hour, collect and ooze out the water yield, can weakly alkaline or neutral water be changed into alkalescent water.
Present invention also offers the inner tube of water bowl that a kind of pottery is made, comprise a round shape inner lining, the below of inner lining is provided with three feets.
The present invention, by providing a kind of water dispenser comprising inner tube of water bowl, comprises from top to bottom the ceramic cap 1 of snapping successively, water purifying chamber 2 and heating chamber 3, in water purifying chamber 2 hollow structure, be provided with inner tube of water bowl 4.
Be provided with the base 5 with filter screen bottom water purifying chamber 2, base 5 is for supporting described inner tube of water bowl 4.
The bottom of heating chamber 3 is provided with well heater 31, the outside of heating chamber 3, has been arranged side by side cold water faucet 32 and hot water effluent's mouth 33 respectively.
Heating chamber 3 side is provided with power switch 34, is provided with the plug 6 be connected with well heater 31 wire bottom heating chamber 3.
Water purifying chamber 2 and heating chamber 3 are all be made up of ceramic material.
The outline of ceramic cap 1, water purifying chamber 2 and heating chamber 3 forms a calabash shaped.
Embodiment 1 utilizes electrothermal dark-red pottery of the present invention to prepare inner tube of water bowl
Get feldspar 10 parts, 20 parts, boccaro stone, 15 parts, rod soil, 30 parts, quartz, clay 20 parts, stone needle 15 parts, medical stone 15 parts and 10 parts, Nishan stone.
Its preparation method is as follows:
(1) get each raw material in described ratio, add ball milling slurrying in ball mill and within 22 hours, reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected the inner tube of water bowl gypsum mold manufactured, place shaping rear continuation placement in 2 hours drying at normal temperatures in 5 days
(3) by dried base substrate removing mould, moisturizing 5 times, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1260 degree, fire 10 hours altogether, after having fired, naturally cool to room temperature, obtain finished product.
Get the water that PH is 7.0, detection water quality wherein content of mineral substances is: sodium 35 μ g/100ml, potassium 18 μ g/100ml, magnesium 26 μ g/100ml, zinc 5 μ g/100ml, calcium 108 μ g/100ml; Fill water with finished product and leave standstill 1-2 hour, collect and ooze out the water yield, and detect and ooze out water quality result and be: sodium 75 μ g/100ml, potassium 38 μ g/100ml, magnesium 46 μ g/100ml, zinc 20 μ g/100ml, calcium 400 μ g/100ml, the pH value of water is the alkalescent water of 8.0.
Embodiment 2 utilizes electrothermal dark-red pottery of the present invention to prepare teacup inner bag
Get feldspar 25 parts, 10 parts, boccaro stone, 10 parts, rod soil, 15 parts, quartz, clay 15 parts, stone needle 10 parts, medical stone 30 parts and 30 parts, Nishan stone.
Its preparation method is as follows:
(1) get each raw material in described ratio, add ball milling slurrying in ball mill and within 20 hours, reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected the teacup inner bag gypsum mold manufactured, place shaping rear continuation placement in 2 hours drying at normal temperatures in 4 days;
(3) by dried base substrate removing mould, moisturizing 4 times, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1230 degree, fire 9 hours altogether, after having fired, naturally cool to room temperature, obtain finished product.
Get the water that PH is 6.5, detecting water quality content of mineral substances is: sodium 46 μ g/100ml, potassium 16 μ g/100ml, magnesium 29 μ g/100ml, zinc 0 μ g/100ml, calcium 188 μ g/100ml; Fill water with finished product and leave standstill 48 hours, collect and ooze out the water yield, and detect and ooze out water quality result and be: sodium 70 μ g/100ml, potassium 48 μ g/100ml, magnesium 56 μ g/100ml, zinc 22 μ g/100ml, calcium 396 μ g/100ml, the pH value of water is the alkalescent water of 7.6.
Embodiment 3 utilizes electrothermal dark-red pottery of the present invention to prepare inner tube of water bowl
Get feldspar 15 parts, 15 parts, boccaro stone, 10 parts, rod soil, 25 parts, quartz, clay 10 parts, stone needle 20 parts, medical stone 25 parts and 25 parts, Nishan stone.
Its preparation method is as follows:
(1) get each raw material in described ratio, add ball milling slurrying in ball mill and within 18 hours, reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected the inner tube of water bowl gypsum mold manufactured, place shaping rear continuation placement in 2 hours drying at normal temperatures in 3 days;
(3) by dried base substrate removing mould, moisturizing 4 times, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1280 degree, fire 9 hours altogether, after having fired, naturally cool to room temperature, obtain finished product.
Get the water that PH is 6.0, detecting water quality content of mineral substances is: sodium 16 μ g/100ml, potassium 26 μ g/100ml, magnesium 33 μ g/100ml, zinc 8 μ g/100ml, calcium 230 μ g/100ml; Fill water with finished product and leave standstill 1-2 hour, the water yield is oozed out in collection, and detect and ooze out water quality result and be: sodium 80 μ g/100ml, K43 μ g/100ml, magnesium 66 μ g/100ml, zinc 29 μ g/100ml, calcium 486 μ g/100ml, the pH value of water is the alkalescent water of 7.80.
Embodiment 4 utilizes electrothermal dark-red pottery of the present invention to prepare inner tube of water bowl
Get feldspar 20 parts, 10 parts, boccaro stone, 15 parts, rod soil, 15 parts, quartz, clay 25 parts, stone needle 15 parts, medical stone 20 parts and 15 parts, Nishan stone.
(1) get each raw material according to the above ratio, add ball milling slurrying in ball mill and within 18 hours, reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected the inner tube of water bowl gypsum mold manufactured, place shaping rear continuation placement in 1 hour drying at normal temperatures in 3 days;
(3) by dried base substrate removing mould, moisturizing 3 times, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1250 degree, fire 8 hours altogether, after having fired, naturally cool to room temperature, obtain finished product.
Get the water that PH is 6.7, detecting water quality content of mineral substances is: sodium 52 μ g/100ml, potassium 19 μ g/100ml, magnesium 17 μ g/100ml, zinc 3 μ g/100ml, calcium 117 μ g/100ml; Fill water with finished product and leave standstill 48 hours, collect and ooze out the water yield, and detect and ooze out water quality result and be: sodium 87 μ g/100ml, potassium 46 μ g/100ml, magnesium 61 μ g/100ml, zinc 21 μ g/100ml, calcium 406 μ g/100ml, the pH value of water is the alkalescent water of 7.9.
Embodiment 5 one kinds comprises the water dispenser of the inner tube of water bowl of the embodiment of the present invention 1
See Fig. 1, a kind of water dispenser comprising inner tube of water bowl, comprises from top to bottom the ceramic cap 1 of snapping successively, water purifying chamber 2 and heating chamber 3, is provided with the inner tube of water bowl 4 prepared by embodiment 1 in water purifying chamber 2 hollow structure.
Inner tube of water bowl 4, comprises a round shape inner lining, and the below of inner lining is provided with three feets.
Be provided with the base 5 with filter screen bottom water purifying chamber 2, base 5 is for supporting described inner tube of water bowl 4.
The bottom of heating chamber 3 is provided with well heater 31, the outside of heating chamber 3, has been arranged side by side cold water faucet 32 and hot water effluent's mouth 33 respectively.
Heating chamber 3 side is provided with power switch 34, is provided with the plug 6 be connected with well heater 31 wire bottom heating chamber 3.
Water purifying chamber 2 and heating chamber 3 are all be made up of ceramic material.
The outline of ceramic cap 1, water purifying chamber 2 and heating chamber 3 forms a calabash shaped.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (9)
1. a ceramic, it is characterized in that, the material of described ceramic is made up of the raw material of following ratio of weight and number: feldspar 10-25 part, boccaro stone 10-20 part, excellent native 10-15 part, quartzy 15-30 part, clay 10-25 part, stone needle 10-20 part, medical stone 15-30 part and Nishan stone 10-30 part.
2. ceramic according to claim 1, it is characterized in that, the material of described ceramic is made up of the raw material of following ratio of weight and number: feldspar 15-20 part, boccaro stone 10-15 part, excellent native 10-15 part, quartzy 15-25 part, clay 15-20 part, stone needle 10-15 part, medical stone 15-25 part and Nishan stone 15-25 part.
3. the inner tube of water bowl utilizing the ceramic described in claim 1 or 2 to make, is characterized in that, comprises a round shape inner lining, and the below of described inner lining is provided with three feets.
4. one kind comprises the water dispenser of inner tube of water bowl according to claim 3, comprise the ceramic cap (1) of snapping successively from top to bottom, water purifying chamber (2) and heating chamber (3), it is characterized in that, in described water purifying chamber (2) hollow structure, be provided with described inner tube of water bowl (4).
5. water dispenser according to claim 4, is characterized in that: described water purifying chamber (2) bottom is provided with the base (5) with filter screen, and described base (5) is for supporting described inner tube of water bowl (4).
6. the water dispenser according to claim 4 or 5, is characterized in that: the bottom of described heating chamber (3) is provided with well heater (31), the outside of described heating chamber (3), has been arranged side by side cold water faucet (32) and hot water effluent's mouth (33) respectively.
7. according to the arbitrary described water dispenser of claim 4 or 5, it is characterized in that: described heating chamber (3) side is provided with power switch (34), be provided with in described heating chamber (3) bottom the plug (6) be connected with described well heater (31) wire.
8., according to the arbitrary described water dispenser of claim 4 or 5, it is characterized in that: described water purifying chamber (2)
All be made up of ceramic material with heating chamber (3).
9. according to the arbitrary described water dispenser of claim 4 or 5, it is characterized in that: the outline of described ceramic cap (1), described water purifying chamber (2) and described heating chamber (3) forms a calabash shaped.