CN104211378A - Ceramic product, preparation method thereof, prepared inner container of drinking fountain and drinking fountain - Google Patents
Ceramic product, preparation method thereof, prepared inner container of drinking fountain and drinking fountain Download PDFInfo
- Publication number
- CN104211378A CN104211378A CN201410475666.2A CN201410475666A CN104211378A CN 104211378 A CN104211378 A CN 104211378A CN 201410475666 A CN201410475666 A CN 201410475666A CN 104211378 A CN104211378 A CN 104211378A
- Authority
- CN
- China
- Prior art keywords
- water
- stone
- ceramic
- parts
- heating chamber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a ceramic product, a preparation method thereof, a prepared inner container of a drinking fountain and the drinking fountain. The ceramic product is prepared from the following raw materials in parts by weight: 10-25 parts of feldspar, 10-20 parts of purple sand, 10-15 parts of attapulgite, 15-30 parts of quartz, 10-25 parts of clay, 10-20 parts of stone needle, 15-30 parts of Maifan stone and 10-30 parts of Nishan stone. The ceramic product disclosed by the invention has the beneficial effects that the purple sand, the Maifan stone and broken powder from a variety of ore plants are taken as raw materials, and the purple sand, the Maifan stone, the stone needle and the Nishan stone contain trace elements which are beneficial to human bodies, so that the ceramic product can adsorb peculiar small in running water and poor-quality water, activate the running water and the poor-quality water into active mineralized water, increase the oxygen content in water, generate weak alkaline water with the pH value of 7.3-8.0, regulate the acid-base balance of the human body, realize an anti-oxidation effect, remove excess free radical rubbish in the human body, enable people to absorb more minerals by long-term drinking and adjust metabolism.
Description
Technical field
The present invention relates to ceramic technology field, particularly the inner tube of water bowl of a kind of ceramic, its preparation method and preparation and water dispenser.
Background technology
Along with growth in the living standard, and the pollution of environment is serious gradually, and people are more and more higher to the requirement of water quality.The pure water nutritive substance that people quote is now more single.Also there is in the market mineral substance water dispenser or alkaline water water dispenser.But existing water dispenser is all to adopt filter core, if need to have in water several mineral materials or want to quote alkaline water, need to allow water through multiple tracks filter core, and often need more renew cartridge, clean and use inconvenient.
Summary of the invention
In order to meet demand easy to use, the embodiment of the present invention provides a kind of ceramic can make water see through, and makes the water seeing through become alkaline water simultaneously, is rich in the multiple mineral substance useful to human body.
In order to realize foregoing invention object, the invention provides a kind of ceramic, the material of described ceramic is comprised of the raw material of following ratio of weight and number: feldspar 10-25 part, boccaro stone 10-20 part, excellent native 10-15 part, quartzy 15-30 part, clay 10-25 part, stone needle 10-20 part, medical stone 15-30 part and Nishan stone 10-30 part.
The material of described ceramic is comprised of the raw material of following ratio of weight and number: feldspar 15-20 part, boccaro stone 10-15 part, excellent native 10-15 part, quartzy 15-25 part, clay 15-20 part, stone needle 10-15 part, medical stone 15-25 part and Nishan stone 15-25 part.
A preparation method for ceramic, comprises the following steps:
(1) in described ratio, get each raw material, add ball milling slurrying in ball mill within 18-22 hour, to reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected to the gypsum mold of having manufactured, after 35 degree are placed moulding in 1-2 hour, continue to place 3-5 days;
(3) dried base substrate is removed to mould, moisturizing 3-5 time, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1200-1300 degree, fire altogether 8-10 hour, after having fired, naturally cool to room temperature, obtain finished product.
The inner tube of water bowl that pottery is made, comprises a round shape inner lining, and the below of described inner lining is provided with three feets.
A water dispenser that comprises inner tube of water bowl, comprises from top to bottom ceramic cap 1, water purifying chamber 2 and the heating chamber 3 of snapping successively, it is characterized in that, in described water purifying chamber 2 hollow structures, is provided with inner tube of water bowl 4.
Described water purifying chamber 2 bottoms are provided with the base 5 with filter screen, and described base 5 is for supporting described inner tube of water bowl 4.
The bottom of described heating chamber 3 is provided with well heater 31, and the outside of described heating chamber 3 has been arranged side by side respectively cold water faucet 32 and hot water effluent's mouth 33.
Described heating chamber 3 one sides are provided with power switch 34, are provided with the plug being connected with described well heater 31 wires in described heating chamber 3 bottoms.
Described water purifying chamber 2 and heating chamber 3 are all to be made by ceramic material.
The outline of described ceramic cap 1, described water purifying chamber 2 and described heating chamber 3 forms a calabash shaped.
The beneficial effect that the technical scheme that the embodiment of the present invention provides is brought is:
(1) to take the multiple ore such as boccaro and medical stone factory flour be raw material in the present invention, material environmental protection, waste product utilization.Boccaro stone, medical stone, stone needle and Nishan stone are containing the trace element useful to human body, can adsorb the peculiar smell in tap water, poor-quality water, can also make tap water, poor-quality water activate into active mineralized water, make water oxygen level abundant, generate pH value 7.3-8.0 alkalescent water, can reconcile the acid base equilibrium of human body, unnecessary free radical rubbish in anti-oxidant removing human body, long-term drinking can make people absorb more mineral substance, adjusts metabolism.
(2) natural permeate under External Force Acting can there is no.
(3) and the prepared using of preparation local resources, raw material sources are easy, save freight charges, cost is low,
Productivity effect is high, with " Nishan, Qufu stone, stone needle ", makes purple sand ceramics product, has local characteristic.
Accompanying drawing explanation
The structural representation of Fig. 1 embodiment of the present invention 5.
Wherein, 1, ceramic cap; 2, water purifying chamber; 3, heating chamber; 31, well heater; 32, cold water faucet, 33, hot water effluent's mouth; 34, power switch; 4, inner tube of water bowl; 5, base; 6, plug.
Embodiment
For the problem of prior art, the invention provides a kind of ceramic and can make water see through, make the water seeing through become alkaline water simultaneously, be rich in the multiple mineral substance useful to human body.
In order to realize foregoing invention object, the invention provides a kind of ceramic, the material of ceramic is comprised of the raw material of following ratio of weight and number: feldspar 10-25 part, boccaro stone 10-20 part, excellent native 10-15 part, quartzy 15-30 part, clay 10-25 part, stone needle 10-20 part, medical stone 15-30 part and Nishan stone 10-30 part.
The material of ceramic is comprised of the raw material of following ratio of weight and number: feldspar 15-20 part, boccaro stone 10-15 part, excellent native 10-15 part, quartzy 15-25 part, clay 15-20 part, stone needle 10-15 part, medical stone 15-25 part and Nishan stone 15-25 part.
A preparation method for ceramic, comprises the following steps:
(1) in described ratio, get each raw material, add ball milling slurrying in ball mill within 18-22 hour, to reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected to the gypsum mold of having manufactured, after 35 degree are placed moulding in 1-2 hour, continue to place 3-5 days;
(3) dried base substrate is removed to mould, moisturizing 3-5 time, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1200-1300 degree, fire altogether 8-10 hour, after having fired, naturally cool to room temperature, obtain finished product.
With finished product, fill the standing 1-2 hour of water, collect and ooze out the water yield, can change weakly alkaline or neutral water into alkalescent water.
The inner tube of water bowl that the present invention also provides a kind of pottery to make, comprises a round shape inner lining, and the below of inner lining is provided with three feets.
The present invention, by a kind of water dispenser that comprises inner tube of water bowl is provided, comprises from top to bottom ceramic cap 1, water purifying chamber 2 and the heating chamber 3 of snapping successively, in water purifying chamber's 2 hollow structures, is provided with inner tube of water bowl 4.
Water purifying chamber 2 bottoms are provided with the base 5 with filter screen, and base 5 is for supporting described inner tube of water bowl 4.
The bottom of heating chamber 3 is provided with well heater 31, and the outside of heating chamber 3 has been arranged side by side respectively cold water faucet 32 and hot water effluent's mouth 33.
Heating chamber 3 one sides are provided with power switch 34, are provided with the plug 6 being connected with well heater 31 wires in heating chamber 3 bottoms.
Water purifying chamber 2 and heating chamber 3 are all to be made by ceramic material.
The outline of ceramic cap 1, water purifying chamber 2 and heating chamber 3 forms a calabash shaped.
Embodiment 1 utilizes electrothermal dark-red pottery of the present invention to prepare inner tube of water bowl
Get 10 parts, 10 parts of feldspars, 20 parts, boccaro stone, 15 parts, quartzy 30 parts, rod soil, 20 parts of clays, 15 parts of stone needles, 15 parts of medical stones and Nishan stone.
Its preparation method is as follows:
(1) in described ratio, get each raw material, add ball milling slurrying in ball mill within 22 hours, to reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected to the inner tube of water bowl gypsum mold of having manufactured, places moulding in 2 hours after continuation placement within 5 days, be dried at normal temperatures
(3) dried base substrate is removed to mould, moisturizing 5 times, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1260 degree, fire altogether 10 hours, after having fired, naturally cool to room temperature, obtain finished product.
Get PH and be 7.0 water, detect water quality wherein content of mineral substances be: sodium 35 μ g/100ml, potassium 18 μ g/100ml, magnesium 26 μ g/100ml, zinc 5 μ g/100ml, calcium 108 μ g/100ml; With finished product, fill the standing 1-2 hour of water, collect and to ooze out the water yield, and detect and ooze out water quality result and be: sodium 75 μ g/100ml, potassium 38 μ g/100ml, magnesium 46 μ g/100ml, zinc 20 μ g/100ml, calcium 400 μ g/100ml, the alkalescent water that the pH value of water is 8.0.
Embodiment 2 utilizes electrothermal dark-red pottery of the present invention to prepare teacup inner bag
Get 30 parts, 25 parts of feldspars, 10 parts, boccaro stone, 10 parts, quartzy 15 parts, rod soil, 15 parts of clays, 10 parts of stone needles, 30 parts of medical stones and Nishan stone.
Its preparation method is as follows:
(1) in described ratio, get each raw material, add ball milling slurrying in ball mill within 20 hours, to reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected to the teacup inner bag gypsum mold of having manufactured, places moulding in 2 hours after continuation placement within 4 days, be dried at normal temperatures;
(3) dried base substrate is removed to mould, moisturizing 4 times, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1230 degree, fire altogether 9 hours, after having fired, naturally cool to room temperature, obtain finished product.
Get PH and be 6.5 water, detect water quality content of mineral substances and be: sodium 46 μ g/100ml, potassium 16 μ g/100ml, magnesium 29 μ g/100ml, zinc 0 μ g/100ml, calcium 188 μ g/100ml; With finished product, fill water standing 48 hours, collect and to ooze out the water yield, and detect and ooze out water quality result and be: sodium 70 μ g/100ml, potassium 48 μ g/100ml, magnesium 56 μ g/100ml, zinc 22 μ g/100ml, calcium 396 μ g/100ml, the alkalescent water that the pH value of water is 7.6.
Embodiment 3 utilizes electrothermal dark-red pottery of the present invention to prepare inner tube of water bowl
Get 25 parts, 15 parts of feldspars, 15 parts, boccaro stone, 10 parts, quartzy 25 parts, rod soil, 10 parts of clays, 20 parts of stone needles, 25 parts of medical stones and Nishan stone.
Its preparation method is as follows:
(1) in described ratio, get each raw material, add ball milling slurrying in ball mill within 18 hours, to reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected to the inner tube of water bowl gypsum mold of having manufactured, places moulding in 2 hours after continuation placement within 3 days, be dried at normal temperatures;
(3) dried base substrate is removed to mould, moisturizing 4 times, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1280 degree, fire altogether 9 hours, after having fired, naturally cool to room temperature, obtain finished product.
Get PH and be 6.0 water, detect water quality content of mineral substances and be: sodium 16 μ g/100ml, potassium 26 μ g/100ml, magnesium 33 μ g/100ml, zinc 8 μ g/100ml, calcium 230 μ g/100ml; With finished product, fill the standing 1-2 hour of water, the water yield is oozed out in collection, and detect and to ooze out water quality result and be: sodium 80 μ g/100ml, K43 μ g/100ml, magnesium 66 μ g/100ml, zinc 29 μ g/100ml, calcium 486 μ g/100ml, the alkalescent water that the pH value of water is 7.80.
Embodiment 4 utilizes electrothermal dark-red pottery of the present invention to prepare inner tube of water bowl
Get 15 parts, 20 parts of feldspars, 10 parts, boccaro stone, 15 parts, quartzy 15 parts, rod soil, 25 parts of clays, 15 parts of stone needles, 20 parts of medical stones and Nishan stone.
(1) get according to the above ratio each raw material, add ball milling slurrying in ball mill within 18 hours, to reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected to the inner tube of water bowl gypsum mold of having manufactured, places moulding in 1 hour after continuation placement within 3 days, be dried at normal temperatures;
(3) dried base substrate is removed to mould, moisturizing 3 times, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1250 degree, fire altogether 8 hours, after having fired, naturally cool to room temperature, obtain finished product.
Get PH and be 6.7 water, detect water quality content of mineral substances and be: sodium 52 μ g/100ml, potassium 19 μ g/100ml, magnesium 17 μ g/100ml, zinc 3 μ g/100ml, calcium 117 μ g/100ml; With finished product, fill water standing 48 hours, collect and to ooze out the water yield, and detect and ooze out water quality result and be: sodium 87 μ g/100ml, potassium 46 μ g/100ml, magnesium 61 μ g/100ml, zinc 21 μ g/100ml, calcium 406 μ g/100ml, the alkalescent water that the pH value of water is 7.9.
The water dispenser of 5 one kinds of inner tube of water bowl that comprise the embodiment of the present invention 1 of embodiment
Referring to Fig. 1, a kind of water dispenser that comprises inner tube of water bowl, comprises from top to bottom ceramic cap 1, water purifying chamber 2 and the heating chamber 3 of snapping successively, is provided with the inner tube of water bowl 4 of being prepared by embodiment 1 in water purifying chamber's 2 hollow structures.
Inner tube of water bowl 4, comprises a round shape inner lining, and the below of inner lining is provided with three feets.
Water purifying chamber 2 bottoms are provided with the base 5 with filter screen, and base 5 is for supporting described inner tube of water bowl 4.
The bottom of heating chamber 3 is provided with well heater 31, and the outside of heating chamber 3 has been arranged side by side respectively cold water faucet 32 and hot water effluent's mouth 33.
Heating chamber 3 one sides are provided with power switch 34, are provided with the plug 6 being connected with well heater 31 wires in heating chamber 3 bottoms.
Water purifying chamber 2 and heating chamber 3 are all to be made by ceramic material.
The outline of ceramic cap 1, water purifying chamber 2 and heating chamber 3 forms a calabash shaped.
The foregoing is only preferred embodiment of the present invention, in order to limit the present invention, within the spirit and principles in the present invention not all, any modification of doing, be equal to replacement, improvement etc., within all should being included in protection scope of the present invention.
Claims (10)
1. a ceramic, it is characterized in that, the material of described ceramic is comprised of the raw material of following ratio of weight and number: feldspar 10-25 part, boccaro stone 10-20 part, excellent native 10-15 part, quartzy 15-30 part, clay 10-25 part, stone needle 10-20 part, medical stone 15-30 part and Nishan stone 10-30 part.
2. ceramic according to claim 1, it is characterized in that, the material of described ceramic is comprised of the raw material of following ratio of weight and number: feldspar 15-20 part, boccaro stone 10-15 part, excellent native 10-15 part, quartzy 15-25 part, clay 15-20 part, stone needle 10-15 part, medical stone 15-25 part and Nishan stone 15-25 part.
3. the preparation method of ceramic according to claim 1 and 2, is characterized in that, comprises the following steps:
(1) in described ratio, get each raw material, add ball milling slurrying in ball mill within 18-22 hour, to reach 120 order fineness, obtain mixed slurry;
(2) mixed slurry in step (1) is injected to the gypsum mold of having manufactured, after 35 degree are placed moulding in 1-2 hour, continue to place 3-5 days;
(3) dried base substrate is removed to mould, moisturizing 3-5 time, polishing burr, makes base substrate neatly smooth;
(4) base substrate is put into kiln, in 3 hours, be warming up to 1200-1300 degree, fire altogether 8-10 hour, after having fired, naturally cool to room temperature, obtain finished product.
4. an inner tube of water bowl that utilizes the arbitrary described pottery of claim 1-3 to make, is characterized in that, comprise a round shape inner lining, the below of described inner lining is provided with three feets.
5. a water dispenser that comprises inner tube of water bowl claimed in claim 4, comprise from top to bottom the ceramic cap of snapping (1), water purifying chamber (2) and heating chamber (3) successively, it is characterized in that, in described water purifying chamber (2) hollow structure, be provided with described inner tube of water bowl (4).
6. ceramic water dispenser according to claim 5, is characterized in that: described water purifying chamber (2) bottom is provided with the base (5) with filter screen, and described base (5) is for supporting described inner tube of water bowl (4).
7. according to the ceramic water dispenser described in claim 5 or 6, it is characterized in that: the bottom of described heating chamber (3) is provided with well heater (31) that the outside of described heating chamber (3) has been arranged side by side respectively cold water faucet (32) and hot water effluent's mouth (33).
8. according to the arbitrary described ceramic water dispenser of claim 5-7, it is characterized in that: described heating chamber (3) one sides are provided with power switch (34), in described heating chamber (3) bottom, be provided with the plug (6) being connected with described well heater (31) wire.
9. according to the arbitrary described ceramic water dispenser of claim 5-8, it is characterized in that: described water purifying chamber (2) and heating chamber (3) are all to be made by ceramic material.
10. according to the arbitrary described ceramic water dispenser of claim 5-8, it is characterized in that: the outline of described ceramic cap (1), described water purifying chamber (2) and described heating chamber (3) forms a calabash shaped.