CN104211372A - 一种陶瓷涂料 - Google Patents
一种陶瓷涂料 Download PDFInfo
- Publication number
- CN104211372A CN104211372A CN201410322062.4A CN201410322062A CN104211372A CN 104211372 A CN104211372 A CN 104211372A CN 201410322062 A CN201410322062 A CN 201410322062A CN 104211372 A CN104211372 A CN 104211372A
- Authority
- CN
- China
- Prior art keywords
- parts
- titanium
- ceramic
- sodium
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种陶瓷涂料,由以下份数的原料组分组成:20-50份陶瓷纤维、50-80份硅微粉、60-95份空心玻璃微珠、200-250份高岭土、6-8份邻苯二甲酸二异辛酯、10-12份丙三醇、2-3份二甲苯、5-8份环氧树脂、6-9份六偏磷酸钠、12-15份氢氧化钠、5-10份磷酸三钠、3-10份羧甲基纤维素钠、2-5份羟乙基纤维素、5-10份羟丙基甲基纤维素、3-10份碳化钛、5-10份二氧化钛、3-5份氮化锆、6-10份氢化钛、5-8份纯碱、8-15份碳酸钙、12-15份硅油、12-15份聚二甲基硅氧烷、10-15份炭黑、15-20份石蜡、12-15份石墨烯、5-10份氮化镁、5-10份氧化镁、3-6份氧化硅、3-8份纳米二氧化硅、300-350份纯净水。该陶瓷涂料所采用的配方组分合理调和,配制好的涂料喷涂或刷涂在衬层上具有高温抗氧化性、抗热震性。
Description
技术领域
本发明涉及陶瓷涂料的技术领域,尤其涉及一种具有高温抗氧化性、抗热震性的陶瓷涂料。
背景技术
保护性表而涂层通常具有包括极高硬度和耐磨特性的性能。陶瓷在用于这种涂层的候选材料中很具有吸引力。不幸的是,由于陶瓷应用于表而上时通常观察到的机械结合能力差,而不能在涂层中广泛使用纯陶瓷。现有的涂装涂料,耐温最高温度仅1200℃,现场操什配制烦琐,价格昂贵。
尽管也已知通常在较高温度保持稳定性的碳化物和硼化物,但在预处理过程中这些化合物软化的程度也是有限的。这种碳化物和硼化物的实例包括碳化硅、碳化铬、碳化硼、硼化钛、硼化锆和硼化铪。与陶瓷氧化物不同,只能在有限的典型应用中使用纯非氧化物陶瓷涂层。即使这样,仍然具有问题。当使用热喷涂时,在应用前首先必须对陶瓷添加金属基质,在复合物中陶瓷作为第二相进行沉积。尽管基本上能实现涂层沉积,但高温下的使用也受到限制。这是因为当达到高温时由于陶瓷-金属基质复合物中金属相的分解降低所需的热阻。
发明内容
本发明的目的是为了克服上述现有技术的缺点,提供一种陶瓷涂料,该陶瓷涂料所采用的配方组分合理调和,配制好的涂料喷涂或刷涂在衬层上具有高温抗氧化性、抗热震性。
本发明解决其技术问题所采用的技术方案是:一种陶瓷涂料,由以下份数的原料组分组成:20-50份陶瓷纤维、50-80份硅微粉、60-95份空心玻璃微珠、200-250份高岭土、6-8份邻苯二甲酸二异辛酯、10-12份丙三醇、2-3份二甲苯、5-8份环氧树脂、6-9份六偏磷酸钠、12-15份氢氧化钠、5-10份磷酸三钠、3-10份羧甲基纤维素钠、2-5份羟乙基纤维素、5-10份羟丙基甲基纤维素、3-10份碳化钛、5-10份二氧化钛、3-5份氮化锆、6-10份氢化钛、5-8份纯碱、8-15份碳酸钙、12-15份硅油、12-15份聚二甲基硅氧烷、10-15份炭黑、15-20份石蜡、12-15份石墨烯、5-10份氮化镁、5-10份氧化镁、3-6份氧化硅、3-8份纳米二氧化硅、300-350份纯净水。
进一步的,20份陶瓷纤维、50份硅微粉、60份空心玻璃微珠、200份高岭土、6份邻苯二甲酸二异辛酯、10份丙三醇、2份二甲苯、5份环氧树脂、6份六偏磷酸钠、12份氢氧化钠、5份磷酸三钠、3份羧甲基纤维素钠、2份羟乙基纤维素、5份羟丙基甲基纤维素、3份碳化钛、5份二氧化钛、3份氮化锆、6份氢化钛、5份纯碱、8份碳酸钙、12份硅油、12份聚二甲基硅氧烷、10份炭黑、15份石蜡、12份石墨烯、5份氮化镁、5份氧化镁、3份氧化硅、3份纳米二氧化硅、300份纯净水。
或者是,各原料组分的份数为: 50份陶瓷纤维、80份硅微粉、95份空心玻璃微珠、250份高岭土、8份邻苯二甲酸二异辛酯、12份丙三醇、3份二甲苯、8份环氧树脂、9份六偏磷酸钠、15份氢氧化钠、10份磷酸三钠、10份羧甲基纤维素钠、5份羟乙基纤维素、10份羟丙基甲基纤维素、10份碳化钛、10份二氧化钛、5份氮化锆、10份氢化钛、8份纯碱、15份碳酸钙、15份硅油、15份聚二甲基硅氧烷、15份炭黑、20份石蜡、15份石墨烯、10份氮化镁、10份氧化镁、6份氧化硅、8份纳米二氧化硅、350份纯净水。
综上所述,本发明的陶瓷涂料所采用的配方组分合理调和,配制好的涂料喷涂或刷涂在衬层上具有高温抗氧化性、抗热震性。
具体实施方式
实施例1
本实施例1所描述的一种陶瓷涂料,由以下份数的原料组分组成:20份陶瓷纤维、50份硅微粉、60份空心玻璃微珠、200份高岭土、6份邻苯二甲酸二异辛酯、10份丙三醇、2份二甲苯、5份环氧树脂、6份六偏磷酸钠、12份氢氧化钠、5份磷酸三钠、3份羧甲基纤维素钠、2份羟乙基纤维素、5份羟丙基甲基纤维素、3份碳化钛、5份二氧化钛、3份氮化锆、6份氢化钛、5份纯碱、8份碳酸钙、12份硅油、12份聚二甲基硅氧烷、10份炭黑、15份石蜡、12份石墨烯、5份氮化镁、5份氧化镁、3份氧化硅、3份纳米二氧化硅、300份纯净水。
实施例2
本实施例2所描述的一种陶瓷涂料,由以下份数的原料组分组成:50份陶瓷纤维、80份硅微粉、95份空心玻璃微珠、250份高岭土、8份邻苯二甲酸二异辛酯、12份丙三醇、3份二甲苯、8份环氧树脂、9份六偏磷酸钠、15份氢氧化钠、10份磷酸三钠、10份羧甲基纤维素钠、5份羟乙基纤维素、10份羟丙基甲基纤维素、10份碳化钛、10份二氧化钛、5份氮化锆、10份氢化钛、8份纯碱、15份碳酸钙、15份硅油、15份聚二甲基硅氧烷、15份炭黑、20份石蜡、15份石墨烯、10份氮化镁、10份氧化镁、6份氧化硅、8份纳米二氧化硅、350份纯净水。
以上所述,仅是本发明的较佳实施例而已,并非对本发明的技术方案作任何形式上的限制。凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均仍属于本发明的技术方案的范围内。
Claims (3)
1.一种陶瓷涂料,其特征在于,由以下份数的原料组分组成:20-50份陶瓷纤维、50-80份硅微粉、60-95份空心玻璃微珠、200-250份高岭土、6-8份邻苯二甲酸二异辛酯、10-12份丙三醇、2-3份二甲苯、5-8份环氧树脂、6-9份六偏磷酸钠、12-15份氢氧化钠、5-10份磷酸三钠、3-10份羧甲基纤维素钠、2-5份羟乙基纤维素、5-10份羟丙基甲基纤维素、3-10份碳化钛、5-10份二氧化钛、3-5份氮化锆、6-10份氢化钛、5-8份纯碱、8-15份碳酸钙、12-15份硅油、12-15份聚二甲基硅氧烷、10-15份炭黑、15-20份石蜡、12-15份石墨烯、5-10份氮化镁、5-10份氧化镁、3-6份氧化硅、3-8份纳米二氧化硅、300-350份纯净水。
2.根据权利要求1所述的一种陶瓷承烧板,其特征在于,各原料组分的份数为:20份陶瓷纤维、50份硅微粉、60份空心玻璃微珠、200份高岭土、6份邻苯二甲酸二异辛酯、10份丙三醇、2份二甲苯、5份环氧树脂、6份六偏磷酸钠、12份氢氧化钠、5份磷酸三钠、3份羧甲基纤维素钠、2份羟乙基纤维素、5份羟丙基甲基纤维素、3份碳化钛、5份二氧化钛、3份氮化锆、6份氢化钛、5份纯碱、8份碳酸钙、12份硅油、12份聚二甲基硅氧烷、10份炭黑、15份石蜡、12份石墨烯、5份氮化镁、5份氧化镁、3份氧化硅、3份纳米二氧化硅、300份纯净水。
3.根据权利要求1所述的一种陶瓷承烧板,其特征在于,各原料组分的份数为: 50份陶瓷纤维、80份硅微粉、95份空心玻璃微珠、250份高岭土、8份邻苯二甲酸二异辛酯、12份丙三醇、3份二甲苯、8份环氧树脂、9份六偏磷酸钠、15份氢氧化钠、10份磷酸三钠、10份羧甲基纤维素钠、5份羟乙基纤维素、10份羟丙基甲基纤维素、10份碳化钛、10份二氧化钛、5份氮化锆、10份氢化钛、8份纯碱、15份碳酸钙、15份硅油、15份聚二甲基硅氧烷、15份炭黑、20份石蜡、15份石墨烯、10份氮化镁、10份氧化镁、6份氧化硅、8份纳米二氧化硅、350份纯净水。