CN1041965A - 改性丙烯酸酯高效粘接剂 - Google Patents
改性丙烯酸酯高效粘接剂 Download PDFInfo
- Publication number
- CN1041965A CN1041965A CN 88107134 CN88107134A CN1041965A CN 1041965 A CN1041965 A CN 1041965A CN 88107134 CN88107134 CN 88107134 CN 88107134 A CN88107134 A CN 88107134A CN 1041965 A CN1041965 A CN 1041965A
- Authority
- CN
- China
- Prior art keywords
- acrylate resin
- resin emulsion
- polyvinyl
- camphor oil
- pine camphor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
改性丙烯酸酯高效粘接剂,属于复合树脂粘合剂。本粘合剂是合成树脂与天然树脂配制成的,其配方为:改性丙烯酸酯树脂乳液(固含量36~40%)30~45%;聚乙烯醇缩醛物溶液(9~11%)35~50%;松醇油18~22%。在常温常压下,将改性丙烯酸酯树脂乳液置入反应釜,在搅拌下徐徐加入松醇油,混合均匀后加入聚乙烯醇缩醛溶液,再搅拌一小时即得产品。其粘接性能优异,可用于木材、皮革、橡胶、陶瓷等粘接。
Description
本发明涉及粘合剂,尤其涉及复合树脂粘合剂。
目前,基于用途和要求的不同,市售粘合剂的品类较为繁多,难于根据其性能指标论其短长。在民用和建筑用粘合剂中,使用最广泛的聚醋酸乙烯类粘合剂,聚丙烯酸和聚丙烯酸腈类粘合剂、丁腈胶和氯丁胶粘合剂、酚醛-聚乙烯醇缩醛粘合剂等,这些粘合剂大多分别存在不耐温度变化、用途比较单一、价格偏高等缺点。
本发明旨在提供一种性能优良、使用范围广泛、耐温变、化学性能稳定、价格适中的复合型树脂粘合剂。
本发明是这样实现上述目的的:
本粘合剂是用合成树脂粘合剂和天然粘合剂配制而成的颗粒型热固性高效粘合剂。它是将改性丙烯酸酯树脂乳液、聚乙烯醇缩醛物、松醇油共混而成的,故该接枝共聚体系具有单组份的特性和交联产生的新特性。
本粘合剂所用的改性丙烯酸酯树脂乳液是用聚乙烯醇缩醛物改性的丙烯酸酯类树脂乳液(其制备详见专利申请88103155.0);所述的聚乙烯醇缩醛物是指聚乙烯醇缩甲醛、聚乙烯醇缩丁醛、聚乙烯醇缩脲醛、用尿素改性的聚乙烯醇缩甲醛等,聚乙烯醇缩醛物或其混合物,出于成本和工业考虑,以采用聚乙烯醇缩甲醛和用尿素改性的聚乙烯醇缩甲醛为佳;所述的松醇油是一分子式为C10H17OH的α-松油醇为主成份,并含有α-蒎烯、β-蒎烯、α-松油烯、β-水茴香烯、异松油烯、萜烯乙醚、萜醚、α-萜烯醇、β-萜烯醇、长叶烯等的复杂混合物。
本粘接剂的配方如下:
改性丙烯酸酯树脂乳液(用含量36-40%) 10~80%
聚乙烯醇缩醛物溶液(9~11%) 10~80%
松醇油 10~20%
制备方法:
在常温常压下,将改性丙烯酸酯树脂乳液置入反应釜,在搅拌下下缓缓加入松醇油,得混合均匀后,再在搅拌下缓缓加入聚乙烯醇缩醛物溶液,继续搅拌一小时出料,即得产品。
实施例与效果
例1、改性丙烯酸酯树脂乳液(固含量36~40%)10%
聚乙烯醇缩甲醛溶液(9~11%) 80%
松醇油 10%
例2、改性丙烯酸酯树脂乳液(固含量36~40%)20%
聚乙烯醇缩甲醛溶液(9~11%) 60%
松醇油 20%
例3、改性丙烯酸酯树脂乳液(固含量36~40%)30%
聚乙烯醇缩甲醛溶液(9~11%) 50%
松醇油 20%
例4、改性丙烯酸酯树脂乳液(固含量36~40%)40%
聚乙烯醇缩甲醛溶液(9~11%) 40%
松醇油 20%
例5、改性丙烯酸酯树脂乳液(固含量36~40%)50%
聚乙烯醇缩甲醛溶液(9~11%) 30%
松醇油 20%
例6、改性丙烯酸酯树脂乳液(固含量36~40%)60%
聚乙烯醇缩甲醛溶液(9~11%) 20%
松醇油 20%
例7、改性丙烯酸酯树脂乳液(固含量36~40%)70%
聚乙烯醇缩甲醛溶液(9~11%) 10%
松醇油 20%
例8、改性丙烯酸酯树脂乳液(固含量36~40%)80%
聚乙烯醇缩甲醛溶液(9~11%) 0%
松醇油 20%
从粘合力看,除例8明显低劣外,例1~例7的粘合剂都有较好的粘结能力,其中尤以例3~例5配方为佳,从成本分析,以例1~例5是可取的。
本人按例1~例4配方,用聚乙烯醇缩丁醛,聚乙烯醇缩尿醛、用尿素改性的聚乙烯醇缩甲醛、或上述聚乙烯醇缩醛物的混合物替代聚乙烯醇缩甲醛,按例1~例4制备粘合剂,其效果基本相同
综上分析并验证,本粘接剂的最佳配方为:
改性丙烯酸酯树脂乳液(固含量36~40%) 32~45%
聚乙烯醇缩甲醛溶液(9~11%) 35~50%
松醇油 18~22%
本粘合剂在应用时可加入适量固化剂,待其自然固化(约4到24小时);在100℃下固化效果更佳。本粘合剂与目前市售的丁腈胶、氯丁胶、酚醛-橡胶、酚醛-有机硅树脂、酚醛-聚乙烯醇缩醛粘合剂相比,具有更大的粘合能力,可广泛用于木材、皮革、橡胶、陶瓷、金属等粘接。具体技术数据待有关检测部门测定后补上。
由于改性丙烯酸酯树脂乳液就是用聚乙烯醇缩醛物将丙烯酸酯树脂改性而得之产品,故本粘接剂可用一般的丙烯酸酯树脂乳液、聚乙烯醇缩醛物与松醇油直接配制。在选用聚乙烯醇缩甲醛时,其最佳配方为:
丙烯酸酯树脂乳液(36~40%) 30~45%
聚乙烯醇缩甲醛(18~20%) 35~52%
松醇油 18~22%
在原料固含量与浓度改变时,可按本配方及原料组分含量换算。
Claims (5)
1、一种复合树脂型高效粘接(合)剂,其特征在于:本改性丙烯酸酯高效粘合剂是用改性丙烯酸酯树脂乳液、聚乙烯醇缩醛物、松醇油共混而成的,其配方为:
改性丙烯酸酯树脂乳液(固含量36~40%) 10~80%
聚乙烯醇缩醛物溶液(9~11%) 10~80%
松醇油 10~20%
其中,较佳配方为
改性丙烯酸酯树脂乳液(固含量36~40%) 30~50%
聚乙烯醇缩醛物溶液(9~11%) 30~50%
松醇油 20%
其制备方法如下:
在常温常压下,将改性丙烯酸酯树脂乳液置入反应釜,在搅拌下徐徐加入松醇油,待混合均匀后,再在搅拌下徐徐加入聚乙烯醇物溶液,继续搅拌一小时即得产品。
2、根据权利要求1所述的改性丙烯酸酯高效粘接剂,其特征在于:所述的改性丙烯酸酯树脂乳液是用聚乙烯醇缩醛物改性的丙烯酸酯树脂乳液;所述的聚乙烯醇缩醛物是指聚乙烯醇缩甲醛、聚乙烯醇缩丁醛、聚乙烯醇缩脲醛,用尿素改性的聚乙烯醇缩甲醛等聚乙烯醇缩醛物或者上述缩醛物的混合物,从成本考虑以用聚乙烯醇缩甲醛或用尿素改性的聚乙烯醇缩甲醛为佳。
3、根据权利要求1所述的改性丙烯酸酯高效粘接剂,其特征在于:本粘接剂的最佳配方为:
改性丙烯酸酯树脂乳液(固含量36~40%) 30~45%
聚乙烯醇缩甲醛(9~11%) 35~50%
松醇油 18~22%
4、根据权利要求1或3所述的改性丙烯酸酯高效粘接剂,其特征在于:在原料固含量或浓度发生改变时,按上述配方和各组分含量核算配制。
5、根据权利要求1所述的改性丙烯酸酯高效粘接剂,其特征在于:由于改性丙烯酸酯树脂乳液就是用聚乙烯醇缩醛物将丙烯酸酯树脂改性而得之产品,故本粘接剂可用一般的丙烯酸酯树脂乳液、聚乙烯醇缩醛物与松醇油直接配制。在选用聚乙烯醇缩甲醛时,其最佳配方为:
丙烯酸酯树脂乳液(36~40%) 30~45%
聚乙烯醇缩甲醛(18~20%) 35~52%
松醇油 18~22%
在原料固含量与浓度改变时,可按本配方及原料组分含量换算。