CN104194589B - 一种陶瓷用不饱和聚酯光固化涂料 - Google Patents
一种陶瓷用不饱和聚酯光固化涂料 Download PDFInfo
- Publication number
- CN104194589B CN104194589B CN201410453546.2A CN201410453546A CN104194589B CN 104194589 B CN104194589 B CN 104194589B CN 201410453546 A CN201410453546 A CN 201410453546A CN 104194589 B CN104194589 B CN 104194589B
- Authority
- CN
- China
- Prior art keywords
- parts
- pottery
- unsaturated polyester
- photocureable coating
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种陶瓷用不饱和聚酯光固化涂料，其原料如下：环氧聚氨酯、乙二醇、乙醇、1,2-丙二醇、水、顺丁烯二酸酐、着色颜料、邻苯二酸酐、三缩丙二醇二丙烯酸酯、己二酸、交联剂、季戊四醇、己二醇二丙烯酸酯、三羟甲基丙烷和三羟甲基丙烷三丙烯酸酯；产品光泽度130％-150％，硬度0.9-1；柔韧性1-3mm，附着力1级，水中浸泡5-15d后无起泡、脱落现象；在饱和氢氧化钙中浸泡1-5d不起泡、皱皮；耐酸性24-48h，耐汽油200#24h，可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于涂料领域，尤其涉及一种陶瓷用不饱和聚酯光固化涂料。
背景技术
陶瓷工业在我国发展较快，销售市场逐渐转旺。我国是一个陶瓷生产大国，对陶瓷的需求量也越来越大。从国内市场情况看，近年形势喜人，名特优新陶瓷产品供不应求，高档陶瓷和中高档卫生陶瓷十分抢手，质量好的传统产品继续畅销，滞销的只是质量差的产品。而随着人性化理念的普及，及新型和谐社会的构成，设计一种柔韧性好、硬度高、光泽好与冲击强度高的陶瓷用不饱和聚酯光固化涂料是非常必要的。
发明内容
解决的技术问题：
本申请针对上述技术问题，提供一种陶瓷用不饱和聚酯光固化涂料，解决现有陶瓷用不饱和聚酯光固化涂料光泽度、硬度和冲击强度低、柔韧性差等技术问题。
技术方案：
一种陶瓷用不饱和聚酯光固化涂料，所述陶瓷用不饱和聚酯光固化涂料的原料按重量份数配比如下：环氧聚氨酯100份；乙二醇30-40份；乙醇35-45份；1,2-丙二醇35-45份；水80-100份；顺丁烯二酸酐50-60份；着色颜料5-15份；邻苯二酸酐25-35份；三缩丙二醇二丙烯酸酯10-20份；己二酸5-15份；交联剂1-5份；季戊四醇4-6份；己二醇二丙烯酸酯20-30份；三羟甲基丙烷1-5份；三羟甲基丙烷三丙烯酸酯1-10份。
作为本发明的一种优选技术方案：所述陶瓷用不饱和聚酯光固化涂料的原料按重量份数配比如下：环氧聚氨酯100份；乙二醇35份；乙醇40份；1,2-丙二醇40份；水90份；顺丁烯二酸酐55份；着色颜料10份；邻苯二酸酐30份；三缩丙二醇二丙烯酸酯15份；己二酸10份；交联剂3份；季戊四醇5份；己二醇二丙烯酸酯25份；三羟甲基丙烷3份；三羟甲基丙烷三丙烯酸酯5份。
作为本发明的一种优选技术方案：所述着色颜料采用氧化铁红或群青。
作为本发明的一种优选技术方案：所述交联剂采用六甲氧甲基三聚氰胺。
有益效果：
本发明所述一种陶瓷用不饱和聚酯光固化涂料采用以上技术方案与现有技术相比，具有以下技术效果：1、产品光泽度130％-150％，硬度0.9-1；2、柔韧性1-3mm，附着力1级，水中浸泡5-15d后无起泡、脱落现象；3、在饱和氢氧化钙中浸泡1-5d不起泡、皱皮；4、耐酸性24-48h，耐汽油200#24h，可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种陶瓷用不饱和聚酯光固化涂料，其原料按重量份数配比如下：环氧聚氨酯100份；乙二醇30份；乙醇35份；1,2-丙二醇35份；水80份；顺丁烯二酸酐50份；群青5份；邻苯二酸酐25份；三缩丙二醇二丙烯酸酯10份；己二酸5份；六甲氧甲基三聚氰胺1份；季戊四醇4份；己二醇二丙烯酸酯20份；三羟甲基丙烷1份；三羟甲基丙烷三丙烯酸酯1份。
在装有回流冷凝管、温度计、搅拌器的反应釜中加入环氧聚氨酯、乙二醇、乙醇、1,2-丙二醇和水，在180℃反应1h，升温至210℃加入剩余原料，反应1h，冷却后过滤，既得产品。
产品光泽度130％，硬度0.9；柔韧性1mm，附着力1级，水中浸泡5d后无起泡、脱落现象；在饱和氢氧化钙中浸泡1d不起泡、皱皮；耐酸性24h，耐汽油200#24h。
实施例2:
一种陶瓷用不饱和聚酯光固化涂料，其原料按重量份数配比如下：环氧聚氨酯100份；乙二醇40份；乙醇45份；1,2-丙二醇45份；水100份；顺丁烯二酸酐60份；氧化铁红15份；邻苯二酸酐35份；三缩丙二醇二丙烯酸酯20份；己二酸15份；六甲氧甲基三聚氰胺5份；季戊四醇6份；己二醇二丙烯酸酯30份；三羟甲基丙烷5份；三羟甲基丙烷三丙烯酸酯10份。
在装有回流冷凝管、温度计、搅拌器的反应釜中加入环氧聚氨酯、乙二醇、乙醇、1,2-丙二醇和水，在200℃反应2h，升温至210℃加入剩余原料，反应2h，冷却后过滤，既得产品。
产品光泽度140％，硬度1；柔韧性2mm，附着力1级，水中浸泡10d后无起泡、脱落现象；在饱和氢氧化钙中浸泡3d不起泡、皱皮；耐酸性36h，耐汽油200#24h。
实施例3:
一种陶瓷用不饱和聚酯光固化涂料，其原料按重量份数配比如下：环氧聚氨酯100份；乙二醇35份；乙醇40份；1,2-丙二醇40份；水90份；顺丁烯二酸酐55份；氧化铁红10份；邻苯二酸酐30份；三缩丙二醇二丙烯酸酯15份；己二酸10份；六甲氧甲基三聚氰胺3份；季戊四醇5份；己二醇二丙烯酸酯25份；三羟甲基丙烷3份；三羟甲基丙烷三丙烯酸酯5份。
在装有回流冷凝管、温度计、搅拌器的反应釜中加入环氧聚氨酯、乙二醇、乙醇、1,2-丙二醇和水，在190℃反应1h，升温至210℃加入剩余原料，反应2h，冷却后过滤，既得产品。
产品光泽度150％，硬度1；柔韧性3mm，附着力1级，水中浸泡15d后无起泡、脱落现象；在饱和氢氧化钙中浸泡5d不起泡、皱皮；耐酸性48h，耐汽油200#24h。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在与本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。
Claims (1)
1.一种陶瓷用不饱和聚酯光固化涂料，其特征在于所述陶瓷用不饱和聚酯光固化涂料的原料按重量份数配比如下：环氧聚氨酯100份；乙二醇35份；乙醇40份；1,2-丙二醇40份；水90份；顺丁烯二酸酐55份；着色颜料10份；邻苯二酸酐30份；三缩丙二醇二丙烯酸酯15份；己二酸10份；交联剂3份；季戊四醇5份；己二醇二丙烯酸酯25份；三羟甲基丙烷3份；三羟甲基丙烷三丙烯酸酯5份；
所述着色颜料采用氧化铁红或群青；
所述交联剂采用六甲氧甲基三聚氰胺。