CN104194576A - 一种耐候性户外帐篷支撑杆用涂料及其制备方法 - Google Patents
一种耐候性户外帐篷支撑杆用涂料及其制备方法 Download PDFInfo
- Publication number
- CN104194576A CN104194576A CN201410431883.1A CN201410431883A CN104194576A CN 104194576 A CN104194576 A CN 104194576A CN 201410431883 A CN201410431883 A CN 201410431883A CN 104194576 A CN104194576 A CN 104194576A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- tent support
- outdoor tent
- support bar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供的一种耐候性户外帐篷支撑杆用涂料,由以下重量份的组份制成:环氧树脂40-60份、颜料5-15份、填料5-10份、分散剂1-2份、流平剂1-2份、防锈剂1-2份、消泡剂1-2份、催干剂1-2份、增塑剂1-2份、成膜助剂1-2份、丙酮30份、水70份。该涂料,原料来源丰富,成本低廉,通过采用各种辅料和主料配合,各个组分的相互作用和协调,从而使该隔热涂料同时具有耐强光照射、耐老化、耐雨水侵蚀、防滑等特性,特别是其防紫外线和隔热性能非常优异。
Description
技术领域
本发明涉及涂料材料领域,特别涉及一种耐候性户外帐篷支撑杆用涂料,还涉及其制备方法。
背景技术
随着人们生活水平的提高,人们越来越喜欢进行户外运动。帐篷是人们选择休息的好用品,作为户外用的帐篷,要具有耐强光照射、耐老化、耐雨水侵蚀、防滑等的特性,特别是要具有优秀的防寒隔热性能,然而现有的用于帐篷的涂料耐候性能不佳。
发明内容
发明目的:为了克服上述现有技术的不足,本发明的目的在于提供一种户外躺椅用复合涂料,该涂料同事具有耐强光照射、耐老化、耐雨水侵蚀、防滑等特性。
本发明的第二目的在于提供上述户外躺椅用复合涂料的制备方法。
技术方案:本发明提供的一种耐候性户外帐篷支撑杆用涂料,由以下重量份的组份制成:环氧树脂40-60份、颜料5-15份、填料5-10份、分散剂1-2份、流平剂1-2份、防锈剂1-2份、消泡剂1-2份、催干剂1-2份、增塑剂1-2份、成膜助剂1-2份、丙酮30份、水70份。
作为优选,所述环氧树脂为双酚A缩水甘油醚。
作为另一种优选,所述颜料为二氧化钛或钛白粉。
作为另一种优选,所述防锈剂为质量比为(3-5):(2-4):(2-4):1的磷酸锌、铁粉、锌粉和铝粉。
作为另一种优选,所述填料为重晶石、偏硅酸钙或云母;所述分散剂为EFKA-5065分散剂和EFKA-4050分散剂按照1:(4-6)的混合物;所述流平剂为的EFKA-3777流平剂和EFKA-3239流平剂按照(3-5):1的混合物;所述消泡剂为疏水改性二氧化硅或矿物油;所述催干剂为环烷酸钴、环烷酸锰或环烷酸铅;所述增塑剂为氯化石蜡或邻苯二甲酸二酯;所述成膜助剂为2,2,4-三甲基-1,3-戊二醇单异丁酸酯。
本发明还提供了上述耐候性户外帐篷支撑杆用涂料的制备方法,包括以下步骤:将各组分混合在一起,恒温匀速搅拌,使各组分均匀分布即可。
其中,所述恒温均速搅拌的条件为25~28℃下80~100r/min的速度搅拌4~5h。
有益效果:本发明提供的耐候性户外帐篷支撑杆用涂料,原料来源丰富,成本低廉,通过采用各种辅料和主料配合,各个组分的相互作用和协调,从而使该隔热涂料同时具有耐强光照射、耐老化、耐雨水侵蚀、防滑等特性,特别是其耐候性能非常优异。
本发明发现采用质量比为(3-5):(2-4):(2-4):1的重晶石、偏硅酸钙、云母和二氧化硅的组合,三种材料互相配合,能够大大提高该涂料的耐候性。
具体实施方式
根据下述实施例,可以更好地理解本发明。然而,本领域的技术人员容易理解,实施例所描述的内容仅用于说明本发明,而不应当也不会限制权利要求书中所详细描述的本发明。
实施例1
耐候性户外帐篷支撑杆用涂料,由以下重量份的组份制成:双酚A缩水甘油醚50份、颜料10份、填料8份、分散剂1.5份、流平剂1.5份、防锈剂1.5份、消泡剂1.5份、催干剂1.5份、增塑剂1.5份、成膜助剂1.5份、丙酮30份、水70份。
其中,颜料为二氧化钛,所述填料为重晶石;分散剂为EFKA-5065分散剂和EFKA-4050分散剂按照1:5的混合物;流平剂为的EFKA-3777流平剂和EFKA-3239流平剂按照4:1的混合物;防锈剂为磷酸锌;消泡剂为矿物油;催干剂为环烷酸钴;增塑剂为氯化石蜡;成膜助剂为2,2,4-三甲基-1,3-戊二醇单异丁酸酯。
其中,防锈剂为质量比为4:3:3:1的磷酸锌、铁粉、锌粉和铝粉。
其制备方法,包括以下步骤:将各组分混合在一起,27℃下00r/min的速度搅拌4.5h,使各组分均匀分布即可。
实施例2
耐候性户外帐篷支撑杆用涂料,由以下重量份的组份制成:双酚A缩水甘油醚40份、颜料5份、填料5份、分散剂1份、流平剂2份、防锈剂2份、消泡剂1份、催干剂1份、增塑剂2份、成膜助剂2份、丙酮30份、水70份。
其中,颜料为钛白粉,所述填料为偏硅酸钙;分散剂为EFKA-5065分散剂和EFKA-4050分散剂按照1:4的混合物;流平剂为的EFKA-3777流平剂和EFKA-3239流平剂按照5:1的混合物;防锈剂为锌粉;消泡剂为矿物油;催干剂为环烷酸铅;增塑剂为邻苯二甲酸二酯;成膜助剂为2,2,4-三甲基-1,3-戊二醇单异丁酸酯。
其中,防锈剂为质量比为5:2:4:1的磷酸锌、铁粉、锌粉和铝粉。
其制备方法,包括以下步骤:将各组分混合在一起,25℃下100r/min的速度搅拌4h,使各组分均匀分布即可。
实施例3
耐候性户外帐篷支撑杆用涂料,由以下重量份的组份制成:双酚A缩水甘油醚60份、颜料15份、填料10份、分散剂2份、流平剂1份、防锈剂1份、消泡剂2份、催干剂2份、增塑剂1份、成膜助剂1份、丙酮30份、水70份。
其中,颜料为二氧化钛,所述填料为云母;分散剂为EFKA-5065分散剂和EFKA-4050分散剂按照1:6的混合物;流平剂为的EFKA-3777流平剂和EFKA-3239流平剂按照3:1的混合物;防锈剂为铝粉;消泡剂为疏水改性二氧化硅;催干剂为环烷酸锰;增塑剂为氯化石蜡;成膜助剂为2,2,4-三甲基-1,3-戊二醇单异丁酸酯。
其中,防锈剂为质量比为3:4:2:1的磷酸锌、铁粉、锌粉和铝粉。
其制备方法,包括以下步骤:将各组分混合在一起,28℃下80r/min的速度搅拌5h,使各组分均匀分布即可。
实施例4
与实施例1基本相同,不同之处仅在于采用磷酸锌作为防锈剂。
实施例5
与实施例1基本相同,不同之处仅在于采铁粉作为防锈剂。
实施例6
与实施例1基本相同,不同之处仅在于采用锌粉为防锈剂。
实施例7
与实施例1基本相同,不同之处仅在于采用铝粉作为防锈剂。
将实施例1至7的涂料涂在帐篷支撑杆上晾干,分别在温度为60℃、湿度为80%条件下放置30h、40h、50h,观察涂层变化。结果见表1。
表1黑色涤纶布涂层耐热性能测试结果
由此可见,本发明采用的填料的组合能够大大提高耐候性能。
Claims (7)
1.一种耐候性户外帐篷支撑杆用涂料,其特征在于:由以下重量份的组份制成:环氧树脂40-60份、颜料5-15份、填料5-10份、分散剂1-2份、流平剂1-2份、防锈剂1-2份、消泡剂1-2份、催干剂1-2份、增塑剂1-2份、成膜助剂1-2份、丙酮30份、水70份。
2.根据权利要求1所述的一种耐候性户外帐篷支撑杆用涂料,其特征在于:所述环氧树脂为双酚A缩水甘油醚。
3.根据权利要求1所述的一种耐候性户外帐篷支撑杆用涂料,其特征在于:所述颜料为二氧化钛或钛白粉。
4.根据权利要求1所述的一种耐候性户外帐篷支撑杆用涂料,其特征在于:所述防锈剂为质量比为(3-5):(2-4):(2-4):1的磷酸锌、铁粉、锌粉和铝粉。
5.根据权利要求1所述的一种耐候性户外帐篷支撑杆用涂料,其特征在于:所述填料为重晶石、偏硅酸钙或云母;所述分散剂为EFKA-5065分散剂和EFKA-4050分散剂按照1:(4-6)的混合物;所述流平剂为的EFKA-3777流平剂和EFKA-3239流平剂按照(3-5):1的混合物;所述防锈剂为磷酸锌、锌粉或铝粉;所述消泡剂为疏水改性二氧化硅或矿物油;所述催干剂为环烷酸钴、环烷酸锰或环烷酸铅;所述增塑剂为氯化石蜡或邻苯二甲酸二酯;所述成膜助剂为2,2,4-三甲基-1,3-戊二醇单异丁酸酯。
6.权利要求1至6任一项所述的耐候性户外帐篷支撑杆用涂料的制备方法,其特征在于:将各组分混合在一起,恒温匀速搅拌,使各组分均匀分布即可。
7.根据权利要求7所述的一种耐候性户外帐篷支撑杆用涂料的制备方法,其特征在于:所述恒温均速搅拌的条件为25~28℃下80~100r/min的速度搅拌4~5h。