CN104193251A - Anticorrosive and antibacterial thermal insulation mortar and preparation method thereof - Google Patents
Anticorrosive and antibacterial thermal insulation mortar and preparation method thereof Download PDFInfo
- Publication number
- CN104193251A CN104193251A CN201410377652.7A CN201410377652A CN104193251A CN 104193251 A CN104193251 A CN 104193251A CN 201410377652 A CN201410377652 A CN 201410377652A CN 104193251 A CN104193251 A CN 104193251A
- Authority
- CN
- China
- Prior art keywords
- thermal insulation
- parts
- add
- insulation mortar
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses anticorrosive and antibacterial thermal insulation mortar which is prepared from the following raw materials in parts by weight: 0.5 to 1 part of coco-glucoside, 0.5 to 1.5 parts of sodium bicarbonate, 1 to 2 parts of carrageenan, 60 to 80 parts of Portland cement, 10 to 20 parts of magnesium soapstone powder, 1 to 2 parts of ramie, 45 to 65 parts of ceramsite, 0.5 to 1 part of magnesium myristate, 0.5 to 1 part of propylparaben, 0.1 to 0.5 part of benzalkonium chloride and 5 to 10 parts of auxiliaries. The thermal insulation mortar has anticorrosive and antibacterial functions, and is good in thermal insulation effect, strong in durability and wide in application range.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of anti-corrosive antibacterial thermal insulation mortar and preparation method thereof.
Background technology
Building heat-insulating mortar refers to by the compound mortar that can be incubated construction wall forming of gelling material, light skeletal and other functional additives, it has the advantage such as have good workability, material property is stable, environmental safety is good, is a kind of widely used building thermal insulation material.Except having basic incubation and thermal insulation function, by the adjustment of matrix material, thermal insulation mortar can also have other functions, as waterproof, sound insulation, anticorrosion etc.
Summary of the invention
The object of this invention is to provide a kind of anti-corrosive antibacterial thermal insulation mortar.
The present invention is achieved by the following technical solutions:
An anti-corrosive antibacterial thermal insulation mortar, it is that raw material by following weight parts makes:
Cocoyl glucoside 0.5-1, sodium bicarbonate 0.5-1.5, carrageenin 1-2, silicate cement 60-80, magnesium soap stone flour 10-20, ramee 1-2, haydite 45-65, magnesium myristate 0.5-1, propylben 0.5-1, benzalkonium chloride 0.1-0.5, auxiliary agent 5-10;
Wherein auxiliary agent is made by the raw material of following weight part:
Polyvinyl alcohol 1-3, petroleum sodium sulfonate 1-2, trolamine 1-3, cetyl trimethylammonium bromide 1-2, calcium phosphate 0.2-1, hexamethylenetetramine 0.5-1, redispersable latex powder 10-20, tea-polyphenol 0.1-0.5, stearic acid 1-2, zinc acetate 1-3;
The preparation method of auxiliary agent is:
By weight polyvinyl alcohol: water=1:20 weighing polyvinyl alcohol is added to the water, be heated to 80-90 ℃ to dissolving completely, add stearic acid, calcium phosphate and hexamethylenetetramine, 200r/min stirs 15min, after being cooled to normal temperature, add all the other raw materials, 150r/min stirs 1h, after drying, grinds evenly, cross 200 mesh sieves, obtain.
A preparation method for anti-corrosive antibacterial thermal insulation mortar, comprises the following steps:
(1) by 200-300 ℃ of processing 30min after ramee and the mixing of magnesium soap stone flour, after grinding evenly, add carrageenin and magnesium myristate, 60-80 ℃ of stirring 1h, cooling rear grinding, crosses 100 mesh sieves, obtains composite granule;
(2) in composite granule, add sodium bicarbonate and cocoyl glucoside, 40-60 ℃ is stirred 1h, adds all the other raw materials after cooling, after packing and get final product.
Advantage of the present invention is:
1. the effect with anti-corrosive antibacterial, prevents growing of bacterium and fungi;
2. and good effect of heat insulation, weather resistance is strong, has wide range of applications;
3. workability is good, constructability.
Embodiment
Non-limiting examples of the present invention is as follows:
Embodiment 1
An anti-corrosive antibacterial thermal insulation mortar, is prepared from by the component raw material of following weight (kg):
Cocoyl glucoside 0.8, sodium bicarbonate 1, carrageenin 1.5, silicate cement 70, magnesium soap stone flour 15, ramee 1.5, haydite 60, magnesium myristate 0.8, propylben 0.8, benzalkonium chloride 0.4, auxiliary agent 8;
Wherein, auxiliary agent is made by the raw material of following weight (kg):
Polyvinyl alcohol 2, petroleum sodium sulfonate 1.5, trolamine 2, cetyl trimethylammonium bromide 1.5, calcium phosphate 0.8, hexamethylenetetramine 0.6, redispersable latex powder 15, tea-polyphenol 0.4, stearic acid 1.5, zinc acetate 2;
The preparation method of auxiliary agent:
By weight polyvinyl alcohol: water=1:20 weighing polyvinyl alcohol is added to the water, be heated to 80-90 ℃ to dissolving completely, add stearic acid, calcium phosphate and hexamethylenetetramine, 200r/min stirs 15min, after being cooled to normal temperature, add all the other raw materials, 150r/min stirs 1h, after drying, grinds evenly, cross 200 mesh sieves, obtain.
The preparation method of anti-corrosive antibacterial thermal insulation mortar comprises the following steps:
(1) by 200-300 ℃ of processing 30min after ramee and the mixing of magnesium soap stone flour, after grinding evenly, add carrageenin and magnesium myristate, 60-80 ℃ of stirring 1h, cooling rear grinding, crosses 100 mesh sieves, obtains composite granule;
(2) in composite granule, add sodium bicarbonate and cocoyl glucoside, 40-60 ℃ is stirred 1h, adds all the other raw materials after cooling, after packing and get final product.
During use, by weight water: mortar=1.2:1 mixes.
According to GB/T 20473-2006 associated viscera, detect thermal insulation mortar performance, detected result is as follows:
Dry density: 332kg/m
3, ultimate compression strength: 0.83MPa, thermal conductivity: 0.045W/(m ﹒ K), press and cut cohesive strength: 80kPa.
Claims (2)
1. an anti-corrosive antibacterial thermal insulation mortar, is characterized in that, it is that raw material by following weight parts makes: cocoyl glucoside 0.5-1, sodium bicarbonate 0.5-1.5, carrageenin 1-2, silicate cement 60-80, magnesium soap stone flour 10-20, ramee 1-2, haydite 45-65, magnesium myristate 0.5-1, propylben 0.5-1, benzalkonium chloride 0.1-0.5, auxiliary agent 5-10;
Described auxiliary agent is made by the raw material of following weight part:
Polyvinyl alcohol 1-3, petroleum sodium sulfonate 1-2, trolamine 1-3, cetyl trimethylammonium bromide 1-2, calcium phosphate 0.2-1, hexamethylenetetramine 0.5-1, redispersable latex powder 10-20, tea-polyphenol 0.1-0.5, stearic acid 1-2, zinc acetate 1-3;
The preparation method of described auxiliary agent is:
By weight polyvinyl alcohol: water=1:20 weighing polyvinyl alcohol is added to the water, be heated to 80-90 ℃ to dissolving completely, add stearic acid, calcium phosphate and hexamethylenetetramine, 200r/min stirs 15min, after being cooled to normal temperature, add all the other raw materials, 150r/min stirs 1h, after drying, grinds evenly, cross 200 mesh sieves, obtain.
2. the preparation method of a kind of anti-corrosive antibacterial thermal insulation mortar according to claim 1, is characterized in that, comprises the following steps:
(1) by 200-300 ℃ of processing 30min after ramee and the mixing of magnesium soap stone flour, after grinding evenly, add carrageenin and magnesium myristate, 60-80 ℃ of stirring 1h, cooling rear grinding, crosses 100 mesh sieves, obtains composite granule;
(2) in composite granule, add sodium bicarbonate and cocoyl glucoside, 40-60 ℃ is stirred 1h, adds all the other raw materials after cooling, after packing and get final product.