CN103159429B - Diatomite composite exterior wall thermal insulation material and production process thereof - Google Patents
Diatomite composite exterior wall thermal insulation material and production process thereof Download PDFInfo
- Publication number
- CN103159429B CN103159429B CN201310080479.XA CN201310080479A CN103159429B CN 103159429 B CN103159429 B CN 103159429B CN 201310080479 A CN201310080479 A CN 201310080479A CN 103159429 B CN103159429 B CN 103159429B
- Authority
- CN
- China
- Prior art keywords
- diatomite
- insulation material
- wall heat
- infusorial earth
- binding agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A diatomite composite exterior wall thermal insulation material is prepared from the following components by weight percent: 35-38% of modified diatomite, 40-42% of expanded perlite, 12-15% of calcium hydroxide, 2-4% of wood fiber, 2-3% of rubber powder and 1-2% of hydrophobic adhesive. The thermal insulation material is formed by drying, repeatedly crushing and sorting the raw ores of diatomite and then modifying the diatomite, and then mixing the modified diatomite with expanded perlite, calcium hydroxide, wood fiber, rubber powder and hydrophobic adhesive in a certain ratio. The diatomite composite exterior wall thermal insulation material is simple in production process and excellent in thermal insulation property, and the diatomite composite exterior wall thermal insulation material is an incombustible material, and simple and convenient for construction; and the diatomite composite exterior wall thermal insulation material is applied at a temperature ranging from -50 to 50 DEG C.
Description
Technical field
The present invention relates to a kind of material of construction, more specifically refer to the compound external-wall heat-insulation material of diatomite and production technique thereof.
Background technology
Having of China's building exterior wall heat preserving technology comparative maturity: the thin outer heat preservation technology of plastering of polystyrol plastic foam plate is EPS External Thermal Insulation Technology for External, built-in cast-in-place concrete mould warming plate system, adhesive powder-polystyrene granule thermal insulation mortar External Walls Heating Insulation system and four kinds of technology of cladding External Walls Heating Insulation, first three quantities of planting system probably accounts for the more than 80% of China's construction wall exterior insulation work.
Yet the cost of above several technology is all higher, and site operation amount is large, and the construction period is long, and some difficulties and other materials are bonding, to successive projects, make troubles, and every kind of material all must detect respectively, and testing cost is very high; Every kind of material all must transport respectively, deposit, this makes transport charge, deposit and safekeeping fee very high, waste of material strengthens; Particularly adopt EPS External Thermal Insulation Technology for External difficult quality to control, because construction market is fiery at present, construction workman lacks, and particularly skilled worker lacks, and construction quality is poor.In addition, with the various materials of EPS External Thermal Insulation Technology for External, march into the arena respectively, the quality control of material and supervision are difficult to, and adopt material with low quality, jerry can be found everywhere, and have left many hidden dangers in project.
At present, occur the coating for wall surface that some have heat insulation function, the Chinese invention patent that is CN1483775 as publication number discloses a kind of hollow silicon tripolite compound building thermal-insulating coating, by preparation of raw material such as hollow silicon, swelling perlite powder, diatomite, light calcium carbonate powder, rock wool, rhoplex, water, formed, it belongs to indoor and outdoor metope finishing material, in addition, this coating is emulsion form, transports and deposit inconvenience.For this reason, we provide the compound external-wall heat-insulation material of a kind of diatomite and production technique thereof.
Summary of the invention
The invention provides the compound external-wall heat-insulation material of a kind of diatomite and production technique thereof, the above-mentioned defect existing to solve prior art.
The present invention adopts following technical scheme:
The compound external-wall heat-insulation material of diatomite, is formed by following component proportion by weight percentage: modification infusorial earth 35～38%, fine perlite 40～42%, calcium hydroxide 12～15%, xylon 2～4%, rubber powder 2～3%, hydrophobic type binding agent 1～2%.
A preferred embodiment, the compound external-wall heat-insulation material of this diatomite is comprised of following compositions in weight percentage: modification infusorial earth 38%, fine perlite 41%, calcium hydroxide 15%, xylon 2%, rubber powder 2%, hydrophobic type binding agent 2%.
Another kind of preferred embodiment, the compound external-wall heat-insulation material of this diatomite is comprised of following compositions in weight percentage: modification infusorial earth 36%, fine perlite 42%, calcium hydroxide 14%, xylon 3%, rubber powder 3%, hydrophobic type binding agent 2%.
Above-mentioned modification infusorial earth by diatomite original ore, be dried, repeatedly pulverize and sorting after carry out again modification gained, above-mentioned hydrophobic type binding agent is edible seaweed powder.
The production technique of the compound external-wall heat-insulation material of this diatomite, comprises the following steps:
One, by diatomite original ore seasoning, weathering, sun-dried mud brick grouping system grade;
Two, being transported to job shop pulverizes and selection by winnowing repeatedly;
Three, at 200-300 ℃, carry out modification and obtain modification infusorial earth;
Four, the hundreds of proportions by subtraction of parts by weights are got modification infusorial earth 35～38%, add fine perlite 40～42%, calcium hydroxide 12～15%, xylon 2～4%, rubber powder 2～3%, hydrophobic type binding agent 1～2% to mix and get final product to obtain the compound external-wall heat-insulation material of diatomite.
From the above-mentioned description to structure of the present invention, compared to the prior art, tool of the present invention has the following advantages:
1, the compound external-wall heat-insulation material of diatomite of the present invention is two component external-wall heat-insulation materials, take fine perlite as base-material, modification infusorial earth be main additive, add again with some auxiliary materials, diatomite main component is amorphous silicon di-oxide, surface arrangement is nanometer level microporous in a large number, therefore thermal and insulating performance is good and be non-fire material, and its use temperature is between-50 ℃-50 ℃.
2, this lagging material can directly be put on skin in use as mortar, reach and be not only incubated but also can fp effect, and in construction, be the form appearance with mortar, the problems such as thereby the gap of having avoided sheet material construction is difficult and cohere, and intensity is large, good integrity, low-temperature construction performance is good, cost performance is high, it is the green lagging material that a kind of novel energy-saving environment-friendly does not fire again, its technical indicator reaches or completely higher than the technical indicator of GB/T20473-2006 < < building heat-insulating mortar > > standard.
3, the compound external-wall heat-insulation material of diatomite of the present invention adds hydrophobic type binding agent, make this lagging material be put on external wall after slowly seasoning, cohesiveness is good, and waters without artificial not timing External Wall, does not occur the phenomenons such as crack after dry.
4, lagging material of the present invention is the particulate state that evenly nothing is lumpd, and it is very convenient to transport and deposit, and can long storage time never degenerate, and only needs it to mix with water in right amount during construction, and in addition, this lagging material production technique is simple.
Accompanying drawing explanation
Fig. 1 is production technological process of the present invention.
Embodiment
The specific embodiment of the present invention is described with reference to the accompanying drawings.
Embodiment mono-
The compound external-wall heat-insulation material of diatomite, is comprised of following compositions in weight percentage: modification infusorial earth 38%, fine perlite 41%, calcium hydroxide 15%, xylon 2%, rubber powder 2%, hydrophobic type binding agent 2%.
Embodiment bis-
The compound external-wall heat-insulation material of diatomite, is comprised of following compositions in weight percentage: modification infusorial earth 36%, fine perlite 42%, calcium hydroxide 14%, xylon 3%, rubber powder 3%, hydrophobic type binding agent 2%.
Embodiment tri-
The compound external-wall heat-insulation material of diatomite, is comprised of following compositions in weight percentage: modification infusorial earth 37%, fine perlite 40%, calcium hydroxide 15%, xylon 4%, rubber powder 2.5%, hydrophobic type binding agent 1.5%.
Embodiment tetra-
The compound external-wall heat-insulation material of diatomite, is comprised of following compositions in weight percentage: modification infusorial earth 35%, fine perlite 42%, calcium hydroxide 14%, xylon 4%, rubber powder 3%, hydrophobic type binding agent 2%.
Modification infusorial earth by diatomite original ore, be dried, repeatedly pulverize and sorting after carry out again modification gained, hydrophobic type binding agent is preferably edible seaweed powder.
The production technique of the compound external-wall heat-insulation material of above-mentioned diatomite, with reference to Fig. 1, comprises the following steps:
One, by diatomite original ore seasoning, weathering, sun-dried mud brick grouping system grade;
Two, being transported to job shop pulverizes and selection by winnowing repeatedly;
Three, at 200-300 ℃, carry out modification and obtain modification infusorial earth;
Four, getting by a certain percentage modification infusorial earth, fine perlite, calcium hydroxide, xylon, rubber powder, hydrophobic type binding agent mixes and gets final product to obtain the compound external-wall heat-insulation material of diatomite.
Lagging material of the present invention can directly be put on skin in use as mortar, reach and be not only incubated but also can fp effect, and in construction, be the form appearance with mortar, the problems such as thereby the gap of having avoided sheet material construction is difficult and cohere, and intensity is large, good integrity, low-temperature construction performance is good, cost performance is high, it is the green lagging material that a kind of novel energy-saving environment-friendly does not fire again, its technical indicator reaches or completely higher than the technical indicator of GB/T20473-2006 < < building heat-insulating mortar > > standard.
Following form is standard-required and the measuring technology index of the compound external-wall heat-insulation material of diatomite
Above are only the specific embodiment of the present invention, but design concept of the present invention is not limited to this, allly utilizes this design to carry out the change of unsubstantiality to the present invention, all should belong to the behavior of invading protection domain of the present invention.
Claims (5)
1. the compound external-wall heat-insulation material of diatomite, it is characterized in that, by following component proportion, formed by weight percentage: modification infusorial earth 35～38%, fine perlite 40～42%, calcium hydroxide 12～15%, xylon 2～4%, rubber powder 2～3%, hydrophobic type binding agent 1～2%, described modification infusorial earth by diatomite original ore, be dried, repeatedly pulverize and sorting after at 200-300 ℃, carry out modification gained again.
2. the compound external-wall heat-insulation material of diatomite as claimed in claim 1, is characterized in that, following compositions in weight percentage, consists of: modification infusorial earth 38%, fine perlite 41%, calcium hydroxide 15%, xylon 2%, rubber powder 2%, hydrophobic type binding agent 2%.
3. the compound external-wall heat-insulation material of diatomite as claimed in claim 1, is characterized in that, following compositions in weight percentage, consists of: modification infusorial earth 36%, fine perlite 42%, calcium hydroxide 14%, xylon 3%, rubber powder 3%, hydrophobic type binding agent 2%.
4. the compound external-wall heat-insulation material of diatomite as described in as arbitrary in claims 1 to 3, is characterized in that: described hydrophobic type binding agent is edible seaweed powder.
5. the production technique of the compound external-wall heat-insulation material of diatomite as claimed in claim 1, is characterized in that, comprises the following steps:
One, by diatomite original ore seasoning, weathering, sun-dried mud brick grouping system grade;
Two, being transported to job shop pulverizes and selection by winnowing repeatedly;
Three, at 200-300 ℃, carry out modification and obtain modification infusorial earth;
Four, the hundreds of proportions by subtraction of parts by weights are got modification infusorial earth 35～38%, add fine perlite 40～42%, calcium hydroxide 12～15%, xylon 2～4%, rubber powder 2～3%, hydrophobic type binding agent 1～2% to mix and get final product to obtain the compound external-wall heat-insulation material of diatomite.