CN104152912A - 一种防止金属零部件生绣的防锈液及其制备方法 - Google Patents
一种防止金属零部件生绣的防锈液及其制备方法 Download PDFInfo
- Publication number
- CN104152912A CN104152912A CN201410366479.0A CN201410366479A CN104152912A CN 104152912 A CN104152912 A CN 104152912A CN 201410366479 A CN201410366479 A CN 201410366479A CN 104152912 A CN104152912 A CN 104152912A
- Authority
- CN
- China
- Prior art keywords
- parts
- paraffin
- soap
- vaseline
- propylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种防止金属零部件生绣的防锈液及其制备方法，该防锈液由下列重量份的原料制成：肥皂6-8份，凡士林1-2份，丙二醇0.5-1份，石蜡0.1-0.5份，水1100-1300份。其制备方法包括以下工艺步骤：1、按上述原料配比提取肥皂，凡士林，丙二醇，石蜡和水，2、将肥皂，石蜡和水装入容器中加热至肥皂和石蜡完全融化，3、将凡士林和丙二醇放入容器中再搅拌直至凡士林，肥皂，丙二醇，石蜡和水完全混和就从容器中出料得到成品。本发明的有益效果是使金属零部件进行防锈处理成本低、效果好特别是处理后的金属零部件表面粘性小，润滑性好，且更容易附着在金属零部件表面，更容易擦除。
Description
技术领域
本发明涉及一种防锈液及其制备方法，尤其涉及到一种防止金属零部件生绣的防锈液及其制备方法。
背景技术
在金属零部件等行业生产过程中，大量的金属零部件必须要进行防锈处理，特别是在热处理生产工艺中经过滚亮发蓝后又不立即使用的金属零部件，在存放阶段很易生锈，在存放阶段必须用防锈液进行防锈处理。一般防锈处理方法是用防锈油浸渍即可。但有些金属零部件需进行连续工艺的组装，浸油后的金属零部件因油浸后粘性大，在连续工艺组装时往往会发生零部件粘连而使组装工艺中断，影响零部件的组装工作。现有的除锈液虽然能克服油浸后粘性大的问题，但是不容易附着在金属表面，且不容易擦除。
发明内容
本发明所要解决的技术问题是提供一种防止金属零部件生绣的防锈液及其制备方法，达到对金属零部件进行防锈处理且在连续工艺组装时不会因发生零部件粘连而使组装工艺中断，从而影响零部件的组装工作，且更容易附着在金属表面，更容易擦除的有益效果。
为解决上述技术问题，本发明提供一种防止金属零部件生绣的防锈液及其制备方法，一种防止金属零部件生绣的防锈液，其特征在于：该防锈液由下列重量份的原料制成：肥皂6-8份，凡士林1-2份，丙二醇0.5-1份，石蜡0.1-0.5份，水1100-1300份。
优选的，各原料的重量份数为：肥皂6份，凡士林1份，丙二醇0.5份，石蜡0.1份，水1100份。
优选的，各原料的重量份数为肥皂8份，凡士林2份，丙二醇1份，石蜡0.5份，1300份。
优选的，各原料的重量份数为肥皂7份，凡士林1.5份，丙二醇0.7份，石蜡0.3份，1200份。
制造上述除锈液的方法步骤为：1、按上述原料配比提取肥皂，凡士林，丙二醇，石蜡和水，2、将肥皂，石蜡和水装入容器中加热至肥皂和石蜡完全融化，3、将凡士林和丙二醇放入容器中再搅拌直至凡士林，肥皂，丙二醇，石蜡和水完全混和就从容器中出料得到成品。
本发明的有益效果是使金属零部件进行防锈处理成本低、效果好特别是处理后的金属零部件表面粘性小，润滑性好，且更容易附着在金属零部件表面，更容易擦除。
具体实施方式
下面结合具体实施方式对本发明的技术方案作进一步具体说明。
实施例1
一种防止金属零部件生绣的防锈液，其特征在于：该防锈液由下列重量份的原料制成：肥皂6份，凡士林1份，丙二醇0.5份，石蜡0.1份，水1100份。制造上述除锈液的方法步骤为：1、按上述原料配比提取肥皂，凡士林，丙二醇，石蜡和水，2、将肥皂，石蜡和水装入容器中加热至肥皂和石蜡完全融化，3、将凡士林和丙二醇放入容器中再搅拌直至凡士林，肥皂，丙二醇，石蜡和水完全混和就从容器中出料得到成品。
实施例2
一种防止金属零部件生绣的防锈液，其特征在于：该防锈液由下列重量份的原料制成：肥皂8份，凡士林2份，丙二醇1份，石蜡0.5份，水1300份。制造上述除锈液的方法步骤为：1、按上述原料配比提取肥皂，凡士林，丙二醇，石蜡和水，2、将肥皂，石蜡和水装入容器中加热至肥皂和石蜡完全融化，3、将凡士林和丙二醇放入容器中再搅拌直至凡士林，肥皂，丙二醇，石蜡和水完全混和就从容器中出料得到成品。
实施例3
一种防止金属零部件生绣的防锈液，其特征在于：该防锈液由下列重量份的原料制成：肥皂7份，凡士林1.5份，丙二醇0.7份，石蜡0.3份，水1100份。制造上述除锈液的方法步骤为：1、按上述原料配比提取肥皂，凡士林，丙二醇，石蜡和水，2、将肥皂，石蜡和水装入容器中加热至肥皂和石蜡完全融化，3、将凡士林和丙二醇放入容器中再搅拌直至凡士林，肥皂，丙二醇，石蜡和水完全混和就从容器中出料得到成品。
本发明的有益效果是使金属零部件进行防锈处理成本低、效果好特别是处理后的金属零部件表面粘性小，润滑性好，且更容易附着在金属零部件表面，更容易擦除。
最后所应说明的是，以上具体实施方式仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的精神和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (5)
1.一种防止金属零部件生绣的防锈液，其特征在于：该防锈液由下列重量份的原料制成：肥皂6-8份，凡士林1-2份，丙二醇0.5-1份，石蜡0.1-0.5份，水1100-1300份。
2.根据权利要求1所述的防止金属零部件生绣的防锈液，其特征在于，所述各原料的重量份数为：肥皂6份，凡士林1份，丙二醇0.5份，石蜡0.1份，水1100份。
3.根据权利要求1所述的防止金属零部件生绣的防锈液，其特征在于，所述各原料的重量份数为肥皂8份，凡士林2份，丙二醇1份，石蜡0.5份，1300份。
4.根据权利要求1所述的防止金属零部件生绣的防锈液，其特征在于，所述各原料的重量份数为肥皂7份，凡士林1.5份，丙二醇0.7份，石蜡0.3份，1200份。
5.一种制造权利要求1-4之一所述的防止金属零部件生绣的防锈液的方法，其步骤为：1、按上述原料配比提取肥皂，凡士林，丙二醇，石蜡和水，2、将肥皂，石蜡和水装入容器中加热至肥皂和石蜡完全融化，3、将凡士林和丙二醇放入容器中再搅拌直至凡士林，肥皂，丙二醇，石蜡和水完全混和就从容器中出料得到成品。